CN1609149A - Ink paint - Google Patents

Ink paint Download PDF

Info

Publication number
CN1609149A
CN1609149A CN 200310106681 CN200310106681A CN1609149A CN 1609149 A CN1609149 A CN 1609149A CN 200310106681 CN200310106681 CN 200310106681 CN 200310106681 A CN200310106681 A CN 200310106681A CN 1609149 A CN1609149 A CN 1609149A
Authority
CN
China
Prior art keywords
resin
solvent
polyethylene wax
modified rosin
polyamide resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200310106681
Other languages
Chinese (zh)
Inventor
张迪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 200310106681 priority Critical patent/CN1609149A/en
Publication of CN1609149A publication Critical patent/CN1609149A/en
Pending legal-status Critical Current

Abstract

The present invention discloses one kind of ink paint, which, when heated, may be transferred to the print carrier completely, and has wide print carrier adaptability, great attachment, high scrape and boiling resistance, and no adhesion. The ink paint consists of polyamide resin, modified rosin resin, polyethylene wax, stuffing, pigment, dispersant, leveling agent and solvent. The present invention is used mainly in producing mark belt.

Description

Printing ink paint
Technical field
The present invention relates to a kind of coating, more particularly relate to a kind of coating that indicates carbon ribbon.
Background technology
Its ink coating of the carbon ribbon of Xiao Shouing can not be transferred on the carrier of undertaking the printing of after being subjected under the suitable temperature to scald fully in the market, and the China ink layer is to the carrier poor adhesive force of undertaking the printing of, and scrape resistant, boiling resistance are poor.
Summary of the invention
The present invention is in order to overcome weak point of the prior art, provide a kind of China ink layer blanching seal performance good, the transferring rate height, thermal adaptation is extensive, stock carrier PP, PE, PVC, aluminium foil, paper chemical fibre etc. all there is good adhesive, wear-resisting wiping, anti-boiling have the coating of the sign carbon ribbon of good bonding force with assistant coating.
The present invention is achieved through the following technical solutions: a kind of printing ink paint, comprise following component by weight percentage, polyamide resin 10-15%, modified rosin resin 6-9%, polyethylene wax 3-7%, filler 7-23%, pigment 9-11%, dispersion agent 0.1-0.5%, flow agent 0.1-0.3%, solvent 35-60%.Polyamide resin is a thermoplasticity, and in 50% ethanolic soln, softening temperature is at 80-180 ℃, 25 ℃ of viscosity, and the amine value is not more than 10.The softening temperature of modified rosin resin is at 100-150 ℃, and acid number is less than 20.Polyethylene wax is a powdery, and softening temperature is 90-140 ℃, and fineness is not more than 10 μ m.
Printing ink paint of the present invention can be transferred on the carrier of undertaking the printing of after being subjected to scald fully, and the China ink layer has adaptability widely to the carrier of undertaking the printing of, and sticking power is good, scrape resistant, anti-boiling, adhesion, the transferring rate height.
Embodiment
Example 1: the present embodiment polyamide resin is selected the P-1155 of Lauth OY for use, modified rosin fat can adopt 210 of Suichuan resin, polyethylene wax can be selected the LumaxAL3 of BASF AG for use, filler can be selected calcium carbonate superfine powder and zinc sulfide white for use, and pigment is that carbon black is selected the Cabet800 of Cabot Co.,Ltd for use, and dispersion agent is selected Bi Ke K-163 for use, flow agent is selected the product of Dow Corning Corporation for use, code 5T, solvent be for being dimethylbenzene 70% by weight percentage, Virahol 30%.Get the raw materials ready by following prescription, elder generation in solvent, is sequentially added into other components to the resin heating for dissolving again, by shredder system is uniformly dispersed, and particle diameter gets final product below 10 μ m.
Polyamide resin 15g
Modified rosin resin 7g
