CN1090105C - Informal note for keeping record and its producing method - Google Patents
Informal note for keeping record and its producing method Download PDFInfo
- Publication number
- CN1090105C CN1090105C CN99109771A CN99109771A CN1090105C CN 1090105 C CN1090105 C CN 1090105C CN 99109771 A CN99109771 A CN 99109771A CN 99109771 A CN99109771 A CN 99109771A CN 1090105 C CN1090105 C CN 1090105C
- Authority
- CN
- China
- Prior art keywords
- note
- pigment
- plastic sheeting
- coated
- smears
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a note used for recording, which forms a sheet-shaped body and is formed by a transparent plastic film. A coating agent used for writing is coated on the surface of the transparent plastic film and is formed by mixing adhesives and pigments. The dry measure of the adhesives and the pigments ranges from 1:1 to 1:10. The plastic film can be polypropylene plastics, polyethylene, polyvinyl chloride, pentaerythritol or a polyester film. Colored pigments can be added to the pigments and accouts for at least 2% of the amount of total pigments. Peeling glue is coated on the back side of each note to form an adhesive surface, and thus, notes can be adhered into a booklet. The manufacturing method of the present invention comprises the following steps which are a feed preparation step, a glue spreading step, a stacking step and a cutting step.
Description
The present invention relates to a kind of note of keeping record usefulness, particularly relate to a kind of transparent frivolous and informal note for keeping record and manufacture method thereof that tensile strength is good.
Common people usually can use informal note for keeping record; so that journal entry at any time; a kind of self-adhesive type note that is a shape is arranged; its back side is provided with the viscose glue that can repeat to attach; therefore can directly at random be attached at places such as desktop, wall, books, file; it is convenient to remind, transmission information, and still, there is following shortcoming in this self-adhesive type note:
One, intensity is limited:
The material of above-mentioned note is generally paper products, and the intensity of stationery fiber is to decide along with the thickness of paper, if the note of thinner thickness is subjected to tearing of improper external force in the use, be easy to damage, and the user normally writes at whole uppermost one of note of volume, after finishing, just tear to attach and use,, then can cause nib to wear out note if a little firmly write, relatively, if note has certain thickness, the note volume that then will be directed at whole volume is along with increase, and note in the past is subject to it and is general paper products, intensity is limited, the damage of breaking easily.
Two, cost height:
As above-mentioned, because constitute required fiber number, arrangement mode and the thickness of stationery, it is the factor of decision paper strength, so on making in order to make paper reach certain strength, increased paper thickness, make consumption of raw materials and relatively increase, and the raw material of stationery has been a timber, use timber as paper making raw material in a large number, the manufacturing cost height.
Three, color and luster dullness:
Because the material of note all was general paper products in the past, that is to say that note is opaque paper, but reach showy effect, otherwise note will be dull, stiff by coating color, pattern.
Four, damage easily:
Because the material of note all was general paper products in the past, do not have the effect of waterproof, therefore,, just damage easily if touch moisture content during use.
The object of the present invention is to provide a kind of frivolous transparent and informal note for keeping record that tensile strength is good.
Another object of the present invention is to provide a kind of manufacture method of above-mentioned note.
For the present invention that achieves the above object takes following measure:
A kind of informal note for keeping record of the present invention, body in the form of sheets is characterized in that:
It is formed by transparent plastic sheeting, and its surface-coated has the smears that can write, and the smears is mixed by adhesive and pigment, the dry measure of adhesive and pigment than scope between 1: 1～1: 10.
Wherein: described plastic sheeting can be polyacrylic film, polyethylene film, polyvinyl chloride film, pentaerythrite or polyester film.
Wherein: can add colored pigment in the described pigment, colored pigment accounts at least 2% of total amount of pigment.
Wherein: the back side of described each note is coated with peels off glue and forms a binding face, and note can be fitted and be bound into book form.
Wherein: attach a release liners on described each note, the release liners surface is coated with peelable mould release.
The manufacture method of informal note for keeping record of the present invention is characterized in that, may further comprise the steps:
A. material preparation step utilizes plastics such as polypropylene plastics, polyethylene, polyvinyl chloride, pentaerythrite or polyester film to make the plastic sheeting of sheet;
B. gluing step, the peelable glue that can repeat to paste in the back side coating with each sheet plastic sheeting of getting ready forms a writing surface;
C. stacking procedure will be handled at the note that the gluing step is finished, and will put in order the volume back side earlier and be coated with peelable glue, and the surface is coated with stacked the binding into book form of many notes of smears;
D. cutting step cuts into suitable size with stacked note of binding into book form.
Because note of the present invention has the main body of plastic sheeting, simultaneously, more the surface-coated at this glue film has the smears, make the writing surface that forms a transparent effect on the poly-plastic material surface, in addition, also can cooperate the smears that is coated with color and luster in good time on plastic sheeting, make the note of making have more the transparent effect that combines with color and luster.
