CN1481677A - 热熔粘鼠胶及其合成方法 - Google Patents

热熔粘鼠胶及其合成方法 Download PDF

Info

Publication number
CN1481677A
CN1481677A CNA031334903A CN03133490A CN1481677A CN 1481677 A CN1481677 A CN 1481677A CN A031334903 A CNA031334903 A CN A031334903A CN 03133490 A CN03133490 A CN 03133490A CN 1481677 A CN1481677 A CN 1481677A
Authority
CN
China
Prior art keywords
polybutene
mouse
glue
liquid
antioxidant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA031334903A
Other languages
English (en)
Other versions
CN1222212C (zh
Inventor
赵振民
林福顺
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DALIAN SANLI DISINFECTING Co Ltd
Original Assignee
DALIAN SANLI DISINFECTING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DALIAN SANLI DISINFECTING Co Ltd filed Critical DALIAN SANLI DISINFECTING Co Ltd
Priority to CN 03133490 priority Critical patent/CN1222212C/zh
Publication of CN1481677A publication Critical patent/CN1481677A/zh
Application granted granted Critical
Publication of CN1222212C publication Critical patent/CN1222212C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

热熔粘鼠胶及其合成方法属于鼠害防治技术领域。热熔粘鼠胶配方是，2～10％固体聚丁烯、80～98％液体聚丁烯、1～10％聚乙烯和0.1～1.0％抗氧剂；将固体聚丁烯和液体聚丁烯放入炼胶机中，在温度为50～180℃、压力为0～0.7MPa的条件下，混炼0.5～3.5小时，然后把聚乙烯、抗氧剂、液体聚丁烯和炼好的混炼胶加入到制胶釜中混合，在温度为100～210℃、压力为0～0.1MPa的条件下，搅拌5～20小时，即得到粘鼠胶。本发明的有益效果是方法简单、设备投资少、能耗低、产品质量稳定。主要应用在鼠害及有害昆虫防治上。

Description

热熔粘鼠胶及其合成方法
技术领域    本发明属于鼠害防治技术领域。
背景技术    目前常用的粘鼠胶粘鼠效果不理想，单位用胶量较大，成本高。
发明内容    本发明的目的是提供一种方法简单、设备投资少、能耗低、产品质量稳定的热熔粘鼠胶及其合成方法。
本发明的技术解决方案是，热熔粘鼠胶，由2～10％固体聚丁烯、80～98％液体聚丁烯、1～10％聚乙烯和0.1～1.0％抗氧剂组成。
热熔粘鼠胶较佳配方是，3％固体聚丁烯、95％液体聚丁烯、1.5％聚乙烯和0.5％抗氧剂。
合成热熔粘鼠胶的方法，步骤是：
a.将2～10％固体聚丁烯和15～25％液体聚丁烯放入炼胶机中，在温度为50～180℃、压力为0～0.7Mpa的条件下，混炼0.5～3.5小时，
b.把1～10％聚乙烯、0.1～1.0％抗氧剂、65～73％液体聚丁烯和炼好的混炼胶加入到制胶釜中混合，在温度为100～210℃、压力为0～0.1Mpa的条件下，搅拌5～20小时，即得到粘鼠胶。
合成热熔粘鼠胶的方法，较佳步骤是：
a.将3％固体聚丁烯和20％液体聚丁烯放入炼胶机中，在温度为110℃、压力为0.35Mpa的条件下，混炼2小时，
b.把1.5％聚乙烯、0.5％抗氧剂、75％液体聚丁烯和炼好的混炼胶加入到制胶釜中混合，在温度为150℃、压力为0.05Mpa的条件下，搅拌12小时，即得到粘鼠胶。
本发明的有益效果是方法简单、设备投资少、能耗低、产品质量稳定。
具体实施方式    下面结合实施例对本发明作进一步的说明。
取3kg固体聚丁烯、95kg液体聚丁烯、1.5kg聚乙烯和0.5kg抗氧剂备用。
合成热熔粘鼠胶的方法，步骤是：
a.将3kg固体聚丁烯和20kg液体聚丁烯放入炼胶机中，在温度为110℃、压力为0.35Mpa的条件下，混炼2小时，
b.把1.5kg聚乙烯、0.5kg抗氧剂、75kg液体聚丁烯和炼好的混炼胶加入到制胶釜中混合，在温度为150℃、压力为0.05Mpa的条件下，搅拌12小时，即得到粘鼠胶。

Claims (4)

1.热熔粘鼠胶，其特征在于，由2～10％固体聚丁烯、80～98％液体聚丁烯、1～10％聚乙烯和0.1～1.0％抗氧剂组成。
2.热熔粘鼠胶，其特征在于，由3％固体聚丁烯、95％液体聚丁烯、1.5％聚乙烯和0.5％抗氧剂组成。
3.合成权利要求1、2所述的热熔粘鼠胶的方法，其特征在于，
a.将2～10％固体聚丁烯和15～25％液体聚丁烯放入炼胶机中，在温度为50～180℃、压力为0～0.7Mpa的条件下，混炼0.5～3.5小时，
b.把1～10％聚乙烯、0.1～1.0％抗氧剂、65～73％液体聚丁烯和炼好的混炼胶加入到制胶釜中混合，在温度为100～210℃、压力为0～0.1Mpa的条件下，搅拌5～20小时，即得到粘鼠胶。
4.根据权利要求3所述的热熔粘鼠胶的合成方法，其特征在于，
a.将3％固体聚丁烯和20％液体聚丁烯放入炼胶机中，在温度为110℃、压力为0.35Mpa的条件下，混炼2小时，
b.把1.5％聚乙烯、0.5％抗氧剂、75％液体聚丁烯和炼好的混炼胶加入到制胶釜中混合，在温度为150℃、压力为0.05Mpa的条件下，搅拌12小时，即得到粘鼠胶。
CN 03133490 2003-06-21 2003-06-21 热熔粘鼠胶及其合成方法 Expired - Fee Related CN1222212C (zh)