CN1640977A - 外墙保温用高分子粘接剂 - Google Patents
外墙保温用高分子粘接剂 Download PDFInfo
- Publication number
- CN1640977A CN1640977A CN 200510000129 CN200510000129A CN1640977A CN 1640977 A CN1640977 A CN 1640977A CN 200510000129 CN200510000129 CN 200510000129 CN 200510000129 A CN200510000129 A CN 200510000129A CN 1640977 A CN1640977 A CN 1640977A
- Authority
- CN
- China
- Prior art keywords
- agent
- water
- adhesive
- polymeric adhesive
- epoxy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
外墙保温用高分子粘接剂是一种含有高分子聚合物的产品,属于精细化工技术领域。现有的这类粘接剂或以环氧树脂为主要成分,或以丙烯酸树脂为主要成分,它们在技术性能上各有各的优缺点,互为补充。本发明之粘接剂其主要成分同时选用丙烯酸树脂和环氧树脂以及高分子复合物,添加剂有增塑剂、增韧剂、稀释剂、活性剂、抗冻剂、乳化剂、阻燃剂、增稠剂、防水剂和水。所制得的粘接剂在粘接性能上具备了现有两类粘接剂的优点,另外,还具有良好的防渗、抗冻、阻燃等性能,能够满足北方建筑外墙保温需要。
Description
技术领域
本发明涉及一种含有高分子聚合物的产品,属于精细化工技术领域。
背景技术
与本发明有关的已知高分子粘接剂有环氧树脂类和丙烯酸树脂类。申请号为85100135的一件中国专利申请公开了一项名为“中温固化高强度环氧胶粘剂”的技术方案,虽然该技术方案是对环氧树脂胶进行改性,但是,在该胶粘剂中起粘接作用的成分仍是环氧树脂。申请号为87107098的一件中国专利申请公开了一项名为“丙烯酸酯系列三种新型乳液胶”的技术方案,该方案是为提供三种产品而提出,其中起粘接作用的成分仍是丙烯酸酯。近期有关本发明的文献有一篇发表在中国《合成材料老化与应用》杂志2001年第4期,题为“聚丙烯酸酯乳液型胶粘剂研究进展”文章,所研究的粘接剂仍属单纯的丙烯酸树脂类。
发明内容
在建筑业,为提高墙体节能技术,往往采用外墙保温及节能材料方式。具体措施是在墙体中粘附一层聚苯乙烯泡沫板(其上粘敷玻璃纤维网格布),再在其上粘挂外墙,以提高楼房的外墙保温性能。在这一过程中均需使用粘接剂来完成各步骤。这一应用领域要求粘接剂应当与聚苯乙烯泡沫板及混凝土有良好的相容性,有较强的耐气候性和抗老化性,足够高的粘接强度和较强的抗碱性能等。然而,单独使用现有的环氧树脂类和丙烯酸树脂类粘接剂,都不会同时取得这些效果。不过,二者各自部分具备这些性能,如丙烯酸树脂与各种填料配比后,具有保温、抗渗、防水、抗冻、凝固等特性;环氧树脂类粘接剂具有粘接牢固,与聚苯乙烯泡沫板相容性好的特性,但价格较高,脆性较大,防渗性能差。如果适量的环氧树脂与丙烯酸树脂及各种填料配比后,除具有上述各自的优点外,还兼有耐碱、抗老化以及使用寿命长的特点。为了制备这种集环氧树脂类粘接剂和丙烯酸树脂类粘接剂二者优点于一身的粘接剂,我们发明了外墙保温用高分子粘接剂。
本发明是这样实现的,提出一套制备高分子粘接剂的配方,在该配方中,主要成分为丙烯酸树脂、环氧树脂和高分子复合物,添加剂有增塑剂、增韧剂、稀释剂、活性剂、抗冻剂、乳化剂、阻燃剂、增稠剂、防水剂和水。其配比为(wt%):
1、丙烯酸树脂 10~40
2、环氧树脂 5~20
3、高分子复合物 5~30
4、增塑剂 2~5
5、增韧剂 2~5
6、稀释剂 5~20
7、活性剂 0.5~1.0
8、抗冻剂 3~7
9、乳化剂 2~5
10、阻燃剂 1~3
11、增稠剂 2~6
12、防水剂 5~30
13、水 16~20
由于在本发明中同时采用现有环氧树脂类和丙烯酸树脂类粘接剂的主要成分,即环氧树脂和丙烯酸树脂,又专门针对外墙保温的特殊需要,掺入了各种添加剂,使得本发明之粘接剂克服了现有两类粘接剂各自的缺点,具备了现有两类粘接剂各自的优点,实现了本发明的目的。所达到的技术指标为:
1、压剪粘结强度(7d) ≥1.8Mpa
2、抗拉粘结强度(7d) ≥1.0Mpa
