CN1498917A - Polypropylene(PP)-wood plate - Google Patents
Polypropylene(PP)-wood plate Download PDFInfo
- Publication number
- CN1498917A CN1498917A CNA021467757A CN02146775A CN1498917A CN 1498917 A CN1498917 A CN 1498917A CN A021467757 A CNA021467757 A CN A021467757A CN 02146775 A CN02146775 A CN 02146775A CN 1498917 A CN1498917 A CN 1498917A
- Authority
- CN
- China
- Prior art keywords
- parts
- orders
- consumption
- polypropylene plastics
- polypropylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A plastic-wood board is prepared from polypropylene, wooden powder, filler chosen from talc powder and calcium carbonate, and assistants, including lubricant, stabilizer, cross-linking agent, coupling agent, flexibilizer, machining aid, and coloring agent.
Description
Technical field that the present invention belongs to
The invention belongs to the composite plastic wood plate material that is mixed and made into polypropylene (PP), wood powder and auxiliary agent.
The prior art background
Sheet material has purposes widely, but because the forest reserves are limited, timber resources is fully used and seeks the surrogate with good use properties.
Summary of the invention
The objective of the invention is to propose a kind of plastic wood sheet technical scheme, can make full use of timber resources, and have good use properties, is a kind of novel material of alternative wood plank.
Polypropylene of the present invention (PP) plastic wood sheet, its component comprises polypropylene, wood powder, filler and auxiliary agent, melt polypropylene index M I=0.2～0.5g/10min, or MI=1.0～80G/min, water content is 0.01%～0.15%; Consumption is 100 parts; The wood powder water content is 0.3%～1%, and granularity 150 orders～300 orders, consumption are 30 parts～170 parts; Filler is talcum powder or lime carbonate, and granularity is 150 orders～300 orders, and consumption is 2 parts～20 parts; Auxiliary agent comprises that the cured consumption of lubricant chlorinatedpolyethylene is 0.2 part～10 parts, 0.2～10 part of ethylene bis stearamide, 0.2～5 part of calcium stearate; Stablizer uses Octabenzone (UV-531) 0.2 part～2 parts, 0.2～5.0 part of lauric acid toxilic acid dibutyl tin, perhaps 2,4,0.2 part～5.0 parts of 6-three (the positive oxygen base of 2-hydroxyl-4-phenyl) 1,3,5 triazines (triazine-5); 0.4～8 part of linking agent Diisopropyl azodicarboxylate, 5～50 parts of 1～30 part of coupling agent gamma-amino propyl trimethoxy silicane or three (dioctyl pyrophosphoryl oxygen base) phthalandione isopropyl esters, 5～20 parts of toughner ethylene/vinyl acetates (EVA), 5～20 parts of polychlorostyrene ethene (POE); 2 parts～10 parts of processing aid styrene/acrylic butyl ester/vinylbenzene (SBS), 0.5～1 part of nucleator LDPE10～15 part and hexanodioic acid; Tinting material is an amount of.
For improving or increasing new functions of use, polypropylene plastics wood plank of the present invention also adds 0.3 part～20 parts of whipping agent Cellmic C 121s (AC); 0.5 part～1.5 parts in 0.5 part～1.5 parts of fire retardant chlorinated paraffins and titanium dioxide two antimony; 0.3 part～1.5 parts of oxidation inhibitor butylation sylvan benzene (BHT) and two bays sulfuration dipropionate (DLTP) 0.3 part～1.5 parts.
The moulding process of plastic wood sheet of the present invention is according to above-mentioned prescription, and PP polymkeric substance and wood powder through processing treatment, mixing, granulation, are mixed different pellet heating and meltings again, adopt extrude, injection moulding, casting or calendering formation make sheet material.The equipment of moulding wooden moulding has been prior art.
