CN1736943A - 一种高强耐磨陶瓷托辊筒体及其生产工艺 - Google Patents

一种高强耐磨陶瓷托辊筒体及其生产工艺 Download PDF

Info

Publication number
CN1736943A
CN1736943A CN 200510093409 CN200510093409A CN1736943A CN 1736943 A CN1736943 A CN 1736943A CN 200510093409 CN200510093409 CN 200510093409 CN 200510093409 A CN200510093409 A CN 200510093409A CN 1736943 A CN1736943 A CN 1736943A
Authority
CN
China
Prior art keywords
carrying roller
clay
ceramic carrying
strength abrasion
proof ceramic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200510093409
Other languages
English (en)
Other versions
CN1300045C (zh
Inventor
李金山
胡定华
王存贵
Original Assignee
李金山
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 李金山 filed Critical 李金山
Priority to CNB2005100934093A priority Critical patent/CN1300045C/zh
Publication of CN1736943A publication Critical patent/CN1736943A/zh
Application granted granted Critical
Publication of CN1300045C publication Critical patent/CN1300045C/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种用于皮带运输机的高强耐磨陶瓷托辊的陶瓷筒体和生产工艺,其重要化学成分为Al2O3,除此之外还包括SiO2等化学成分,按重量百分比分别为:Al2O3≥40%,(SiO2+其它成分)≤60%。生产工艺流程是,将原材料按一定配比配方后经球磨、压滤、真空练泥机成型、干燥、精坯、烧结、打磨而成;与普通陶瓷托辊简体相比,本发明的高强耐磨陶瓷托辊筒体具有弯曲强度更高、耐磨性能更好、耐腐蚀性能更好、寿命更长等优点。

Description

一种高强耐磨陶瓷托辊筒体及其生产工艺
技术领域
本发明涉及一种皮带运输机的陶瓷托辊,特别是一种高强耐磨陶瓷托辊简体及其生产工艺。
背景技术
在现有技术中,皮带运输机上滚动部件——托辊,一般是采用金属材料或胶合材料,近年来也有采用普通陶瓷托辊的。
普通陶瓷托辊筒体的化学成分中Al2O3含量都在40%以下,其弯曲强度不高、抗冲击力差、易碎、易折、磨耗较大、成品率低,在运输和组装时容易破损。
发明内容
本发明旨在提供一种耐磨性能更好、弯曲强度更高、耐腐蚀性能更好、寿命更长的高强耐磨陶瓷托辊简体。
为达到上述目的,本发明采用如下技术方案:
本发明的高强耐磨陶瓷托辊筒体的重要化学成分为Al2O3,除此之外还可包括SiO2、Fe2O3、CaO、MgO、TiO2、K2O、Na2O等化学成分,按重量百分比分别为:Al2O3≥40%,(SiO2等其它成分之和)≤60%;本发明进一步将Al2O3按重量百分比提升到≥60%;本发明再进一步将Al2O3按重量百分比提升到≥70%。普通陶瓷托辊简体的Al2O3含量都小于40%。本发明的高强耐磨陶瓷托辊简体Al2O3含量则不小于40%,和普通陶瓷托辊筒体相比,可以提高弯曲强度、耐磨度等关键性能指标。
制作本发明涉及的原材料可以灵活多变,但要满足烧成后产品化学成份中Al2O3≥40%及(SiO2等其它成分之和)≤60%即可。
本发明的主要生产工艺流程是:配料、球磨、压滤、成型、干燥、精坯、烧结、打磨。
除以上工艺流程外,经球磨制成的泥浆还可以进行除铁、除杂,经压滤机压滤成泥饼后还可以将泥饼堆在一起进行陈腐,陈腐后的泥饼还可以用真空练泥机进行练制及抽真空,在成型、精坯之后还可进行上釉等辅助工艺,进一步提升成品质量。
本发明的高强耐磨陶瓷托辊筒体可带釉,也可不带釉,带釉的工艺和其它带釉陶瓷制品的工艺相同。
按本发明将烧制好的高强耐磨陶瓷托辊筒体配上轴承和轴,其附件配套有芯轴、密封圈、稳定器、螺帽、钢稳定架、钢块稳定方子等零件,便成为陶瓷托辊,再配上支架、皮带、减速机等便可组装成皮带运输机。
具体实施方式
实施例1:
原材料配方按重量百分比为:
铝矾土40%、钾长石15%、粘土45%。
原料化学成份按重量百分比组成是:铝矾土(可选用河南巩县):SiO2(7.88)、Al2O3(85.57)、TiO2(3.42)、Fe2O3(0.84)、CaO(1.01)、K2O(0.84)、Na2O(0.22);钾长石(可选用湖南平江长石):SiO2(65.22)、Al2O3(19.18)、Fe2O3(0.02)、CaO(0.40)、MgO(0.23)、K2O(9.74)、Na2O(4.20);粘土SiO2(96-68)、Al2O3(15-31)、Fe2O3<1.5、CaO<1、MgO<1、K2O(1-2)、Na2O(0.5-1)。
将上述原材料按上述配比配齐3吨,加入球磨机内,再往球磨机中加水,球磨36小时,制成泥浆,泥浆在除铁、除杂后经压滤机压滤成泥饼,再通过真空练泥机挤出成型为粗坯,粗坯干燥后,用车床加工成半成品,经高温烧成后成为粗成品,再经磨床打磨后成为高强耐磨陶瓷托辊筒体成品。
本实施例制成的高强耐磨陶瓷托辊筒体Al2O3含量为44.13%,其弯曲强度为140MPa大于普通陶瓷托辊筒体120MPa的弯曲强度,而磨耗为0.08%小于普通陶瓷托辊筒体0.1%的磨耗,相比普通陶瓷托辊筒体,其关键性能指标明显改善。
实施例2:
原材料配方按重量百分比为:铝矾土70%、钾长石15%、粘土12%、白云石3%;再外加以上配方总重3%的有机溶剂CMC作为增塑剂。
原料化学成分百分比组成是:铝矾土(河南巩县):SiO2(7.88)、Al2O3(85.57)、TiO2(3.42)、Fe2O3(0.84)、CaO(1.01)、K2O(0.84)、Na2O(0.22);钾长石(湖南平江长石):SiO2(65.22)、Al2O3(19.18)、Fe2O3(0.02)、CaO(0.40)、MgO(0.23)、K2O(9.74)、Na2O(4.20);粘土SiO2(96-68)、Al2O3(15-31)、Fe2O3<1.5、CaO<1、MgO<1、K2O(1-2)、Na2O(0.5-1);白云石(江西上高)CaO>30%、MgO>21%。
将上述原材料按上述配比配齐3吨,加入球磨机内,再往球磨机中加水,球磨36小时,制成泥浆,泥浆在除铁、除杂后经压滤机压滤成泥饼,再通过真空练泥机挤出成型为粗坯,粗坯干燥后,用车床加工成半成品,经高温烧成后成为粗成品,再经磨床打磨后成为高强耐磨陶瓷托辊筒体成品。
本实施例制成的高强耐磨陶瓷托辊筒体Al2O3含量为62.37%,其弯曲强度为180MPa远大于普通陶瓷托辊筒体120MPa的弯曲强度,而磨耗为0.05%远小于普通陶瓷托辊筒体0.1%的磨耗,相比普通陶瓷托辊筒体,其关键性能指标得到非常大的改善。
实施例3:
原材料配方按重量百分比为:三氧化二铝粉70%、粘土20%、白云石7%、碳酸钡粉3%;再外加以上配方总重2%的CMC(羧甲基纤维素)作为增塑剂。
原料化学成分百分比组成是:三氧化二铝粉:Al2O3(99.99%);粘土SiO2(96-68)、Al2O3(15-31)、Fe2O3<1.5、CaO<1、MgO<1、K2O(1-2)、Na2O(0.5-1);白云石(可选用江西上高)Ca0>30%、MgO>21%;碳酸钡粉:BaCO3(99.99%)。
将上述原材料按上述配比配齐3吨,加入球磨机内,再往球磨机中加水,球磨36小时,制成泥浆,泥浆在除铁、除杂后经压滤机压滤成泥饼,再通过真空练泥机挤出成型为粗坯,粗坯干燥后,用车床加工成半成品,经高温烧成后成为粗成品,再经磨床打磨后成为高强耐磨陶瓷托辊筒体成品。
本实施例制成的高强耐磨陶瓷托辊筒体Al2O3含量为74.01%,其弯曲强度为200MPa远大于普通陶瓷托辊筒体120MPa的弯曲强度,而磨耗为0.04%远小于普通陶瓷托辊筒体0.1%的磨耗,相比普通陶瓷托辊筒体,其关键性能指标得到大大的改善。

