CN1560173A - 车皮防冻液及其配制方法 - Google Patents
车皮防冻液及其配制方法 Download PDFInfo
- Publication number
- CN1560173A CN1560173A CNA2004100211831A CN200410021183A CN1560173A CN 1560173 A CN1560173 A CN 1560173A CN A2004100211831 A CNA2004100211831 A CN A2004100211831A CN 200410021183 A CN200410021183 A CN 200410021183A CN 1560173 A CN1560173 A CN 1560173A
- Authority
- CN
- China
- Prior art keywords
- railway carriage
- calcium chloride
- deicing fluid
- water
- chloride powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种车皮防冻液及其配制方法,该防冻液包括下列重量百分比的组分:无水氯化钙20~50%,乙醇8~10%,水40~70%,还可以加入1~2%的防锈剂亚硝酸钠。配制方法为:先往搅拌罐中加水,再加入无水氯化钙,进行搅拌至完全溶化,去除泡沫,再搅拌至温度为19℃~21℃,加入乙醇,再加入防锈剂,搅拌30分钟后结束。采用这种防冻液可以确保车皮在露天条件下10个小时之内不和含水散装物料相冻结,彻底解决了铁矿粉之类含水散装物料在寒冬的冻结问题,从而不必进解冻室解冻即可顺利卸车,节省了能源,缩短了车皮周转周期,减轻劳动强度,降低了运输成本。
Description
技术领域
本发明属于防冻制品领域,特别是一种车皮防冻液及其配制方法,适用于在寒冷季节和高寒地区用车皮运输散装物料的防冻。
背景技术
在严寒的冬季或严寒地带,用车皮装运含水的散装料,例如选矿的精矿粉、开采出的煤炭等,都会和车皮冻成一体,无法卸车,在卸车前必须进解冻室进行解冻,这不仅浪费大量的时间,而且还要消耗大量的能源,降低了车辆的使用效率,增加了运输成本,也会延误生产。如果有一种物质加到含水的散状料中或喷涂在装散状料的车皮上,能将冰点大幅度降低,防止散装含水物料与车皮冻结,这不仅将会节省大量能源,而且还会大幅度降低运输成本,加快车皮周转速度,促进生产发展。
发明内容
本发明的目的是提供一种能够降低散装物料中水分冰点的防止含水散状料冻结在车皮上的防冻液。
本发明的另一个目的是提供这种防冻液的配制方法。
按照本发明的车皮防冻液,包括下列重量百分比的组分:
无水氯化钙 20~50%
乙醇 8~10%
水 40~70%。
当将防冻液用于铁精矿之类易生锈的散装物料或使用铁制车皮时,可在配方中加入亚硝酸钠之类防锈剂,这时的防冻液重量百分比为:
无水氯化钙 20~50%
乙醇 8~10%
亚硝酸钠 1~2%
水 40~70%
按照本发明,所述的无水氯化钙可采用工业级无水氯化钙,乙醇可采用90%~96%的乙醇,水可采用自来水、河水或深井水。
配制本发明的车皮防冻液配制方法,包括下列步骤:
1)将重量百分比为40~70%的水注入搅拌罐中,
2)将按重量百分比为20~50%的无水氯化钙投入罐中,进行搅拌,直至全部溶解,
3)清除搅拌、溶解过程中所产生的泡沫,
4)继续搅拌以释放出无水氯化钙溶解时产生的热量,使溶液温度降至19℃~21℃,
5)加入重量百分比为8~10%的乙醇,搅拌均匀,制成车皮防冻液。
按照本发明车皮防冻液需要防锈时,其配制方法包括下列步骤:
1)将重量百分比为40~70%的水注入搅拌罐中,
2)将重量百分比为20~50%的无水氯化钙投入罐中,进行搅拌,直至全部溶解,
3)清除搅拌、溶解过程中所产生的泡沫,
4)继续搅拌以释放出无水氯化钙溶解时产生的热量,使溶液温度降至19℃~21℃,
5)加入重量百分比为8~10%的乙醇,搅拌均匀,
6)投入重量百分比为1~2%的亚硝酸钠搅拌30分钟后结束,制成具有防锈功能的车皮防冻液。
