CN1441005A - Asphalt modified with desulfurized rubber powder - Google Patents
Asphalt modified with desulfurized rubber powder Download PDFInfo
- Publication number
- CN1441005A CN1441005A CN 03118863 CN03118863A CN1441005A CN 1441005 A CN1441005 A CN 1441005A CN 03118863 CN03118863 CN 03118863 CN 03118863 A CN03118863 A CN 03118863A CN 1441005 A CN1441005 A CN 1441005A
- Authority
- CN
- China
- Prior art keywords
- desulfurization
- rubber powder
- asphalt
- powder
- modified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to asphalt modified with desulfurized rubber powder for road construction. The modified asphalt is produced with desulfurized rubber powder 5-30 wt%, asphalt 70-95 wt% and compatibilizer 0-1.5 wt% and through high speed shearing stirring for grinding in colloid mill. The modifier desulfurizing rubber powder has good dissolving and swelling performance in asphalt and has much active radicals in the surface for bonding with asphalt, and the compatilizer can further increase the interaction between the rubber powder and asphalt, so that the modified asphalt has excellent high and low temperature performance and storage stability.
Description
Technical field
The present invention relates to a kind of desulfurization glue powder-modified asphalt that is suitable for Road construction.
Background technology
Pitch is a kind of important material of construction, has obtained in fields such as Road construction, buildings waterproofs using widely.But plain asphalt owing to exist fragile under low temperaturely splits, shortcomings such as high temperature is easily softening, poor flexibility, can not satisfy modern high grade pavement to its performance demands.And along with the development of communications and transportation cause, building in a large number of high-grade highway, increasing to high-performance bituminous demand.For this reason, must carry out modification to pitch.Asphalt modification normally improves the bituminous thermotolerance by admixture polymkeric substance in pitch, reduces its low temperature brittleness, improves its elasticity, plasticity and low-temperature deformation, increases its survivability.The polymkeric substance that is used for asphalt modification at present mainly contains styrene-butadiene-styrene thermoplastic elastomer (SBS), styrene-butadiene rubber(SBR) (SBR), polyethylene (PE) etc.But the modification of these materials all makes the cost increase of modifying asphalt bigger, has limited its use in Road construction.
Waste old is the important component part of solid waste, and the annual waste old that produces in the whole world has 1,200 ten thousand tons at least.So no matter a large amount of waste olds is the landfill or the burning that acts as a fuel, and all can cause serious pollution to environment.Because waste rubber has the characteristics of the big and good springiness of molecular weight; the rubber powder modified asphalt that makes through pulverizing with waste old; not only can reduce the bituminous temperature sensitivity; increase bituminous elasticity; the be full of cracks of minimizing bituminous pavement and aging; improve the driving safety and the service life of road surface of vehicle, and the cost of modifying asphalt is reduced significantly, and the recycling, the protection environment that can be waste old contribute.
The application for a patent for invention name is called " using technological process of producing modified asphalt with waste polymer " (notification number 1347960 open day on Mays 8th, 2002) and discloses and a kind ofly will produce the method for modifying asphalt after waste or used plastics and the rubber granulation; this method reduces manufacturing cost greatly, has also effectively solved the pollution problem of waste polymer.Yet, because the rubber grain after pulverizing is big, modification dissolving difficulty, the pitch package stability is poor.
In the prior art, the preparation of waste rubber powder modified asphalt generally is rubber powder is mixed stirred for several hour with pitch and to make under comparatively high temps.Yet, because this rubber powder is in sulfided state, swelling on a small quantity in pitch, rubber powder only is similar to elastic filler and is present in the pitch, modified effect to the bituminous high temperature performance is limited, in storage and use, the modifying asphalt package stability is very poor, and rubber powder and pitch is laminated segregation very easily.In addition, because the not dissolved swelling of rubber powder has certain rebound resilience, easily cause bituminous concrete pavement compacting deficiency, voidage is bigger, and the road surface is easy to destroy.
Summary of the invention
In view of the defective of above-mentioned waste rubber powder modified asphalt, the object of the present invention is to provide the desulfurization glue powder-modified asphalt that a kind of modified effect is good, storage stability is high.
The objective of the invention is to adopt following manner to realize that the desulfurization glue powder-modified asphalt is made up of pitch, desulfurization rubber powder and compatilizer, wherein asphalt content is 70～95%, and desulfurization rubber powder consumption is 5～30%, and the compatilizer consumption is 0～1.5%.
