CN1199793A - Tarpaulin and its making method - Google Patents
Tarpaulin and its making method Download PDFInfo
- Publication number
- CN1199793A CN1199793A CN 97107508 CN97107508A CN1199793A CN 1199793 A CN1199793 A CN 1199793A CN 97107508 CN97107508 CN 97107508 CN 97107508 A CN97107508 A CN 97107508A CN 1199793 A CN1199793 A CN 1199793A
- Authority
- CN
- China
- Prior art keywords
- tarpaulin
- slurry
- heating
- production technology
- base cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The novel tarpaulin is made through soaking base cloth in size compounded with VAE emulsion, heating to cure and painting organosilicon stickiness preventing layer. The present invention is excellent in compounding and simple and reliable in technological process and the product has good property of waterproofing, anticorrosive, resisting UV ray and resisting microbe degradation.
Description
The invention belongs to water-proof tarpaulin and production Technology.
At present general water-proof tarpaulin adopts to be coated with cured or to be coated with polyvinyl chloride resin mostly and makes.Its shortcoming is to use the life-span short, and UV resistant is poor.In number being 92110333.8,91218620.8,94117409.3,94103844 patent, the Chinese patent application of having announced proposed with natural rubber, heat is melted the method that composite algorithm and carboxyl diene, polyvinyl formal coated etc. are made tarpaulin, it is complicated all to exist manufacture craft, the cost height, the weakness of water resistance difference has bigger difficulty in promotion and application.
Purpose of the present invention is exactly in order to overcome the deficiency of above-mentioned prior art, also open up a new road for the application of VAE, and a kind of tarpaulin and production technology thereof of novelty be provided, be that slurry that major ingredient adds some additives preparations pads base cloth and makes tarpaulin promptly with the VAE emulsion.
Major technique content characteristic of the present invention is:
This be by base cloth by at vinyl acetate and vinyl monomer be add in the synthetic VAE emulsion of raw material pad in the formulated slurry of plasticizer, antistatic additive, fire retardant and a large amount of additives such as cheap filler or blade coating after, heating cure, and then coat organosilicon (Organic fluoride) adherent layer, promptly make.The prescription of its slurry is:
VAE 100 (part)
Plasticizer 5-10 (part)
Antistatic additive is an amount of
Fire retardant 20-30 (part)
Filler (potter's clay, talcum powder etc.) 20-30 (part) (add fire retardant after just not filled)
Dispersant 1-2 (part)
Mill base 3 (part)
Its technical process is:
Base cloth (grey cloths such as day combustion fiber, artificial fibre, chemical fibre) → in prepared slurry, pad (or blade coating) → heating cure → coat organosilicon (or Organic fluoride) adherent layer → heating cure → finished product tarpaulin.
The present invention compared with the prior art, this has following advantage:
1, prescription of the present invention is excellent, and production technology is simpler, and is reliable, easy to implement, product cost is lower, and its function admirable has high water proofing property, and anti-uv-ray is strong, good corrosion resistance can not damage among hydrochloric acid 20% and the 20%NaoH, the degraded of anti-microorganism, long service life.Therefore bigger application value is arranged.
2, the present invention has also opened up a new road for the application of VAE, and this tarpaulin can be according to application person's different requirements, and available neoprene glue bond is made various goods.
The embodiment explanation:
Factory formula:
1, the preparation of the cooperation emulsion of VAE:
Under 55 degree ⊥, 5 situations, splash into 1: 1 toluene, toluene diethyl cyanic acid courage mixed liquor, 10 of per minutes, adding amount is the 3-5% of emulsion, stirs.It is standby to be cooled to 30 degree.
2, the preparation of slurry:
Filler: 20-50 part (cooperating emulsion by VAE is 100 parts) dispersant: 1-2 part mill base: 3 parts of moisture content: 50 parts of plasticizer: 5-10 part antistatic additive: add as required various fillers and water are mixed, ground 24 hours, it is stand-by to cooperate emulsion to mix with aqueous dispersion.
3, tarpaulin production technology: gluing: base cloth → pad and blade coating → heating cure → WATERPROOF FABRIC
Release treatment: the organosilicon → finished fabric goods of WATERPROOF FABRIC → pad 10% are bonding: neoprene adds 10% lek sodium as adhesive, and sticking face polishing is closed, double spread, treat solution evaporation after, firmly pressing.
Claims (3)
1, a kind of water-proof tarpaulin and production technology thereof, it is characterized in that, it be by base cloth by vinyl acetate and vinyl monomer be add in the synthetic VAE emulsion of raw material pad in the slurry that plasticizer, antistatic additive, fire retardant and a large amount of additives such as filler be made into or blade coating after, be heating and curing, and then coat organosilicon (Organic fluoride) adherent layer, promptly make.
According to described tarpaulin of claim 1 and production technology thereof, it is characterized in that 2, the prescription of its slurry is:
100 parts of VAE
Plasticizer 5-10 part
Fire retardant 20-30 part (perhaps filled)
Dispersant 1-2 part
3 parts of mill bases
According to described tarpaulin of claim 1 and production technology thereof, it is characterized in that 3, its technological process of production is:
Base cloth → pad in slurry (or blade coating) → organosilicon (Organic fluoride) adherent layer → heating cure → finished product tarpaulin is heating and curing → is coated with.