CN1746129A - Composite semi-transparent polish brick with micropowdery and production thereof - Google Patents
Composite semi-transparent polish brick with micropowdery and production thereof Download PDFInfo
- Publication number
- CN1746129A CN1746129A CN 200410051380 CN200410051380A CN1746129A CN 1746129 A CN1746129 A CN 1746129A CN 200410051380 CN200410051380 CN 200410051380 CN 200410051380 A CN200410051380 A CN 200410051380A CN 1746129 A CN1746129 A CN 1746129A
- Authority
- CN
- China
- Prior art keywords
- super
- lining
- transparent material
- brick
- chemical constitution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A composite semi-transparent micro-powder polished brick and its production are disclosed. The brick consists of shell fabric which comprises ultra-white material and ultra-transparent material, and base material, the ultra-transparent material consists of SiO2 60-75wt%, Al2O3 15-24wt%, Fe2O3 0.25-0.35wt%, TiO2 0.15-0.25wt%, KnaO 6-9wt%, MgO 1-3wt% and CaO 2.5-4.0wt%. The process is carried out by preparing base material, distributing pattern effect from distributing device, pressing by shaping, sintering, edging, polishing, inspecting, packing and obtaining product. It has colorful patterns and good three-dimensional effect and can be used for inner wall, outer wall and ground.
Description
The invention belongs to a kind of compound translucent micro-powdered polishing brick, and the production method of compound translucent micro-powdered polishing brick.
Existing micro-powder brick has the wear resisting property height than common polished tile, and water-intake rate is low, and antifouling property is good, and coloury characteristics are high-grade finishing material that a kind of suitable skin, interior wall and ground are used.But this brick global pattern effect is very unnatural, abundant, stereoscopic sensation is not strong.
The purpose of this invention is to provide a kind of global pattern effect nature, abundant, the compound translucent micro-powdered polishing brick that stereoscopic sensation is strong.
Another object of the present invention provides a kind of global pattern effect nature, abundant, the production method of the compound translucent micro-powdered polishing brick that stereoscopic sensation is strong
The object of the present invention is achieved like this: it is to be composited by lining and base-material, and lining comprises super-white marerial, and lining also comprises super transparent material, and the chemical constitution of super transparent material (Wt%) is: SiO
260-75, Al
2O
315-24, Fe
2O
30.25-0.35, TiO
20.15-0.25, KNaO 6-9, MgO 1-3, Cao 2.5-4.0
Super transparent material of the present invention has adopted the following raw materials according proportioning formulated by above-mentioned chemical constitution (Wt%) scope: feldspar 60-80%, quartz sand 4-15%, clay 10-30%, talcum 2-8%.
Another purpose of the present invention is to realize like this, its production method is as follows: 1) lining preparation: the raw material that will have super-white marerial is produced a kind of lining by the common process process, and super transparent material is produced another kind of lining by the common process process by its chemical constitution (Wt%) scope respectively by following formulated raw material feldspar, quartz sand, clay, talcum; Super-white marerial and two kinds of linings of super transparent material are made ultra-fine micropowder respectively, require to tail over 5-20% by 80 mesh standard sieves.2) base-material preparation: the base-material powder that existing base-material raw material is produced by the common process process; 3) two kinds of different lining powders of super-white marerial and super transparent material and binder layer powder are put into the multitube distributor by layout cloth, press compression moulding, go in the roller kiln to burn till after the brick drying after the moulding, firing temperature is 1160-1230 ℃, firing period 65-120min, cooling back work in-process become finished product after polishing, check, packing.
The present invention is because lining is common flour charge level material and super transparent charge level material, use multitube road cloth technology again, make that the brick after burning till has not only kept full sized brick intensity height, glossiness is good, the advantage that antifouling property is good, also further improved every physical and chemical index and sense organ effect, global pattern effect nature, abundant, stereoscopic sensation is strong, be fit to mass production simultaneously, have the extremely strong market competitiveness, can apply to the exterior wall built, the decoration on interior wall and ground widely.
Embodiment
Embodiment 1,
1) lining preparation:
A kind of chemical group composition (Wt%) of lining Snow Flower White material is: SiO
272.2, Al
2O
319.6Fe
2O
30.1%, TiO
20.15, KNaO 6%, MgO 2%.Its Snow Flower White material has adopted the following raw materials according proportioning formulated by above-mentioned chemical constitution (Wt%) scope: feldspar 50%, quartz sand 20%, clay 275%, talcum 3%, above-mentioned raw materials is produced by technological processs such as selected → weathering → fragmentation → stacking → scale material → ball milling → powder process → old;
The chemical constitution (Wt%) of the super transparent material of another kind of lining is: SiO
275, Al
2O
315, Fe
2O
30.25, TiO
20.15, KNaO 6, MgO 1, Cao 2.5.Its super transparent material has adopted the following raw materials according proportioning formulated by above-mentioned chemical constitution (Wt%) scope: feldspar 63%, quartz sand 10%, clay 20%, talcum 7%, above-mentioned raw materials is produced by technological processs such as selected → weathering → fragmentation → stacking → scale material → ball milling → powder process → old;
Above-mentioned two kinds of linings producing are made ultra-fine micropowder respectively, require to tail over 5-20% by 80 mesh standard sieves.
