CN1552656A - 干粉砂浆组合物 - Google Patents
干粉砂浆组合物 Download PDFInfo
- Publication number
- CN1552656A CN1552656A CNA2003101049214A CN200310104921A CN1552656A CN 1552656 A CN1552656 A CN 1552656A CN A2003101049214 A CNA2003101049214 A CN A2003101049214A CN 200310104921 A CN200310104921 A CN 200310104921A CN 1552656 A CN1552656 A CN 1552656A
- Authority
- CN
- China
- Prior art keywords
- cellulose
- dry powder
- mortar composition
- powder mortar
- pearl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种干粉砂浆组合物，该组合物中含有55－90％的空心或者真空漂珠和5－35％的粘结剂和增稠剂，及1－10％的石灰精。用该组合物砌筑墙体比用苯板的保温效果能提高2倍以上，其风干后的硬度或强度与水泥基本相近，而重量低于水泥的3倍以上；同时，甲酸钙可产生二氧化碳气体并与氧化钙反应生成碳酸钙，进而可增加墙体内的强度。
Description
技术领域：
本发明涉及一种用于砌筑墙体且与水混合并经养护后能形成硬化物的干粉砂浆组合物。
背景技术：
粉煤灰主要是由氧化硅玻璃球组成的具有高度分散的微细颗粒集合体，各种微细颗粒根据其在水中沉降性能的差异可分为漂珠、轻珠和沉珠。漂珠是一种球形的空心微珠，其内含有氮气和二氧化碳负压气体，故漂珠具有高的抗压强度和高耐腐蚀率，低的热传导系数和热收缩系数，其熔点在1500℃以上，是一种多功能材料。特别是漂珠用于建筑材料上，由于空心内的惰性气体的存在，可有效地控制自由空气分子移动，能更好地实现保温。但，作为建筑上使用的砂浆至少应具有一定的粘稠度，就上述漂珠而言，由于其是分立的颗粒集合体，所以，它不能直接用作建筑砂浆使用。
水泥被广泛地用作砂浆、混凝土和类似的用途中的硬化组合物。而传统的水泥通常由石灰石作为主要原料在炉内焙烧制得，所以，该种水泥除浪费能源和造成环境污染以外，不具有漂珠的保温等优良特性，为此，利用漂珠制作水泥已成为本领域的主要研究课题。
如CN1096277A公告的“超导特异水泥”就利用了漂珠，该种水泥以100份硅酸盐水泥熟料为基料，加5-20份明矾石，5-25份石膏混合粉磨至水泥细度，再加入10-45份粉煤灰提取物的漂珠和微珠。该种水泥的漂珠利用率最高仅在总重量的20％左右，其保温、容重和抗渗等方面的问题最多只能改善20％左右，而成本方面并没有多大改变，大部分还仍然保留着传统水泥的基本特性。
而CN1061014A公告的“空心微珠硅酸盐水泥”注重提高空心微珠的比率，在给出的一个方案中，空心微珠含量的重量百分比为15-65％，且是将其加入由石灰石、粘土、铁粉经焙烧所构成的硅酸盐水泥中制成。这种水泥与普通的硅酸盐或粉煤灰等类似水泥一样，在使用时，需要按预定比例填充沙子或类似物，而不能直接作砂浆或混凝土使用；其次，该种水泥实际上是利用硅酸盐水泥作为粘结剂，其水化后的强度和保温等方面的性能也没有得到根本的改善。
发明内容：
本发明的任务是提供一种利用炉渣颗粒为主料制成的具有优良的保温效果和理想强度的且可直接水化使用的干粉砂浆组合物。
