CN1480584A - 利用纳米银与活性碳纤维的结合制作抗菌材料的方法 - Google Patents

利用纳米银与活性碳纤维的结合制作抗菌材料的方法 Download PDF

Info

Publication number
CN1480584A
CN1480584A CNA021293589A CN02129358A CN1480584A CN 1480584 A CN1480584 A CN 1480584A CN A021293589 A CNA021293589 A CN A021293589A CN 02129358 A CN02129358 A CN 02129358A CN 1480584 A CN1480584 A CN 1480584A
Authority
CN
China
Prior art keywords
drying
activated carbon
carbon fiber
concentrated
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA021293589A
Other languages
English (en)
Inventor
刘维春
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNA021293589A priority Critical patent/CN1480584A/zh
Publication of CN1480584A publication Critical patent/CN1480584A/zh
Pending legal-status Critical Current

Abstract

一种利用纳米银与活性碳纤维的结合制作抗菌材料的方法，其特征在于：用离子交换法将纳米量级的银与氧化银的结合(使其达到10－9m)酌床在活性碳纤维的表面。本发明的优点是：1.大大增强了纳米银的杀菌力。纳米银与活性碳纤维结合后其间接杀菌的直径为15mm左右。2.将纳米银处理过的活性碳纤维做成栓状剂型，可用于治疗妇女的各种阴道感染以及宫颈糜烂，经北京协和医院、中国人民解放军总医院等多家著名医院的临床验证：其杀菌率不受酸碱度的影响，改变了传统用药的理念，再通过碳纤维的强引流性将阴道的致病菌清除，使其恢复正常的生理自洁功能，其抑菌的总有效率达90％以上。

Description

利用纳米银与活性碳纤维的结合制作抗菌材料的方法
所属领域：
本发明涉及一种纳米银与织物相结合的方法，特别涉及一种利用纳米银的抗菌性能与活性碳纤维的结合制作抗菌材料的方法。
背景技术：
纳米银的长效广谱抗菌性能已被世界多国科学家研究证实并应用于医学临床上。目前临床上将纳米银与功能性织物相结合，用于各种伤口的愈合，由于纳米银的杀菌直径比较小，其抑菌圈其直径为2毫米左右，因此杀菌的空间比较小也比较被动，而且纳米银离不开银与氧化银的载体，而功能性织物其吸附性比较小，遇水后吸附性更差，其杀菌的直径为2mm-5mm。这就需要纳米银与一种能让各种致病菌与其结合的材料相结合。
发明内容：
本发明的目的就在于克服上述现有技术中存在的不足，而提供一种利用纳米银与活性碳纤维的结合制作抗菌材料的方法，通过这种方法可大大地提高纳米银的杀菌力。
本发明的技术方案是：一种利用纳米银与活性碳纤维的结合制作抗菌材料的方法，其特征在于：用离子交换法将纳米量级的银与氧化银的结合(使其达到10-9m)酌床在活性碳纤维的表面。
上述离子交换法依下列步骤进行：①根据溶液的配比取AgNO3溶于水中，再加入浓NH3H2O、浓NaOH、NH4NO3使之溶解并混合均匀；②取葡萄糖、溶于水中，加浓HNO3、乙醇并混合均匀；③将1、2所得的两种溶液混合均匀，并放入活性碳纤维浸泡在室温下搅拌使之充分均匀；④加入氧化剂充分搅拌使之湿润，取出，挤去多余的溶液或甩干，放入烘箱烘干，以后多次漂洗烘干，即可。
上述AgNO3取100克、取AgNO3100克，溶于40升的水中，加浓NH3H2O500毫升、浓NaOH50克、NH4NO3500克使之溶解并混合均匀。取葡萄糖20克、溶于5升水中，加浓HNO310毫升，乙醇1.5升。将这两种溶液混合均匀，加入10公斤活性碳纤维浸泡5分钟，在室温下搅拌使之充分均匀，再加入1升的双氧水充分搅拌使之湿润。5分钟后取出，挤去多余的溶液或甩干，放入烘箱烘干，以后多次漂洗烘干，即可。
本发明的具体反应机理为： 本发明的抑菌机理为：
Ag+易与带阳电的细菌蛋白中的巯基-SH结合使这些致病菌赖以生存的酶丧失活性，从而达到抑菌效果。由此所制得的纳米银经检测其对致病菌的MIC为0.16～8.97毫克/毫升，MBC为3.05～82.90毫克/毫升，其杀菌的直径为2mm-5mm。活性碳具有高吸附性，其吸附的重量大于自身重量的20倍，而且利用其动力学微孔填充原理，其吸附细菌的参数大于其吸附液体的参数。因此纳米银与活性碳纤维结合后其间接杀菌的直径为15mm左右。
本发明的优点是：1、大大增强了纳米银的杀菌力。纳米银与活性碳纤维结合后其间接杀菌的直径为15mm左右。2、将纳米银处理过的活性碳纤维做成栓状剂型，可用于治疗妇女的各种阴道感染以及宫颈糜烂，经北京协和医院、中国人民解放军总医院等多家著名医院的临床验证：其杀菌率不受酸碱度的影响，改变了传统用药的理念，再通过碳纤维的强引流性将阴道的致病菌清除，使其恢复正常的生理自洁功能，其抑菌的总有效率达90％以上。
具体实施方式：
称取AgNO3100克，溶于40升的水中，加浓NH3H2O500毫升、浓NaOH50克、NH4NO3500克使之溶解并混合均匀。取葡萄糖20克、溶于5升水中，加浓HNO310毫升，乙醇1.5升。将这两种溶液混合均匀，加入10公斤活性碳纤维浸泡5分钟，在室温下搅拌使之充分均匀，再加入1升的双氧水充分搅拌使之湿润。5分钟后取出，挤去多余的溶液或甩干，放入烘箱烘干，以后多次漂洗烘干，即可得到本发明产品。

Claims (3)

1、一种利用纳米银与活性碳纤维的结合制作抗菌材料的方法，其特征在于：用离子交换法将纳米量级的银与氧化银的结合(使其达到10-9m)酌床在活性碳纤维的表面。
2、根据权利要求1所述的利用纳米银与活性碳纤维的结合制作抗菌材料的方法，上述离子交换法依下列步骤进行：①根据溶液的配比取AgNO3溶于水中，再加入浓NH3H2O、浓NaOH、NH4NO3使之溶解并混合均匀；②取葡萄糖、溶于水中，加浓HNO3乙醇并混合均匀；③将1、2所得的两种溶液混合均匀，并放入活性碳纤维浸泡在室温下搅拌使之充分均匀；④加入氧化剂充分搅拌使之湿润，取出，挤去多余的溶液或甩干，放入烘箱烘干，以后多次漂洗烘干，即可。
3、根据权利要求2所述的利用纳米银与活性碳纤维的结合制作抗菌材料的方法，上述AgNO3取100克、取AgNO3100克，溶于40升的水中，加浓NH3H2O500毫升、浓NaOH50克、NH4NO3500克使之溶解并混合均匀。取葡萄糖20克、溶于5升水中，加浓HNO310毫升，乙醇1.5升。将这两种溶液混合均匀，加入10公斤活性碳纤维浸泡5分钟，在室温下搅拌使之充分均匀，再加入1升的双氧水充分搅拌使之湿润。5分钟后取出，挤去多余的溶液或甩干，放入烘箱烘干，以后多次漂洗烘干，即可。
CNA021293589A 2002-09-06 2002-09-06 利用纳米银与活性碳纤维的结合制作抗菌材料的方法 Pending CN1480584A (zh)