Earlier base-material is heated to 160～210 ℃, adds desulfurization rubber powder and compatilizer then, under constant temperature, stir or the grinding of colloidal mill and making through high speed shear.
Used pitch softening point is 40～60 ℃ among the present invention, and penetration degree is 50～300dmm
Used desulfurization rubber powder is the waste old rubber powder after desulfurization is handled among the present invention.This desulfurization rubber powder can be to adopt high speed rotating heating method or dynamic desulfurization desulfurization to handle.
As everyone knows, desulfurization is a rubber powder under the effect of heat, oxygen and high shear force, makes the ruined process of cross-link bond of cross-linked rubber by the autoxidation reaction.The desulfurization rubber powder is because the partial cross-linked key in the rubber is interrupted, and the tridimensional network of rubber powder is destroyed, has certain dissolving swelling property.Therefore, can improve dissolving and the swelling of rubber powder in pitch with the desulfurization glue powder-modified asphalt, help to form submicroscopic homogeneous system, improve the high and low temperature and the elasticity of modifying asphalt, simultaneously because desulfurization has produced more active group (hydroxyl, carbonyl, carboxyl etc.) at vulcanized rubber powder, help producing chemical action, so the package stability of desulfurization glue powder-modified asphalt is also well improved with the polar group in the pitch.
Used compatilizer is epoxidized polybutadiene, glytidyl methacrylate, glycidyl methacrylate or maleic acid among the present invention.Its objective is that the polar group and the unsaturated double-bond that utilize compatilizer can produce chemical action with desulfurization rubber powder and pitch respectively, with the storage stability of further raising desulfurization glue powder-modified asphalt.
Embodiment
To make further instruction to the present invention by means of embodiment below, but should be understood that these embodiment only are used for that the present invention is further illustrated, rather than limitation of the present invention.Unless point out in addition, following per-cent all refers to weight percent.
Embodiment 1
The desulfurization rubber powder 10% of pitch (46 ℃ of softening temperatures, penetration degree 88dmm) 89.5%, the preparation of high speed rotating heating method, epoxidized polybutadiene 0.5%.Its manufacture method adds desulfurization rubber powder and epoxidized polybutadiene then for earlier pitch being heated to 180～190 ℃, and controlled temperature is constant, stirs 3h through high speed shear, promptly gets the desulfurization glue powder-modified asphalt after the cooling.This modifying asphalt is compared with desulfurization glue powder-modified asphalt not, softening temperature is brought up to 59 ℃ from 57 ℃, and 5 ℃ of ductilities are brought up to 10.5cm from 8.3cm, through 163 ℃, 48h storage back levels softening temperature difference reduces to 6.5 ℃ from 9.2 ℃, thereby has better high temperature performance and storage stability.
Embodiment 2
Pitch (44 ℃ of softening temperatures, penetration degree 121dmm) 84.7%, the desulfurization rubber powder 15% of dynamic desulfurization preparation, glytidyl methacrylate 0.3%.Make according to manufacturing step similar to Example 1.The gained modifying asphalt is compared with desulfurization glue powder-modified asphalt not, softening temperature is brought up to 63 ℃ from 60 ℃, and 5 ℃ of ductilities are brought up to 15.5cm from 12.6cm, through 163 ℃, 48h storage back levels softening temperature difference reduces to 7.2 ℃ from 11.4 ℃, shows better modified effect.
Claims (5)
1. a desulfurization glue powder-modified asphalt is characterized in that it is made up of pitch, desulfurization rubber powder and compatilizer, wherein:
Pitch, it accounts for 70～95% of raw material gross weight;
The desulfurization rubber powder, it accounts for 5～30% of raw material gross weight;
Compatilizer, it accounts for 0～1.5% of raw material gross weight.
2. desulfurization glue powder-modified asphalt according to claim 1 is characterized in that this bituminous softening temperature is 40～60 ℃, and penetration degree is 50～300dmm..
3. desulfurization glue powder-modified asphalt according to claim 1 is characterized in that this desulfurization rubber powder is the waste old rubber powder after handling through desulfurization.
4. according to claim 1 or 3 described desulfurization glue powder-modified asphalts, it is characterized in that this desulfurization rubber powder can be the rubber powder that adopts high speed rotating heating method or dynamic desulfurization desulfurization to handle.
5. desulfurization glue powder-modified asphalt according to claim 1 is characterized in that this compatilizer can be epoxidized polybutadiene, glytidyl methacrylate, glycidyl methacrylate or maleic acid.