CN1563169A - Agglomerate of weeding mulching film - Google Patents
Agglomerate of weeding mulching film Download PDFInfo
- Publication number
- CN1563169A CN1563169A CN 200410024009 CN200410024009A CN1563169A CN 1563169 A CN1563169 A CN 1563169A CN 200410024009 CN200410024009 CN 200410024009 CN 200410024009 A CN200410024009 A CN 200410024009A CN 1563169 A CN1563169 A CN 1563169A
- Authority
- CN
- China
- Prior art keywords
- weedicide
- polyethylene
- mulch film
- master batch
- kilograms
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A master batch consisting of polyethylene, weedcide and emulsifier is prepared by mixing polyethylene with weedcide uniformly, adding emulsifier on the mixture, extruding pelletizing and drying. The prepared masterbatch can be used in blow-moulding process directly to form weeding mulch film.
Description
Technical field
The present invention relates to weed removal mulch film, is a kind of master batch of making weed removal mulch film.
Background technology
Because weed removal mulch film has more advantage, by China's agricultural widespread use.Making weed removal mulch film at present all is to begin until producing the mulch film product from proportion of raw materials, because the characteristics of its manufacturing process, it generally is liquid making the raw material that enters in the blowing ground membrane process, therefore its deficiency of existing is: production cost height, because the consumption of weedicide is unreasonable, in expressing technique, very easily skid, cause and extrude instability, make the became uneven of film, and weedicide is in volatile contaminate environment etc. in the liquid state always.
Summary of the invention
The present invention seeks to, a kind of weed removal mulch film master batch is provided, it provides a kind of granulated product for the production of weed removal mulch film, can directly product of the present invention be used for blowing ground film production process, thereby avoided the production cost height that causes because of liquid formulation, the expressing technique mulch film became uneven that skids, problem such as weedicide is volatile.
The present invention is in order to finish goal of the invention, following technical scheme is provided: it comprises following by weight percentage: polyethylene 20-70%, weedicide 10-30%, emulsifying agent 1-3%, polyethylene and weedicide are mixed, add emulsifier mix again and stir, with forcing machine extruding pelletization drying.The component of described weight percent is: mineral filler 35-60%.The component of described weight percent is: plasticizing stabilizer 0.1-0.4%, do not have material filler 35-60%.The component of its weight percent is: polyethylene 25-50%, weedicide 10-25%, emulsifying agent 1-3%.Mineral filler is pulverized standby, again polyethylene and weedicide are mixed standby, then emulsifying agent, mineral filler and plasticizing stabilizer are inserted stir in polyethylene and the weedicide mixed solution after, with forcing machine extruding pelletization drying.Stepless filler is ground into micron or nano level standby, again polyethylene and weedicide are mixed standby, then emulsifying agent, mineral filler and plasticizing stabilizer are inserted stir in polyethylene and the weedicide mixed solution after, usefulness forcing machine extruding pelletization drying.
Weedicide of the present invention is acetochlor, Jin Douer and alachlor.Plasticizing stabilizer is epoxy soybean oil, epoxy fat.Described polyethylene is a new LDPE (film grade), linear low density polyethylene, high density polyethylene(HDPE).
Product of the present invention in pelletized form, can be used as the raw material of producing mulch film, directly use product of the present invention in the extrusioning blowing process, avoided the loss of volatilization, contaminate environment and the weedicide of weedicide, because the consumption of new LDPE (film grade) reduces, so production cost is low, the present invention is through repetition test, and its component is reasonable, the mulch film thickness of producing is even, and herbicidal effect is good, makes the production technique of mulch film simple, reduces production costs.
Embodiment
Technical solution of the present invention is not limited only to the embodiment of the invention, and extruding and pelletizing process of the present invention is a known technology.
1, get 70 kilograms of new LDPE (film grade)s, 28 kilograms of acetochlors, 2 kilograms in tensio-active agent is standby, and 28 kilograms of acetochlors and new LDPE (film grade) are mixed, and adds the tensio-active agent mixing and stirring then, makes granulated product with forcing machine extruding pelletization drying.
2, the line taking new LDPE (film grade) is 37 kilograms, 20 kilograms of acetochlors, 40 kilograms in lime carbonate, 0.3 kilogram of epoxy soybean oil, 2.7 kilograms of 2101 emulsifying agents are pulverized lime carbonate standby, earlier acetochlor are inserted mixing and stirring in the linear low density polyethylene, add crushed calcium carbonate, epoxy soybean oil and 2101 emulsifier mix again and stir, make granulated product with forcing machine extruding pelletization drying.