Embodiments of the invention are as follows:
One of embodiment:
The polypropylene water content is 0.01%～0.15%, and consumption is 100 parts; The wood powder water content is 0.3%～1%, and granularity 150 orders～300 orders, consumption are 50 parts～170 parts; Filler is talcum powder or lime carbonate, and granularity is 150 orders～300 orders, and consumption is 3 parts～20 parts; Auxiliary agent comprises that the cured consumption of lubricant chlorinatedpolyethylene is 0.2 part～10 parts; Stablizer uses Octabenzone (UV-531) 0.2 part～2 parts, and perhaps 2,4,0.2 part-5.0 parts of 6-three (the positive oxygen base of 2-hydroxyl-4-phenyl) 1,3,5 triazines (triazine-5); 0.4～2 part of linking agent Diisopropyl azodicarboxylate; 5～50 parts of 1～30 part of coupling agent gamma-amino propyl trimethoxy silicane or three (dioctyl pyrophosphoryl oxygen base) phthalandione isopropyl esters; 2 parts～10 parts of processing aid styrene/acrylic butyl ester/vinylbenzene (SBS); Tinting material is an amount of.
This example belongs to the plastic wood sheet of common performance.
Two of embodiment:
The polypropylene water content is 0.10%, and consumption is 100 parts; The wood powder water content is below 0.5%, and granularity 150 orders～300 orders, consumption are 50 parts; Filler is talcum powder or lime carbonate, and granularity is 150 orders～300 orders, and consumption is 3 parts; Auxiliary agent comprises that the cured consumption of lubricant chlorinatedpolyethylene is 0.5 part, 0.5 part of ethylene bis stearamide, 0.2 part of calcium stearate; Stablizer uses Octabenzone (UV-531) 0.2 part, 0.2 part of lauric acid toxilic acid dibutyl tin, perhaps 2,4,0.2 part of 6-three (the positive oxygen base of 2-hydroxyl-4-phenyl) 1,3,5 triazine (triazine-5); Linking agent Diisopropyl azodicarboxylate 0.4,10 parts of coupling agent γ-methacrylic aminopropyl dimethylamino silane, 10 parts of toughner ethylene/vinyl acetates (EVA), 10 parts of polychlorostyrene ethene (POE); 2 parts of processing aid styrene/acrylic butyl ester/vinylbenzene (SBS); 25 parts of 15 parts of coupling agent gamma-amino propyl trimethoxy silicanes or three (dioctyl pyrophosphoryl oxygen base) phthalandione isopropyl esters; Tinting material is an amount of.
Three of embodiment:
The polypropylene water content is 0.1 following %, and consumption is 100 parts; The wood powder water content is below 0.5%, and granularity 150 orders～300 orders, consumption are 110 parts, and filler is talcum powder or lime carbonate, and granularity is 150 orders-300 orders, and consumption is 4 parts; Auxiliary agent comprises that the cured consumption of lubricant chlorinatedpolyethylene is 2 parts, 1 part of ethylene bis stearamide, 2 parts of calcium stearates; Stablizer uses Octabenzone (UV-531) 0.5 part, 0.5 part of lauric acid toxilic acid dibutyl tin, perhaps 2,4,2.5 parts of 6-three (the positive oxygen base of 2-hydroxyl-4-phenyl) 1,3,5 triazines (triazine-5); 1 part of linking agent Diisopropyl azodicarboxylate, 20 parts of coupling agent γ-methacrylic aminopropyl dimethylamino silane, 10 parts of toughner ethylene/vinyl acetates (EVA), 10 parts of polychlorostyrene ethene (POE); 5 parts of processing aid styrene/acrylic butyl ester/vinylbenzene (SBS); 40 parts of 20 parts of coupling agent gamma-amino propyl trimethoxy silicanes or three (dioctyl pyrophosphoryl oxygen base) phthalandione isopropyl esters; Tinting material is an amount of.