Polyethylene wax Luwax AL3 ?5g
Lime carbonate 20g
Zinc sulfide white 3g
Carbon black 11g
Dispersion agent 0.5g
Flow agent 0.3g
Solvent 38.2g
Example 2: the present embodiment polyamide resin is selected the P-1155 of Lauth OY for use, modified rosin fat can adopt 210 of Suichuan resin, polyethylene wax can be selected the LumaxAL3 of BASF AG for use, filler can be selected calcium carbonate superfine powder and zinc sulfide white for use, and pigment is that carbon black is selected the Cabet800 of Cabot Co.,Ltd for use, and dispersion agent is selected Bi Ke K-163 for use, flow agent is selected the product of Dow Corning Corporation for use, code 5T, solvent are dimethylbenzene 60% by weight percentage, Virahol 40%.Get the raw materials ready by following prescription, elder generation in solvent, is sequentially added into other components to the resin heating for dissolving again, by shredder system is uniformly dispersed, and particle diameter gets final product below 10 μ m.
Get the raw materials ready by following prescription, elder generation in solvent, is sequentially added into other components to the resin heating for dissolving again, by shredder system is uniformly dispersed, and grain is through getting final product below 10 μ m.
Polyamide resin 10g
Modified rosin resin 9g
Polyethylene wax Luwax AL3 5g
Lime carbonate 12g
Zinc sulfide white 3g
Carbon black 11g
Dispersion agent 0.5g
Flow agent 0.3g
Solvent 49.2g
Embodiment 3: the present embodiment polyamide resin is selected the P-1155 of Lauth OY for use, modified rosin fat can adopt 210 of Suichuan resin, polyethylene wax can be selected the LumaxAL3 of BASF AG for use, filler can be selected calcium carbonate superfine powder and zinc sulfide white for use, and pigment is that carbon black is selected the Cabet800 of Cabot Co.,Ltd for use, and dispersion agent is selected Bi Ke K-163 for use, flow agent is selected the product of Dow Corning Corporation for use, code 5T, solvent be for being dimethylbenzene 70% by weight percentage, Virahol 30%.By following prescription, elder generation in solvent, is sequentially added into other components to the resin heating for dissolving again, by shredder system is uniformly dispersed, and grain is through getting final product below 10 μ m.
Polyamide resin 12g
Modified rosin resin 6g
Polyethylene wax Luwax AL3 6g
Lime carbonate 12g
Zinc sulfide white 3g
Carbon black 11g
Dispersion agent 0.5g
Flow agent 0.3g
Solvent 49.2g
Embodiment 4: the present embodiment polyamide resin is selected the P-1155 of Lauth OY for use, modified rosin fat can adopt 210 of Suichuan resin, polyethylene wax can be selected the LumaxAL3 of BASF AG for use, filler can be selected calcium carbonate superfine powder and zinc sulfide white for use, and pigment is that carbon black is selected the Cabet800 of Cabot Co.,Ltd for use, and dispersion agent is selected Bi Ke K-163 for use, flow agent is selected the product of Dow Corning Corporation for use, code 5T, solvent be for being dimethylbenzene 70% by weight percentage, Virahol 30%.By following prescription, elder generation in solvent, is sequentially added into other components to the resin heating for dissolving again, by shredder system is uniformly dispersed, and grain is through getting final product below 10 μ m.
Polyamide resin 12g
Modified rosin resin 7g
Polyethylene wax Luwax AL3 3g
Lime carbonate 12g
Zinc sulfide white 3g
Carbon black 11g
Dispersion agent 0.5g
Flow agent 0.3g
Solvent 51.2g
Embodiment 5: the present embodiment polyamide resin is selected the P-1155 of Lauth OY for use, modified rosin fat can adopt 210 of Suichuan resin, polyethylene wax can be selected the LumaxAL3 of BASF AG for use, filler can be selected calcium carbonate superfine powder and zinc sulfide white for use, and pigment is that carbon black is selected the Cabet800 of Cabot Co.,Ltd for use, and dispersion agent is selected Bi Ke K-163 for use, flow agent is selected the product of Dow Corning Corporation for use, code 5T, solvent be for being dimethylbenzene 70% by weight percentage, Virahol 30%.By following prescription, elder generation in solvent, is sequentially added into other components to the resin heating for dissolving again, by shredder system is uniformly dispersed, and grain is through getting final product below 10 μ m.
