CN1515428A - Crystalinformal note - Google Patents

Abstract

The present invention relates to a kind of crystal informal note. It includes several note pieces, every note piece includes a plastic film, said plastic film has a transparent writing layer which is applied on its one surface, and an adhesion layer which is applied on another opposite surface of it. The writing layer is made up by using adhesive and pigment according to the ratio (by dried weight ratio range) of 1:1-1:10 and mixing them, so that the opaqueness of said note piece is less than 55.

Description

Crystalinformal note

Technical field

The present invention relates to a kind of note, particularly relate to a kind of transparent frivolous and Crystalinformal note that tensile strength is good.

Background technology

Because the prosperity of industrial and commercial society; the diversification that becomes of healing of the form of work life; it is frequent further to come and go between the person to person, and common people regular meeting uses note, even it is carried; so that write down points for attention at any time; remind oneself work on plan or the empty forms trival matters of daily life, simultaneously, under hasty at ordinary times step; note more can transmit message, as the bridge of interpersonal communication.Especially, the product that the self-adhesive type note is generally popular at present especially, and include most stacked note scraps of paper, make that note is to be a shape.And there is the viscose glue design that can repeat to attach at the back side of each note scraps of paper, and can allow the note scraps of paper directly at random be attached on desktop, wall, the books file, reaches and reminds and the effect of transmitting message, and is quite convenient in the use.Yet traditional self-adhesive type note has the following desirable part of not attaining on reality is used:

(1) damaged easily:

The material of the tradition note scraps of paper is general paper products, and the intensity of stationery fiber is often decided along with its thickness degree, the note scraps of paper that thickness is less, excessive or when being subjected to the tearing of improper external force, the as easy as rolling off a log nib that causes is worn out disrepair phenomenons such as the note scraps of paper in writing power.

(2) cost up and run counter to environmental friendly principle:

Because the thickness of traditional note scraps of paper is keys of its intensity of decision, so under the consideration of writing intensity substantially, can wait the thickness of the note scraps of paper with increase usually is means, well imagines that its consumables cost then increases relatively.Because the raw material of stationery is the valve of cutting that comes from timber, increase the timber consumption relatively, with the big Divergence mutually of environmental friendly principle.In addition, for fear of the thickness of note, volume thereby increase then must reduce note scraps of paper quantity, reduce the convenience on using greatly.

(3) non-watertight, fragile:

Owing to traditional note scraps of paper are paperys, do not have the effect of waterproof, therefore,, not only cause damage easily, even make the data information on the note scraps of paper blur or loss if on using, very do not touch moisture content, can't bring into play both getting effect.

Summary of the invention

The purpose of this invention is to provide a kind of Crystalinformal note, overcome the drawback of prior art, reach frivolous transparent and purpose that tensile strength is good.

The object of the present invention is achieved like this: a kind of Crystalinformal note, it is characterized in that: it includes most note sheets, each note sheet comprises a plastic sheeting, this plastic sheeting has a transparent writing layer that is coated on the surface thereof, an and adhesion layer that is coated on its another opposed surface, this writing layer is to be mixed by stick and pigment, and the dry measure of this stick and pigment is between 1: 1～1: 10 than scope, and the opacity of this note sheet is less than 55.

The opacity of this note sheet is preferably less than 40 or less than 30.

This stick is to be selected from following constitute at least a: polyvinyl alcohol, polyacrylate, polyvinyl acetate, synthetic rubber or its combination.

This plastic sheeting is to be selected from following constitute at least a: polypropylene plastics, polyethylene, polyvinyl chloride, polypentaerythritol or its combination.

This note sheet comprises that more a surface is coated with mould release, and is covered on the release liners on this writing layer.

Describe in detail below in conjunction with accompanying drawing and preferred embodiment.

Description of drawings

Fig. 1 is the cross-sectional schematic of note sheet of the present invention.

Fig. 2 is the schematic perspective view that the present invention includes the Crystalinformal note of most note sheets.