Four of embodiment:
The polypropylene water content is below 0.1%, and consumption is 100 parts; The wood powder water content is below 0.5%, and granularity 150 orders～300 orders, consumption are 150 parts; Filler is talcum powder or lime carbonate, and granularity is 150 orders～300 orders, and consumption is 8 parts; Auxiliary agent comprises that the cured consumption of lubricant chlorinatedpolyethylene is 8 parts, 8 parts of ethylene bis stearamides, 4 parts of calcium stearates; Stablizer uses Octabenzone (UV-531) 2 parts, 4 parts of lauric acid toxilic acid dibutyl tins, perhaps 2,4,4.5 parts of 6-three (the positive oxygen base of 2-hydroxyl-4-phenyl) 1,3,5 triazines (triazine-5); 1.5 parts of linking agent Diisopropyl azodicarboxylates, 25 parts of coupling agent γ-methacrylic aminopropyl dimethylamino silane, 10 parts of toughner ethylene/vinyl acetates (EVA), 15 parts of polychlorostyrene ethene (POE); 8 parts of processing aid styrene/acrylic butyl ester/vinylbenzene (SBS); Tinting material is an amount of.
More than each routine composition identical, the ratio difference, all example belongs to the good common plastic wood sheet of use properties.
Five of embodiment:
The polypropylene water content is 0.01%～0.15%, and consumption is 100 parts; The wood powder water content is 0.3%～1%, and granularity 150 orders～300 orders, consumption are 50 parts～170 parts; Filler is talcum powder or lime carbonate, and granularity is 150 orders～300 orders, and consumption is 3 parts～20 parts; Auxiliary agent comprises that the cured consumption of lubricant chlorinatedpolyethylene is 0.2 part～10 parts, 0.5～10 part of ethylene bis stearamide, 0.2～5 part of calcium stearate; Stablizer uses Octabenzone (UV-531) 0.2 part～2 parts, and perhaps 2,4,0.2 part～5.0 parts of 6-three (the positive oxygen base of 2-hydroxyl-4-phenyl) 1,3,5 triazines (triazine-5); 0.4～2 part of linking agent Diisopropyl azodicarboxylate; 10～30 parts of coupling agent γ-methacrylic aminopropyl dimethylamino silane; 5～20 parts of toughner ethylene/vinyl acetates (EVA), 5～20 parts of polychlorostyrene ethene (POE); 2 parts～10 parts of processing aid styrene/acrylic butyl ester/vinylbenzene (SBS); 0.5 part～20 parts of whipping agent Cellmic C 121s (AC); Tinting material is an amount of.
This routine plastic wood sheet is a foaming plate.
Six of embodiment:
The polypropylene water content is 0.01%～0.15%, and consumption is 100 parts; The wood powder water content is 0.3%～1%, and granularity 150 orders～300 orders, consumption are 50 parts～170 parts; Filler is talcum powder or lime carbonate, and granularity is 150 orders～300 orders, and consumption is 3 parts～20 parts; Auxiliary agent comprises that the cured consumption of lubricant chlorinatedpolyethylene is 0.2 part～10 parts, 0.5～10 part of ethylene bis stearamide, 0.2～5 part of calcium stearate; Stablizer uses Octabenzone (UV-531) 0.2 part～2 parts, and perhaps 2,4,0.2 part～5.0 parts of 6-three (the positive oxygen base of 2-hydroxyl-4-phenyl) 1,3,5 triazines (triazine-5); 0.4～2 part of linking agent Diisopropyl azodicarboxylate; 5～30 parts of coupling agent γ-methacrylic aminopropyl dimethylamino silane; 5～20 parts of toughner ethylene/vinyl acetates (EVA), 5～20 parts of polychlorostyrene ethene (POE); 0.5 part～1.5 parts in 0.5 part～1.5 parts of fire retardant chlorinated paraffins and titanium dioxide two antimony; 2 parts～10 parts of processing aid styrene/acrylic butyl ester/vinylbenzene (SBS); Tinting material is an amount of.
This routine plastic wood sheet is a flame-proof sheet material.