Polyamide resin 12g
Modified rosin resin 7g
Polyethylene wax Luwax AL3 7g
Lime carbonate 12g
Zinc sulfide white 3g
Carbon black 11g
Dispersion agent 0.5g
Flow agent 0.3g
Solvent 47.2g
Embodiment 6: the present embodiment polyamide resin is selected the P-1155 of Lauth OY for use, modified rosin fat can adopt 210 of Suichuan resin, polyethylene wax can be selected the LumaxAL3 of BASF AG for use, filler can be selected calcium carbonate superfine powder and zinc sulfide white for use, and pigment is that carbon black is selected the Cabet800 of Cabot Co.,Ltd for use, and dispersion agent is selected Bi Ke K-163 for use, flow agent is selected the product of Dow Corning Corporation for use, code 5T, solvent be for being dimethylbenzene 70% by weight percentage, Virahol 30%.By following prescription, elder generation in solvent, is sequentially added into other components to the resin heating for dissolving again, by shredder system is uniformly dispersed, and grain is through getting final product below 10 μ m.
Polyamide resin 12g
Modified rosin resin 7g
Polyethylene wax Luwax AL3 7g
Lime carbonate 20g
Zinc sulfide white 3g
Carbon black 11g
Dispersion agent 0.5g
Flow agent 0.3g
Solvent 39.2g
Embodiment 7: the present embodiment polyamide resin is selected the P-1155 of Lauth OY for use, modified rosin fat can adopt 210 of Suichuan resin, polyethylene wax can be selected the LumaxAL3 of BASF AG for use, filler can be selected calcium carbonate superfine powder and zinc sulfide white for use, and pigment is that carbon black is selected the Cabet800 of Cabot Co.,Ltd for use, and dispersion agent is selected Bi Ke K-163 for use, flow agent is selected the product of Dow Corning Corporation for use, code 5T, solvent be for being dimethylbenzene 70% by weight percentage, Virahol 30%.By following prescription, elder generation in solvent, is sequentially added into other components to the resin heating for dissolving again, by shredder system is uniformly dispersed, and grain is through getting final product below 10 μ m.
Polyamide resin 12g
Modified rosin resin 7g
Polyethylene wax Luwax AL3 7g
Lime carbonate 4g
Zinc sulfide white 3g
Carbon black 11g
Dispersion agent 0.5g
Flow agent 0.3g
Solvent 55.2g
Embodiment 8: the present embodiment polyamide resin is selected the P-1155 of Lauth OY for use, modified rosin fat can adopt 210 of Suichuan resin, polyethylene wax can be selected the LumaxAL3 of BASF AG for use, filler can be selected calcium carbonate superfine powder and zinc sulfide white for use, and pigment is selected red for use, and dispersion agent is selected Bi Ke K-163 for use, flow agent is selected the product of Dow Corning Corporation for use, code 5T, solvent are dimethylbenzene 60% by weight percentage, Virahol 40%.Get the raw materials ready by following prescription, elder generation in solvent, is sequentially added into other components to the resin heating for dissolving again, by shredder system is uniformly dispersed, and particle diameter gets final product below 10 μ m.By following prescription, elder generation in solvent, is sequentially added into other components to the resin heating for dissolving again, by shredder system is uniformly dispersed, and grain is through getting final product below 10 μ m.
Polyamide resin 12g
Modified rosin resin 7g
Polyethylene wax Luwax AL3 7g
Lime carbonate 12g
Zinc sulfide white 3g
Red 9g
Dispersion agent 0.5g
Flow agent 0.3g
Solvent 49.2g
