CN1760297A - Environmental protection fire retardant hot-melt film adhesive in user for electric clothes - Google Patents
Environmental protection fire retardant hot-melt film adhesive in user for electric clothes Download PDFInfo
- Publication number
- CN1760297A CN1760297A CN 200510094909 CN200510094909A CN1760297A CN 1760297 A CN1760297 A CN 1760297A CN 200510094909 CN200510094909 CN 200510094909 CN 200510094909 A CN200510094909 A CN 200510094909A CN 1760297 A CN1760297 A CN 1760297A
- Authority
- CN
- China
- Prior art keywords
- user
- fire retardant
- environmental protection
- film adhesive
- melt film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
An environment protection type flame-retarding thermofusible adhesive film able to be adhered on the surface of electrically conductive fabric for flame retarding purpose is proportionally prepared from thermofusible adhesive, Sb2O3, ZnB, tri(2,3-dibromopropyl) isotripolycyanate, and hexabromododecane. Its advantages are no poison and high flame-retarding performance.
Description
Technical field:
The present invention relates to a kind of hot melt adhesive film, be specifically related to a kind of environmental protection fire retardant hot-melt film adhesive in user that is used for conductive fabric.Be compound in the conductive fabric surface, play fire retardation.
Background technology:
Conductive fabric is applied to electron trade and plays electric action, because therefore the singularity of electron trade be furnished with fire-retardant requirement to conduction.Before effect of the present invention, traditional conductive fabric flame resistant method is that conductive fabric is flooded fire retardant, as polybromodiphenyl ether, but polybromodiphenyl ether when burning syntheticly generate poisonous carcinogens and disabled, and the conductive fabric electrical and thermal conductivity is good, is difficult to realize fire-retardant than general cloth.
Summary of the invention:
The objective of the invention is to overcome above-mentioned deficiency, a kind of environmental protection fire retardant hot-melt film adhesive in user that is used for conductive fabric of realizing fire-retardant requirement and meeting environmental protection again of being easy to is provided.
The object of the present invention is achieved like this: a kind of environmental protection fire retardant hot-melt film adhesive in user that is used for conductive fabric is characterized in that: it is made up of the raw material of following weight part:
30~50 parts of hot melt adhesives
5~10 parts of antimonous oxides
5~10 parts of zinc borates
10~30 parts of three (2, the 3-dibromopropyl) isocyanuric acid esters
10~30 parts of hexabromo dodecanes
The present invention is used for the environmental protection fire retardant hot-melt film adhesive in user of conductive fabric, and described hot melt adhesive adopts polyester or urethane.
Hot melt adhesive plays the melted by heat bonding effect in the raw material of the present invention in fire retardant hot-melt film adhesive in user, has higher softening temperature and good cementability;
Antimonous oxide plays fire retardation in fire retardant hot-melt film adhesive in user, halogen flame is had tangible synergistic effect;
Zinc borate is a kind of inorganic combustion inhibitor, plays fire-retardant synergistic effect in fire retardant hot-melt film adhesive in user, and Heat stability is good eliminates smoke, and is nontoxic, effective with other fire retardant compositional flame-retardant;
Three (2, the 3-dibromopropyl) isocyanuric acid ester plays fire retardation in fire retardant hot-melt film adhesive in user, good flame retardation effect, and volatility is low, and consistency is good, and is durable, fast light, water-fast and nontoxic;
The hexabromo dodecane plays fire retardation in fire retardant hot-melt film adhesive in user, have enough thermostabilitys, and good free-running property is minimum to the hot melt adhesive performance impact;
Three (2, the 3-dibromopropyl) isocyanuric acid esters and hexabromo dodecane are used in combination the performance impact of hot melt adhesive less; Antimonous oxide and three (2, the 3-dibromopropyl) isocyanuric acid ester and hexabromo dodecane are used in combination and have good synergistic function, flame retardant effect obviously improves, because at high temperature decomposing, halogen compounds emits hydrogen halide, except suppressing the burning by Mulberry Extract HO terminating chain lock reactor, also, generate low melting point quantized antimony halides of energy and zirconyl oxyhalides antimony with the antimonous oxide reaction; Three (2, the 3-dibromopropyl) isocyanuric acid esters and antimonous oxide are used in combination, and obviously reduce the material combustion smoke density, reduce environmental pollution.
Therefore, good flame resistance of the present invention can reach the UL94V-O level, it is compound in the conductive fabric surface is easy to realize fire-retardant requirement; Raw materials used in addition nontoxic, tasteless, compliance with environmental protection requirements.
Embodiment:
Embodiment 1;
Step 1, get polyester 50 weight parts and add in the stirrer, be heated to 150 ℃, add antimonous oxide 5 weight parts, zinc borate 5 weight parts, three (2, the 3-dibromopropyl) isocyanuric acid ester 30 weight parts and hexabromo dodecane 10 weight parts again, heating keeps 150 ℃, stir compound;
Step 2, step 1 got compound place granulation in the tablets press, oven dry, hot melt adhesive tablet;
Step 3, step 2 is got hot melt adhesive tablet place and be blow molded into the tubular glued membrane in the blowfilm shaping machine;
Step 4, use side cutter cuts both sides make the tubular glued membrane become biplate shape glued membrane, film thickness 0.08mm.
Embodiment 2:
Step 1, get urethane 30 weight parts and add in the stirrer, be heated to 130 ℃, add antimonous oxide 10 weight parts, zinc borate 10 weight parts, three (2 again, the 3-dibromopropyl) isocyanuric acid ester 20 weight parts and hexabromo dodecane 30 weight parts, heating and keep 130 ℃ of temperature, stir compound, all the other steps are with embodiment one.
Embodiment 3:
Step 1, get urethane 45 weight parts to going in the stirrer, be heated to 130 ℃, add antimonous oxide 8 weight parts, zinc borate 7 weight parts, three (2 again, the 3-dibromopropyl) isocyanuric acid ester 10 weight parts and hexabromo dodecane 30 weight parts, heating and keep 130 ℃ of temperature, stir compound, all the other steps are with embodiment one.
Claims (2)
1, a kind of environmental protection fire retardant hot-melt film adhesive in user that is used for conductive fabric, it is characterized in that: it is made up of the raw material of following weight part: hot melt adhesive 30%~50%, Sb
2O
35%~10%, ZnB5~10%, TBC? 10~30% and hexabromo dodecane 10%~30%, each weight percent sum of forming is 100%.
2, a kind of environmental protection fire retardant hot-melt film adhesive in user that is used for conductive fabric according to claim 1 is characterized in that: described hot melt adhesive adopts polyester or urethane.