3, get 50 kilograms of high density polyethylene(HDPE)s, 15 kilograms of alachlors, 33 kilograms of talcum powder, 0.2 kilogram in epoxy fat, 500 1.8 kilograms of farming breasts are standby, and it is standby that talcum powder is ground into micron order, earlier alachlor inserted mixing and stirring in the high density polyethylene(HDPE), add micron order talcum powder, epoxy fat and 500 agricultural newborn mixing and stirring again, make granulated product with forcing machine extruding pelletization drying.
4, get 30 kilograms of new LDPE (film grade)s, gold all you 10 kilograms, 59 kilograms in lime carbonate, 1 kilogram of 2201 emulsifying agent, it is standby that Paris white is broken into nano level, with gold all you 10 kilograms with the new LDPE (film grade) mixing and stirring, add 2001 emulsifier mix then and stir, make granulated product with forcing machine extruding pelletization drying.
5, get 45 kilograms of new LDPE (film grade)s, gold all you 15 kilograms, 3 kilograms of 600 emulsifying agents, 37 kilograms of talcum powder, talcum powder is pulverized standby, with gold all you with the new LDPE (film grade) mixing and stirring, add 600 emulsifying agents, talcum powder mixing and stirring then, make granulated product with forcing machine extruding pelletization drying.
6, the line taking new LDPE (film grade) is 30 kilograms, 25 kilograms of acetochlors, 44 kilograms in lime carbonate, 1 kilogram of 2101 emulsifying agent, it is standby that Paris white is broken into nano level, earlier acetochlor is inserted mixing and stirring in the linear low density polyethylene, add nanometer grade calcium carbonate again and 2101 emulsifier mix stir, make granulated product with forcing machine extruding pelletization drying.
7, get 25 kilograms of new LDPE (film grade)s, gold all you 13 kilograms, 59 kilograms in lime carbonate, 2.6 kilograms of 2201 emulsifying agents, 0.4 kilogram in epoxy fat, it is standby that Paris white is broken into micron order, with gold all you with the new LDPE (film grade) mixing and stirring, add 2001 emulsifying agents, epoxy fat and micron order lime carbonate mixing and stirring then, make granulated product with forcing machine extruding pelletization drying.
8, get 52 kilograms of new LDPE (film grade)s, 14.8 kilograms of alachlors, 30 kilograms in lime carbonate, 3 kilograms of 2201 emulsifying agents, 0.2 kilogram in epoxy fat, it is standby that Paris white is broken into micron order, earlier alachlor inserted mixing and stirring in the new LDPE (film grade), add micron order lime carbonate, epoxy fat and 2201 emulsifier mix again and stir, make granulated product with forcing machine extruding pelletization drying.
Claims (6)
1, weed removal mulch film master batch, it is characterized in that: it comprises following by weight percentage: polyethylene 20-70%, weedicide 10-30%, and emulsifying agent 1-3% mixes polyethylene and weedicide, add emulsifier mix again and stir, with forcing machine extruding pelletization drying.
2, weed removal mulch film master batch according to claim 1, it is characterized in that: the component of described weight percent is: mineral filler 35-60%.
3, weed removal mulch film master batch according to claim 1, it is characterized in that: the component of described weight percent is: plasticizing stabilizer 0.1-0.4%, do not have material filler 35-60%.
4, weed removal mulch film master batch according to claim 1 and 2, it is characterized in that: the component of its weight percent is: polyethylene 25-50%, weedicide 10-25%, emulsifying agent 1-3%.
5, weed removal mulch film master batch according to claim 3, it is characterized in that: mineral filler is pulverized standby, mix polyethylene and weedicide standby again, then emulsifying agent, mineral filler and plasticizing stabilizer are inserted stir in polyethylene and the weedicide mixed solution after, with forcing machine extruding pelletization drying.
6, weed removal mulch film master batch according to claim 3, it is characterized in that: with stepless filler be ground into the micron or nano level standby, mix polyethylene and weedicide standby again, then emulsifying agent, mineral filler and plasticizing stabilizer are inserted stir in polyethylene and the weedicide mixed solution after, with forcing machine extruding pelletization drying.