CN1442055A - Fishing rod - Google Patents
Fishing rod Download PDFInfo
- Publication number
- CN1442055A CN1442055A CN03105147A CN03105147A CN1442055A CN 1442055 A CN1442055 A CN 1442055A CN 03105147 A CN03105147 A CN 03105147A CN 03105147 A CN03105147 A CN 03105147A CN 1442055 A CN1442055 A CN 1442055A
- Authority
- CN
- China
- Prior art keywords
- fiber
- bamboo
- fishing rod
- bamboo fibre
- fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
To provide a fishing rod which can be produced with comparatively uniform quality, excellent in fishing touch with bamboo rod like mild return to bending. The fishing rod is provided with a rod tube comprising a fiber reinforced resin and the fiber reinforced resin contains opened bamboo fibers with fiber diameter of 0.01-0.5 mm as the reinforcing fiber.
Description
Technical field
The present invention relates to fishing rod, be specifically related to have fishing rod by the pole pipe of fiber-reinforced resin system.
Background technology
Because the light and slow ground of bamboo pole is crooked, resilience (reinstatements) is also releived, and is acknowledged as feeling good of fishing always, so the bamboo pole fishing rod of many types of having pass by produce and market.
But, bamboo pole is that natural bamboo process is added hot-working, goes to save processing back uses such as processing, kinking japanning processing, its performance is subjected to the growing state of bamboo and the influence of processing method to a great extent, the quality of the flexibility of each pole etc. is uneven, for this reason, there is the problem that is difficult to produce the uniform product of quality in bamboo pole.
So in recent years, as the substitute of bamboo pole, use the fishing rod of making as the fiber-reinforced resin of reinforcing fiber by carbon fiber or glass fibre to become main flow.
The fishing rod that forms with fiber-reinforced resin like this, owing to be not the natural products that directly uses as the bamboo pole,, compare with bamboo pole simultaneously so product quality is more even, owing to have advantage in light weight, that intensity is high, be almost in recent years all fish use.
But, the fishing rod that the fiber-reinforced resin that carbon fiber or glass fibre are used as reinforcing fiber is made, can external force bendings such as hook have been gone up because of pulling or the fish of fish, in case but this external force reduces or disappears just to restore to the original state at once easily, so the recovery to bending is too responsive, consequently exist reaction to lack the problem of the sensation of fishing than machinery.
Summary of the invention
The present invention be directed to above-mentioned the problems of the prior art, can producing the uniform product of quality, and provide and as bamboo pole, the recovery of bending is relatively releived and rich fishing rod of fishing sensation is that problem is finished.
The inventor inquires into keen determination at above-mentioned problem, found that as in the fishing rod of making by the fiber-reinforced resin that uses reinforcing fiber, the fiber of the appointment thickness that use is extracted out from bamboo is as the situation of reinforcing fiber, than the situation of having used glass fibre or carbon fiber with the same manner, recovery action to bending is releived, thereby has finished the present invention.
That is for solving above-mentioned problem, fishing rod of the present invention is the fishing rod with pole pipe of being made by fiber-reinforced resin,
It is characterized in that: as reinforcing fiber, above-mentioned fiber-reinforced resin contains the fine bamboo fibre of opening of diameter 0.01~0.5mm.
Diameter 0.01~0.5mm opens fine bamboo fibre, usually spring rate within the specific limits, this fiber by using specified amount is compared with the fishing rod (bamboo pole) that uses bamboo as reinforcing fiber, can make the quality discrepancies such as flexibility of each pole less.
And, though its effect is indeterminate, but be to use above-mentioned bamboo fibre as reinforcing fiber, can make above-mentioned fishing rod after because of the external force bending in case reduce or when removing this external force, the plasticity that is for the moment a little than the occasion of using carbon fiber, needs the long time to restore to the original state, richer sensation of fishing is releived in recovery action to bending.