The specific embodiment

Consult Fig. 1-shown in Figure 2, Crystalinformal note of the present invention comprises most note sheets 1, and each note sheet 1 comprises a plastic sheeting 11, and plastic sheeting 11 is to have a transparent writing layer 112 that is coated on its end face, and an adhesion layer 111 that is coated on its bottom surface.This writing layer 112 can be provided as writes record.

This plastic sheeting 11 is to be selected from the following group that constitutes: polypropylene plastics (PP), polyethylene (PE), polyvinyl chloride (PVC), polypentaerythritol (PET) or polyester film (Mylar), or its combination.

In the present embodiment, this plastic sheeting 11 is polyacrylic films, has that matter is thin, smooth, the transparency is fabulous, tensile strength is big, resistance to water is good and characteristic such as gloss is beautiful.This adhesion layer 111 is to repeat to peel off the acrylic ester type viscose glue that pastes.

This writing layer 112 is to be mixed by stick and pigment.This stick is to be selected from the following group that constitutes: polyacrylate stick (Polyacrylate type adhesive), polyvinyl alcohol stick (PolyvinylAlcohol; PVA), polyvinyl acetate stick (Polyvinyl Acetate; PVAc), synthetic rubber stick (Synthetic rubber; SBR) or its combination.

This pigment then is to be selected from the following group that constitutes: titanium dioxide (TiO ₂), calcium carbonate (CaCO ₃), carclazyte (Clay) or its combination.And the dry measure of this stick and pigment is between 1: 1～1: 10 than scope, and with after pigment mixes, its mixed liquor is to show slightly pellucidity, makes this writing layer 112 present and can be made for the transparent characteristic of writing in stick.

It should be noted that especially: the opacity of this note sheet 1 (opacity) can be along with the dry measure ratio of this stick and pigment, and writing layer 112 thickness on this plastic sheeting 11 and changing.

By the transparent characteristic of this note sheet 1, this note sheet 1 can be used in file copy.This note sheet 1 can be attached on the paper to be xeroxed (the printed paper sheet), carry out image or literal via duplicator or facsimile machine again and duplicate, and this is waited to xerox the image or the literal that are hidden by this note sheet 1 on the paper and still can duplicate on the copier paper that is produced (a copy sheet).And do not need this note sheet 1 is removed, just can directly inspect image or the literal of writing in waiting to xerox on the paper.

The opacity of this note sheet 1 is less than 55, is preferably less than 40, and the best then is less than 30, makes above-mentioned image or the literal that duplicates on the copier paper that produces clearly to present.

The writing layer 112 of this note sheet 1 more is mixed with the dyestuff that can make this note sheet 1 colour developing.And the use amount of this dyestuff accounts for more than 2% of total amount of pigment of interpolation, and this writing layer 112 that can make stick and pigment mix out has painted effect.

This note sheet 1 comprises that more a surface is coated with mould release, can be covered on the release liners (not shown) on this writing layer 112, in order to protect the writing layer 112 on this plastic sheeting 11.

Moreover this note sheet 1 decapacitation is piled up to make and is bound into book form, and forms outside the Crystalinformal note, and writing layer 112 is attached on the release liners, just can finish the note sheet 1 of individual kenel.

By the release interface that mould release is produced release liners and writing layer 112, make note sheet 1 can attach or peel off this release liners repeatedly.

The following example can illustrate the note sheet 1 with different sticks and dry measure ratio of pigment, and the difference that is presented is write quality.

One, embodiment numbers 1-48

Note sheet 1 write attribute test be distinguished into the best (excellect, e), good (good g) and still can (fair, f) Three Estate, and mainly be for judging foundation with aspects such as its writing property, adherence and absorbencys.

In an embodiment, the plastic sheeting 11 of all note sheets 1 all is that polypropylene plastics is made, and 112 of writing layers have the dry measure ratio of different sticks and pigment respectively.And the stick that is applied among these embodiment has PVA, PVAc, and SBR etc., the pigment that is applied to has TiO ₂, CaCO ₃, carclazyte (Clay) etc., and the dry measure of stick and pigment ratio is between 1: 10-1: between 1, be to add the stick of Different Weight respectively with the pigment of every 100g, and form the proportioning of different sticks and pigment, both proportionings are as shown in subordinate list one, two, three.Wherein

Embodiment numbers 1-19 and lists in the subordinate list one,

Embodiment numbers 20-34 and lists in the subordinate list two,

Embodiment numbers 35-48 and lists in the subordinate list three.

