CN1607071A - Composition of vitreous brick buffing wheel - Google Patents
Composition of vitreous brick buffing wheel Download PDFInfo
- Publication number
- CN1607071A CN1607071A CN 200310111771 CN200310111771A CN1607071A CN 1607071 A CN1607071 A CN 1607071A CN 200310111771 CN200310111771 CN 200310111771 CN 200310111771 A CN200310111771 A CN 200310111771A CN 1607071 A CN1607071 A CN 1607071A
- Authority
- CN
- China
- Prior art keywords
- polishing
- vitreous brick
- grinding
- oxide
- calcium carbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The polishing wheel for glazed tile is composed of abradant made of polishing powder and silicon carbide, binder made of magnesite cement and thermoplastic phenolic resin, and auxiliary filling made of rareearth and its oxide, atearic acid and light calcium carbonate. The advantage is low price, simple preparation, quickly raised brightness, long brightness preservation time and without work piece cracking due to low grinding temperature.
Description
Technical field
The present invention relates to the composition of vitreous brick buffing wheel.
Background technology
The vitreous brick is meant that with clay, feldspar, quartz or clay, feldspar (porcelain stone), talcum etc. be primary raw material, is pressed into the ceramic product that base, high temperature sintering form through ball milling, mist projection granulating, height.Its Mohs' hardness and wearability all are higher than marble and general granite.According to the difference of manufacturing process etc., the vitreous brick can be divided into artificial granite brick, brindled brick and pattern permeating tile or the like again.
The high rigidity of vitreous brick and wearability, poor thermal shock resistance, crisp fritter, characteristics such as can not fix, make that the grinding and polishing processed finished products rate of vitreous brick is lower, surface gloss is inhomogeneous.Our experimental study shows that vitreous brick grinding and polishing processing is adopted with granite and processed similar equipment and processing technology, and stone material grinding and buffing wheel and processing technology, and be not suitable for processing vitreous brick.
Suitable vitreous brick grinding and polishing processing technology should be to add man-hour at abrasive grinding wheel at corase grind, can excise a large amount of workpiece materials, but be unlikely to produce deep torn grain.Add man-hour at half correct grinding, the processing pit that abrasive grinding wheel should make former procedures produce shoals, and produces enough plasticity grooves, improves the preceding crudy of fine finishining; The fine finishining abrasive grinding wheel should make polish the surface and tiny plasticity groove be main, the raising surface smoothness, the surface microstructure glassy surface is exposed.
Buffing wheel must make crystal gloss improve, and reduces surperficial light scattering degree by the roughness that reduces the surface, makes the surface present certain gloss; In the process, must prevent that buffing wheel from stopping up and cooling is not enough, cause possible grinding temperature too high, produce crack due to thermal stress and workpiece fragmentation.
The polishing efficiency of buffing wheel and polishing glossiness have directly influenced the quality of vitreous brick product; The cost of buffing wheel has been determined the machining tool cost of grinding and polishing operation to a great extent.The buffing wheel composition of open report is exemplified below:
Chinese patent publication number CN1260334A has proposed a kind of vitreous brick grinding and polishing prescription, it is characterized in that adopting vitrified bond, injects abrasive tool moulding behind the batch mixing pulping, uses the high temperature sintering finished product at last.Japan Patent JP2002-361562 discloses a kind of processing of stone grinding tool that is abrasive particle with white fused alumina micro mist and Cr, has also adopted sintering process.The sintering process of these grinding tools makes grinding tool manufacturing process complexity, and manufacturing cost improves.Chinese patent publication number CN1016892A has proposed a kind of stone grinding or composition for use in polishing and manufacture method thereof, forms main the use by abrasive material and bond and chemical grinding or polishing oxide lead oxide, oxalic acid of polishing part.Be applicable to that mainly main component is the polishing of the materials such as marble of calcium carbonate.Chinese patent publication number CN1275601A proposes a kind of grinding tool of crystallized glass, relates generally to the manufacturing process of corase grind grinding tool, is main target to improve grinding productivity ratio.Chinese patent publication number CN1387976A has proposed a kind of stone material grinding tool that contains poultry hair, graphitic lubricant and rare earth metal and oxide, and the polishing stone material is obtained higher glossiness.
Summary of the invention
The objective of the invention is the polishing process characteristics at brokenization brick, a kind of composition of vitreous brick buffing wheel is provided, this emery wheel has high polishing efficiency and polishing glossiness.
The invention provides a kind of composition that is used for vitreous brick buffing wheel, it contains grinding abrasive material, binding agent and auxiliary packing; Adopt polishing powder and carborundum as the grinding abrasive material, magnesia cement and novolac resin are as binding agent, and rare earth and oxide thereof, stearic acid, precipitated calcium carbonate are as auxiliary packing.It is as follows that it forms the percentage by weight ratio:
Component ratio (percentage by weight %)
MgO 32-45
MgCl
2 40-46
Phenolic resins 1.5-5
SiC 7-12
Al
2O
3 1.8-7.2
Precipitated calcium carbonate 1.3-4
Stearic acid 0.3-0.8
Rare earth and oxide 0.5-2.0 thereof
The present invention adopts magnesia cement as binding agent, because our experimental study shows that its technology is simple, cheap and have certain intensity simultaneously, can reach good polishing effect.