Embodiment 9: the present embodiment polyamide resin is selected the P-1155 of Lauth OY for use, modified rosin fat can adopt 210 of Suichuan resin, polyethylene wax can be selected the LumaxAL3 of BASF AG for use, filler can be selected calcium carbonate superfine powder and zinc sulfide white for use, and pigment is that carbon black is selected the Cabet800 of Cabot Co.,Ltd for use, and dispersion agent is selected Bi Ke K-163 for use, flow agent is selected the product of Dow Corning Corporation for use, code 5T, solvent are dimethylbenzene 60% by weight percentage, Virahol 40%.Get the raw materials ready by following prescription, elder generation in solvent, is sequentially added into other components to the resin heating for dissolving again, by shredder system is uniformly dispersed, and particle diameter gets final product below 10 μ m.By following prescription, elder generation in solvent, is sequentially added into other components to the resin heating for dissolving again, by shredder system is uniformly dispersed, and grain is through getting final product below 10 μ m.
Polyamide resin 12g
Modified rosin resin 7g
Polyethylene wax Luwax AL3 7g
Lime carbonate 20g
Zinc sulfide white 3g
Carbon black 10g
Dispersion agent 0.5g
Flow agent 0.3g
Solvent 40.2g
Embodiment 10: the polyamide resin present embodiment is selected the P-1155 of Lauth OY for use, modified rosin fat can adopt 210 of Suichuan resin, polyethylene wax can be selected the LumaxAL3 of BASF AG for use, filler can be selected calcium carbonate superfine powder and zinc sulfide white for use, pigment is selected red for use, and dispersion agent is selected the K-100 of Germany for use, and flow agent is selected U.S. Yi Si Man flow agent product for use, solvent is dimethylbenzene 60% by weight percentage, Virahol 40%.By following prescription, elder generation in solvent, is sequentially added into other components to the resin heating for dissolving again, by shredder system is uniformly dispersed, and grain is through getting final product below 10 μ m.
Polyamide resin 12g
Modified rosin resin 7g
Polyethylene wax Luwax AL3 7g
Lime carbonate 20g
Zinc sulfide white 3g
Red 10g
Dispersion agent 0.1g
Flow agent 0.3g
Solvent 40.6g
Embodiment 11: the polyamide resin present embodiment is selected the P-1155 of Lauth OY for use, modified rosin fat can adopt 210 of Suichuan resin, polyethylene wax can be selected the LumaxAL3 of BASF AG for use, filler can be selected calcium carbonate superfine powder and zinc sulfide white for use, pigment is selected red for use, and dispersion agent is selected the K-100 of Germany for use, and flow agent is selected U.S. Yi Si Man flow agent product for use, solvent is dimethylbenzene 60% by weight percentage, Virahol 40%.By following prescription, elder generation in solvent, is sequentially added into other components to the resin heating for dissolving again, by shredder system is uniformly dispersed, and grain is through getting final product below 10 μ m.
Polyamide resin 12g
Modified rosin resin 7g
Polyethylene wax Luwax AL3 7g
Lime carbonate 20g
Zinc sulfide white 3g
Red 10g
Dispersion agent 0.3g
Flow agent 0.3g
Solvent 40.4g
Embodiment 12: the polyamide resin present embodiment is selected the P-1155 of Lauth OY for use, modified rosin fat can adopt 210 of Suichuan resin, polyethylene wax can be selected the LumaxAL3 of BASF AG for use, filler can be selected calcium carbonate superfine powder and zinc sulfide white for use, pigment is selected red for use, and dispersion agent is selected the K-100 of Germany for use, and flow agent is selected U.S. Yi Si Man flow agent product for use, solvent is dimethylbenzene 60% by weight percentage, Virahol 40%.By following prescription, elder generation in solvent, is sequentially added into other components to the resin heating for dissolving again, by shredder system is uniformly dispersed, and grain is through getting final product below 10 μ m.
Polyamide resin 12g
Modified rosin resin 7g
Polyethylene wax Luwax AL3 7g
Lime carbonate 20g
Zinc sulfide white 3g
Red 10g
Dispersion agent 0.3g
Flow agent 0.1g
Solvent 40.7g
Embodiment 13: the polyamide resin present embodiment is selected the P-1155 of Lauth OY for use, modified rosin fat can adopt 210 of Suichuan resin, polyethylene wax can be selected the LumaxAL3 of BASF AG for use, filler can be selected calcium carbonate superfine powder and zinc sulfide white for use, pigment is selected red for use, and dispersion agent is selected the K-100 of Germany for use, and flow agent is selected U.S. Yi Si Man flow agent product for use, solvent is dimethylbenzene 70% by weight percentage, Virahol 30%.By following prescription, elder generation in solvent, is sequentially added into other components to the resin heating for dissolving again, by shredder system is uniformly dispersed, and grain is through getting final product below 10 μ m.