3、压剪粘接强度(7d+4d浸水) ≥1.5Mpa
4、粘接强度(28d) ≥0.13Mpa
5、粘接强度(28d+10d浸水) ≥0.12Mpa
6、冻融粘接强度(28d+D30次±30℃) ≥0.12Mpa
具体实施方式
在此提出几个典型的配方,关于配方成分,主要成分除采用上文介绍的环氧树脂、丙烯酸树脂外,高分子复合物为聚氨酯弹性体和聚丙烯酸酯;各种添加剂除了水外,选用情况为,增塑剂为邻苯二甲酸酯,增韧剂为聚氨酯,稀释剂为缩水甘油醚,活性剂为聚酰氨树脂,抗冻剂为缩乙二醇和乙二醇,乳化剂为山梨醇酐单油酯、聚氧乙烯脱水山梨醇单油酸酯、多元醇和胺类,阻燃剂为四溴代邻苯二甲酸酐和多孔氢氧化铝,增稠剂为氯化钠和纤维素,防水剂为松香酸钠。配方中各组分的含量均为重量百分含量(Wt%)。
配方一:
1、丙烯酸树脂 25
2、环氧树脂 15
3、聚氨酯弹性体+聚丙烯酸酯 15
4、邻苯二甲酸酯 2
5、聚氨酯 3
6、缩水甘油醚 8
7、聚酰氨树脂 1
8、缩乙二醇+乙二醇 3
9、山梨醇酐单油酯和聚氧乙烯脱水山梨醇单油酸酯
和多元醇和胺类 3
10、四溴代邻苯二甲酸酐+多孔氢氧化铝 2
11、氯化钠+纤维素 2
12、松香酸钠 5
13、水 16
按此配方制得的产品其特点是:环氧树脂和丙烯酸树脂的用量适宜,得到的产品粘接性能良好,抗老化能力强,抗碱性、抗介质性能强,稳定性好,寿命较长并且可以达到如下技术指标:
压剪粘结强度(7d) 1.8Mpa
抗拉粘结强度(7d) 1.0Mpa
压剪粘接强度(7d+4d浸水) 1.5Mpa
粘接强度(28d) 0.13Mpa
粘接强度(28d+10d浸水) 0.12Mpa
配方二:
1、丙烯酸树脂 33
2、环氧树脂 7
3、聚氨酯弹性体+聚丙烯酸酯 15
4、邻苯二甲酸酯 2
5、聚氨酯 3
6、缩水甘油醚 7
7、聚酰氨树脂 1
8、缩乙二醇+乙二醇 3
9、山梨醇酐单油酯和聚氧乙烯脱水山梨醇单油酸酯
和多元醇和胺类 3
10、四溴代邻苯二甲酸酐+多孔氢氧化铝 2
11、氯化钠+纤维素 2
12、松香酸钠 5
13、水 17
按此配方制得的产品其特点是:丙烯酸树脂比例相对较大,抗老化能力较好,粘接性能不如配方一。技术指标如下:
压剪粘结强度(7d) 1.2Mpa
抗拉粘结强度(7d) 1.0Mpa
压剪粘接强度(7d+4d浸水) 1.1Mpa
粘接强度(28d) 0.10Mpa
粘接强度(28d+10d浸水) 0.10Mpa
配方三:
1、丙烯酸树脂 30
2、环氧树脂 9
3、聚氨酯弹性体+聚丙烯酸酯 15
4、邻苯二甲酸酯 2
5、聚氨酯 3
6、缩水甘油醚 9
7、聚酰氨树脂 1
8、缩乙二醇+乙二醇 3
9、山梨醇酐单油酯和聚氧乙烯脱水山梨醇单油酸酯
和多元醇和胺类 5
10、四溴代邻苯二甲酸酐+多孔氢氧化铝 2
11、氯化钠+纤维素 2
12、松香酸钠 5
13、水 16
按此配方制得的产品其特点是:环氧树脂用量与配方二相比相对较多,抗老化能力和粘接性能与配方二相比差别不大。技术指标如下:
压剪粘结强度(7d) 1.2Mpa
抗拉粘结强度(7d) 1.0Mpa
压剪粘接强度(7d+4d浸水) 1.2Mpa
粘接强度(28d) 0.11Mpa
粘接强度(28d+10d浸水) 0.10Mpa
Claims (3)
1、一种外墙保温用高分子粘接剂,经反应制得,配料包括主要成分和添加成分,其特征在于,主要成分包括丙烯酸树脂、环氧树脂和高分子复合物,添加成分有增塑剂、增韧剂、稀释剂、活性剂、抗冻剂、乳化剂、阻燃剂、增稠剂、防水剂和水,其配比为(wt%):
(1)丙烯酸树脂 10~40
(2)环氧树脂 5~20
(3)高分子复合物 5~30
(4)增塑剂 2~5
(5)增韧剂 2~5
(6)稀释剂 5~20
(7)活性剂 0.5~1.0
(8)抗冻剂 3~7
(9)乳化剂 2~5
(10)阻燃剂 1~3
(11)增稠剂 2~6
(12)防水剂 5~30
(13)水 16~20
2、根据权利要求1所述的外墙保温用高分子粘接剂,其特征在于,其中的高分子复合物为聚氨酯弹性体和聚丙烯酸酯。
3、根据权利要求1所述的外墙保温用高分子粘接剂,其特征在于,各种添加成分的选用情况为,增塑剂为邻苯二甲酸酯,增韧剂为聚氨酯,稀释剂为缩水甘油醚,活性剂为聚酰氨树脂,抗冻剂为缩乙二醇和乙二醇,乳化剂为山梨醇酐单油酯和聚氧乙烯脱水山梨醇单油酸酯和多元醇和胺类,阻燃剂为四溴代邻苯二甲酸酐和多孔氢氧化铝,增稠剂氯化钠和纤维素,防水剂为松香酸钠。