Subordinate list one

Embodiment number	TiO 2g	Carclazyte g	Calcium carbonate g	PVAg	Embodiment number	TiO 2g	Carclazyte g	Calcium carbonate g	PVAg
										????1	100	-	-	100	????11	-	100	-	25
????2	100	-	-	75	????12	-	100	-	20
										????3	100	-	-	50	????13	-	100	-	15
????4	100	-	-	25	????14	-	100	-	10
										????5	100	-	-	20	????15	-	100	-	5
????6	100	-	-	15	????16	-	-	100	75
										????7	-	100	-	100	????17	-	-	100	50
????8	-	100	-	75	????18	-	-	100	30
										????9	-	100	-	50	????19	-	-	100	20
????10	-	100	-	30	????-	-	-	-	-

Subordinate list two

Embodiment number	TiO 2g	Carclazyte g	Calcium carbonate g	PAcg	Embodiment number	TiO 2g	Carclazyte g	Calcium carbonate g	PAcg
										????20	-	-	100	100	????28	100	-	-	25
????21	-	-	100	75	????29	100	-	-	5
										????22	-	-	100	50	????30	-	100	-	100
????23	-	-	100	25	????31	-	100	-	75
										????24	-	-	100	5	????32	-	100	-	50
????25	100	-	-	100	????33	-	100	-	25
										????26	100	-	-	75	????34	-	100	-	5
????27	100	-	-	50	????-	-	-	-	-

Subordinate list three

Embodiment number	TiO 2g	Carclazyte g	Calcium carbonate g	SBRg	Embodiment number	TiO 2g	Carclazyte g	Calcium carbonate g	SBR?g
										????35	100	-	-	100	????42	-	100	-	25
????36	100	-	-	75	????43	-	100	-	5
										????37	100	-	-	50	????44	-	-	100	100
????38	100	-	-	25	????45	-	-	100	75
										????39	-	100	-	100	????46	-	-	100	50
????40	-	100	-	75	????47	-	-	100	25
										????41	-	100	-	50	????48	-	-	100	5

The test result of writing property (Writab-ility), anchorage (Anchor-age) and the absorbency (Ink bsorb-ability) of these embodiment 1-48 then is presented in the subordinate list four.

By subordinate list four as can be known:

Include TiO ₂Embodiment number 1-2;

The embodiment that includes clay numbers 12-14,33-34 and 42-43,

Include CaCO ₃Embodiment number 19, even 45-47 presents good the writing property of the best, adherence and absorbency.

Two, embodiment numbers 49-82

And in these embodiment, the plastic sheeting 11 of all note sheets 1 all is that polypropylene plastics is made, and these writing layers 112 then have the dry measure ratio of different sticks and pigment respectively.And the stick that is applied among these embodiment has PVA, PVAc, and SBR etc., the pigment that is applied to has TiO ₂, CaCO ₃, Clay etc., and the opacity value of these embodiment is as shown in subordinate list five, six, seven.

Subordinate list four

Embodiment number	Writing property	Adherence	Absorbency	Embodiment number	Writing property	Adherence	Absorbency
								????1	????e	????g	????e	????25	???f	????e	????f
????2	????e	????g	????e	????26	???f	????e	????f
								????3	????e	????f	????g	????27	???f	????g	????e
????4	????g	????f	????g	????28	???g	????g	????g
								????5	????g	????g	????g	????29	???peeling	????-	????-
????6	????f	????f	????e	????30	???f	????g	????f
								????7	????f	????f	????e	????31	???f	????e	????f
????8	????f	????f	????e	????32	???f	????e	????f
								????9	????e	????f	????f	????33	???g	????e	????g
????10	????f	????f	????e	????34	???e	????e	????g
								????11	????g	????f	????e	????35	???g	????e	????f
????12	????g	????g	????g	????36	???e	????e	????f
								????13	????g	????g	????g	????37	???e	????e	????f
????14	????g	????e	????g	????38	???g	????f	????f
								????15	????g	????e	????f	????39	???g	????e	????f
????16	????e	????f	????g	????40	???g	????e	????f
								????17	????e	????f	????f	????41	???g	????e	????f
????18	????e	????f	????F	????42	???e	????e	????g
								????19	????e	????g	????g	????43	???g	????g	????g
????20	????f	????e	????f	????44	???g	????e	????f
								????21	????f	????g	????f	????45	???e	????e	????g
????22	????e	????g	????f	????46	???g	????e	????g
								????23	????g	????g	????f	????47	???g	????g	????g
????24	????g	????g	????f	????48	???g	????f	????g

