CN1635951A - Printing paper and method of manufacturing the same - Google Patents
Printing paper and method of manufacturing the same Download PDFInfo
- Publication number
- CN1635951A CN1635951A CNA038013754A CN03801375A CN1635951A CN 1635951 A CN1635951 A CN 1635951A CN A038013754 A CNA038013754 A CN A038013754A CN 03801375 A CN03801375 A CN 03801375A CN 1635951 A CN1635951 A CN 1635951A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- printing paper
- paper
- ink
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a printing paper which can be repositioned freely and printed at high resolution up to 2,800 dpi even by ink-jet printers as well as laser printers. Thus, the printing paper is variously utilized for reports, colored-printing paper and public information paper. In particular, the printing paper for using in public information paper or guidance paper can be attached to any surface in a typical office, and separated therefrom, and again attached to other surfaces. In addition, when a printing paper is separated from the attached surface, the paper as well as the surface remains undestroyed, and no impurities are left on the attached surface, proving best availability. The invention also provides a method of manufacturing the printing paper.
Description
Technical field
The present invention relates to a kind of novel printing paper and manufacture method thereof, it is characterized in that, this printing paper can repeatedly be reorientated, even and under the situation of using ink-jet printer, also can further guarantee high-resolution printability.
Background technology
Usually, the printing paper of A4 size (210 * 297 millimeters) use 90% or more office in, and the printing paper of this size also is applicable to most printer.That is to say that the printing paper of A4 size is general.
But, when the A4 paper that will have print What (advertisement, information etc.) is attached on wall or the bulletin board, all inconvenience is just arranged,, perhaps on paper, be coated with paste as using adhesive tape or drawing pin.Perhaps, become known for the label paper of mail, it is provided with an adhesive surface that is used for sticking on the overlay paper.But, because this label paper is previously cut to predetermined size, so the necessary special text file that uses based on word-processing equipment.Therefore, be difficult in the content that printing is wanted on the label paper.And, owing to after label paper is attached on the predetermined surface, just can't again the label paper that strips down be attached on another surface disposable adhering to.
In addition, after using printing of inkjet printer, the ink trickling on the printing paper is very serious.Therefore, in order to guarantee high-resolution printability, mainly adopt laser printer.As for ink-jet printer, because print procedure realizes by nozzle ink jet, so resolution ratio depends on the printing paper material that makes ink be adhered to the time required on the printing paper and can absorb ink to a great extent.Thereby the print procedure that uses ink-jet printer to be carried out on the printing paper of routine produces the resolution ratio of 800 of per inch at most.
Summary of the invention
Therefore, the problem that the objective of the invention is to alleviate in correlation technique and run into, and a kind of A4 size marking paper with the adhesion system that makes things convenient for the user is provided.
Another purpose of the present invention provides a kind of printing paper of A4 size, by coating one repositionable adhesive on the adhesive surface of this printing paper, thereby can freely adhere to and peel off.
A further object of the invention provides a kind of printing paper, and its characteristics are, apply a kind of coating agent to printing on the recto (prints the surface), in order to the adhesion of raising ink, thereby realize high-resolution inkjet printing.
A further object of the invention provides the method that a kind of manufacturing has the printing paper of above-mentioned feature.
The accompanying drawing summary
Fig. 1 shows the figure of a kind of printing paper of the present invention when being used.
The specific embodiment
Hereinafter, will be described in detail a kind of printing paper and manufacture method thereof in conjunction with the accompanying drawings.
Try Fig. 1, the printing paper of the present invention when there is shown actual use.
As shown in Figure 1, the characteristics of printing paper of the present invention are, the back side of printing paper (b) has applied the repositionable adhesive of one deck, adhere to then on PET (polyethylene terephthalate) paper (stacked paper of PE or overlay paper) of a PVC (polyvinyl chloride) vinyl coating, and this recto that is printer surface-coated one coating agent of print What thereon, in order to improve the adhesion of ink.
In the present invention, the adhesive that on the printing paper back side that adheres on the PET paper, applies, comprise " the inorganic filler (calcium carbonate), 1 of the non-ionic surface active agent of the vinyl acetate-acrylate copolymer resin of 43-47 weight portion, 1.5-2.5 weight portion (polyoxyethylene nonyl phenylate (poly ory ethylene nonyl phenyl ether)), 16-20 weight portion; 000-2; 000 millionth vinyl acetate monomer, 1; 000-2, the water of 000 millionth 2-EHA (EHA) monomer and 32-36 weight portion.
As for known " Post-it
" (" the newspaper thing is pasted "), this is a kind of repositionable adhesive that almost can use on any adhesive surface, is the esters of acrylic acid material that is dissolved in such as in the toluene volatile organic solvent.But, in the present invention, such esters of acrylic acid substance dissolves in water, thereby alleviated the smell of volatile ingredient, and also overcome the problem that viscosity that the evaporation because of volatile ingredient causes further reduces.Equally, the pollution to environment also reduces.
Therefore, adhesive of the present invention can show the cohesiveness of predetermined extent.And, when printing paper when attaching surface peels, paper and attaching surface can not be damaged.In addition, on attaching surface, do not stay impurity yet.
Adhesive of the present invention preferably is coated on the surface of printing paper with 25 microns thickness.
Therefore, the advantage of printing paper of the present invention just is, use word-processing equipment to make print What, and with them to be printed on the state output on the printing paper, after this printing paper is separated from PET paper, then, these printing papers of having printed content just may be attached on the surface of wanting to attach, can also easily peel and adhere again on other surface, resemble conventional newspaper thing and paste (" Post-it from these surfaces
") the same.
