CN1696396A - 制浆原料的微波预处理方法 - Google Patents

制浆原料的微波预处理方法 Download PDF

Info

Publication number
CN1696396A
CN1696396A CNA2005100186247A CN200510018624A CN1696396A CN 1696396 A CN1696396 A CN 1696396A CN A2005100186247 A CNA2005100186247 A CN A2005100186247A CN 200510018624 A CN200510018624 A CN 200510018624A CN 1696396 A CN1696396 A CN 1696396A
Authority
CN
China
Prior art keywords
microwave
raw material
preprocessing
radiation treatment
pulp
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2005100186247A
Other languages
English (en)
Other versions
CN100335715C (zh
Inventor
付建生
袁世炬
文琼菊
邱先琴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hubei University of Technology
Hubei Polytechnic University
Original Assignee
Hubei University of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hubei University of Technology filed Critical Hubei University of Technology
Priority to CNB2005100186247A priority Critical patent/CN100335715C/zh
Publication of CN1696396A publication Critical patent/CN1696396A/zh
Application granted granted Critical
Publication of CN100335715C publication Critical patent/CN100335715C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

制浆原料的微波预处理方法，其特征在于：对传统制浆的植物原料的料片，预先用微波进行辐射处理。植物原料料片经微波辐射处理后，相对封闭的植物原料内部物理结构通道得以改善，有利于制浆化学药品的快速均匀渗透；木素大分子得以活化，有利于化学脱木素反应；纤维素化学结构的活性基团“钝化”，有利于保护纤维素，提高纸浆质量。

Description

制浆原料的微波预处理方法
技术领域
本发明涉及一种制纸浆中对植物原料料片进行预处理的技术，应用于采用植物纤维原料进行制浆的制浆造纸技术领域。
背景技术
传统的化学法(包括半化学法和化学机械法)制浆技术的化学处理过程中，因化学药品与植物原料的接触渗透均匀性差，而导致纸浆得率和质量降低。目前使用的改进方法是添加助剂的化学方法，如添加蒽醌、表面活性剂，来强化制浆脱木素化学反应和改善化学药品的渗透。蒽醌具有毒性造成对人体的危害，表面活性剂的多泡性增加了制浆后续处理难度及加剧了环境污染。
经检索未发现一种用微波对植物原料料片进行辐射预处理再制浆的方法被公开或使用。
发明内容
为了提高纸浆得率和质量，克服目前添加助剂方法存在的缺陷，本发明提供一种纸浆原料的微波预处理方法，是一种不增加化学污染的物理方法，能有效改善制浆得率和质量。
本发明的技术方案是：制浆原料的微波预处理方法，其特征在于：对传统制浆的植物原料的料片，预先用微波进行辐射处理。辐射处理后的料片，再进行传统的化学法(包括半化学法和化学机械法)制浆的化学反应。植物原料料片经微波辐射处理后，相对封闭的植物原料内部物理结构通道得以改善，有利于制浆化学药品的快速均匀渗透；木素大分子得以活化，有利于化学脱木素反应；纤维素化学结构的活性基团“钝化”，有利于保护纤维素，提高纸浆质量。
如上所述的制浆原料的微波预处理方法，其特征在于：辐射处理的微波频率为1500-5000MHz，料片的重量为100-1000克时，微波功率为500-1000瓦，辐射处理时间为1-5分钟。
如上所述的纸浆原料的预处理方法，其特征在于：辐射处理的微波频率为2450MHz，辐射处理时间为3分钟。
有益效果
经微波进行辐射预处理再制浆的纸浆，与未经微波进行辐射预处理直接制浆相比，其纸浆得率提高2％～4％；纸浆硬度(K值)降低1～5；原浆白度提高2％～8％；浆纸裂断长提高3％～18％；浆纸耐折度提高3％～15％。
经微波进行辐射预处理再制浆的纸浆，与未经微波进行辐射预处理直接制浆相比，其可漂性明显增加。采用同样的化学漂白条件对比，其漂白浆白度提高2％～8％。
具体实施方式
实例1：
原料料片：杨木片800G(绝干重量)
微波处理条件：2450MHz；650W；3min
蒸煮工艺条件：
方法     烧碱法
用碱量   22％
最高温度 165℃
保温时间 30min
液比     1∶6
漂白工艺条件
方法   次氯酸盐单段漂白
用氯量 5％
浆浓   5％
温度   39℃
蒸煮结果：
得率55.20％(比未处理样品提高2.98％)
高锰酸钾值16.89(比未处理样品降低2.70)
原浆白度29.38％(比未处理样品提高3.82％)
漂白结果：白度52.67％(比未处理样品提高3.75％)
未漂浆手抄片性能：(打浆度28.6°SR)
定量60.51g/m2
裂断长4259m(比未处理样品提高14.78％)
耐折度14.75(比未处理样品提高11.23％)
实例2：
原料料片：松木750G(绝干重量)
微波处理条件：2450MHz；700W；3min
蒸煮工艺条件：
方法   硫酸盐法
用碱量 26％
硫化度   25％
最高温度 170℃
保温时间 60min
液比     1∶6
漂白工艺条件：
方法   次氯酸盐单段漂白
用氯量 5％
浆浓   5％
温度   39℃
蒸煮结果：得率54.60％(比未处理样品提高3.60％)
高锰酸钾值20.36(比未处理样品降低4.22)
原浆白度25.38％(比未处理样品提高3.98％)
漂白结果：白度49.66％(比未处理样品提高4.01％)
未漂浆手抄片性能：(打浆度38.66°SR)
定量60.27g/m2
裂断长5683m(比未处理样品提高12.36％)
耐折度16.5(比未处理样品提高10.33％)
实例3：
原料：芦苇700G(绝干重量)
微波处理条件：2450MHz；700W；1.2min
蒸煮工艺条件：
方法     烧碱法
用碱量   18％
最高温度 160℃
保温时间 20min
液比     1∶6
漂白工艺条件
方法    次氯酸盐单段漂白
用氯量  5％
浆浓    5％
温度    39℃
蒸煮结果：
得率53.64％(比未处理样品提高3.98％)
高锰酸钾值7.82(比未处理样品降低3.23)
原浆白度31.95％(比未处理样品提高4.88％)
漂白结果：白度71.81％(比未处理样品提高5.63％)
未漂浆手抄片性能：(打浆度27.02°SR)
定量60.11g/m2
裂断长3859m(比未处理样品提高8.96％)
耐折度9.5(比未处理样品提高9.65％)

Claims (3)

1、制浆原料的微波预处理方法，其特征在于：对传统制浆的植物原料的料片，预先用微波进行辐射处理。
2、如权利要求1所述的制浆原料的微波预处理方法，其特征在于：辐射处理的微波频率为1500-5000MHz，料片的重量为100-1000克时，微波功率为500-1000瓦，辐射处理时间为1-5分钟。
3、如权利要求2所述的纸浆原料的微波预处理方法，其特征在于：辐射处理的微波频率为2450MHz，辐射处理时间为3分钟。
CNB2005100186247A 2005-04-28 2005-04-28 制浆原料的微波预处理方法 Expired - Fee Related CN100335715C (zh)