Seven of embodiment:
The polypropylene water content is 0.01%～0.15%, and consumption is 100 parts; The wood powder water content is 0.3%～1%, and granularity 150 orders～300 orders, consumption are 50 parts～170 parts; Filler is talcum powder or lime carbonate, and granularity is 150 orders～300 orders, and consumption is 3 parts～20 parts; Auxiliary agent comprises that the cured consumption of lubricant chlorinatedpolyethylene is 0.2 part～10 parts, 0.5～10 part of ethylene bis stearamide, 0.2～5 part of calcium stearate; Stablizer uses Octabenzone (UV-531) 0.2 part～2 parts, and perhaps 2,4,0.2 part～5.0 parts of 6-three (the positive oxygen base of 2-hydroxyl-4-phenyl) 1,3,5 triazines (triazine-5); Linking agent Diisopropyl azodicarboxylate 0.4-2 part; 10～25 parts of coupling agent γ-methacrylic aminopropyl dimethylamino silane; 5～20 parts of toughner ethylene/vinyl acetates (EVA), 5～20 parts of polychlorostyrene ethene (POE); 0.3 part～1.5 parts of oxidation inhibitor butylation sylvan benzene (BHT) and two bays sulfuration dipropionate (DLTP) 0.3 part～1.5 parts; 2 parts-10 parts of processing aid styrene/acrylic butyl ester/vinylbenzene (SBS); Tinting material is an amount of.
This routine plastic wood sheet material is anti-aging sheet material.
Eight of embodiment:
The polypropylene water content is 0.01%～0.15%, and consumption is 100 parts; The wood powder water content is 0.3%～1%, and granularity 150 orders～300 orders, consumption are 50 parts～170 parts; Filler is talcum powder or lime carbonate, and granularity is 150 orders～300 orders, and consumption is 3 parts～20 parts; Auxiliary agent comprises that the cured consumption of lubricant chlorinatedpolyethylene is 0.2 part～10 parts, 0.5～10 part of ethylene bis stearamide, 0.2～5 part of calcium stearate; Stablizer uses Octabenzone (UV-531) 0.2 part～2 parts, and perhaps 2,4,0.2 part～5.0 parts of 6-three (the positive oxygen base of 2-hydroxyl-4-phenyl) 1,3,5 triazines (triazine-5); Linking agent Diisopropyl azodicarboxylate 0.4-2 part; 10～30 parts of coupling agent γ-methacrylic aminopropyl dimethylamino silane; 5～20 parts of toughner ethylene/vinyl acetates (EVA), 5～20 parts of polychlorostyrene ethene (POE); 2 parts-10 parts of processing aid styrene/acrylic butyl ester/vinylbenzene (SBS); Whipping agent Cellmic C 121 (AC) 0.3-3.0 part; 0.5 part-1.5 parts in 0.5 part-1.5 parts of fire retardant chlorinated paraffins and titanium dioxide two antimony; Tinting material is an amount of.
This example is a foaming flame retardant type sheet material.
Nine of embodiment:
The polypropylene water content is 0.01%～0.15%, and consumption is 100 parts; The wood powder water content is 0.3%～1%, and granularity 150 orders～300 orders, consumption are 50 parts～170 parts; Filler is talcum powder or lime carbonate, and granularity is 150 orders～300 orders, and consumption is 3 parts～20 parts; Auxiliary agent comprises that the cured consumption of lubricant chlorinatedpolyethylene is 0.2 part～10 parts, 0.5～10 part of ethylene bis stearamide, 0.2～5 part of calcium stearate; Stablizer uses Octabenzone (UV-531) 0.2 part～2 parts, and perhaps 2,4,0.2 part～5.0 parts of 6-three (the positive oxygen base of 2-hydroxyl-4-phenyl) 1,3,5 triazines (triazine-5); 0.4～2 part of linking agent Diisopropyl azodicarboxylate; 10～30 parts of coupling agent γ-methacrylic aminopropyl dimethylamino silane; 5～20 parts of toughner ethylene/vinyl acetates (EVA), 5～20 parts of polychlorostyrene ethene (POE); 0.3～3.0 part of whipping agent Cellmic C 121 (AC); 0.5 part～1.5 parts in 0.5 part～1.5 parts of fire retardant chlorinated paraffins and titanium dioxide two antimony; 0.3 part～1.5 parts of oxidation inhibitor butylation sylvan benzene (BHT) and two bays sulfuration dipropionate (DLTP) 0.3 part～1.5 parts; 2～10 parts of processing aid styrene/acrylic butyl ester/vinylbenzene (SBS); Tinting material is an amount of.
