CN1525095A - 非金属法兰盘 - Google Patents
非金属法兰盘 Download PDFInfo
- Publication number
- CN1525095A CN1525095A CNA031263623A CN03126362A CN1525095A CN 1525095 A CN1525095 A CN 1525095A CN A031263623 A CNA031263623 A CN A031263623A CN 03126362 A CN03126362 A CN 03126362A CN 1525095 A CN1525095 A CN 1525095A
- Authority
- CN
- China
- Prior art keywords
- parts
- butyl
- hdpe
- propyl group
- high density
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种非金属法兰盘，由高密度聚乙烯、玻璃纤维、丁基或丙基醋酸纤维素按照下述配比混合后与钢丝网按下述步骤制成：配比：高密度聚乙烯：25－60份；玻璃纤维：10－30份；丁基或丙基醋酸纤维素：0.5－2.5份；步骤：第一步，按配比取高密度聚乙烯、玻璃纤维、丁基或丙基醋酸纤维素；将上述材料粉碎后混和，置于造粒机中造粒；第二步，将第一步所得颗粒材料进行烘干处理，温度100℃－140℃；第三步，将预先制备的金属网置于法兰盘膜具腔内，将第二步所得物置于膜具内后合膜，通过压力机压制成型，压力为100－150MPa；保压时间为100－150秒后开膜取出即为成品。本发明不仅解决了金属法兰盘存在的不足，同时对环境保护起到了积极的社会效益。
Description
技术领域：
本发明涉及一种用于管道连接的法兰盘，具体说是涉及一种非金属法兰盘。
背景技术：
现有用于管道连接的法兰盘多由金属材料制成，有钢制法兰盘和铸铁法兰盘。金属法兰盘以其强度高而广泛用于管道的连接中，但其美中不足主要表现在：其一，耐腐蚀性差，尤其是使用在化工管道连接处；其二，原材料及加工成本高；其三，质量大，给产品的运输、安装带来诸多不便。
发明内容：
本发明之目的在于针对上述现有技术所存在的不足而提供一种非金属法兰盘。
为达到上述目的，本发明可通过下述技术方案实现：
本发明是由高密度聚乙烯、玻璃纤维、丁基或丙基醋酸纤维素按照下述配比混合后与钢丝网按下述步骤制成：
(1)、配比
高密度聚乙烯：25-60份；
玻璃纤维：10-30份；
丁基或丙基醋酸纤维素：0.5-2.5份；
(2)、步骤
第一步，按上述配比取高密度聚乙烯、玻璃纤维、丁基或丙基醋酸纤维素；将上述材料粉碎后混和，置于造粒机中造粒；
第二步，将第一步所得颗粒材料进行烘干处理，温度100℃-140℃；
第三步，将预先制备的金属网置于法兰盘膜具腔内，将第二步所得物置于膜具内后合膜，通过压力机压制成型，压力为100-150MPa；保压时间为100-150秒；
第四步，开膜取出成品，整形、冷却喷漆后既的成品。
本发明所述的配比可选择为：
高密度聚乙烯：60份；玻璃纤维：10份；丁基或丙基醋酸纤维素2.5份；
本发明所述的烘干处理温度可选择为100℃；所述保压时间为150秒。
本发明所述的配比也可选择为：
高密度聚乙烯：40份；玻璃纤维：20份；丁基或丙基醋酸纤维素1.5份；
所述烘干处理温度也可为120℃；所述保时间为130秒。
本发明所述的配比还可选择为：
高密度聚乙烯：20份；玻璃纤维：30份；丁基或丙基醋酸纤维素0.5份；
所述烘干处理温度还可为140℃；所述保时间为100秒。
本发明的优点在于利用废旧塑料，配以玻璃纤维、丁基或丙基醋酸纤维素以及金属加强网，按照科学配比和生产工艺制成，其产品的试验数据为：
