CN1669972A - 快硬硫铝酸盐水泥复合缓凝剂 - Google Patents

快硬硫铝酸盐水泥复合缓凝剂 Download PDF

Info

Publication number
CN1669972A
CN1669972A CNA2005100425093A CN200510042509A CN1669972A CN 1669972 A CN1669972 A CN 1669972A CN A2005100425093 A CNA2005100425093 A CN A2005100425093A CN 200510042509 A CN200510042509 A CN 200510042509A CN 1669972 A CN1669972 A CN 1669972A
Authority
CN
China
Prior art keywords
quick hardening
hardening sulphoaluminate
sulphoaluminate cement
compound retarder
molasses
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2005100425093A
Other languages
English (en)
Inventor
刘茂平
刘元明
李明国
刘敏
任秀娥
Original Assignee
刘茂平
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 刘茂平 filed Critical 刘茂平
Priority to CNA2005100425093A priority Critical patent/CN1669972A/zh
Publication of CN1669972A publication Critical patent/CN1669972A/zh
Pending legal-status Critical Current

Abstract

公开了一种快硬硫铝酸盐水泥复合缓凝剂，它是由粉煤灰II级、糖蜜、硼酸均匀混合制成。本发明是以多种无机和有机材料复合制成的粉状材料，对快硬硫铝酸盐水泥具有较强的缓凝作用，并且不影响混凝土的强度和性能。适用于快硬硫铝酸盐水泥及其混凝土调节凝结时间。可提高快硬硫铝酸盐水泥的工作性能。

Description

快硬硫铝酸盐水泥复合缓凝剂
技术领域
本发明属于水泥外加剂技术领域。具体地说是一种适用于快硬硫铝酸盐水泥及其混凝土调节凝结时间和提高快硬硫铝酸盐水泥的工作性能的复合缓凝剂。
背景技术
经检索尚未发现有专门针对快硬硫铝酸盐水泥产品使用的复合缓凝剂。
发明内容
本发明的目的就是实现快硬硫铝酸盐水泥凝结时间的灵活调整，具有较强的缓凝作用，更好的满足各种工程建设对特种混凝土的需要，而提供一种不影响混凝土的强度和性能、并且使用方便的快硬硫铝酸盐水泥复合缓凝剂。
实现本发明的技术方案：采用粉煤灰II级、糖蜜、硼酸均匀混合制成，其重量百分比、计量单位克，分别粉煤灰II级占92-95％、硼酸占3-4％、糖蜜占2-4％，细度大于370m2/kg。
使用方法：根据环境温度和工程需要调整掺加量来实现调整凝结时间的目的，缓凝剂掺加量1-5％，以水泥用量为基数按比例外掺。复合缓凝剂最大掺加量不超过水泥用量的5％。
通过本发明在快硬硫铝酸盐水泥中掺加复合缓凝剂，可以实现夏季高温施工，在30℃的自然环境温度下，掺加不同比例的缓凝剂，可以作到正常施工，不影响混凝土的强度。通过掺加复合缓凝剂，还可以使用快硬硫铝酸盐水泥配制商品泵送混凝土。
具体实施方式
配方(重量比，单位：克)将粉煤灰II级92-95％、硼酸3-4％、糖蜜2-4％，按适当比例均匀混和制成，细度大于370m2/kg。根据环境温度和工程需要调整掺加量来实现调整凝结时间的目的。复合缓凝剂最大掺加量不超过水泥用量的5％。
实施例
实施例1，配方：粉煤灰II级92％；硼酸4％，，糖蜜4％混合制成。按快硬硫铝酸盐水泥用量的1-5％掺加，实验结果如下表。
   缓凝剂掺量％   流动度mm   水灰比W/C   凝结时间(min)         抗压强度(MPa)         抗折强度(MPa)
  初凝   终凝   1d   3d  28d   1d   3d  28d
    0％   121   0.41   0:11   0:23   34.7   46.3   7.8   7.0
    1％   121   0.39   0:18   0:33   45.5   51.0   8.1   7.4
    3％   122   0.38   0:27   0:44   38.7   52.5   7.8   7.7
    5％   124   0.38   1:12   1:47   39.2   51.7   8.4   7.0
实施例2，配方：粉煤灰II级94％；硼酸4％，，糖蜜2％混合制成。按快硬硫铝酸盐水泥用量的1-5％掺加，实验结果如下表。
   缓凝剂掺量％   流动度mm   水灰比W/C       凝结时间(min)          抗压强度(MPa)        抗折强度(MPa)
  初凝   终凝   1d   3d  28d   1d   3d  28d
    0％   121   0.41   0:11   0:23   34.7   46.3   7.8   7.0
    01％   126   0.40   0:13   0:25   42.7   52.0   8.3   7.0
    3％   123   0.40   0:22   0:48   42.9   48.2   7.4   7.0
    5％   129   0.40   0:58   1:32   42.7   48.7   7.8   7.1
实施例3，配方：粉煤灰II级94％；硼酸3％，，糖蜜3％混合制成。按快硬硫铝酸盐水泥用量的1-5％掺加，实验结果如下表。
   缓凝剂掺量％   流动度mm   水灰比W/C    凝结时间(min)          抗压强度(MPa)         抗折强度(MPa)
  初凝   终凝   1d   3d  28d   1d   3d  28d
    0％   121   0.41   0:11   0:23   34.7   46.3   7.8   7.0
    01％   121   0.40   0:12   0:25   43.6   50.8   7.5   6.0
    3％   127   0.40   0:25   0:40   42.4   48.5   7.7   7.7
    5％   126   0.40   0:36   0:54   41.4   50.6   5.7   7.1
最佳实施例：配方：粉煤灰II级92％；硼酸4％，，糖蜜4％混合制成。按快硬硫铝酸盐水泥用量的1-5％掺加，实验结果如下表。
  缓凝剂掺量％   流动度mm   水灰比W/C    凝结时间(min)           抗压强度(MPa)           抗折强度(MPa)
  初凝   终凝   1d   3d  28d   1d   3d  28d
    0％   121   0.41   0:11   0:23   34.7   46.3   7.8   7.0
    1％   121   0.39   0:18   0:33   45.5   51.0   8.1   7.4
    3％   122   0.38   0:27   0:44   38.7   52.5   7.8   7.7
    5％   124   0.38   1:12   1:47   39.2   51.7   8.4   7.0
使用方法：特殊混凝土可以增减缓凝剂的掺加量，从而实现调整凝结时间的目的。复合缓凝剂最大掺加量不超过水泥用量的5％。
因此，本发明是以多种无机和有机材料复合制成的粉状材料，对快硬硫铝酸盐水泥具有较强的缓凝作用，且不影响混凝土的强度和性能。适用于快硬硫铝酸盐水泥及其混凝土调节凝结时间。可以提高快硬硫铝酸盐水泥的工作性能。

Claims (1)

  1. 一种快硬硫铝酸盐水泥复合缓凝剂，其特征是：由粉煤灰II级、糖蜜、硼酸均匀混合制成，其重量百分比、计量单位克，分别粉煤灰II级占92-95％、硼酸占3-4％、糖蜜占2-4％，细度大于370m2/kg。
CNA2005100425093A 2005-02-23 2005-02-23 快硬硫铝酸盐水泥复合缓凝剂 Pending CN1669972A (zh)