The present invention adopts the bond strength of novolac resin raising magnesia cement, increases the elasticity of grinding tool simultaneously, reduces polish temperature and brings the possibility on burn vitreous brick surface thus.
The present invention is also adding precipitated calcium carbonate and stearic acid aspect raising emery wheel mechanical performance and the self-sharpening energy.
The present invention adopts SiC and Al
2O
3As polish abrasive.The a small amount of polishing scratch that utilizes the good cutting power of SiC further correct grinding to be stayed is removed; Simultaneously, Al
2O
3The micro-cutting effect of abrasive material; after making that polishing is processed; vitreous brick surface is made up of pit (pore), flat surfaces and trickle plasticity groove etc.; the crystal glassy surface exposes; add the specific physical chemical action that interpolation rare earth and oxide cmp emery wheel thereof bring; make grinding skin smooth, glossiness improves.Our experimental study shows, does not generate any new structure of matter or polished film, SiC, Al at polished surface
2O
3With the mechanical micro-cutting of rare earth and oxide cmp thereof and physics chemical action be the main cause that vitreous brick surface obtains glossiness.
The manufacture method of emery wheel of the present invention is as follows: at first with abrasive material SiC, Al
2O
3, rare earth and oxide, precipitated calcium carbonate, stearic acid, phenolic resins and magnesia (MgO) stir together, adds MgCl again
2, the material that will stir again at last is poured in the plastics mould, and the demoulding after 3-4 hour can be used in maintenance 12-15 days.The removal of contamination that must sieve such as abrasive material and MgO.MgCl
2Answer removal of contamination after the dissolving, and before stirring, stir well even.
MgO/MgCl
2, ratio should suitably adjust according to the spice situation, guarantee to stir evenly moulding of material, but the proportion of composing scope can not exceed above-mentioned scope, to guarantee enough grinding tool intensity and performance.Simultaneously, throwing preceding vitreous brick glossiness should be more than 20.
The invention has the advantages that: it is fast that low price, manufacturing process are simply, glossiness improves speed, the gloss longer duration, and grinding temperature is low simultaneously can not cause workpiece to break.
The specific embodiment
Further specify the present invention below by some representational example, but do not limit the scope of the invention.In following examples, except as otherwise noted, otherwise all parts, ratio and percentage number average are by weight.
Embodiment 1:
At first with 8.2 parts of abrasive material SiC (granularity 1.5-2.5 μ m), Al
2O
3(granularity 28-40 μ m) 8.5, rare earth and 0.5 part of oxide thereof, 1.4 parts of precipitated calcium carbonates (granularity 90 μ m are following), 0.5 part of stearic acid, 3 parts of phenol-formaldehyde resin powders (granularity 50 μ m are following) and magnesia (MgO) stir for 33.4 parts together, add MgCl again
246 parts.The last material that will stir again is poured in the plastics mould, and the demoulding after 3-4 hour can be used in maintenance 12-15 days.More than polishing vitreous brick glossiness 80 degree on the tinuous production.
Embodiment 2:
At first with 11 parts of abrasive material SiC (granularity 1.5-2.5 μ m), Al
2O
3(granularity 28-40 μ m50%; Granularity 2.5-1.5 μ m50%; ) 6 parts, rare earth and 1.0 parts of oxides, precipitated calcium carbonate (granularity 90 μ m are following) 2,0.6 part of stearic acid, 4 parts of phenol-formaldehyde resin powders (granularity 50 μ m are following) and 32.4 parts of stirrings together of magnesia (MgO), add MgCl again
243 parts.The last material that will stir again is poured in the plastics mould, and the demoulding after 3-4 hour can be used in maintenance 12-15 days.More than polishing vitreous brick glossiness 82 degree on the tinuous production of ordinary production.
Embodiment 3:
At first with 9 parts of abrasive material SiC (granularity 1.5-2.5 μ m), Al
2O
3(granularity 28-40 μ m30%; Granularity 2.5-1.5 μ m70%; ) 8 parts, rare earth and 1.0 parts of oxides, 1 part of precipitated calcium carbonate (granularity 90 μ m are following), 0.3 part of stearic acid, (50% powdery is below the granularity 50 μ m for phenolic resins; 50% liquid resin) 3 parts and 33.8 parts of stirrings together of magnesia (MgO) add MgCl again
243.9 part.The last material that will stir again is poured in the plastics mould, and the demoulding after 3-4 hour can be used in maintenance 12-15 days.More than polishing vitreous brick glossiness 85 degree on the tinuous production of ordinary production.
Claims (1)
1. the composition of a vitreous brick buffing wheel, comprise grinding abrasive material, binding agent and auxiliary packing, it is characterized in that above-mentioned grinding abrasive material adopts polishing powder and carborundum, above-mentioned binding agent adopts magnesia cement and novolac resin, above-mentioned auxiliary packing employing rare earth and oxide thereof, stearic acid, precipitated calcium carbonate; It is as follows that it forms the percentage by weight ratio:
Weight percentages of components
MgO 36-45
MgCl
2 40-46
Novolac resin 1.5-5
SiC 7-12
Al
2O
3 5-9
Precipitated calcium carbonate 1.3-4
Stearic acid 0.3-0.8
Rare earth and oxide 0.5-2.0 thereof