CN1778507A - High-frequency Welding method - Google Patents
High-frequency Welding method Download PDFInfo
- Publication number
- CN1778507A CN1778507A CN 200410052431 CN200410052431A CN1778507A CN 1778507 A CN1778507 A CN 1778507A CN 200410052431 CN200410052431 CN 200410052431 CN 200410052431 A CN200410052431 A CN 200410052431A CN 1778507 A CN1778507 A CN 1778507A
- Authority
- CN
- China
- Prior art keywords
- copper pipe
- joint
- welding method
- frequency
- frequency welding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A high-frequency weld method for welding copper pipe with jointer includes such steps as making slots on the external surface of jointer, winding the welding wire in the slot, coating flux, inserting part of jointer in said copper pipe, fixing said copper pipe by fixture, and high-frequency heating.
Description
Technical field
The present invention relates to the processing method of radiator, particularly radiator distributes the processing method that is connected of copper pipe and joint.
Background technology
Continuous development along with science and technology, more and more higher in the industrial production to the welding requirements of copper pipe (for example the distribution copper pipe of radiator and being connected of jointing), especially the copper pipe after will guaranteeing to weld uses and does not have the phenomenon of leaking, and traditional processing method adopts manual soldering.This kind production technology, production efficiency is lower, and the welding quality instability occurs causing the defective of product because of human factor easily, and production cost is higher, and product is back rework rate height after testing.And working strength of workers is also bigger, can not satisfy the big needs of producing of modernization.
Summary of the invention
The technical problem to be solved in the present invention is, provides a kind of high-frequency welding method, the technical problem low with the production efficiency that solves manual soldering, that welding quality is unstable, production cost is high, rework rate is high, labour intensity is big.
The technical solution adopted for the present invention to solve the technical problems is: the method for a kind of high-frequency welding copper pipe and joint is provided, and its step comprises:
1) insert on the link outer wall be connected to copper pipe at joint and offer groove, the external diameter of described link equates substantially with the internal diameter of copper pipe;
2) link at described joint is provided with scolder, i.e. welding wire on described groove twines, and on described link outer wall coated with flux;
3) will be through step 2) joint handled is inserted in the described copper pipe;
4) use the described copper pipe of clamp, utilize the high frequency hypertherm to heat in the junction of described joint and copper pipe, the described scolder of fusion makes it full and uniformly soak into and fill seam between described joint and the copper pipe.
Above-mentioned high-frequency welding method drives described joint and copper pipe rotates continuously by described anchor clamps when utilizing high frequency hypertherm heating.
The described anchor clamps of above-mentioned high-frequency welding method are installed in the reducing motor rotating shaft, and drive rotation continuously by described reducing motor rotating shaft.
The induction heating circle of the above-mentioned described high frequency hypertherm of high-frequency welding method is for can be set in the circular of described joint and periphery, copper pipe junction.
The above-mentioned described induction heating circle of high-frequency welding method when heating, can pour into cooling water by hollow heat pipe coiled continuously in described heat pipe, prevent that described heat pipe is overheated.
Above-mentioned high-frequency welding method also comprises being provided with and drives and control device, starts or stops described high frequency hypertherm and described reducing motor by described driving and control device.
High-frequency welding method of the present invention utilizes high frequency heating machine to come heating and melting to be located at welding wire and solder flux on the chuck in advance, has replaced the technology of existing staff soldering, thereby has production efficiency height, welding quality stable, cost is low, labour intensity is low advantage; And because welding wire and solder flux are to be located at uniformly between joint and the copper pipe in advance, thereby when welding, welding wire and solder flux can be full and uniform soaks into and fills seam between joint and the copper pipe, has welding quality height, advantage that rework rate is low.In addition, when utilizing high frequency hypertherm heating, drive joint and copper pipe rotates continuously by anchor clamps, thereby make, welding wire and solder flux can be more full and uniform soaks into and fills seam between joint and the copper pipe, has improved welding quality, has reduced rework rate.
Description of drawings
Below in conjunction with drawings and Examples a kind of high-frequency welding method of the present invention is described further, in the accompanying drawing:
Fig. 1 is the welded condition schematic diagram of a kind of high-frequency welding method of the present invention.
Fig. 2 is the local enlarged diagram of the I portion of Fig. 1.
