CN1673161A - 复合型水泥外加剂 - Google Patents

复合型水泥外加剂 Download PDF

Info

Publication number
CN1673161A
CN1673161A CN 200510017440 CN200510017440A CN1673161A CN 1673161 A CN1673161 A CN 1673161A CN 200510017440 CN200510017440 CN 200510017440 CN 200510017440 A CN200510017440 A CN 200510017440A CN 1673161 A CN1673161 A CN 1673161A
Authority
CN
China
Prior art keywords
cement
weight portions
parts
cement admixture
composite cement
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200510017440
Other languages
English (en)
Inventor
张坦然
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 200510017440 priority Critical patent/CN1673161A/zh
Publication of CN1673161A publication Critical patent/CN1673161A/zh
Pending legal-status Critical Current

Abstract

本发明属于水泥添加剂技术领域，尤其涉及一种可以增加水泥产量、降低水泥成本、增强水泥强度、防冻助磨、调节水泥凝结时间、增加混凝土密实度的复合型水泥外加剂，由硫酸钠30份、硫酸铝10份、氯化钙30份、硫酸钙20份、熟石灰10份按重量份数制成，在研磨水泥过程中，加入本发明后，可提高水泥的产量，增强水泥强度，提高水泥的防冻助磨性能，调节水泥凝结时间，增加混凝土密实度，明显达到节水、节电、节约煤用量的作用。

Description

复合型水泥外加剂
技术领域
本发明属于水泥添加剂技术领域，尤其涉及一种可以增加水泥产量、降低水泥成本、增强水泥强度、防冻助磨、调节水泥凝结时间、增加混凝土密实度的复合型水泥外加剂。
背景技术
目前，立窑水泥生产成本越来越高，水泥企业的能耗也越来越大，尤其是目前，煤的价格不断上涨，为了降低水泥熟料标准耗煤，八十年代开始逐步用萤石、石膏复合矿化剂，并配以低温烧成工艺，以降低物料共熔点温度，使煅烧过程中提前出现液相，以达到节煤的目的，用这种方式虽可以节煤，但增加了生产控制难度，尤其是氟硫比，稍有波动，便导致水泥凝结时间不正常，同时水泥生产安定性不良，生产成本高。
发明内容
本发明的目的在于克服现有技术中存在的不足而提供一种可以增加水泥产量、降低水泥成本、增强水泥强度、防冻助磨、调节水泥凝结时间、增加混凝土密实度的复合型水泥外加剂。
本发明的目的是这样实现的：由下列各原料按重量份数制成：硫酸钠30份、硫酸铝10份、氯化钙30份、硫酸钙20份、熟石灰10份。
本发明具有如下积极效果：
(1)、在研磨水泥过程中，加入本发明后，可提高水泥的产量；
(2)、添加本发明后，可以增强水泥强度；
(3)、添加本发明后，可以提高水泥的防冻助磨性能；
(4)、添加本发明后，可以调节水泥凝结时间、增加混凝土密实度；
(5)、添加本发明后，明显达到节水、节电、节约煤用量的作用；磨1吨成品水泥只须加10公斤就可以。
质量标准：
  3天强度     28天
  抗拆4pmu     8pmu
  抗压20pmu     35-38pmu
功能表现：
(1)、出沫安定性100％
(2)、3天提高ISO规定65％，比继续增值
(3)、密实度很好
(4)、零下5摄氏度施工混凝土不冻不会影响质量
(5)、壳子灌溉前不须刷润滑剂不粘布或壳子
(6)、节水型节水与ISO标准节水15-20％
具体实施方式
实施例：由下列各原料按重量份数制成：硫酸钠30千克、硫酸铝10千克、氯化钙30千克、硫酸钙20千克、熟石灰10千克，将上述各原料研磨成粉即为本品。

Claims (1)

1、一种复合型水泥外加剂，其特征在于：由下列各原料按重量份数制成：硫酸钠30份、硫酸铝10份、氯化钙30份、硫酸钙20份、熟石灰10份，将上述各原料研磨成粉即为本品。
CN 200510017440 2005-03-24 2005-03-24 复合型水泥外加剂 Pending CN1673161A (zh)