In addition, in the present invention, the diameter of bamboo fibre be meant with the perpendicular cross section of direction of principal axis in farthest the distance (being maximum diameter) of point-to-point transmission, this numerical value is measured with the microscope cross-section photograph.
Among the present invention, more satisfactory is the direction of principal axis that above-mentioned bamboo fibre points to the pole pipe.
Like this structure function has the effect of releiving to the recovery action of bending, takes place because crooked to produce the possibility that perfect plasticity is out of shape also less.
In addition, above-mentioned bamboo fibre preferably implements to add hot-working.
The bamboo fibre of having implemented to add after the hot-working is used as reinforcing fiber, can make it become high resiliency and be not easy to produce the product of perfect plasticity distortion.
At this, adding hot-working is exactly with bamboo state before fiber is drawn out of or the fiber condition that has been drawn out of, heats and makes the processing of its moisture and oil content evaporation in the mode that does not make its carbonization.
This adds hot-working, usually heating several seconds (being about 1~10 second specifically) and finishing in 150~800 ℃.
This adds hot-working and also can use, and for example when making the pole pipe of making as the fiber-reinforced resin of reinforcing fiber with carbon fiber (as the carbon pole), is used to heat so that the firing furnace that uses during hardening of resin.
Also have, in the present invention,, it is desirable to further have carbon fiber or glass fibre as above-mentioned reinforcing fiber.
Only use bamboo fibre, under the very big situation of power effect outside, have big bending takes place, the possibility of the plastic deformation that permanent not resilient is such, but, reduced the possibility that this type of plastic deformation takes place owing to further have carbon fiber or glass fibre as reinforcing fiber.
This carbon fiber or glass fibre preferably point to circumferencial direction.
According to structure like this, even because very big bending etc., pole pipe section is deformed into ellipse from circle, also owing to have the carbon fiber or the glass fibre that point to circumferencial direction to play booster action, not frangibility, burst apart.
Description of drawings
Fig. 1 represents the fishing rod of an embodiment of the invention, (a) is summary side elevation, (b) is the X-X line cross section of (a).
Fig. 2 (a) (b) is the brief strabismus map of manufacturing process of the pole pipe of this embodiment of expression.
Embodiment
Below, to embodiments of the present invention, describe with reference to accompanying drawing.
The fishing rod of present embodiment, for example, as shown in Figure 1, by more piece pole pipe 4 with and continue form or extraction form connect and compose (with reference to Fig. 1 (a)).
This pole pipe 4 is formed by fiber-reinforced resin, from the inboard laterally, is followed successively by: the tubular layer surface construction of innermost layer A, intermediate layer B, outermost layer C (with reference to Fig. 1 (b)).
Above-mentioned in addition intermediate layer B comprises intermediate layer, the outside B1 that is assigned in the outside and is assigned in inboard inboard intermediate layer B2.
As reinforcing fiber, above-mentioned innermost layer A has the carbon fiber (spring rate 15000~60000kgf/mm that points to circumferencial direction S1
2, spring rate is 24000~40000kgg/mm usually
2, following carbon fiber is together).
As reinforcing fiber, above-mentioned inboard intermediate layer B2 has the carbon fiber that points to direction of principal axis S2.
As reinforcing fiber, above-mentioned outside intermediate layer B1 has the fine bamboo fibre 5 of opening of the fiber bundle of phloem of bamboo and diameter 0.01~0.5mm of being made of the bundle of this fiber bundle.
As this bamboo fibre 5, can use the bamboo fibre of for example wild village Industry Co., Ltd as the raw fibre of making " バ Application Block-ア エ ラ-ト " (trade name).
This bamboo fibre 5 is orientated on same direction, and it is oriented to the direction of principal axis S2 of pole pipe 4.
As reinforcing fiber, above-mentioned innermost layer A has the carbon fiber that points to circumferencial direction S1.