Subordinate list five

Embodiment number	TiO 2g	Carclazyte g	Calcium carbonate g	???PVAg	Dry measure compares g/m 2	Opacity value
							????49	-	????100	????-	????5	????2.4	????25.93
????50	-	????100	????-	????5	????5.6	????43.63
							????51	-	????100	????-	????5	????8.1	????52.87
????52	-	????100	????-	????50	????1.6	????15.60
							????53	-	????100	????-	????50	????3.8	????19.50
????54	-	????100	????-	????50	????9.2	????26.21
							????55	-	????100	????-	????100	????2.5	????12.98
????56	-	????100	????-	????100	????6.7	????21.27
							????57	-	????100	????-	????100	????9.0	????23.58
????58	-	????-	????100	????50	????1.6	????30.15
							????59	-	????-	????100	????50	????4.1	????34.93
????60	-	????-	????100	????50	????8.6	????43.92
							????61	100	????-	????-	????50	????1.9	????35.71
????62	100	????-	????-	????50	????4.2	????44.78
							????63	100	????-	????-	????50	????7.7	????55.74

The note sheet 1 that has different opacities among these embodiment is attached at respectively waits to xerox on the paper, see through the copying operation of duplicator, observe the image or the literal quality of duplicating on the copier paper that is produced immediately, test of the influence of the opacity of these note sheets 1 for the copier paper quality in order to research.

And the quality quality of duplicating the copier paper that is produced, be with duplicate thereon image or the definition (Clearness) of literal as judging foundation, and be categorized as the best (excellect, e), good (good, g), still can (fair, f), and not good (poor, four grades such as p), test result is then shown in subordinate list eight.

Subordinate list six

Embodiment number	TiO 2g	Carclazyte g	Calcium carbonate g	???PVAg	The dry measure ratio, g/m 2	Opacity value
							????64	-	????100	????-	????50	????6.1	????12.61
????65	-	????100	????-	????50	????22.4	????12.71
							????66	-	????100	????-	????50	????29.1	????12.53
????67	-	????-	????100	????50	????3.3	????27.18
							????68	-	????-	????100	????50	????4.7	????28.70
????69	-	????-	????100	????50	????9.1	????47.12
							????70	100	????-	????-	????50	????1.1	????29.33
????71	100	????-	????-	????50	????3.5	????40.97
							????72	100	????-	????-	????50	????8.0	????61.82

Subordinate list seven

Embodiment number	???TiO 2g	Carclazyte g	Calcium carbonate g	??PVAg	Dry measure compares g/m 2	Opacity value
							????73	????-	100	????-	????50	????3.0	????20.61
????74	????-	100	????-	????50	????5.7	????23.38
							????75	????-	100	????-	????50	????11.1	????31.55
????76	????-	-	????100	????50	????3.3	????28.69
							????77	????-	-	????100	????50	????4.1	????40.21
????78	????-	-	????100	????50	????8.6	????50.04
							????79	????100	-	????-	????50	????1.7	????46.73
????80	????100	-	????-	????50	????3.1	????49.63
							????81	????100	-	????-	????50	????9.1	????65.83
????82	????100	-	????-	????50	????10.6	????71.49

Subordinate list eight

Embodiment number	Definition	Embodiment number	Definition	Embodiment number	Definition
						????49	????g	????61	????G	????73	????g
????50	????f	????62	????F	????74	????g
						????51	????f	????63	????P	????75	????g
????52	????e	????64	????E	????76	????g
						????53	????e	????65	????E	????77	????f
????54	????g	????66	????E	????78	????p
						????55	????e	????67	????G	????79	????f
????56	????g	????68	????G	????80	????f
						????57	????g	????69	????F	????81	????p
????58	????g	????70	????G	????82	????p
						????59	????g	????71	????F
????60	????f	????72	????P

By among the subordinate list five-table seven as can be known: the suitable opacity of the note sheet 1 of Crystalinformal note of the present invention is less than 50, is preferably less than 40, and the best then is less than 30.