螺栓压强式试验，试验压力在50公斤-60公斤下：
a、热态试验：60℃不变形；
b、冷态试验：-18℃不断裂。
本发明所述非金属法兰盘的出现不仅解决了现有金属法兰盘所存在的原材料成本高、耐腐蚀性差、质量大等不足，同时也给废旧塑料的再生利用提供了一条广泛的道路，对消除废旧塑料对环境的污染起到了积极的社会效益。
具体实施方式：
施实例1：
本发明是由高密度聚乙烯、玻璃纤维、丁基或丙基醋酸纤维素按照下述配比混合后与钢丝网按下述步骤制成：
(1)、配比
高密度聚乙烯：60份；玻璃纤维：10份；丁基或丙基醋酸纤维素2.5份；
(2)、步骤
第一步，按上述配比取高密度聚乙烯、玻璃纤维、丁基或丙基醋酸纤维素；将上述材料粉碎后混和，置于造粒机中造粒；
第二步，将第一步所得颗粒材料进行烘干处理，温度为100℃；
第三步，将预先制备的金属网置于法兰盘膜具腔内，将第二步所得物置于膜具内后合膜，通过压力机压制成型，压力为100-150MPa；保压时间为150秒；
第四步，开膜取出成品，整形、冷却喷漆后既的成品。
施实例2：
本发明是由高密度聚乙烯、玻璃纤维、丁基或丙基醋酸纤维素按照下述配比混合后与钢丝网按下述步骤制成：
(1)、配比
高密度聚乙烯：40份；玻璃纤维：20份；丁基或丙基醋酸纤维素1.5份；
(2)、步骤
第一步，按上述配比取高密度聚乙烯、玻璃纤维、丁基或丙基醋酸纤维素；将上述材料粉碎后混和，置于造粒机中造粒；
第二步，将第一步所得颗粒材料进行烘干处理，温度为120℃；
第三步，将预先制备的金属网置于法兰盘膜具腔内，将第二步所得物置于膜具内后合膜，通过压力机压制成型，压力为100-150MPa；保压时间为130秒；
第四步，开膜取出成品，整形、冷却喷漆后既的成品。
施实例3：
本发明是由高密度聚乙烯、玻璃纤维、丁基或丙基醋酸纤维素按照下述配比混合后与钢丝网按下述步骤制成：
(1)、配比
高密度聚乙烯：20份；玻璃纤维：30份；丁基或丙基醋酸纤维素0.5份；
(2)、步骤
第一步，按上述配比取高密度聚乙烯、玻璃纤维、丁基或丙基醋酸纤维素；将上述材料粉碎后混和，置于造粒机中造粒；
第二步，将第一步所得颗粒材料进行烘干处理，温度为140℃；
第三步，将预先制备的金属网置于法兰盘膜具腔内，将第二步所得物置于膜具内后合膜，通过压力机压制成型，压力为100-150MPa；保压时间为100秒；
第四步，开膜取出成品，整形、冷却喷漆后既的成品。
Claims (4)
1、一种非金属法兰盘，其特征在于：它是由高密度聚乙烯、玻璃纤维、丁基或丙基醋酸纤维素按照下述配比混合后与钢丝网按下述步骤制成：
(1)、配比
高密度聚乙烯：25-60份；
玻璃纤维：10-30份；
丁基或丙基醋酸纤维素：0.5-2.5份；
(2)、步骤
第一步，按上述配比取高密度聚乙烯、玻璃纤维、丁基或丙基醋酸纤维素；将上述材料粉碎后混和，置于造粒机中造粒；
第二步，将第一步所得颗粒材料进行烘干处理，温度100℃-140℃；
第三步，将预先制备的金属网置于法兰盘膜具腔内，将第二步所得物置于膜具内后合膜，通过压力机压制成型，压力为100-150MPa；保压时间为100-150秒；
第四步，开膜取出成品，整形、冷却喷漆后既的成品。
2、根据权利要求1所述的非金属法兰盘，其特征在于：所述配比为：
高密度聚乙烯：60份；玻璃纤维：10份；丁基或丙基醋酸纤维素2.5份；
所述烘干处理温度为100℃；所述保压时间为150秒。
3、根据权利要求1所述的非金属法兰盘，其特征在于：所述配比为：
高密度聚乙烯：40份；玻璃纤维：20份；丁基或丙基醋酸纤维素1.5份；
所述烘干处理温度为120℃；所述保压时间为130秒。
4、根据权利要求1所述的非金属法兰盘，其特征在于：所述配比为：
高密度聚乙烯：20份；玻璃纤维：30份；丁基或丙基醋酸纤维素0.5份；
所述烘干处理温度为140℃；所述保压时间为100秒。