Below, the situation of making this pole pipe 4 is described with reference to Fig. 2.
At first, shown in Fig. 2 (a), film shape pre-preg material A (to call " innermost layer pre-preg material " in the following text) is wound on the core 3, wherein, described pre-preg material A be impregnated in matrix resins such as epoxy resin and gets by the thin-film body that will only contain the carbon fiber that is orientated on same direction, and, when reeling, make described carbon fiber 1 point to circumferencial direction S1.
Also have, the resin pickup of this innermost layer pre-preg material A is set to 20~40% of weight usually.A constitutes above-mentioned innermost layer A by this innermost layer pre-preg material.
Then, with the film that will only contain the carbon fiber 1 that on same direction, is orientated, similarly impregnated in matrix resin such as epoxy resin and pre-preg material (to call " inboard intermediate layer pre-preg material " in the following text) B2 so that the mode that carbon fiber 1 points to direction of principal axis S2 is wound on the periphery of innermost layer pre-preg material A.
The resin pickup of this intermediate layer, inboard pre-preg material B2 is set to 20~50% of weight usually.Constitute above-mentioned inboard intermediate layer B2 by this inboard intermediate layer pre-preg material B.
Then, with with above-mentioned bamboo fibre 5 at the thin-film body that on same direction, is oriented under the fiber condition, similarly impregnated in pre-preg material (to call " bamboo fibre pre-preg material " in the following text) B1 that matrix resin such as epoxy resin forms, so that the mode that its bamboo fibre 5 points to direction of principal axis S2 is wound on the periphery of inboard intermediate layer pre-preg material B2.
The resin pickup of this bamboo fibre pre-preg material B1 is set to 20~50% of weight usually.B1 constitutes aforementioned intermediate layer B1 by this bamboo fibre pre-preg material.
Then, shown in Fig. 2 (b), the outermost layer pre-preg material C of the band shape that carbon fiber 1 is orientated in the longitudinal direction so that the mode that carbon fiber 1 points to circumferencial direction is reeled.
The resin pickup of this outermost layer pre-preg material C is set to 20~50% of weight usually.C constitutes aforementioned outermost layer C by this outermost layer pre-preg material.
So in the periphery of the blank of the multilayer pre-preg material A that reeled, B2, B1, C, belt (not shown) limit that moulding is used is adjusted to suitable pressure limit reel after, burn till with the assigned temperature heating.
After heating is burnt till, pull out core 3, peel off the belt that moulding is used, then cut into designated length, just can obtain the pole pipe 4 that forms with tubulose.
The following describes one of method that bamboo fibre 5 is extracted example from bamboo.
At first, the bamboo of felling is removed leaf, former state or is cut into designated length, after the natural seasoning, add hot-working.
As adding hot-working, can adopt the method that for example bakes that bamboo is heated several seconds in 150~800 ℃ with fire.
Add hot-working by this, the moisture and the oil content of bamboo are evaporated, and become the state of carbonization eve.
Then, the pectin that from the bamboo of heating behind the dry processing fiber bundle will be bondd mutually becomes solubility and with its removal.Make pectin become the method for solubility, can adopt the fermentation method or the medicine method that adopt when from fiber crops, extracting fiber.
As the medicine method, can lift bamboo is soaked back heating in sodium hydrate aqueous solution method is example.
Below, make it further carry out coarse crushing after the drying by calender device.By coarse crushing make all sides in the bamboo wooden partial crushing and with its removal.
As calender device, can use present known Rolling type calender device, smash calendering such as formula calender device device to pieces.When making bamboo pass the Rolling type calender device, make it pass through this device in mode along the direction of growth of bamboo fibre 5, make it be broken into pencil along the direction of growth.
Utilize this bamboo rag opener to open fibre.The size of the tooth by adjusting rag opener, quantity, speed of gyration etc. make the bamboo fibre 5 of desirable diameter of the bundle formation of the fiber bundle of phloem or fiber bundle.
