CN1597342A - Gold porcelain technology - Google Patents
Gold porcelain technology Download PDFInfo
- Publication number
- CN1597342A CN1597342A CN 200410020325 CN200410020325A CN1597342A CN 1597342 A CN1597342 A CN 1597342A CN 200410020325 CN200410020325 CN 200410020325 CN 200410020325 A CN200410020325 A CN 200410020325A CN 1597342 A CN1597342 A CN 1597342A
- Authority
- CN
- China
- Prior art keywords
- filigree
- stove
- sintering
- gold
- pattern
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Gold-like porcelain as special ornaments is products by: making formworks, binding patterned stainless steel or brass wires onto them, enameling with pigments, firing in a common furnace at 550-700 deg.C for 20-30 minutes, cooling ni a thermal keeping furnace to the amtosphere, and polishing the patterned wires. It is a metal-porcelain combined handicraft in small sizes or a large picture on wall with lively appearance and stereo visual feeling.
Description
Technical field
The present invention relates to a kind of technology of making extraordinary ornament, relate in particular to a kind of pottery combines the form of expression with metal Gold porcelain technology.
Background technology
Because ware sturdy and durable is clean attractive in appearance, not perishable, cheap more than gold, silver, copper, jade, lacquerware again, and feed distribution is extremely wide, contain abundantly, thereby development is rapidly.Ceramic process mainly contains pugging, throwing, hand-pressing, sharp base, texturing, glazing, firing and color.The representation style of pottery is plane Freehandhand-drawing, relief color-painting, applique, color glaze, pearl color effect.Ceramic industry for a long time thirsts for solving metal with the ceramic form of expression that combines but fail all the time to succeed always.
Summary of the invention
The object of the invention aims to provide a kind of Gold porcelain technology, has solved the metal and the ceramic form of expression that combines, and its technology is simple, can make small-sized handicraft, also can make as large-scale handicrafts such as mural paintings.
For realizing purpose of the present invention, the technical scheme that is adopted is: a kind of Gold porcelain technology, comprise make base, haircuts, colouring, sintering, insulation, light handle, manufacturing process is as follows:
A. make base: make ceramic mold by the ceramic product demand;
B. haircuts: will be fixed on by the filigree that pattern is pinched with adhesive on the mold of pottery, according to the pattern needs, filigree can use stainless steel wire and brass wire on same goods;
C. colouring: use the recess of traditional cloisonne enamel enamel toner point on the mold surface according to layout;
D. sintering, insulation: only carry out once sinteredly in the ordinary sinter stove, sintering temperature is 550 ℃-700 ℃, comes out of the stove after 20-30 minute, reduces to normal temperature naturally from 550 ℃-700 ℃ again in holding furnace and comes out of the stove;
E. light is handled: only filigree is carried out light and handle, adopt small-sized hand mill corundum wheel corase grind, antioxidizing paint is brushed in polishing wheel polishing back.
Described adhesive adopts latex.
Described antioxidizing paint adopts Yongming lacquer.
Described filigree can use stainless steel wire or brass wire separately according to pattern.
The invention has the beneficial effects as follows that solved ceramic industry thirsts for the metal and the ceramic form of expression that combines that solve always.Its technology is simple, and sintering only needs once can finish, and only needs the polishing filigree, and the increasing of the making scope of its product, has both gone for the making of small-sized handicraft such as vase, disk, three-dimensional personage or animal, also can make mural painting on the large size ceramic tire.Pattern on the goods is life-like, third dimension is strong.
The specific embodiment
Further specify the specific embodiment of the invention below in conjunction with embodiment.
Embodiment 1
A kind of Gold porcelain technology, comprise make base, haircuts, colouring, sintering, insulation, light handle, manufacturing process is as follows:
1, make base: ceramic material is made molds such as ceramic wafer, dish or bottle by product demand;
2, haircuts: will be fixed on by the filigree that pattern is pinched with latex on the mold of pottery, according to the pattern needs, filigree can use stainless steel wire and brass wire on same goods, also can use stainless steel wire or brass wire separately;
3, colouring: use the recess of traditional cloisonne enamel enamel frit point on the mold surface according to layout;
4, sintering, insulation: sintering in the ordinary sinter stove, sintering temperature are 550 ℃, come out of the stove in 20 minutes, reduce to normal temperature naturally from 550 ℃ again in holding furnace and come out of the stove;
5, light is handled: only filigree is carried out light and handle, adopt small-sized hand mill corundum wheel corase grind, antioxidizing paint is brushed in polishing wheel polishing back, and coating can use Yongming lacquer.
