CN1593781A - Unifilar tungsten arc spray equipment - Google Patents
Unifilar tungsten arc spray equipment Download PDFInfo
- Publication number
- CN1593781A CN1593781A CN 200410043643 CN200410043643A CN1593781A CN 1593781 A CN1593781 A CN 1593781A CN 200410043643 CN200410043643 CN 200410043643 CN 200410043643 A CN200410043643 A CN 200410043643A CN 1593781 A CN1593781 A CN 1593781A
- Authority
- CN
- China
- Prior art keywords
- wire
- spraying
- spray
- compressed air
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a kind of arc spray device. The existing spraying devices have disadvantage of poor spraying quality. An air- compressed tube is fixed at the inner of the device's body, and it connects to negative pole of the electric source and the metal gun spout. Above center shaft of the gun body is a metal tube .At the place where the metal tube is near to the gun spout is a conducting spout .The invention is used for surface modifying of new workpiece .It can prolong the service life of the machine save material and energy , and therefore cut down the cost .
Description
Technical field:
The invention belongs to the invention of a kind of arc spraying technology, particularly a kind of spraying equipment in the Surface Engineering subject.
Background technology:
Spraying technology is a significant surfaces modification technology in the Surface Engineering, and plasma spray technology is by thermals source such as flame, electric arc, plasma or light, and certain wire or dusty material are heated to fusing or molten condition, and quickens to spray to matrix surface formation coating.Can spray any matrix material on this engineering philosophy, can select for use various materials (conduction, non-conductive, meltable, refractory material are as ferrous metal, non-ferrous metal, alloy, pottery, cermet, plastics, organic matter, compound etc.) as coating material.Can strengthen or regenerate material surfaceization, can realize high temperature resistant, anticorrosive, wear-resistant, shock resistance, anti-oxidant, improve electric conductivity, insulating properties, thermal boundary etc. and be coated with layer function.Can prepare dissimilar metal coating, composite coating, composite material coating, gradient coating, thicken coating, soft basic hard point coating etc.Be applicable to the modification on new product structural member surface, and the reparation of waste product.Thermal spraying has is heated little indeformablely to workpiece, do not change the internal performance of workpiece, can spray the workpiece of different shape, and its coating layer thickness can be controlled freely, the coating material wide accommodation that can spray, characteristics such as spraying coating process is simple, easy to operate, efficient height.Plasma spray technology is widely used in space flight, aviation, machine-building, power, atomic energy, metallurgy, chemical industry, oil, coal, railway, shipbuilding, communications and transportation, light industry, weaving, electronics, instrument manufacturing, material science, building, water conservancy, power station, environmental protection or the like nearly all industrial circle through developing rapidly in recent years.It has not only obtained rational application in the new product manufacturing industry, and is also playing a part very importantly aspect the waste product repairing and reusing, and the support of new technology, new material also is provided for development of high-tech.
Electric arc spraying is one of them in the plasma spray technology, compares with other spraying method, and its distinguishing feature is that equipment is simple, and production cost is low, operation at the scene, and operation is convenient, grasps applied range easily.Existing arc spraying apparatus is to adopt mariages (Spray Wire) as two electrodes, is angle between two, contacts by wire feed formation short circuit and sets up electric arc, make two fusings simultaneously, by compressed air molten metal is atomized accelerating jetting to workpiece, form coating, as shown in Figure 1.But because spraying wire as electrode, requires good conductivity, thus can not be used for the preparation of arc spraying coating to electrically non-conductive material, so limited application as special materials such as potteries.The soft silk of flame material spray equipment is that the employing oxy-acetylene is a thermal source, spraying soft silk material is the medicine core tubular filament material that the low fluorine point chemical industry material of a kind of usefulness wraps up, atomize accelerating jetting to workpiece by compressed air, form coating, as shown in Figure 2, this device can spray the soft silk of ceramic tubular material, but because flame temperature is lower, the ceramic coating of preparation is of low quality.Through on-the-spot investigation and investigation, and look into newly by international online science and technology, technology related to the present invention situation at home and abroad is as follows: at present, the application of arc spraying apparatus is very general both at home and abroad, application to the spraying of tubular metal silk is also many, but also is not used in the report of ceramic medicine core tubular filament material arc spraying technology aspect at present.There are the application of the soft silk of flame pottery material spraying technology in France and Russia, and China has also introduced this equipment and relevant spraying technology successively in recent years.The higher plasma spraying technology of cost is still adopted in the preparation of ceramic coating at present.
