CN1785859A - Manufacturing method of glass product having ice decorative pattern - Google Patents
Manufacturing method of glass product having ice decorative pattern Download PDFInfo
- Publication number
- CN1785859A CN1785859A CN 200510095038 CN200510095038A CN1785859A CN 1785859 A CN1785859 A CN 1785859A CN 200510095038 CN200510095038 CN 200510095038 CN 200510095038 A CN200510095038 A CN 200510095038A CN 1785859 A CN1785859 A CN 1785859A
- Authority
- CN
- China
- Prior art keywords
- glasswork
- decorative pattern
- ice
- glass product
- manufacture method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The method for making ice-patterned glass product includes the following steps: (1), press-forming molten glass, and taking out glass product from hot mould; (2), heating surface of glass product to softening state; (3), utilizing low-temperature water-air mixed liquor to quickly cool the glass product and make its surface produce cracked ice pattern; and (4), annealing and removing stress.
Description
Technical field
The present invention relates to a kind of manufacture method that has the glasswork of ice decorative pattern.
Background technology
The ice decorative pattern of existing glass article surface is by its surface being heated, be placed on then in the preprepared tank, carries out surperficial explosion and produces decorative pattern.There is following defective in the glasswork that this method is produced: one, decorative pattern outward appearance lines are rough, not nature; Two, lines are unintelligible, and surface irregularity has quick-fried scarce face; Three, yield rate is low, and quality product is difficult to control, can't produce on a large scale.
Summary of the invention
The invention provides a kind of manufacture method that has the glasswork of ice decorative pattern, adopt the present invention can improve the output of product, carry out scale operation, significantly improve the appearance effect of ice decorative pattern, make its outward appearance the lines flow smoothly nature, clear, surface-brightening is not coarse, has improved the stress effect of glasswork simultaneously yet.
Technical scheme of the present invention is as follows: have the manufacture method of the glasswork of ice decorative pattern, it is characterized in that it comprises the steps:
Step 1:, from hot-die, take out glasswork with the compression moulding of fused glass metal;
Step 2: glass article surface is heated to soft state;
Step 3: utilize low temperature aqueous vapor mixed solution that glasswork is sharply cooled off, produce the ice decorative pattern of explosion on its surface;
Step 4: stress relieving by annealing.
When sharply cooling off in step 3, be glass article surface to be placed 0 ℃-50 ℃ gas-vapor mix liquid surface, air pressure is a bit larger tham atmospheric pressure, in second glasswork is carried out rapid cooling process at 2-6; The Heating temperature scope is 400-550 ℃ in the step 2.
Beneficial effect of the present invention is as follows:
One, outward appearance contrast.The ice decorative pattern of existing glasswork is watched under magnifying glass, and the surface is quick-fried to be lacked seriously, tarnish, and feel is jagged.The ice decorative pattern of the glasswork that the present invention makes watches the surface no quick-fried scarce under magnifying glass, and glossy, feel does not have burr.
Two, lines contrast.The ice decorative pattern of existing glasswork is watched coarse under magnifying glass, measures line thickness greater than 1mm.The ice decorative pattern lines of the glasswork that the present invention makes are smooth, measure line thickness less than 0.5mm.
Three, decorative pattern quantity contrast.Existing glasswork is at 5cm
2Surface-area in, have two greater than 1cm
2Scope in do not have the decorative pattern lines.The glasswork that the present invention makes is at 5cm
2Surface-area in not greater than 1cm
2The decorative pattern vacancy, only less than 0.5cm
2The decorative pattern vacancy.
Four, lines naturalness contrast.The ice decorative pattern of existing glasswork is regular, rounded or olive shape.The ice decorative pattern of the glasswork that the present invention makes is random, is irregular trilateral, and nature more seems.
Five, the internal surface of glasswork contrast.The decorative pattern lines that existing glasswork internal surface has one to two explosion to form.The internal surface of the glasswork that the present invention makes does not have explosion decorative pattern and light.
Six, output contrast.Production weight is the glasswork that has ice decorative pattern of 60 grams, and existing output is at 50/hour, and adopting present method output is 300/hour.
Description of drawings
Fig. 1 is a process flow sheet of the present invention
Embodiment
With reference to accompanying drawing, the present invention has the manufacture method of the glasswork of ice decorative pattern, fused soda-lime-silica glass or high-boron-silicon glass is taken out from 1500 ℃-1600 ℃ kiln, by compression moulding.The glasswork workpiece that suppresses is taken out from hot-die, heat by the outside surface of indirect heating then, generally its surface is heated to glass transition temperature, promptly 400-550 ℃ glass pieces.The glasswork workpiece is placed preprepared 0 ℃ to 50 ℃ gas-vapor mix liquid surface, gas-vapor mix liquid is to feed gas to obtain in water, gas pressure intensity is a bit larger tham normal atmosphere, can be between 1.05-1.3 atmospheric pressure, greatly cooling process is carried out on its surface, will soon produce tiny, the random ice decorative pattern of explosion at glass article surface about the moment of 2-6 second.At last glasswork is put back in 400 ℃-500 ℃ the stove, carried out anneal, eliminate stress.
Claims (3)
1, the manufacture method that has the glasswork of ice decorative pattern is characterized in that it comprises the steps:
Step 1:, from hot-die, take out glasswork with the compression moulding of fused glass metal;
Step 2: glass article surface is heated to soft state;
Step 3: utilize low temperature aqueous vapor mixed solution that glasswork is sharply cooled off, produce the ice decorative pattern of explosion on its surface;
Step 4: stress relieving by annealing.
2, the manufacture method that has the glasswork of ice decorative pattern according to claim 1, when it is characterized in that sharply cooling off, be glass article surface to be placed 0 ℃-50 ℃ gas-vapor mix liquid surface, air pressure is a bit larger tham atmospheric pressure, in second glasswork is carried out rapid cooling process at 2-6.
3, the manufacture method that has the glasswork of ice decorative pattern according to claim 1 is characterized in that the Heating temperature scope is 400-550 ℃ in the step 2.