Embodiment 2
A kind of Gold porcelain technology, comprise make base, haircuts, colouring, sintering, insulation, light handle, manufacturing process is as follows:
A. make base: ceramic material is made molds such as ceramic wafer, dish or bottle by product demand;
B. haircuts: will be fixed on by the filigree that pattern is pinched with adhesive on the mold of pottery, according to the pattern needs, filigree can use stainless steel wire and brass wire on same goods;
C. colouring: use the recess of traditional cloisonne enamel enamel toner point on the mold surface according to layout;
D. sintering, insulation: only carry out once sinteredly in the ordinary sinter stove, sintering temperature is 620 ℃, comes out of the stove in 25 minutes, reduces to normal temperature naturally from 620 ℃ again in holding furnace and comes out of the stove.
E. light is handled: only filigree is carried out light and handle, adopt small-sized hand mill corundum wheel corase grind, antioxidizing paint is brushed in polishing wheel polishing back.
Embodiment 3
A kind of Gold porcelain technology, comprise make base, haircuts, colouring, sintering, insulation, light handle, manufacturing process is as follows:
A. make base: ceramic material is made molds such as ceramic wafer, dish or bottle by product demand;
B. haircuts: will be fixed on by the filigree that pattern is pinched with adhesive on the mold of pottery, according to the pattern needs, filigree can use stainless steel wire and brass wire on same goods;
C. colouring: use the recess of traditional cloisonne enamel enamel toner point on the mold surface according to layout;
D. sintering, insulation: only carry out once sinteredly in the ordinary sinter stove, the sintering temperature of its sintered heat insulating operation is 700 ℃, comes out of the stove in 30 minutes, reduces to normal temperature naturally from 700 ℃ again in holding furnace and comes out of the stove.
E. light is handled: only filigree is carried out light and handle, adopt small-sized hand mill corundum wheel corase grind, antioxidizing paint is brushed in polishing wheel polishing back.
Adopt process of the present invention to go for also can on the large size ceramic tire, making mural painting as vase, disk, three-dimensional personage or small-sized handicraft such as animal, wall hanging.
The above only is preferred embodiment of the present invention, is not structure of the present invention is done any pro forma restriction.Every foundation technical spirit of the present invention all still belongs in the scope of technical scheme of the present invention any simple modification, equivalent variations and modification that above embodiment did.
Claims (4)
1, a kind of Gold porcelain technology, comprise make base, haircuts, colouring, sintering, insulation, light handle, manufacturing process is as follows:
A. make base: make ceramic mold by the ceramic product demand;
B. haircuts: will be fixed on by the filigree that pattern is pinched with adhesive on the mold of pottery, according to the pattern needs, filigree can use stainless steel wire and brass wire on same goods;
C. colouring: use the recess of traditional cloisonne enamel enamel toner point on the mold surface according to layout;
D. sintering, insulation: only carry out once sinteredly in the ordinary sinter stove, sintering temperature is 550 ℃-700 ℃, comes out of the stove after 20-30 minute, reduces to normal temperature naturally from 550 ℃-700 ℃ again in holding furnace and comes out of the stove;
E. light is handled: only filigree is carried out light and handle, adopt small-sized hand mill corundum wheel corase grind, antioxidizing paint is brushed in polishing wheel polishing back.
2, Gold porcelain technology according to claim 1 is characterized in that: described adhesive adopts latex.
3, Gold porcelain technology according to claim 1 is characterized in that: described antioxidizing paint adopts Yongming lacquer.
4, Gold porcelain technology according to claim 1 is characterized in that: filigree can use stainless steel wire or brass wire separately according to pattern.