CN1749348A - Glass fog-proof agent and its preparing method - Google Patents
Glass fog-proof agent and its preparing method Download PDFInfo
- Publication number
- CN1749348A CN1749348A CN 200510061116 CN200510061116A CN1749348A CN 1749348 A CN1749348 A CN 1749348A CN 200510061116 CN200510061116 CN 200510061116 CN 200510061116 A CN200510061116 A CN 200510061116A CN 1749348 A CN1749348 A CN 1749348A
- Authority
- CN
- China
- Prior art keywords
- tensio
- active agent
- glass antidimmer
- glass
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to surfactant, and provides one kind of glass antifogging agent and its preparation process. The glass antifogging agent consists of surfactant 0.2-1.5wt%, polyether modified organic silicon surfactant 1.5-3.0wt%, and alcohol 9-20wt% except water. The glass antifogging agent is re-compounded with several kinds of surfactant, and has long antifogging period and wide application range and may be used also as glass cleaning agent. In addition, it has water as solvent and has no danger of explosion and is easy to carry about.
Description
Technical field
The present invention relates to a kind of tensio-active agent and preparation method thereof, more particularly, the present invention relates to a kind of glass antidimmer and preparation method thereof.
Background technology
In rainy season, winter, the place of the temperature difference or high humidity is arranged, run into the problem of glass surface knot mist in people's life through regular meeting, life brings inconvenience, as windshield mist is arranged, and can influence driving safety, even bring life danger.
Present antifogging product is that tensio-active agent is the liquid product of raw material substantially, be sprayed on glass after, with paper or towel as the wiping instrument.Such product, the anti-fog effect of single surfactant component is limited, and the anti-fog effect of compounded surfactant improves, and does not leave spot but often consistency is good after causing doing.
Summary of the invention
The objective of the invention is to overcome deficiency of the prior art, a kind of glass antidimmer of good antifogging effect is provided, further object of the present invention is to provide the preparation method of this glass antidimmer.
Each component of glass antidimmer provided by the invention and content (weight %) are: tensio-active agent 0.2~1.5%, and organic silicon modified by polyether class tensio-active agent: 1.5~3%, alcohols 9~20%, surplus is a water.
Described tensio-active agent is that polyoxyethylene surfactant, sulfonic acid or Phenylsulfonic acid tensio-active agent are wherein at least a.
Described polyoxyethylene surfactant be fatty alcohol-polyoxyethylene ether, tween, polyoxyethylene carboxylate or alkylphenol polyoxyethylene wherein any one.
Described sulfonic acid or Phenylsulfonic acid tensio-active agent be linear alkylbenzene sulphonic acid, alkyl sodium sulfonate or α-sodium olefin sulfonate wherein any one.
Described organic silicon modified by polyether tensio-active agent is polyether-modified organopolysiloxane.
Described alcohols is that single alcohol or glycol are wherein at least a.
Described single alcohol is ethanol.
Described glycol is an ethylene glycol.
Described water is distilled water.
The present invention also provides a kind of method for preparing aforementioned glass antidimmer, may further comprise the steps:
(1) under 10~35 ℃, tensio-active agent added in the suitable quantity of water stir until dissolving;
(2) add organic silicon modified by polyether tensio-active agent, alcohols successively in the stirring;
(3) add the water of surplus and stirring, each component concentration is met the requirements.
Compared with prior art, the invention has the beneficial effects as follows:
Glass antidimmer provided by the invention is composite owing to using the kinds of surface promoting agent to carry out repeatedly, can prolong the antifog time; The product use range is wide, also can have cleaning glass concurrently.Owing to make water as solvent, there is not explosion hazard, be easy to carry.
Embodiment
Below the present invention is further described by example.