This example is a foaming flame-proof anti-aging plastic wood sheet.
Ten of embodiment:
The polypropylene water content is 0.01%～0.15%, and consumption is 100 parts; The wood powder water content is 0.3%～1%, and granularity 150 orders～300 orders, consumption are 70 parts～80 parts; Filler is talcum powder or lime carbonate, and granularity is 150 orders～300 orders, and consumption is 3 parts～20 parts; Auxiliary agent comprises that the cured consumption of lubricant chlorinatedpolyethylene is 0.2 part～10 parts, 0.5～10 part of ethylene bis stearamide, 0.2～5 part of calcium stearate; Stablizer uses Octabenzone (UV-531) 0.2 part～2 parts, and perhaps 2,4,0.2 part～5.0 parts of 6-three (the positive oxygen base of 2-hydroxyl-4-phenyl) 1,3,5 triazines (triazine-5); 0.4～2 part of linking agent Diisopropyl azodicarboxylate; 10～20 parts of coupling agent γ-methacrylic aminopropyl dimethylamino silane; 5～20 parts of toughner ethylene/vinyl acetates (EVA), 5～20 parts of polychlorostyrene ethene (POE); 2 parts-10 parts of processing aid styrene/acrylic butyl ester/vinylbenzene (SBS); Tinting material is an amount of.
This routine plastic wood sheet has favorable waterproof property.
11 of embodiment:
The polypropylene water content is 0.01%～0.15%, and consumption is 100 parts; The wood powder water content is 0.3%～1%, and granularity 150 orders～300 orders, consumption are 80 parts～100 parts; Filler is talcum powder or lime carbonate, and granularity is 150 orders～300 orders, and consumption is 3 parts～20 parts; Auxiliary agent comprises that the cured consumption of lubricant chlorinatedpolyethylene is 0.2 part～10 parts, 0.5～10 part of ethylene bis stearamide, 0.2～5 part of calcium stearate; Stablizer uses Octabenzone (UV-531) 0.2 part～2 parts, and perhaps 2,4,0.2 part～5.0 parts of 6-three (the positive oxygen base of 2-hydroxyl-4-phenyl) 1,3,5 triazines (triazine-5); Linking agent Diisopropyl azodicarboxylate 0.4-2 part; 10～20 parts of coupling agent γ-methacrylic aminopropyl dimethylamino silane; 5～20 parts of toughner ethylene/vinyl acetates (EVA), 5～20 parts of polychlorostyrene ethene (POE); 2 parts-10 parts of processing aid styrene/acrylic butyl ester/vinylbenzene (SBS), tinting material is an amount of.
This routine plastic wood sheet has resistance to elevated temperatures.
12 of embodiment:
The polypropylene water content is 0.01%～0.15%, and consumption is 100 parts; The wood powder water content is 0.3%～1%, and granularity 150 orders～300 orders, consumption are 50 parts～170 parts; Filler is talcum powder or lime carbonate, and granularity is 150 orders～300 orders, and consumption is 3 parts～20 parts; Auxiliary agent comprises that the cured consumption of lubricant chlorinatedpolyethylene is 0.2 part～10 parts, 0.5～10 part of ethylene bis stearamide, 0.2～5 part of calcium stearate; Stablizer uses Octabenzone (UV-531) 0.2 part～2 parts, and perhaps 2,4,0.2 part～5.0 parts of 6-three (the positive oxygen base of 2-hydroxyl-4-phenyl) 1,3,5 triazines (triazine-5); Linking agent Diisopropyl azodicarboxylate 0.4-2 part; 1～30 part of coupling agent γ-methacrylic aminopropyl dimethylamino silane; 5～20 parts of toughner ethylene/vinyl acetates (EVA), 5～20 parts of polychlorostyrene ethene (POE); 0.5～5 part of static inhibitor polyetheramides imines; 2 parts～10 parts of processing aid styrene/acrylic butyl ester/vinylbenzene (SBS); Tinting material is an amount of.
