CN1555962A - 一种不锈铁——铝钎焊用的新型钎剂 - Google Patents

一种不锈铁——铝钎焊用的新型钎剂 Download PDF

Info

Publication number
CN1555962A
CN1555962A CNA2004100021150A CN200410002115A CN1555962A CN 1555962 A CN1555962 A CN 1555962A CN A2004100021150 A CNA2004100021150 A CN A2004100021150A CN 200410002115 A CN200410002115 A CN 200410002115A CN 1555962 A CN1555962 A CN 1555962A
Authority
CN
China
Prior art keywords
fluoride
stainless iron
potassium
aluminium
kalf
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2004100021150A
Other languages
English (en)
Inventor
张攸彭
张锡清
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNA2004100021150A priority Critical patent/CN1555962A/zh
Publication of CN1555962A publication Critical patent/CN1555962A/zh
Pending legal-status Critical Current

Abstract

一种不锈铁—铝钎焊用的新型钎剂，由以下物品按一定重量比配制而成：四氟铝酸钾+六氟铝酸钾(KALF4+K3ALF6)共晶体97.05～98.87％、氟化镉0.6～1.4％、氟化锌0.5～1.4％、氟化铜0.03～0.15％。使用本发明的新型焊剂焊接不锈铁—铝的拉伸强度较高，钎焊合格率大于98％。同时本发明使用方便，制作工艺简单。

Description

一种不锈铁—铝钎焊用的新型钎剂
本发明涉及一种不锈铁—铝钎焊用的新型钎剂。
四氟铝酸钾+六氟铝酸钾(KALF4+K3ALF6)共晶体自二十世纪六十年代发明以来，经不断的改进，其性质有了很大的提高，它与铝硅钎料配用，用于不锈钢—铝复合钎焊是成功的，钎焊合格率大于99％，并且实现了工业化生产。但是这种钎剂用于不锈铁—铝的焊接，其焊接的不锈铁—铝的拉伸强度较低，钎焊合格率一般在60％左右，不能用于该行业的工业化生产。
本发明的目的在于提供一种焊接不锈铁—铝的拉伸强度较高，钎焊合格率大于98％的不锈铁—铝钎焊用的新型钎剂。
本发明的目的可以通过以下措施来达到：一种不锈铁—铝钎焊用的新型钎剂，由以下物品按一定重量比配制而成：四氟铝酸钾+六氟铝酸钾(KALF4+K3ALF6)共晶体97.05～98.87％、氟化镉0.6～1.4％、氟化锌0.5～1.4％、氟化铜0.03～0.15％。
本发明的目的还可以通过以下措施来达到：可取四氟铝酸钾+六氟铝酸钾(KALF4+K3ALF6)共晶体97.21％、氟化镉1.4％、氟化锌1.35％、氟化铜0.04％混合配制而成。
将以上组分混合，球磨至150目即可得到本发明所述的不锈铁—铝钎焊用的新型钎剂。使用时，将本发明的新型钎剂与铝硅钎料配用，钎焊不锈铁—铝的极限拉伸强度达45-48N/mm2。而在同样条件下，用四氟铝酸钾+六氟铝酸钾(KALF4+K3ALF6)共晶体焊接的极限拉伸强度只有24-25N/mm2。
本发明相比现有技术具有如下优点：使用本发明的新型焊剂焊接不锈铁—铝的拉伸强度较高，钎焊合格率大于98％，同时本发明使用方便，制作工艺简单。
下面结合实例对本发明作进一步说明：
实施例一：
按重量百分比，取四氟铝酸钾+六氟铝酸钾(KALF4+K3ALF6)共晶体97.21％、氟化镉1.4％、氟化锌1.35％、氟化铜0.04％，混合后球磨至150目。测得极限拉伸强度为48N/mm2。
实施例二：
按重量百分比，取四氟铝酸钾+六氟铝酸钾(KALF4+K3ALF6)共晶体98.5％、氟化镉0.8％、氟化锌0.67％、氟化铜0.03％，混合后球磨至150目。测得极限拉伸强度为46N/mm2。
实施例三：
按重量百分比，取四氟铝酸钾+六氟铝酸钾(KALF4+K3ALF6)共晶体97.55％、氟化镉1.2％、氟化锌1.18％、氟化铜0.07％，混合后球磨至150目。测得极限拉伸强度为45N/mm2。

Claims (2)

1、一种不锈铁—铝钎焊用的新型钎剂，其特征在于：由以下物品按一定重量比配制而成：四氟铝酸钾+六氟铝酸钾(KALF4+K3ALF6)共晶体97.05～98.87％、氟化镉0.6～1.4％、氟化锌0.5～1.4％、氟化铜0.03～0.15％。
2、根据权利要求1所述的一种不锈铁—铝钎焊用的新型钎剂，其特征在于：可取四氟铝酸钾+六氟铝酸钾(KALF4+K3ALF6)共晶体97.21％、氟化镉1.4％、氟化锌1.35％、氟化铜0.04％混合配制而成。
CNA2004100021150A 2004-01-08 2004-01-08 一种不锈铁——铝钎焊用的新型钎剂 Pending CN1555962A (zh)