Each component of the specific embodiment of glass antidimmer provided by the invention and content (weight %) are as shown in the table:
The specific embodiment sequence number | 1 | 2 | 3 | 4 | 5 |
Polyoxyethylene tensio-active agent (OP10) | 0.2 | 0.3 | 0.4 | 0.5 | |
Sulfonic acid or Phenylsulfonic acid class tensio-active agent (Sodium dodecylbenzene sulfonate) | 0.8 | 0.9 | 1.0 | 1.5 | |
Organic silicon modified by polyether class tensio-active agent (polyether-modified organopolysiloxane) | 1.5 | 1.8 | 2.3 | 2.7 | 3 |
Ethanol | 9 | 10 | 15 | 5 | |
Ethylene glycol | 2 | 13 | 20 | ||
Distilled water | 89.3 | 85.1 | 81.4 | 77.8 | 75.5 |
The polyoxyethylene tensio-active agent can be fatty alcohol-polyoxyethylene ether (AEO), tween, polyoxyethylene carboxylate, alkylphenol polyoxyethylene (APEO) etc. in the table; Sulfonic acid or Phenylsulfonic acid class tensio-active agent can be linear alkylbenzene sulphonic acid (LAS), alkyl sodium sulfonate (SAS), α-sodium olefin sulfonate (AOS) etc.; Organic silicon modified by polyether class tensio-active agent is a polyether-modified organopolysiloxane etc.
The anti-fog performance characterizing method
Eyesight test method according to standard hangs standard visual acuity chart, and with each sign row on the visual chart from minimum row upwards name successively grade be 10,9,8 ... 2,1, promptly subtract one from minimum row every row that makes progress.
Antifogging agent is wiped on glass, dry under the room temperature and be placed in the refrigerator, take out behind the 5min, place at the moment and stand on suitable position, observe the minimum row of the standard visual acuity chart that can see through this test plate, and be defined as the antifog grade of this antifogging agent with the grade of this row.
As figure below is the antifog effect data grade of example.
According to above-mentioned antifog grade characterizing method, measure antifog gradation of effects of contrast and antifog life-span frequency table:
Title | Antifog grade | Antifog number of times (by being reduced to 6) to antifog grade |
The commercial goods antifogging agent | 7 | 3 |
Antifogging agent among the present invention | 10 | 20 |
At last, it is also to be noted that what more than enumerate only is specific embodiments of the invention.Obviously, the invention is not restricted to above examples of implementation, many distortion can also be arranged.All distortion that those of ordinary skill in the art can directly derive or associate from content disclosed by the invention all should be thought protection scope of the present invention.
Claims (10)
1, a kind of glass antidimmer is characterized in that each component and content (weight %) are: tensio-active agent 0.2~1.5%, and organic silicon modified by polyether class tensio-active agent: 1.5~3%, alcohols 9~20%, surplus is a water.
2, glass antidimmer according to claim 1 is characterized in that, described tensio-active agent is that polyoxyethylene surfactant, sulfonic acid or Phenylsulfonic acid tensio-active agent are wherein at least a.
3, glass antidimmer according to claim 2 is characterized in that, described polyoxyethylene surfactant be fatty alcohol-polyoxyethylene ether, tween, polyoxyethylene carboxylate or alkylphenol polyoxyethylene wherein any one.
4, glass antidimmer according to claim 2 is characterized in that, described sulfonic acid or Phenylsulfonic acid tensio-active agent be linear alkylbenzene sulphonic acid, alkyl sodium sulfonate or α-sodium olefin sulfonate wherein any one.
5, glass antidimmer according to claim 1 is characterized in that, described organic silicon modified by polyether tensio-active agent is polyether-modified organopolysiloxane.
6, glass antidimmer according to claim 1 is characterized in that, described alcohols is that single alcohol or glycol are wherein at least a.
7, glass antidimmer according to claim 3 is characterized in that, described single alcohol is ethanol.
8, glass antidimmer according to claim 3 is characterized in that, described glycol is an ethylene glycol.
9, glass antidimmer according to claim 1 is characterized in that, described water is distilled water.
10, a kind of method for preparing glass antidimmer in the claim 1 may further comprise the steps:
(1) under 10~35 ℃, tensio-active agent added in the suitable quantity of water stir until dissolving;
(2) add organic silicon modified by polyether tensio-active agent, alcohols successively in the stirring;
(3) add the water of surplus and stirring, each component concentration is met the requirements.