Summary of the invention:
The object of the present invention is to provide a kind of spraying scope wide, the monofilament tungsten electrode arc spray equipment that spray efficiency is high, it comprises air compressor machine 1, spraying source 2, wire-feed motor 3, paint spray gun 4, described paint spray gun 4 comprises housing 4-1, handle 4-2, on the inwall of described housing 4-1, be connected with compressed air hose 4-3, the terminal of compressed air hose 4-3 is connected with power cathode with air compressor machine 1 simultaneously, on the tube wall that is positioned at housing 4-1 inside of compressed air hose, be provided with pore 4-3-1, the front end of compressed air hose 4-3 is connected with metal rifle mouth 4-4, described metal rifle mouth 4-4 is connected with tungsten electrode 4-5 simultaneously, tungsten electrode 4-5 is three, three tungsten electrode 4-5 are evenly distributed on rifle mouth 4-4 is circumferential, also are provided with atomizing compressed air apertures 4-7 on described rifle mouth 4-4; The central shaft of housing 4-1 is to being provided with metal tube 4-6, and metal tube 4-6 connects positive source, is provided with Spray Wire 5 in metal tube 4-6, is provided with the ignition tip 4-8 that fully contacts with Spray Wire 5 at metal tube 4-6 near rifle mouth 4-4 position.Apparatus of the present invention are mainly used in carries out surface modification to new workpiece, to improve the service life of product, workpiece overproof or that scrap is carried out the surface to be repaired, realize twice laid, economize on resources and the energy, the purpose that reduces cost, apparatus of the present invention have following advantage: (1) is compared with the soft silk of flame (about 3000 ℃) spraying tubular ceramic medicine core material, have the high characteristics of electric arc (about 6000 ℃) spraying flame stream temperature, in spraying process, help fusing and quickening fusion speed, can improve Bond Strength of Coating significantly sprayed on material, the quality of spray efficiency and assurance coating.Use flame-spraying Al
2O
3The soft silk of tubular ceramic medicine core material anchoring strength of coating is between 0.1MPa~0.3MPa, and the anchoring strength of coating after employing apparatus of the present invention spray is between 5MPa~10MPa, and the coating densification, and spray efficiency can improve 0.5~0.7 times.(2) spraying of adopting tungsten electrode of the present invention to melt the soft silk of single tubular powder core material, arc stability, it is little to splash, sprayed on material apposition rate height, the molten drop uniform particles of spraying wire fusing helps the atomizing effect that sprays, coating quality height.The apposition rate of conventional electric arc spraying is 50~55%, and the apposition rate of the soft silk of tubular powder core material flame-spraying is 40~50%, and the spraying apposition rate that tungsten electrode melts the soft silk of single tubular powder core material can reach more than 60%.(3) owing to adopt the individual thread spraying method, realize the wire feeding mode variation easily, as push away silk, wire drawing, push away-the wire drawing mode can both realize easily.Wire feed equipment is oversimplified, and is convenient to regulate wire feed rate, guarantees the stability of wire feed easily, thereby has guaranteed the smooth combustion of electric arc.(4) apparatus of the present invention can not only spray the soft silk of tubular powder core material, and are applicable to the spraying of real core metal silk material.(5) compare with solid core wire material, under the condition of same sectional area, the spraying energy needed of medicine core-wire material is little, so under the condition of equal spraying energy, it is thicker that the diameter of single medicine core-wire material can be selected, thereby improved spray efficiency.Such as, under the technological specification condition of spraying Φ 2mm solid core wire material, can spray the medicine core-wire material of Φ 3mm same type of material.(6) electric arc spraying be two silks at an angle as consumable electrode, the size of general electric current is to regulate according to the thickness and the material kind of silk, the adjustable range of electric current is smaller, often is subjected to certain restriction.This spray equipment is that central shaft is to wire feeding mode, as shown in Figure 4, three tungsten electrodes be trapped among equably silk around, Spray Wire is fusing in the middle of electric arc, the size adjustment wide ranges of electric current, so this version can guarantee the smooth combustion of electric arc well and guarantee that spraying wire melts fully, can improve spray efficiency and atomizing effect significantly.(7) lance body structure as shown in Figure 4, the compressed-air actuated outlet that atomizes is an open grain structure, give vent to anger and flow to parallel and surround axial spraying wire, that is to say that atomization gas just in time directly blows the sprayed on material of fusing, form the parallel atomizing effect of bushing type, can gather spraying flame stream effectively, can not only improve spraying rate, improve the apposition rate of sprayed on material, and improved the quality of coating significantly.(8) present device is simple, and volume is little, and is in light weight, and the spray gun lead is few, and wire feeder is simple, and is easy to operate, is convenient to indoor or field operation.