2) base-material preparation: a kind of chemical constitution of base-material (Wt%) is: SiO
272.2, Al
2O
319.6, Fe
2O
30.1, TiO
20.15, KNaO 6,, MgO 2.Its base-material has adopted the following raw materials according proportioning formulated by above-mentioned chemical constitution (Wt%) scope: feldspar 50%, quartz sand 20%, clay 27%, talcum 3%, above-mentioned raw materials is produced by technological processs such as selected → weathering → fragmentation → stacking → scale material → ball milling → powder process → old; By 30 orders, tail over 7-20%, make powder.
3) two kinds of different lining powders and base-material powder are put into the multitube distributor by layout cloth, adopt the compression moulding of SACMl PH4200 swaging machine, go in the roller kiln to burn till after the brick drying of compression moulding, firing temperature is 1160-1230 ℃, firing period 65-120min, cooling back work in-process become finished product after polishing, check, packing.
Embodiment 2,
The chemical constitution (Wt%) of the super transparent material of another kind of lining of present embodiment is: SiO
260, Al
2O
324, Fe
2O
30.35, TiO
20.25, KNaO 9, MgO 3, CaO 4.Its super transparent material has adopted the following raw materials according proportioning formulated by above-mentioned chemical constitution (Wt%) scope: feldspar 72%, quartz sand 5%, clay 18%, talcum 5%.
All the other are identical with embodiment 1.
Embodiment 3,
Present embodiment the chemical constitution (Wt%) of the super transparent material of another kind of lining be: SiO
269.16, Al
2O
318.63, Fe
2O
30.30, TiO
20.18, KnaO 8.18, MgO proportioning 2.28, CaO 1.36.Its super transparent material has adopted following raw materials according formulated by above-mentioned chemical constitution (Wt%) scope: feldspar 68%, quartz sand 10%, clay 20%, talcum 2%
All the other are identical with embodiment 1.
Embodiment 4
The chemical constitution (Wt%) of the super transparent material of another kind of lining of present embodiment is: SiO
266.82, Al
2O
321.50, Fe
2O
30.26, TiO
20.18, KNaO 7.93, MgO 2.06, CaO 1.28.Its super transparent material has adopted the following raw materials according proportioning formulated by above-mentioned chemical constitution (Wt%) scope: feldspar 70%, quartz sand 6%, clay 19%, talcum 5%.
All the other are identical with embodiment 1.
Embodiment 5
The chemical constitution (Wt%) of the super transparent material of another kind of lining of present embodiment is: SiO
272.8, Al
2O
316.42, Fe
2O
30.28, TiO
20.19, KNaO 6, MgO 2.4, CaO 1.91.Its super transparent material has adopted following raw materials according formulated by above-mentioned chemical constitution (Wt%) scope: feldspar 65%, quartz sand 12%, clay 20%, talcum 3%.
All the other are identical with embodiment 1.
Claims (3)
1, a kind of compound translucent micro-powdered polishing brick and production method thereof, it is to be composited by precoat and binder layer, and lining comprises super-white marerial, it is characterized in that: lining also comprises super transparent material, and the chemical constitution of super transparent material (Wt%) is: SiO
260-75, Al
2O
315-24, Fe
2O
30.25-0.35, TiO
20.15-0.25, KNaO 6-9, MgO 1-3, Cao 2.5-4.0.
2, compound translucent micro-powdered polishing brick according to claim 1 is characterized in that: described super transparent material has adopted following raw materials according proportioning formulated by the described chemical constitution of claim 1 (Wt%) scope: feldspar 60-80%, quartz sand 4-15%, clay 10-30%, talcum 2-8%.
3, the production method of compound translucent micro-powdered polishing brick according to claim 1 and 2 is characterized in that: its production method is as follows:
1) lining preparation: the raw material that will have super-white marerial is produced a kind of lining by the common process process, and super transparent material is produced another kind of lining by the common process process by its chemical constitution (Wt%) scope respectively by following formulated raw material feldspar, quartz sand, clay, talcum; Super-white marerial and two kinds of linings of super transparent material are made ultra-fine micropowder respectively, require to tail over 5-20% by 80 mesh standard sieves.
2) base-material preparation: the base-material powder that existing base-material raw material is produced by the common process process;
3) two kinds of different lining powders of super-white marerial and super transparent material and binder layer powder are put into the multitube distributor by layout cloth, press compression moulding, go in the roller kiln to burn till after the brick drying after the moulding, firing temperature is 1160-1230 ℃, firing period 65-120min, cooling back work in-process become finished product after polishing, check, packing.