If among above-mentioned these embodiment, if to be the Post-it of yellow and opacity about 90% ^TMNote sheet (drawing materials from 3M corporation, is a u s company) replaces note sheet 1 of the present invention, and can obviously find: the quality of copier paper then is on duty mutually.

Comprehensively above-mentioned, Crystalinformal note of the present invention has more following advantage:

(1) intensity is preferable:

Because it is made that plastic sheeting 11 of the present invention is transparent materials such as PP, PE, PVC, PET or Mylar, its surperficial tensile strength is big, even thinner thickness, can not damage easily yet, so be not easy breakage in the use, under the note scraps of paper of known note were compared, 1 of this note sheet of same thickness had preferable intensity.

(2) have low cost and environmental protection concurrently:

Because the big characteristic of tensile strength that plastic sheeting 11 of the present invention has, under the situation that intensity increases, the thickness of this note sheet 1 then can be less than the note scraps of paper thickness of known note, phase shape can be saved material cost, and in the volume shape note of same thickness, note sheet 1 quantity of Crystalinformal note of the present invention relatively then can be more than the note scraps of paper quantity of more known note, and effectively promote ease of use.Moreover the cost of note sheet 1 of the present invention is also low than the stationery cost, and can avoid lumber consumption, quite meets the demand of environmental protection.

(3) resistance to water is good:

Because plastic sheeting 11 of the present invention is the plastic materials with waterproof effect, and transparent writing surface of the present invention 112 has good writing property and absorbency, the scraps of paper that can effectively overcome known note are papery, and easy low-priced water is damaged or the shortcoming of the information of destruction, and can effectively bring into play the function that its message is transmitted or reminded.

In sum, Crystalinformal note of the present invention, plastic sheeting 11 by each note sheet 1, can promote its tensile strength, thereby effectively reduce thickness, more can effectively promote the note sheet quantity of Crystalinformal note of the present invention, and this plastic sheeting 11 has more fire resistance characteristic, the note scraps of paper that effectively overcome known note are the shortcoming that runs off of breakage or data in adhesional wetting and easily, obviously promotes whole ease of use.And this writing layer 112 of writing record can be provided, more following than mixing in suitable stick with the pigment dry measure, except presenting good writing property and absorbency, more make note sheet 1 of the present invention have suitable opacity less than 55, make and write in last literal or pattern and can clearly present, effectively brought into play the function that message is transmitted, so can reach purpose of the present invention really.

Claims (6)

1, a kind of Crystalinformal note, it is characterized in that: it includes most note sheets, each note sheet comprises a plastic sheeting, this plastic sheeting has a transparent writing layer that is coated on the surface thereof, an and adhesion layer that is coated on its another opposed surface, this writing layer is to be mixed by stick and pigment, and the dry measure of this stick and pigment is between 1: 1～1: 10 than scope, and the opacity of this note sheet is less than 55.

2, Crystalinformal note according to claim 1 is characterized in that: the opacity of this note sheet is less than 40.

3, Crystalinformal note according to claim 1 is characterized in that: the opacity of this note sheet is less than 30.

4, Crystalinformal note according to claim 1 is characterized in that: this stick is to be selected from following constitute at least a: polyvinyl alcohol, polyacrylate, polyvinyl acetate, synthetic rubber or its combination.

5, Crystalinformal note according to claim 1 is characterized in that: this plastic sheeting is to be selected from following constitute at least a: polypropylene plastics, polyethylene, polyvinyl chloride, polypentaerythritol or its combination.

6, Crystalinformal note according to claim 1 is characterized in that: this note sheet comprises that more a surface is coated with mould release, and is covered on the release liners on this writing layer.