CN1432607A - 石蜡腻子膏及其制备方法 - Google Patents

石蜡腻子膏及其制备方法 Download PDF

Info

Publication number
CN1432607A
CN1432607A CN 02110557 CN02110557A CN1432607A CN 1432607 A CN1432607 A CN 1432607A CN 02110557 CN02110557 CN 02110557 CN 02110557 A CN02110557 A CN 02110557A CN 1432607 A CN1432607 A CN 1432607A
Authority
CN
China
Prior art keywords
parts
paraffin
water
putty paste
putty
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 02110557
Other languages
English (en)
Inventor
王天龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 02110557 priority Critical patent/CN1432607A/zh
Publication of CN1432607A publication Critical patent/CN1432607A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种石蜡腻子膏，它包括石蜡、聚丙烯酰胺、硫酸锌、重质碳酸钙、滑石粉、水泥改性剂、氢氧化钙和水。其中水泥改性剂为APR－968LO、AC－200P和ARS200AP(均为美国罗马哈斯公司生产)中的一种或几种。本发明还公开了石蜡腻子膏的制备方法。按照本发明配制的石蜡腻子膏，在正常使用中无开裂现象，手感细腻光滑，可以水洗保持清洁，且无有害物质，是一种环保型腻子膏，施工方便，无需覆盖其它涂料，降低了建筑物的造价。

Description

石蜡腻子膏及其制备方法
技术领域
本发明涉及一种腻子膏及其制备方法，特别涉及一种可防水的腻子膏及其制备方法。
背景技术
随着社会的进步和人们生活水平的提高，各式各样的民用和商用建筑正在大量兴建，而在建筑和装修过程中，腻子膏是不可缺少的辅助材料。目前，市场上使用的腻子膏主要由水溶性甲基纤维素、碳酸钙、聚乙烯醇和滑石粉等成分所组成，使用中存在着不耐水、容易开裂、手感差的缺陷。
发明内容
本发明需要解决的技术问题是公开一种石蜡腻子膏及其制备方法，以克服现有技术中存在的不可水洗、易开裂、手感差的缺陷。
本发明的石蜡腻子膏为一种组合物，其组分和重量份数包括：
石蜡                      5～40份
聚丙烯酰胺                2～40份
硫酸锌                    5～20份
重质碳酸钙               30～80份
滑石粉                    5～40份
水泥改性剂               0.5～5份
氢氧化钙             5～60份
水                   10～60份
其中水泥改性剂为APR-968LO、AC-200P和ARS200AP(均为美国罗马哈斯公司生产)中的一种或几种。
本发明优选的重量份数包括：
石蜡                     5～25份
聚丙烯酰胺               3～10份
硫酸锌                   8～15份
重质碳酸钙              35～50份
滑石粉                   8～20份
水泥改性剂              0.5～5份
氢氧化钙                10～30份
水                      35～50份
其中水泥改性剂为AC-200P和APR-968LO(均为美国罗马哈斯公司生产)的混合物。
本发明的石蜡腻子膏中还可加入建筑用的色素，使腻子膏具有丰富色彩，可直接用于墙面而无需使用彩色涂料。
本发明的石蜡腻子膏的制备方法包括下列步骤：
1.先将石蜡加热至熔化，一般为90～100℃，搅拌状态下向石蜡中加入热水，维持混合温度在90～100℃，热水温度最好为90～100℃，再将石蜡和水的混合物冷却至20～40℃，随后加入聚丙烯酰胺，搅拌均匀；
2.向步骤1所得的混合物中加入硫酸锌、重质碳酸钙、滑石粉、氢氧化钙和水泥改性剂，搅拌均匀后即可得到石蜡腻子膏，搅拌时间最好为1～4小时。
本发明由于加入了石蜡，提高了耐水性能、耐污垢性能、柔韧性和光滑度，并且抗开裂，手感良好；加入的聚丙烯酰胺作为粘结剂，增加了光滑度，提高了施工进度；硫酸锌的加入提高了产品的白度；氢氧化钙可提高产品耐水性及坚固度；而加入水泥改性剂后，使腻子膏耐水性、耐候性和强度均得到提高，增加了对水泥基层的附着力。所以，按照本发明配制的石蜡腻子膏，具有如下优点：正常使用中无开裂现象，手感细腻光滑，可以水洗保持清洁，并且无有害物质，是一种环保型腻子膏，施工方便，无需覆盖其它涂料，降低了建筑物的造价。
具体实施方式
                      实施例1
按照下列各组分的重量份数配制石蜡腻子膏：
石蜡                      15份
聚丙烯酰胺                 4份
硫酸锌                    10份
重质碳酸钙                40份
滑石粉                    10份
AC-200P                    2份
APR-968LO                  1份
氢氧化钙                  20份
水                        45份
所得石蜡腻子膏浸水360小时无变化。

Claims (7)

1.一种石蜡腻子膏，其特征在于，其组分和重量份数包括：
石蜡                        5～40份
聚丙烯酰胺                  2～40份
硫酸锌                      5～20份
重质碳酸钙                 30～80份
滑石粉                      5～40份
水泥改性剂                 0.5～5份
氢氧化钙                    5～60份
水                         10～60份
其中水泥改性剂为美国罗马哈斯公司生产的APR-968LO、AC-200P和ARS200AP中的一种或几种。
2.如权利要求1所述的石蜡腻子膏，其特征在于，其组分和重量份数包括：
石蜡                        5～25份
聚丙烯酰胺                  3～10份
硫酸锌                      8～15份
重质碳酸钙                 35～50份
滑石粉                      8～20份
水泥改性剂                 0.5～5份
氢氧化钙                   10～30份
水                       35～50份
其中水泥改性剂为AC-200P和APR-968LO的混合物。
3.如权利要求2所述的石蜡腻子膏，其特征在于，其组分和重量份数包括：
石蜡                        15份
聚丙烯酰胺                   4份
硫酸锌                      10份
重质碳酸钙                  40份
滑石粉                      10份
AC-200P                      2份
APR-968LO                    1份
氢氧化钙                    20份
水                          45份。
4.如权利要求1～3任一所述的石蜡腻子膏，其特征在于，石蜡腻子膏中加入适量建筑用色素。
5.如权利要求1所述的石蜡腻子膏的制备方法，其特征在于，该制备方法包括下列步骤：
(1)先将石蜡加热至熔化，搅拌状态下向石蜡中加入热水，维持混合温度在90～100℃，再将石蜡和水的混合物冷却至20～40℃，随后加入聚丙烯酰胺，搅拌均匀；
(2)向步骤(1)所得的混合物中加入硫酸锌、重质碳酸钙、滑石粉、氢氧化钙和水泥改性剂，搅拌均匀后即可得到石蜡腻子膏。
6.如权利要求5所述的石蜡腻子膏的制备方法，其特征在于，热水温度为90～100℃。
7.如权利要求5或6所述的石蜡腻子膏的制备方法，其特征在于，搅拌时间为1～4小时。
CN 02110557 2002-01-15 2002-01-15 石蜡腻子膏及其制备方法 Pending CN1432607A (zh)