This routine plastic wood sheet has antistatic property.
13 of embodiment:
The polypropylene water content is 0.01%～0.15%, and consumption is 100 parts; The wood powder water content is 0.3%～1%, and granularity 150 orders～300 orders, consumption are 50 parts～170 parts; Filler is talcum powder or lime carbonate, and granularity is 150 orders～300 orders, and consumption is 3 parts～20 parts; Auxiliary agent comprises that the cured consumption of lubricant chlorinatedpolyethylene is 0.2 part～10 parts, 0.5～10 part of ethylene bis stearamide, 0.2～5 part of calcium stearate; Stablizer uses Octabenzone (UV-531) 0.2 part～2 parts, and perhaps 2,4,0.2 part～5.0 parts of 6-three (the positive oxygen base of 2-hydroxyl-4-phenyl) 1,3,5 triazines (triazine-5); 0.4～2 part of linking agent Diisopropyl azodicarboxylate; 1～30 part of coupling agent γ-methacrylic aminopropyl dimethylamino silane; 5～20 parts of toughner ethylene/vinyl acetates (EVA), 5～20 parts of polychlorostyrene ethene (POE); Mould resistant N, 0.5～2 part of N '-diacetyl-hexanoyl two hydrazides; 2 parts-10 parts of processing aid styrene/acrylic butyl ester/vinylbenzene (SBS); Tinting material is an amount of.
This routine plastic wood sheet has mildew-resistant sex change energy.
14 of embodiment:
The polypropylene water content is 0.01%～0.15%, and consumption is 100 parts; The wood powder water content is 0.3%～1%, and granularity 150 orders～300 orders, consumption are 50 parts～170 parts; Filler is talcum powder or lime carbonate, and granularity is 150 orders～300 orders, and consumption is 3 parts～20 parts; Auxiliary agent comprises that the cured consumption of lubricant chlorinatedpolyethylene is 0.2 part～10 parts, 0.5～10 part of ethylene bis stearamide, 0.2～5 part of calcium stearate; Stablizer uses Octabenzone (UV-531) 0.2 part～2 parts, and perhaps 2,4,0.2 part～5.0 parts of 6-three (the positive oxygen base of 2-hydroxyl-4-phenyl) 1,3,5 triazines (triazine-5); 0.4～2 part of linking agent Diisopropyl azodicarboxylate; 10～30 parts of coupling agent γ-methacrylic aminopropyl dimethylamino silane; 5～20 parts of toughner ethylene/vinyl acetates (EVA), 5～20 parts of polychlorostyrene ethene (POE); 2～10 parts of anti-termite agent 4-chloro-2-phenylphenols; 2 parts-10 parts of processing aid styrene/acrylic butyl ester/vinylbenzene (SBS); Tinting material is an amount of.
This routine plastic wood sheet has the performance of anti-ant and insect pest infestation.
The waste and scrap that the PP polymkeric substance that plastic wood sheet of the present invention uses can be to use, wood powder can become powder with depleted timber tankage, water footpath material, brush wood, waste and old wood and low-quality wood working, and timber resources is fully used.The plastic wood sheet of making according to above-mentioned prescription can substitute wood plank and use, and is easy to process, but can follow closely, can bore, can dig, can glue greasepaint; And there is not timber inherent defective, as knot, be full of cracks, warpage, the spot that easily adds lustre to, malicious spot and rotten etc.
Plastic wood sheet of the present invention can also reclaim second stage employ.
That the plastic wood sheet of making according to above-mentioned prescription has is water-fast, acid and alkali-resistance, do not damaged by worms, long fungi and characteristics such as pollution-free.These characteristics relevant with the ratio of wood powder in the prescription, the wood powder ratio changes, and the performance of moulding sheet material will change.The scope that the ratio of wood powder provides less than the present invention also can be made plastic wood sheet, but increases cost, improves seldom on use properties, and the ratio of performance to price is unreasonable.