Claims (9)

1、一种高强耐磨陶瓷托辊筒体,化学成份包括SiO2和Al2O3,其特征是化学成分Al2O3按重量百分比含量为≥40%。
2、根据权利要求1所述的高强耐磨陶瓷托辊筒体,其特征是化学成分Al2O3按重量百分比含量为≥60%。
3、根据权利要求2所述的高强耐磨陶瓷托辊筒体,其特征是化学成分Al2O3按重量百分比含量为≥70%。
4、根据权利要求1或2或3所述的高强耐磨陶瓷托辊筒体,其特征是化学成份还包括Fe2O3、CaO、MgO、TiO2、K2O、Na2O。
5、根据权利要求1或2或3所述的高强耐磨陶瓷托辊筒体的生产工艺,其特征在于工艺程序包括配料、球磨、压滤、成型、干燥、精坯、烧结、打磨。
6、根据权利要求5所述的工艺,其特征在于工艺还包括配料经球磨制成的泥浆进行除铁、除杂,经压滤机压滤成泥饼后将泥饼堆在一起进行陈腐,陈腐后的泥饼用真空练泥机进行练制及抽真空,在成型、精坯之后进行上釉。
7、根据权利要求5引用权利要求1所述的生产工艺,其特征在于配料原材料重量配方采用铝矾土40%、钾长石15%、粘土45%,其中原材料铝矾土成份按重量比为:SiO2为7.88%、Al2O3为85.57%、TiO2为3.42%、Fe2O3为0.84%、CaO为1.01%、K2O为0.84%、Na2O为0.22%;钾长石成份按重量比为:SiO2为65.22%、Al2O3为19.18%、Fe2O3为0.02%、CaO为0.40%、MgO为0.23%、K2O为9.74%、Na2O为4.20%;粘土成份按重量比为SiO2为96-68%、Al2O3为15-31%、Fe2O3<1.5、CaO<1、MgO<1、K2O为1-2%、Na2O为0.5-1%。
8、根据权利要求5引用权利要求2所述的生产工艺,其特征在于配料原材料重量配方采用铝矾土70%、钾长石15%、粘土12%、白云石3%,再外加3%的CMC作为增塑剂。
9、根据权利要求5引用权利要求3所述的生产工艺,其特征在于配料原材料重量配方采用三氧化二铝粉70%、粘土20%、白云石7%、碳酸钡粉3%,再外加2%的CMC作为增塑剂。
CNB2005100934093A 2005-08-29 2005-08-29 一种高强耐磨陶瓷托辊筒体及其生产工艺 Active CN1300045C (zh)