Below in conjunction with drawings and Examples informal note for keeping record of the present invention and manufacture method thereof are elaborated:
Description of drawings:
Fig. 1: the schematic perspective view of the embodiment of the invention.
Fig. 2: the cross-sectional schematic of individual note of the embodiment of the invention.
Fig. 3: the making step schematic diagram of the note of binding into book form of the embodiment of the invention.
As shown in Figure 1, 2, note 1 of the present invention is plates and is made of the plastic sheeting 11 that is transparence, also the ink of writing is adhered to and be subject on the plastic sheeting 11, so on the surface of plastic sheeting 11, be coated with the smears in addition, the smears is mixed by adhesive and pigment etc., and the dry measure of adhesive and pigment, went up plastic sheeting 11 surfaces and forms a transparent writing face between 1: 1～1: 10 than scope.
As shown in Figure 3, note 1 of the present invention is formed the preparation method of volume, be to include material preparation step 21, gluing step 22, stacking procedure 23 and cutting step 24 in regular turn, and above-mentioned steps will be described as follows.
Material preparation step 21 is to utilize polypropylene plastics (PP), polyethylene (PE), polyvinyl chloride (PVC), pentaerythrite (PET) or polyester film plastics such as (Mylar) to make the plastic sheeting 11 of sheet, because available plastics are a lot, in the present invention only to being illustrated by the film 11 that polypropylene plastics constituted.
Gluing step 22 is the peelable glue that can repeat to paste with in the coating of the back side of each sheet plastic sheeting 11 of material preparation step 21, make the back side of each sheet plastic sheeting 11 form a binding face 111, and the use kind of peelable glue is a lot, for example acrylic ester type (Acrylatetype) sticks together glue etc., the processing procedure and the operating characteristic thereof of peelable glue are same as the prior art simultaneously, so no longer be described in detail at this, in addition, in plastic sheeting 11 surface-coated the smears is arranged, plastic sheeting 11 surfaces are gone up form a writing surface 112, and comprise adhesive and pigment because of the smears, the dry measure of adhesive and pigment than scope between 1: 1～1: 10, make adhesive with after pigment mixes, its mixed liquor shows slightly transparent state, and adhesive can be polyacrylate adhesive (Polyacrylate type adhesive) or poly (vinyl alcohol) binder (Polyvinyl Alcohol; PVA) or polyvinyl acetate ester adhesive (Polyvinyl Acetate; Or synthetic rubber binder (Syntheticrubber PVAc); And pigment can be titanium dioxide (TiO SBR) etc.,
2), calcium carbonate (CaCO
3), carclazyte materials such as (Clay), and that above-mentioned pigment is coated with is attached, the color that is manifested is white in color, therefore if present different colors after making pigment and adhesive mixing, just can add colored pigment handles, and the use amount of colored pigment accounts for more than 2% of total amount of pigment of interpolation, and just the smears that adhesive is mixed with pigment has the effect of staining.
Stacking procedure 23 is that the note 1 that will finish in gluing step 22 is handled, just will put in order the volume back side earlier and be coated with peelable glue, and many notes 1 that the surface is coated with the smears stacked binding into book form in addition.
Cutting step 24 is that the stacked note of binding into book form 1 is cut into suitable size, just can finish the making that note 1 is bound into book form.
For further understanding the optimum mixture ratio example of adhesive and pigment, no matter obtain optimum efficiency to reach note 1 in the absorbency of writing property, writing surface and the aspects such as adherence of smears, the experimental data of following table one～three is illustrated:
Sampling:
Respectively with the TiO of every 100g weight
2, CaCO
3, pigment such as Clay is to PVA, PVAc, adhesives such as SBR are done an adding proportion and are changed test (not adding any colored pigment in aforesaid pigment), and the proportioning of the adhesive of its test and pigment, test sample as shown in table one, two, three shows, just the shown PVA of table one respectively with TiO
2, CaCO
3, (totally 19 of Clay equal sampleses; The numbering 1～19) test, and table two promptly show PVAc respectively with TiO
2, CaCO
3, (totally 10 of Clay equal sampleses; Numbering 20～29) test, as for table three item expression SBR respectively with TiO
2, CaCO
3, (totally 19 of Clay equal sampleses; Numbering 30～48) test.