Claims (11)
1, a kind of polypropylene plastics wood plank, its component comprises polypropylene (PP), wood powder, filler and auxiliary agent, it is characterized in that melt polypropylene index M I=0.2～0.5g/10min, and water content is 0.01%～0.15%, and consumption is 100 parts; The wood powder water content is 0.3%～1%, and granularity 150 orders～300 orders, consumption are 30 parts～170 parts; Filler is talcum powder or lime carbonate, and granularity is 150 orders～300 orders, and consumption is 2 parts～20 parts; Auxiliary agent comprises that the cured consumption of lubricant chlorinatedpolyethylene is 0.2 part～10 parts, 0.2～10 part of ethylene bis stearamide, 0.2～5.0 part of calcium stearate; Stablizer uses Octabenzone (UV-531) 0.2 part～2 parts, 0.2～5 part of lauric acid toxilic acid dibutyl tin, perhaps 2,4,0.2 part～5.0 parts of 6-three (the positive oxygen base of 2-hydroxyl-4-phenyl) 1,3,5 triazines (triazine-5); 2 parts～10 parts of processing aid styrene/acrylic butyl ester/vinylbenzene (SBS), 0.4～8 part of linking agent Diisopropyl azodicarboxylate, coupling agent gamma-amino propyl trimethoxy silicane 1-30 part or three (dioctyl pyrophosphoryl oxygen base) phthalandione isopropyl ester 5-50 part, toughner ethylene/vinyl acetate (EVA) 5-20 part, polychlorostyrene ethene (POE) 5-20 part, 0.5～1 part of nucleator LDPE10～15 part and hexanodioic acid; Tinting material is an amount of.
2, polypropylene plastics wood plank as claimed in claim 1 is characterized in that: also add 0.5 part-20 parts of whipping agent Cellmic C 121s (AC).
3, polypropylene plastics wood plank as claimed in claim 1 is characterized in that: also add 0.5 part-1.5 parts in 0.5 part-1.5 parts of fire retardant chlorinated paraffins and titanium dioxide two antimony.
4, polypropylene plastics wood plank as claimed in claim 1 is characterized in that: also add 0.3 part-1.5 parts of oxidation inhibitor butylation sylvan benzene (BHT) and two bays sulfuration dipropionate (DLTP) 0.3 part-1.5 parts.
5, polypropylene plastics wood plank as claimed in claim 1 is characterized in that: also add 0.5 part-20 parts of whipping agent Cellmic C 121s (AC), 0.5 part-1.5 parts in fire retardant chlorinated paraffin part-1.5 part and titanium dioxide two antimony.
6, polypropylene plastics wood plank as claimed in claim 1, it is characterized in that: also add 0.5 part-20 parts of whipping agent Cellmic C 121s (AC), 0.5 part-1.5 parts in 0.5 part-1.5 parts of fire retardant chlorinated paraffins and titanium dioxide two antimony, 0.3 part-1.5 parts of oxidation inhibitor butylation sylvan benzene (BHT) and two bays sulfuration dipropionate (DLTP) 0.3 part-1.5 parts.
7, polypropylene plastics wood plank as claimed in claim 1 is characterized in that: also add static inhibitor polyetheramides imines 0.5-5 part, or 30～80 parts of 0.1～1 part of polyethylene glycol monolaurate and methylsulphonic acid lithiums (10% content).
8, polypropylene plastics wood plank as claimed in claim 1 is characterized in that: also add mould resistant N, the acyl two hydrazides 0.5-2 parts of N '-diacetyl-.
9, polypropylene plastics wood plank as claimed in claim 1 is characterized in that: also add anti-termite agent 4-chloro-2-phenylphenol 2-10 part.
10, polypropylene plastics wood plank as claimed in claim 1 is characterized in that: the usage quantity of wood powder is 70 parts-80 parts.
11, polypropylene plastics wood plank as claimed in claim 1 is characterized in that: the usage quantity of wood powder is 90 parts--100 parts.