Polyamide resin 12g
Modified rosin resin 7g
Polyethylene wax Luwax AL3 7g
Lime carbonate 20g
Zinc sulfide white 3g
Red 11g
Dispersion agent 0.3g
Flow agent 0.2g
Solvent 39.5g
Embodiment 14 polyamide resin present embodiments are selected the P-1155 of Lauth OY for use, modified rosin fat can adopt 210 of Suichuan resin, polyethylene wax can be selected the LumaxAL3 of BASF AG for use, filler can be selected calcium carbonate superfine powder and zinc sulfide white for use, pigment is selected red for use, and dispersion agent is selected the K-100 of Germany for use, and flow agent is selected U.S. Yi Si Man flow agent product for use, solvent is dimethylbenzene 70% by weight percentage, Virahol 30%.By following prescription, elder generation in solvent, is sequentially added into other components to the resin heating for dissolving again, by shredder system is uniformly dispersed, and grain is through getting final product below 10 μ m.：
Polyamide resin 10g
Modified rosin resin 6g
Polyethylene wax Luwax AL3 3g
Lime carbonate 8g
Zinc sulfide white 3g
Red 9.5g
Dispersion agent 0.3g
Flow agent 0.2g
Solvent 60g
Embodiment 15: the polyamide resin present embodiment is selected the P-1155 of Lauth OY for use, modified rosin fat can adopt 210 of Suichuan resin, polyethylene wax can be selected the LumaxAL3 of BASF AG for use, filler can be selected calcium carbonate superfine powder and zinc sulfide white for use, pigment is selected red for use, and dispersion agent is selected the K-100 of Germany for use, and flow agent is selected U.S. Yi Si Man flow agent product for use, solvent is dimethylbenzene 60% by weight percentage, Virahol 40%.By following prescription, elder generation in solvent, is sequentially added into other components to the resin heating for dissolving again, by shredder system is uniformly dispersed, and grain is through getting final product below 10 μ m.
Polyamide resin 15g
Modified rosin resin 9g
Polyethylene wax Luwax AL3 7g
Lime carbonate 20g
Zinc sulfide white 3g
Red 10.5g
Dispersion agent 0.3g
Flow agent 0.2g
Solvent 35g
The coating that makes with printing ink paint of the present invention can be transferred on the carrier of undertaking the printing of after being subjected to scald fully, the China ink layer will have adaptability widely to the carrier of undertaking the printing of, sticking power is good, scrape resistant, anti-boiling, adhesion, can be fit to the undertake the printing of blanching formula of carrier of various speed, differing temps, difference and indicate band.
Fundamental property sees the following form:
Performance Index Remarks
Color Black The condition of boiling be 100 ℃ following 30 minutes
Thickness ??12-14μm
Light Yin Wendu ??100-150℃
Adapt to base material PP, PE, PET aluminium foil etc.
Sticking power Anti-set-off, scrape resistant, anti-boiling

Claims (4)

1. printing ink paint, it is characterized in that, comprise following component by weight percentage, polyamide resin 10-15%, modified rosin resin 6-9%, polyethylene wax 3-7%, filler 7-23%, pigment 9-11%, dispersion agent 0.1-0.5%, flow agent 0.1-0.3%, solvent 35-60%.
2. printing ink paint according to claim 1 is characterized in that, described polyamide resin is a thermoplasticity, and in 50% ethanolic soln, softening temperature is at 80-180 ℃, 25 ℃ of viscosity, and the amine value is not more than 10.
3. printing ink paint according to claim 1 is characterized in that the softening temperature of described modified rosin resin is at 100-150 ℃, and acid number is less than 20.
4. printing ink paint according to claim 1 is characterized in that described polyethylene wax is a powdery, and softening temperature is 90-140 ℃, and fineness is not more than 10 μ m.
CN 200310106681 2003-10-20 2003-10-20 Ink paint Pending CN1609149A (en)