The specific embodiment
Below in conjunction with accompanying drawing a kind of high-frequency welding method of the present invention is described in further detail.
As shown in Figure 1 and Figure 2, a kind of high-frequency welding method of the present invention, it is the welding (certainly being applied to being welded to connect of other workpiece) that is used for radiator copper pipe 20 and joint 10, its step comprises: at first offer ring-shaped groove 12 at the outer wall of the link 11 of joint 10, the external diameter of described link 11 and copper pipe 20 internal diameters are basic identical, thereby make described joint 10 can be inserted in the copper pipe 20, closely connect into an integral body with described copper pipe 20.Then, on the link 11 of described joint 10, scolder is set, promptly in described groove 12, twines welding wire 30, and in the outer wall coated with flux (figure does not show) of link 11.Then, the joint 10 that sets scolder is inserted in the described copper pipe 20.Use anchor clamps that described copper pipe 20 is clamped then, utilize high frequency hypertherm 40 to heat in the described joint 10 and the junction of copper pipe 20, the described scolder of fusion, make it full and uniformly soak into and fill seam between described joint 10 and the copper pipe 20, thereby described joint 10 is welded on the described copper pipe 20 closely.
In the present embodiment, when utilizing high frequency hypertherm 40 heating, drive described joint 10 and copper pipe 20 rotates continuously by described anchor clamps.Described anchor clamps are installed in the reducing motor rotating shaft 50, and drive rotation continuously by described reducing motor rotating shaft 50.Described anchor clamps are located at the two ends of described copper pipe 20 respectively, comprise mandrel 61 and baffle plate 62.Described mandrel 61 is inserted in the copper pipe 20, and compress the joint 10 at copper pipe 20 two ends by described baffle plate 62, rotating shaft driven rotary by reducing motor, thereby make, welding wire 30 and solder flux can be more full and uniform soak into and fill seam between joint 10 and the copper pipe 20, improved welding quality, reduced rework rate.
Described high frequency hypertherm 40 is provided with induction heating circle 41, and described induction heating circle 41 is for can be set in the circular of described joint 10 and periphery, copper pipe 20 junction.Described induction heating circle 41 when heating, can pour into cooling water by hollow heat pipe coiled continuously in described heat pipe, prevent that described heat pipe is overheated.
In the present embodiment, high-frequency welding method of the present invention also comprises being provided with and drives and control device 70, starts or stops described high frequency hypertherm 40 and described reducing motor by described driving and control device 70.Described driving and control device 70 can be industrial computer, programmable single chip computer etc., thereby can control the work of described reducing motor and high frequency hypertherm 40 automatically, reduce manual operations.
Claims (6)
1, a kind of high-frequency welding method is characterized in that, its step comprises:
1) insert on the link outer wall be connected to copper pipe at joint and offer groove, the external diameter of described link equates substantially with the internal diameter of copper pipe;
2) link at described joint is provided with scolder, i.e. welding wire on described groove twines, and on described link outer wall coated with flux;
3) will be through step 2) joint handled is inserted in the described copper pipe;
4) use the described copper pipe of clamp, utilize the high frequency hypertherm to heat in the junction of described joint and copper pipe, the described scolder of fusion makes it full and uniformly soak into and fill seam between described joint and the copper pipe.
2, a kind of high-frequency welding method according to claim 1 is characterized in that, when utilizing high frequency hypertherm heating, drives described joint and copper pipe rotates continuously by described anchor clamps.
3, a kind of high-frequency welding method according to claim 2 is characterized in that described anchor clamps are installed in the reducing motor rotating shaft, and drives rotation continuously by described reducing motor rotating shaft.
4, according to claim 2 or 3 described a kind of high-frequency welding methods, it is characterized in that the induction heating circle of described high frequency hypertherm is for can be set in the circular of described joint and periphery, copper pipe junction.
5, a kind of high-frequency welding method according to claim 4 is characterized in that, described induction heating circle when heating, can pour into cooling water by hollow heat pipe coiled continuously in described heat pipe, prevent that described heat pipe is overheated.
6, a kind of high-frequency welding method according to claim 5 is characterized in that, described high-frequency welding method also comprises being provided with and drives and control device, starts or stops described high frequency hypertherm and described reducing motor by described driving and control device.