＜table one〉expression PVA respectively with TiO
2, CaCO
3, the Clay equal samples test chart
＜table two〉expression PA respectively with TiO
2, CaCO
3, the Clay equal samples test chart
＜table three〉expression SBR respectively with TiO
2, CaCO
3, the Clay equal samples test chart
*Other has test piece the 49th is the result who adds the yellow uitramarine more than 2% in coating again:
| Contained PVA adhesive dry measure ratio in every 100g pigment | 5 | 10 | 15 | 20 | 25 | 30 | 50 | 75 | 100 |
| Sample number into spectrum | |||||||||
| TiO 2 | -- | -- | 6 | 5 | 4 | -- | 3 | 2 | 1 |
| Clay | 15 | 14 | 13 | 12 | 11 | 10 | 9 | 8 | 7 |
| CaCO 3 | -- | -- | -- | 19 | -- | 18 | 17 | 16 | -- |
| Contained PA adhesive dry measure ratio in every 100g pigment | 5 | 10 | 15 | 20 | 25 | 30 | 50 | 75 | 100 |
| Sample number into spectrum | |||||||||
| TiO 2 | 29 | -- | -- | -- | 28 | -- | 27 | 26 | 25 |
| Clay | 34 | -- | -- | -- | 33 | -- | 32 | 31 | 30 |
| CaCO 3 | 24 | -- | -- | -- | 23 | -- | 22 | 21 | 20 |
| Contained SBR adhesive dry measure ratio in every 100g pigment | 5 | 10 | 15 | 20 | 25 | 30 | 50 | 75 | 100 |
| Sample number into spectrum | |||||||||
| TiO 2 | -- | -- | -- | -- | 38 | -- | 37 | 36 | 35 |
| Clay | 43 | -- | -- | -- | 42 | -- | 41 | 40 | 39 |
| CaCO 3 | 48 | -- | -- | -- | 47 | -- | 46 | 45 | 44 |
The test sample book of gained after these tests, more respectively with aspects such as writing property, adherence and absorbencys as a basis for estimation, and can distinguish the best (excellent; E), good (good; G), still can (fair; Three kinds of grades such as f) are as shown in following table four, five, six.
＜table four〉be that PVA is respectively to the judged result table of writing property, adherence and absorbency.
＜table five〉be that PA is respectively to the judged result table of writing property, adherence and absorbency.
＜table six〉be that SBR is respectively to the judged result table of writing property, adherence and absorbency.Conclusion:
| PVA | ||||||||||
| No | 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 |
| Writing property | e | e | e | g | g | f | f | f | e | f |
| Adherence | g | g | f | f | g | f | f | f | f | f |
| Absorbency | e | e | g | g | g | e | e | e | f | e |
| No | 11 | 12 | 13 | 14 | 15 | 16 | 17 | 18 | 19 | |
| Writing property | g | g | g | g | g | e | e | e | e | |
| Adherence | f | g | g | e | e | f | f | f | g | |
| Absorbency | e | g | g | g | f | g | f | f | g | |
| PA | ||||||||||
| No | 20 | 21 | 22 | 23 | 24 | 25 | 26 | 27 | 28 | 29 |
| Writing property | f | f | e | g | g | f | f | f | g | f |
| Adherence | e | g | g | g | g | e | e | g | g | Shedding |
| Absorbency | f | f | f | f | f | f | f | e | g | |
| No | 30 | 31 | 32 | 33 | 34 | |||||
| Writing property | f | f | f | g | e | |||||
| Adherence | g | e | e | e | e | |||||
| Absorbency | f | f | f | g | g | |||||
| SBR | ||||||||||
| No | 35 | 36 | 37 | 38 | 39 | 40 | 41 | 42 | 43 | 44 |
| Writing property | g | e | e | g | g | g | g | e | g | g |
| Adherence | e | e | e | f | e | e | e | e | g | e |
| Absorbency | f | f | f | f | f | f | f | g | g | f |
| No | 45 | 46 | 47 | 48 | 49 | |||||
| Writing property | e | g | g | g | g | |||||
| Adherence | e | e | g | f | f | |||||
| Absorbency | g | g | g | g | g | |||||
1, the pigment result of use is preferable with Clay, CaCO
3Take second place TiO
2The poorest.
2, the effect of adhesive is with PVA the best, and SBR takes second place, and PVAc is the poorest.
3, the dry measure of adhesive and pigment than usable range between 1: 1～1: 10.