Description of drawings:
Fig. 1 is an electric arc spraying theory structure schematic diagram, Fig. 2 is soft silk material flame-spraying theory structure schematic diagram, and Fig. 3 is a structural representation of the present invention, and Fig. 4 is the structural representation of monofilament tungsten electrode paint spray gun 4, Fig. 5 is the wire-feed motor structural representation, and Fig. 6 is the B-B cutaway view of Fig. 5.
The specific embodiment:
The specific embodiment one: principle of the present invention is to adopt tungsten electrode (connecing power cathode) and single Spray Wire (connecing positive source), set up electric arc by high-frequency arc strike, make the Spray Wire fusing, by a kind of novel arc spraying apparatus of compressed air atomizing accelerating jetting to the workpiece, Spray Wire of the present invention can be the real core silk of metal, it also can be medicine core tubular filament, because Arc Temperature doubles than the temperature of flame, so apparatus of the present invention are specially adapted to the spraying (metal skin parcel ceramic powder) of ceramic medicine core tubular filament, thereby realized adopting low-cost, the arc spray process of high-performance coating quality prepares the purpose of ceramic coating.The inventive system comprises air compressor machine 1, spraying source 2, wire-feed motor 3, paint spray gun 4, described paint spray gun 4 comprises housing 4-1, handle 4-2, on the inwall of described housing 4-1, be connected with compressed air hose 4-3, the terminal of compressed air hose 4-3 is connected with power cathode with air compressor machine 1 simultaneously, on the tube wall that is positioned at housing 4-1 inside of compressed air hose, be provided with pore 4-3-1, the front end of compressed air hose 4-3 is connected with metal rifle mouth 4-4, described metal rifle mouth 4-4 is connected with tungsten electrode 4-5 simultaneously, tungsten electrode 4-5 is three, three tungsten electrode 4-5 are evenly distributed on rifle mouth 4-4 is circumferential, also are provided with atomizing compressed air apertures 4-7 on described rifle mouth 4-4; The central shaft of housing 4-1 is to being provided with metal tube 4-6, and metal tube 4-6 connects positive source, is provided with Spray Wire 5 in metal tube 4-6, is provided with the ignition tip 4-8 that fully contacts with Spray Wire 5 at metal tube 4-6 near rifle mouth 4-4 position.The key technology of paint spray gun of the present invention is in the structure of rifle head, it adopts axial wire feeding mode, to be the thick tungsten electrode of Φ 4mm build arc by 60 ° of angles are equidistant with the Spray Wire periphery for three diameters, compressed air by porous along the parallel atomizing of electric arc direction and quicken spraying.Spray Wire, compressed air line, positive source cable combination are a cable, adopt the loose joint joint to connect spray gun and wire-feed motor, and lance body structure is simple, and is in light weight, easy accessibility.
Described wire-feed motor 3 is single wire-feed motor, it comprises body 3-1, in body 3-1, be provided with buncher 3-2, buncher 3-2 is connected with driving wheel 3-4 by gearbox 3-3, the top of driving wheel 3-4 is provided with follower 3-5, and follower 3-5 is fixed on that wire feed rolls compressor arm 3-6 goes up and regulates distance between follower 3-5 and the driving wheel 3-4 by wire feed rolls compressor arm 3-6.
Common wire-feed motor need be sent two rhizoids simultaneously, generally requires the feed rate of two rhizoids identical.Wire-feed motor of the present invention is only required the function of single wire feed, so drive motors power is little, overall structure is simple, volume is little, realizes wire drawing easily, pushes away silk or push away-the wire feed structure of wire drawing type, and wire feed rolls is according to the thickness with silk, arbitrarily dismounting transposing easily, its structure is seen Fig. 5, shown in Figure 6.
Use the parameter of device of the present invention in process to be set at: spray voltage 20V~40V; Compressed-air actuated gas pressure 0.6MPa~0.85MPa; Blow force of arc electric current 0A~30A; Spraying current 60A~300A; Wire feed rate 0.2~5m/min; Spraying wire diameter of phi 0.8mm~Φ 5mm.