As rag opener, can use for example IM-34 type rag opener of spring south system pin manufacturing.
In addition, open finely when insufficient, can use turbo-mill etc. further to open fibre as required, the Shu Chengwei that makes the fiber bundle of phloem or fiber bundle is the bamboo fibre 5 of diameter 0.01~0.5mm for example.
In addition, in the present embodiment, the pre-preg material that has used bamboo fibre 5 to be orientated on same direction with fiber condition still, uses and for example utilizes cotton spinning weave etc. that the spinning that bamboo fibre 5 is formed by weaving is also passable under the situation of the pre-preg material that is orientated on the same direction.And then use textile with this spinning to impregnated in matrix resin and the situation of pre-preg material also in the intent of the present invention scope.
Also have, in the present embodiment, for example understand the pole pipe 4 of 4 layers of structure, the intermediate layer B that wherein is clipped between outermost layer C and the innermost layer A is two-layer, but among the present invention pole pipe 4 no matter which floor structure all can, for example 3-tier architecture or more than 5 layers structure etc. also can.
Further, in the present embodiment, bamboo fibre 5 only is used as the reinforcing fiber of intermediate layer B, and still, the situation as the reinforcing fiber of outermost layer C of being used for is also in the intent of the present invention scope; In addition, only be used for also belonging to the intent of the present invention scope as the situation of the reinforcing fiber of outermost layer C.
In addition, by more piece pole pipe 4 with and the fishing rod that connects and composes of continue form or extraction form in, as the reinforcing fiber that coupling part 4a, the 4a (or coupling part 4a, 4a of folk prescription) of two joints of the pole pipe 4 of mutual chimeric connection locate, also can make the structure (with reference to Fig. 1) that contains bamboo fibre 5.
So fishing rod not only is imbued with above-mentioned sensation of fishing, and because bamboo fibre comes more softly compared with carbon fiber, so tail off in the 4a of coupling part, the frictional dissipation of 4a, mutually the possibility of damage also reduces to some extent.
In addition, rely on the appropriateness fluffing and the high section (special-shaped section) of non-circular degree of bamboo fibre, can reduce the fixed mutually of two coupling part 4a, 4a.
And the fishing rod of the form that continues, need connecting portion 4a japanning sometimes with chimeric inboard, in this case, the connecting portion 4a in the chimeric outside is not easy to damage filming of chimeric inboard as using bamboo fibre as reinforcing fiber.In addition, implement as mentioned above can send sound during connection under the situation of japanning, can reduce this sound when using bamboo fibre.
As mentioned above, fishing rod of the present invention, compare with the bamboo pole that uses the bamboo thing, following advantage is arranged: can reduce the quality discrepancy of the flexibility etc. of each pole, and use above-mentioned bamboo fibre as reinforcing fiber, after because of the external force bending in case reduce or eliminate this external force, fishing rod is the plasticity of a little for the moment, compared with occasions such as use carbon fibers, needs the longer time to restore to the original state, resilience to bending is also releived, and more is imbued with the sensation of fishing.
Claims (5)
1. a fishing rod has the pole pipe of being made by the reinforcing fiber resin 4, it is characterized by: as reinforcing fiber, described fiber-reinforced resin contains the fine bamboo fibre 5 of opening of diameter 0.01~0.5mm.
2. as claims 1 described fishing rod, it is characterized by: described bamboo fibre 5 points to the direction of principal axis S2 of pole pipe 4.
3. as claims 1 or 2 described fishing rods, it is characterized by: described bamboo fibre 5 has been implemented to add hot-working.
4. as any one described fishing rod of claims 1 to 3, it is characterized by: as above-mentioned reinforcing fiber, this fishing rod further has carbon fiber 1 or glass fibre.
5. as claims 4 described fishing rods, it is characterized by: described carbon fiber 1 or glass fibre point to circumferencial direction S1.