本发明所提出的干粉砂浆组合物，含有55-90％的空心或者真空漂珠和5-35％的粘结剂和增稠剂，及1-10％的石灰精。由于空心漂珠内具有惰性气体或二氧化碳负压气体，它能有效地抑制空气自由分子的运动，它可以阻碍热量传导，增大空气分子的反弹速度，因此，要想获得保温和其它性能好的砂浆，砂浆内漂珠的含量应该是越大其性能越好，考虑到砂浆水化后的强度等方面的问题，漂珠的含量不宜超过90％；同时，需要有适量的粘稠剂和增稠剂与之配合，而粘稠剂和增稠剂的含量不应低于5％；另外，石灰精具有早强、增容、减重之功能，一公斤石灰精可代替二千五百公斤水泥。
所述粘结剂可由高铝水泥或者氯氧镁水泥或者两者的混合物构成；所述的增稠剂由纤维素醚构成，且使增稠剂和粘结剂之间的重量比为1∶50-90。
含有70-90％的空心或者真空漂珠、10-25％粘结剂、2-6％的石灰精、1-5‰的纤维素醚和1-5％的甲酸钙。
所述纤维素醚由离子型纤维素或者非离子型纤维素构成。
所述离子型纤维素包括羧甲基纤维素，而非离子型纤维素包括乙基纤维素或甲基纤维素或羟乙基纤维素。
含有80-90％的空心或者真空漂珠、10-25％粘结剂、2-6％的石灰精、1-5‰的纤维素醚和1-5％的甲酸钙。
本发明所提出的干粉砂浆组合物采用空心或者真空漂珠为主料，再加上粘结剂和增稠剂，及石灰精等混合制成，由于漂珠具有保温和质轻的特性，所以，用其砌筑墙体比用苯板的保温效果能提高2倍以上，其风干后的硬度或强度与水泥基本相近，而重量低于水泥的3倍以上；同时，由于混合物中含有甲酸钙，甲酸钙可产生二氧化碳气体，当该混合物与水混合后，用其砌筑的墙体内由于二氧化碳气体的增加与氧化钙反应生成碳酸钙，进而可增加墙体内的强度。
具体实施方式：
实施例1
选55千克的空心或者真空漂珠和32.5千克的高铝水泥或者氯氧化镁水泥或者两者的混合物作为粘结剂，及0.5千克的纤维素醚作增稠剂、2千克的甲酸钙和10千克的石灰精，将各物料混合均匀后装入包装袋或类似的包装容器中即可制成本发明所提出的干粉砂浆组合物100千克。
实施例2
选87千克的空心或者真空漂珠和5千克的高铝水泥或者氯氧化镁水泥或者两者的混合物作为粘结剂，及0.1千克的纤维素醚作增稠剂、3千克的甲酸钙和4.9千克的石灰精，将各物料混合均匀后装入包装袋或类似的包装容器中即为本发明所提出的干粉砂浆组合物。
实施例3
选80千克的空心或者真空漂珠和14.8千克的高铝水泥或者氯氧化镁水泥或者两者的混合物作为粘结剂，及0.2千克的纤维素醚作增稠剂、1千克的甲酸钙和4千克的石灰精，将各物料混合均匀后装入包装袋或类似的包装容器中即为本发明所提出的干粉砂浆组合物。
所述纤维素醚由离子型纤维素或者非离子型纤维素构成，而离子型纤维素包括羧甲基纤维素，非离子型纤维素包括乙基纤维素或甲基纤维素或羟乙基纤维素。
Claims (6)
1、一种干粉砂浆组合物，其特征在于：含有55-90％的空心或者真空漂珠和5-35％的粘结剂和增稠剂，及1-10％的石灰精。
2、根据权利要求1所述的干粉砂浆组合物，其特征在于：所述粘结剂可由高铝水泥或者氯氧镁水泥或者两者的混合物构成；所述的增稠剂由纤维素醚构成，且使增稠剂和粘结剂之间的重量比为1∶50-90。
3、根据权利要求1或2所述的干粉砂浆组合物，其特征在于：含有70-90％的空心或者真空漂珠、10-25％粘结剂、2-6％的石灰精、1-5‰的纤维素醚和1-5％的甲酸钙。
4、根据权利要求1或2所述的干粉砂浆组合物，其特征在于：所述纤维素醚由离子型纤维素或者非离子型纤维素构成。
5、根据权利要求4所述的干粉砂浆组合物，其特征在于：所述离子型纤维素包括羧甲基纤维素，而非离子型纤维素包括乙基纤维素或甲基纤维素或羟乙基纤维素。
6、根据权利要求1所述的干粉砂浆组合物，其特征在于：含有80-90％的空心或者真空漂珠、10-25％粘结剂、2-6％的石灰精、1-5‰的纤维素醚和1-5％的甲酸钙。