In addition, in the present invention, used a coating agent to improve the adherence of the ink that sprays from ink-jet printer, this coating agent comprises the quartz (SiO of 23-27 weight portion
2) the ink sticker of the polymerization binding material of powder, 46-50 weight portion, the routine of 1 weight portion, the ink fixative of the routine of 1 weight portion and the water of 20 weight portions.
Coating agent covered to be applied to equably prints on the recto, and under 120 ℃ temperature dry about 20 seconds, thereby finish the preparation of printing paper of the present invention.
About coating agent of the present invention, used the quartz of volume, by this, compare the regular situation of only using the ink sticker, coating agent of the present invention except characteristic with organic material, comprise reactivity, dissolubility, elasticity and the adherence, also further show the general physical characteristic of inorganic material, comprise heat endurance, chemical stability, glossiness and mar proof.Even speckle with water on ink-jet printed surface, coating agent also can play the effect that prevents the ink trickling.
Therefore, be coated with the ink that printing paper can transient absorption and fixedly ink-jet printer sprayed of this coating agent, thereby realization is up to the high-resolution of 2,800 of per inch.
In addition, a kind of method of making according to printing paper of the present invention may further comprise the steps: (1) prepares a kind of coating agent, and this coating agent mainly comprises the quartz of 23-27 weight portion, the polymerization binding material of 46-50 weight portion, the ink sticker of 1 weight portion, the ink fixative of 1 weight portion and the water of 20 weight portions; (2) coating agents of 8.4 grams are coated to one and print on the recto, this is coated to about 20 seconds of coating agent on the printing paper front at 120 ℃ temperature drying then.This method also comprises: (3) prepare a kind of adhesive, this adhesive comprises the inorganic fillings (calcium carbonate), 1 of the vinyl acetate-acrylate copolymer resin of 43-47 weight portion, the non-ionic surface active agent of 1.5-2.5 weight portion (polyoxyethylene nonyl phenylate), 16-20 weight portion, 000-2,000 millionth vinyl acetate monomer, 1,000-2, the water of 000 millionth 2-EHA monomer and 32-36 weight portion; (4) with 8.4 the gram adhesive coated to the back side of printing paper; (5) the printing paper back side that will be coated with this adhesive is attached on the PET paper at last.
Said method also comprises step (6): the printing paper that will be attached on the PET paper cuts into predetermined size (A4 or B5).
Industrial applicability
As mentioned above, the invention provides the method for a kind of printing paper and this printing paper of manufacturing.The advantage of this printing paper is, promptly uses ink-jet printer (also comprise and use laser printer), also can realize the high-resolution up to 2,800 of per inch; It is also advantageous in that, can be applicable to the various application scenarios of report, colour print paper and notice information paper.Particularly, can be used as this printing paper of notice information paper or guiding paper can be freely attached to bulletin board, wall, be arranged on the dividing plate of office desk front, and can take off from it easily, and adhere again on other the surface.
In addition, repositionable adhesive of the present invention can not damage paper and attaching surface when attaching surface separates this paper.And, on attaching surface, can not leave impurity, thereby give the convenient to greatest extent of user.
Although disclosed preferred embodiment of the present invention for illustrative purposes, those those skilled in the art that will appreciate that, many interpolations and to substitute all be possible are not as long as and exceed the protection domain of the present invention and the spirit of appended claims.
Claims (5)
1. printing paper, it comprises a back side, is coated with a kind of repositionable adhesive on this back side, and is attached to the covering on the coating surface of a PET paper.
2. printing paper as claimed in claim 1 is characterized in that, prints on the recto and is coated with a kind of coating agent, in order to improve the level of adhesion of the ink that ink-jet printer sprayed.
3. printing paper as claimed in claim 1 or 2, it is characterized in that, described adhesive comprises: the inorganic fillings (calcium carbonate), 1 of the non-ionic surface active agent of the vinyl acetate-acrylate copolymer resin of 43-47 weight portion, 1.5-2.5 weight portion (polyoxyethylene nonyl phenylate), 16-20 weight portion, 000-2,000 millionth vinyl acetate monomer, 1,000-2, the water of 000 millionth 2-EHA monomer and 32-36 weight portion.
4. printing paper as claimed in claim 1 or 2, it is characterized in that described coating agent comprises: the ink fixative of the routine of the polymerization binding material of the quartz of 23-27 weight portion, 46-50 weight portion, the ink sticker of 1 weight portion, 1 weight portion and the water of 20 weight portions.
5. method of making printing paper, it may further comprise the steps;
(1) prepare a kind of coating agent, this coating agent comprises the quartz of 23-27 weight portion, the polymerization binding material of 46-50 weight portion, the ink sticker of 1 weight portion, the ink fixative of 1 weight portion and the water of 20 weight portions;
(2) coating agents of 8.4 grams are coated to one and print on the recto, about 20 seconds then at 120 ℃ temperature drying.
(3) prepare a kind of adhesive, this adhesive comprises the inorganic fillings (calcium carbonate), 1 of the vinyl acetate-acrylate copolymer resin of 43-47 weight portion, the non-ionic surface active agent of 1.5-2.5 weight portion (polyoxyethylene nonyl phenylate), 16-20 weight portion, 000-2,000 millionth vinyl acetate monomer, 1,000-2, the water of 000 millionth 2-EHA monomer and 32-36 weight portion;
(4) with 8.4 the gram adhesive coated to the back side of printing paper;
(5) the printing paper back side that will be coated with this adhesive is attached on the polyethylene terephthalate paper;
(6) printing paper that will be attached on the PET paper cuts into predetermined size.