The specific embodiment two: the present embodiment spraying process is as follows: 1. surface of the work alligatoring: will be by the clean degreasing of surface clean of spraying workpiece, and machined into or polish off defective and fatigue layer is carried out surface coarsening with sandblast then.2. online: the specific embodiment one described paint spray gun, wire-feed motor, air compressor machine are connected with spraying source, Spray Wire is penetrated wire-feed motor and send in the paint spray gun, see shown in Figure 3.3. adjusting spraying parameter: mix up atomizing compressed air pressure and flow in advance, spray voltage, spraying current, striking electric current, wire feed rate.The material kind of the adjusting of this technological parameter and spraying wire, the format diameter size of spraying wire is relevant, varying in size of material and diameter, pairing technological parameter is also different: the selected spraying wire of present embodiment is the tubular powder core-wire material, the material of coating is Q235, the material of medicine core is the NiCrBSi powder, the format diameter of silk material is Φ 3.0mm, the compressed-air actuated pressure of being regulated is 0.6MPa~0.8MPa, compressed-air actuated gas flow size is decided with the atomizing effect of spraying flame stream, flow is too big or too little, spraying arc flame stream all can be dispersed chap and not concentrate, when being transferred to the thinnest state of spraying arc flame stream, compressed-air actuated gas flow be the best.The adjusting spray voltage is 30V, and spraying current is 120A, and the blow force of arc electric current is 10A, and wire feed rate is 1m/min.4. being installed on the special fixture by the spraying workpiece, if spraying axis products, workpiece is installed on the turntable, the specific embodiment one described paint spray gun is installed on the automatic walking gun rack, regulate the desired rotation and the speed of travel in the Workpiece painting process, regulate muzzle and the distance that is sprayed the position, realize spraying automatically.The size of workpiece rotation rotating speed and the speed of travel and spraying workpiece external diameter is relevant with the thickness of coating, and for the big workpiece of external diameter with when requiring once to spray thick coating, the rotating speed that needs and the speed of travel are wanted slowly.As external diameter is Φ 200mm, and the thickness of a spray-on coating is 0.3mm, and rotating speed is 80~100 rev/mins, and the speed of travel is 20~30mm/ branch, muzzle with by the spraying position apart from 150mm.5. the preparation of spraying and coating: start Work turning table, workpiece rotates or walking, opens the compressed air valve, starts power supply, and the wire feed striking sprays.
The specific embodiment three: present embodiment is the spraying process of bent axle:
1. condition: sprayed product is the imported auto bent axle of wearing and tearing, and material is a spheroidal graphite cast-iron, and it is oval that maximum wearing depth 0.5mm, bent axle external diameter have been, needs resizing.
2. spraying coating process: earlier to the bent axle decontamination of deoiling, fatigue layer and ovality to the bent axle external diameter have been carried out grinding, sandblast alligatoring subsequently, bent axle is installed on has on the spinfunction crankshaft spraying dedicated, connected equipment, mix up the desired every technological parameter of spraying, spray voltage 25V; Compressed-air actuated gas pressure 0.65MPa; Blow force of arc electric current 10A; Spraying current 100A; Wire feed rate 1m/min; Spraying wire diameter of phi 1.5mm.Just the spraying of can starting shooting after everything is ready.
3. coating preparation: sprayed on material is selected homemade tubular powder core-wire material for use, and the material of coating is Q235, and the material of medicine core is self-fluxing nature NiCrBSi alloy 50%+Al
2O
3The mixed-powder of pottery 50%, the format diameter of silk material is Φ 3mm.Consider allowance, final coating layer thickness is 0.8mm.The mode of paint spray gun hand-manipulated is adopted in the preparation of coating.
4. coating processing: the bent axle after the spraying adopts the bent axle mill to shape.
5. quality and cost: the bent axle after the spraying is through using examination, and its life-span improves more than 3 times than new product.Spraying required cost is about 1/10 of new bent axle, aliquation does not in use take place fall any defective that piece etc. influences traffic safety.
The specific embodiment four: present embodiment is the spraying process of thermal power generation unit draught fan impeller sheet:
1. material: impeller blade is the new Q235 steel of changing.
2. surface preparation: because impeller blade is the new material of changing, so directly carry out the requirement that the sandblast alligatoring can be satisfied spraying.