采用本发明的车皮防冻液在车皮静止状态下,用喷雾器在车皮的车底及四壁均匀喷洒一层防冻液。气温极低时,在装完车后在物料上喷洒一层防冻液,这样一来,物料不再冻结在车皮上,从而不必进解冻室解冻即可顺利卸车。
按照本发明的车皮防冻液,是一种多级单体+极性物-[大分子化合物]所形成的大分子化合物,其冰点可达-45℃。此化合物可与物料(例如铁矿粉)中的水份相结合,结合物的冰点仍可低于-42℃。在车皮上喷洒此防冻液后,使车皮表面与物料之间保持液动相,在10个小时内物料中的水份不会与车皮表面冻结,避免了翻卸车的困难。采用本发明的车皮防冻液,具有下列效果:
1)可免除重车进解冻室解冻,节约能源,并且可以解决解冻室能力不足导致车皮在厂内滞留时间过长的现象,加速车皮的周转速度。
2)可以解决因解冻不充分而导致卸车后车皮仍带料而出现二次冻结现象,同时避免了空车带料导致空车必须返回及过磅的过程,降低了运输成本,提高了车皮的利用率。
3)降低了装卸工人的劳动强度,节省了劳务费用,同时抑制了物料流失。
4)由于车皮不必进解冻室,从而避免了车皮因受到高温烘烤而导致转动部位的润滑油烧损现象。
具体实施方式
下面结合实例说明本发明的具体实施方式。
实施例1
按照本发明所述的车皮防冻液,由下列重量百分比组分所组成:
无水氯化钙(工业级) 30%
乙醇 (95%) 10%
水 60%,
其制备方法包括下列步骤:
1)将重量百分比为60%的水注入搅拌罐中,
2)将按重量百分比为30%的无水氯化钙投入罐中,进行搅拌,直至全部溶解,
3)清除搅拌、溶解过程中所产生的泡沫,
4)继续搅拌以释放出无水氯化钙溶解时产生的热量,使溶液温度降至19℃~21℃,
5)加入重量百分比为10%的乙醇,搅拌均匀,即制成车皮防冻液。
实施例2
当防冻液需要用于易生锈的物料和车皮时,可以在组分中添加防锈剂,例如亚硝酸钠,这种车皮防冻液的重量百分比组成为:
无水氯化钙 25%
乙醇 9%
亚硝酸钠 1%
水 65%。
其制备方法包括下列步骤:
1)将重量百分比为65%的水注入搅拌罐中,
2)将按重量百分比为25%的无水氯化钙投入罐中,进行搅拌,直至全部溶解,
3)清除搅拌、溶解过程中所产生的泡沫,
4)继续搅拌以释放出无水氯化钙溶解时产生的热量,使溶液温度降至19℃~21℃,
5)加入重量百分比为9%的乙醇,搅拌均匀。
6)投入重量百分比为1%的亚硝酸钠,搅拌30分钟后结束,即制成具有防锈功能的车皮防冻液。
Claims (7)
1、一种车皮防冻液,其特征在于包括下列重量百分比的组分:
无水氯化钙 20~50%
乙醇 8~10%
水 40~70%。
2、根据权利要求1所述的车皮防冻液,其特征在于在上述组分中添加防锈剂亚硝酸钠,其重量百分比的组分为:
无水氯化钙 20~50%
乙醇 8~10%
亚硝酸钠 1~2%
水 40~70%。
3、根据权利要求1所述的车皮防冻液,其特征在于所述的无水氯化钙可采用工业级无水氯化钙,乙醇可采用90%~96%的乙醇,水可采用自来水、河水或深井水。
4、根据权利要求1所述的车皮防冻液,其特征在于由下列重量百分比组分所组成:
无水氯化钙(工业级) 30%
乙醇(95%) 10%
水 60%
5、根据权利要求2所述的车皮防冻液,其特征在于由下列重量百分比组分所组成:
无水氯化钙(工业级) 25%
乙醇(95%) 9%
亚硝酸钠(工业级) 1%
水 65%。
6、一种配制权利要求1所述的车皮防冻液配制方法,其特征在于包括下列步骤:
1)将重量百分比为40~70%的水注入搅拌罐中,
2)将按重量百分比为20~50%的无水氯化钙投入罐中,进行搅拌,直至全部溶解,
3)清除搅拌、溶解过程中所产生的泡沫,
4)继续搅拌以释放出无水氯化钙溶解时产生的热量,使溶液温度降至19℃~21℃,
5)加入重量百分比为8~10%的乙醇,搅拌均匀,制成车皮防冻液。
7、根据权利要求6所述的车皮防冻液的配制方法,其特征在于包括下列步骤:
1)将重量百分比为40~70%的水注入搅拌罐中,
2)将按重量百分比为20~50%的无水氯化钙投入罐中,进行搅拌,直至全部溶解,
3)清除搅拌、溶解过程中所产生的泡沫,
4)继续搅拌以释放出无水氯化钙溶解时产生的热量,使溶液温度降至19℃~21℃,
5)加入重量百分比为8~10%的乙醇,搅拌均匀,
6)投入重量百分比为1~2%的亚硝酸钠,搅拌30分钟后结束,制成车皮防冻液。