So, can make various change in color in order to make note 1, with convenient identification, in the use of note 1 surface-coated smears, the dry measure ratio that adhesive mixes with pigment is between 1: 1～1: 10, make when being coated on note 1 surface formation writing surface 112, still can make note 1 keep its transparency, and, in the smears that this experiment was coated with, coat that formed writing surface is the vaporific transparent body on the note 11, if for making each note 1 can have change in color and writing property concurrently, can in the smears, add colored pigment, the use amount of this colored pigment accounts for adds more than 2% of total amount of pigment, and can reach the effect that stains, in addition, because of the addition of colored pigment few, so to this note 1 surface nature did not influence.
Cooperate shown in Fig. 1,2, the note 1 that present embodiment is made according to above-mentioned steps is except each note 1 can utilize transparent polypropylene (Polypropylene again; P.P) plastics, or constitute with materials such as PE, PVC, PET, Mylar, and have that matter is thin, smooth, the transparency is fabulous, tensile strength is big, resistance to water is good and characteristic such as formed products gloss is beautiful, in addition, cooperate present embodiment again, the surface of note 1, be coated with the smears that adhesive mixes with pigment, when making the smears coat note 1 surperficial, can form one in the smooth surface of note 1 and slightly be vaporific writing surface 112, and that writing surface 112 is is transparent, vaporific, when writing, can make ink be easy to be attached on the writing surface 112 simultaneously.
Crystalinformal note 1 except can according to the foregoing description described made bind into book form, and can adopt individual form, when just making through material preparation step 21, after the gluing step 22, save stacking procedure 23, note 1 is directly carried out with cutting step 24, to determine individual note of appropriate size, last again individual note 1 be attached at the surface and be coated with on the release liners (figure does not show) of mould release, just can form individual note 1, in addition, above-mentioned spendable mould release kind is a lot, and the composition of smears is same as the prior art, so no longer be described in detail, during use,, can make note 1 in use because of note 1 is that the mat mould release makes release liners and its produce release interface, directly tear off use, or note 1 is attached on the release liners again from release liners.
In sum, compared with prior art, the present invention has following effect:
(1) intensity is better:
Because the material of note of the present invention is transparent polypropylene plastics, PE, PVC, PET or Mylar etc., its surperficial tensile strength is large, even thinner thickness also is not easy to damage, so can not cause nib to wear out note because writing, therefore, is not easy to break.
(2) cost is low:
Because note of the present invention is the plastic sheeting that is made of materials such as propylene plastics, PE, PVC, PET or Mylar, its tensile strength is large, thus low cost of manufacture, and thin thickness, conservation.
(3) note has changeability:
Because note of the present invention is polypropylene plastics, transparency is good, and the smears that note surface applies can attach various pigment, makes the note surface present the transparency of different colours, and can increase the diversity of water-based note.
(4) resistance to water is good:
Because note of the present invention is to be made of plastics, itself just has water proofing property, therefore, damages if touch moisture content during use and be not easy, and can guarantee information intact on the note.
Claims (10)
1, a kind of informal note for keeping record, body in the form of sheets is characterized in that:
It is formed by transparent plastic sheeting, and its surface-coated has the smears that can write, and the smears is mixed by adhesive and pigment, the dry measure of adhesive and pigment than scope between 1: 1～1: 10.
2, note according to claim 1 is characterized in that:
Described plastic sheeting is a polyacrylic film.
3, note according to claim 1 is characterized in that:
Add colored pigment in the described pigment, colored pigment accounts at least 2% of total amount of pigment.
4, note according to claim 1 is characterized in that:
The back side of described each note is coated with peels off glue and forms a binding face, and note can be fitted and be bound into book form.
5, note according to claim 1 is characterized in that:
Attach a release liners on described each note, the release liners surface is coated with peelable mould release.
6, note according to claim 1 is characterized in that, described plastic sheeting is a polyethylene film.
7, note according to claim 1 is characterized in that, described plastic sheeting is a polyvinyl chloride film.
8, note according to claim 1 is characterized in that, described plastic sheeting is the pentaerythrite film.
9, note according to claim 1 is characterized in that, described plastic sheeting is a polyester film.
10, a kind of manufacture method of informal note for keeping record is characterized in that, may further comprise the steps:
A. material preparation step utilizes plastics such as polypropylene plastics, polyethylene, polyvinyl chloride, pentaerythrite or polyester film to make the plastic sheeting of sheet;
B. gluing step, the peelable glue that can repeat to paste in the back side coating with each sheet plastic sheeting of getting ready forms a writing surface;
C. stacking procedure will be handled at the note that the gluing step is finished, and will put in order the volume back side earlier and be coated with peelable glue, and the surface is coated with stacked the binding into book form of many notes of smears;
D. cutting step cuts into suitable size with stacked note of binding into book form.