3. sprayed on material: sprayed on material selects for use homemade medicine core-wire material as working lining, and a silk material diameter is 5mm, and a silk skin material is Q235, and medicine core matter is 30% self-fluxing nature nickel-base alloy+70%Al
2O
3The spraying powder.Prime coat material selection format diameter is the commercially available Ni5Al solid core wire material of Φ 2mm.
4. spraying coating process and parameter: adopt the specific embodiment one described paint spray gun, adopt spraying method hand-manipulated, on impeller blade, spray the coating of 0.1mm earlier with prime material, carry out the working lining spraying then, total coating thickness 1.1mm, the coating after the spraying is not done any processing and is handled.It is the most concentrated for well that spray voltage 32V, spraying current 210A, compressed air gas pressure 0.8MPa, gas flow are transferred to spraying flame stream, blow force of arc electric current 15A, wire feed rate 1.2m/min.
5. detect the spraying result: the anti-300 ℃ of long term high temperature oxidations of impeller, anti-dust erosive wear, coating layer thickness 〉=1mm does not in use have coating shedding.
The specific embodiment five: present embodiment is for changing the cylinder iron anti-aluminium of the crucible preparation process of melting erosion resisting coating of aluminium:
1. condition: this product is the cast-iron pot by cast form, uses under 720 ℃ of constant temperatures, is used to store the container of cast aluminum liquid.Because producing heat release with metal under hot conditions, aluminium melts the erosion reaction, can not directly use, so people are adopting the way of daub to prevent the erosion of melting of aluminium liquid always, it is longer that this method is smeared the oven dry cycle, and service life is low, and needing often stops work smears, and only just scraps in 20 days but at most also surpass service life, and coating is very easy to come off and sneaks in the aluminium liquid, causes whole pot aluminium liquid to scrap.Applying unit is badly in need of solving this difficult problem.
2. spraying coating process: adopt device of the present invention, select homemade ceramic medicine core Spray Wire for use, a silk material diameter is 5mm, and a silk skin material is Al, and medicine core matter is 13%TiO
2+ 87%Al
2O
3The spraying powder.Adopt spraying method hand-manipulated, spray voltage is 40V; Compressed-air actuated gas pressure is 0.85MPa; The blow force of arc electric current is 30A; Spraying current is 300A; Wire feed rate is 5m/min; The spraying wire diameter of phi is 5mm.Do not feel secure, directly spray working lining, about coating layer thickness 0.6mm, the coating after the spraying is not done any processing and is handled.
3. testing result: the crucible after the spraying reaches more than four months in continuous service life, and the position of melting erosion is that the casting sand hole defective is caused, and other position is still excellent.
The present invention has not only filled up a blank in the technical field of hot, and can widen the range of application of ceramic material significantly, therefore has far-reaching social effect and huge economic benefit.
Claims (2)
1, a kind of monofilament tungsten electrode arc spray equipment, it comprises air compressor machine (1), spraying source (2), wire-feed motor (3), paint spray gun (4), it is characterized in that described paint spray gun (4) comprises housing (4-1), handle (4-2), on the inwall of described housing (4-1), be connected with compressed air hose (4-3), the terminal of compressed air hose (4-3) is connected with power cathode with air compressor machine (1) simultaneously, be provided with pore (4-3-1) being positioned on the inner tube wall of housing (4-1) of compressed air hose, the front end of compressed air hose (4-3) is connected with metal rifle mouth (4-4), described metal rifle mouth (4-4) is connected with tungsten electrode (4-5) simultaneously, tungsten electrode (4-5) is three, three tungsten electrodes (4-5) are evenly distributed on rifle mouth (4-4) is circumferential, also are provided with atomizing compressed air apertures (4-7) on described rifle mouth (4-4); The central shaft of housing (4-1) is to being provided with metal tube (4-6), metal tube (4-6) connects positive source, in metal tube (4-6), be provided with Spray Wire (5), be provided with the ignition tip (4-8) that fully contacts with Spray Wire (5) near rifle mouth (4-4) position at metal tube (4-6).
2, monofilament tungsten electrode arc spray equipment according to claim 1, it is characterized in that described wire-feed motor (3) is single wire-feed motor, it comprises body (3-1), in body (3-1), be provided with buncher (3-2), buncher (3-2) is connected with driving wheel (3-4) by gearbox (3-3), the top of driving wheel (3-4) is provided with follower (3-5), and follower (3-5) is fixed on that wire feed rolls compressor arm (3-6) is gone up and regulates distance between follower (3-5) and the driving wheel (3-4) by wire feed rolls compressor arm (3-6).