CN102634244B - 一种环保型防钢构件热膨胀涂料 - Google Patents
一种环保型防钢构件热膨胀涂料 Download PDFInfo
- Publication number
- CN102634244B CN102634244B CN 201210120500 CN201210120500A CN102634244B CN 102634244 B CN102634244 B CN 102634244B CN 201210120500 CN201210120500 CN 201210120500 CN 201210120500 A CN201210120500 A CN 201210120500A CN 102634244 B CN102634244 B CN 102634244B
- Authority
- CN
- China
- Prior art keywords
- environment
- thermal expansion
- steel member
- expansion coating
- friendly anti
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及钢铁领域及一些预制耐火材料里面的钢筋锚固件表面涂层,即环保型防钢构件热膨胀涂料。它由石蜡,结合剂制成。具有成本低,效益好,无污染,涂刷牢固,改善施工条件,提高施工效率,保障施工质量的特点。
Description
技术领域
本发明涉及钢铁领域及一些预制耐火材料里面的钢筋锚固件表面涂层,即环保型防钢构件热膨胀涂料。
背景技术
在现有技术中,钢铁领域及一些耐火混凝土里面的钢筋锚固件表面涂层,涂上后,在高温下,钢材锚固件膨胀,涂层融化留有间隙,使钢材不易因膨胀收缩把预制耐火材料破坏。大多数预制件产品在受热时,因钢材膨胀,预制件产生裂纹,剥落,钢结构被烧坏,使产品报废,造成浪费。传统的钢结构涂层方法:一种是用塑料薄膜,缠裹在钢结构表面;另一种是用沥青涂刷上一层。其中用塑料薄膜缠裹,费时、费力,浇注时还容易脱落;用沥青涂抹,烘烤时有特殊气味,加热到260℃在5小时以后,其所含的蒽、菲、芘等成分就会挥发出来,这些成分是有毒的,污染空气,容易伤害人的身体。
发明内容
本发明的目的是针对上述不足而提供一种熔化后对耐火材料影响小,不污染环境的一种环保型防钢构件热膨胀涂料。
本发明的技术解决方案是:一种环保型防钢构件热膨胀涂料由以下重量百分比的原料制成:石蜡80-90%,结合剂10-20%。
所述的石蜡是矿物蜡的一种,也是石油蜡的一种,它是从原油蒸馏所得的润滑油馏分经溶剂精制、溶剂脱蜡或经蜡冷冻结晶、压榨脱蜡制得蜡膏,再经溶剂脱油、精制而得的片状或针状结晶,又称晶形蜡,碳原子数约为18~30的烃类混合物,主要组分为直链烷烃(约为80%~95%),通常是白色、无色无味的蜡状固体,在47℃-64℃溶化,密度约0.9g/cm3,具有良好的绝缘性和可塑性,加热后有良好的流动性。
所述的结合剂为三聚磷酸钠、六偏磷酸钠一种或二者组合。
环保型防钢构件热膨胀涂料的制作方法:选取石蜡,按上述配比进行计量配比,加热石蜡熔化,加入结合剂搅拌5~10分钟,搅拌均匀即可。
环保型防钢构件热膨胀涂料的使用方法:用刷子均匀涂刷在锚固件的表面即可。烘烤时,石蜡融化燃烧,形成CO2,一部分渗入料中,留有一定间隙,没有其他有害气体产生,是一种极其环保的产品。
该产品在预制件的生产过程中得到应用,特别是在铁水预处理脱硫喷枪、脱磷喷枪、加热炉炉顶的使用中,对于钢构件的保护,取得了良好的效果。
本发明的优点是:1、成本低,效益好,无污染,属于环保型产品。2、涂刷既均匀,又牢固,涂时方便,清洁卫生,改善施工条件,提高施工效率,保障施工质量。3、成本减少20~30%,施工人员减少40~50%。
下面将结合实施例对本发明的实施方式作进一步详细描述。
具体实施方式
实施例1
一种环保型防钢构件热膨胀涂料,由以下重量百分比的原料制成:
石蜡80%,三聚磷酸钠10%,六偏磷酸钠10%。
实施例2
一种环保型防钢构件热膨胀涂料,由以下重量百分比的原料制成:
石蜡80%,三聚磷酸钠20%
实施例3
一种环保型防钢构件热膨胀涂料,由以下重量百分比的原料制成:
石蜡80%,六偏磷酸钠20%。
Claims (4)
1.一种环保型防钢构件热膨胀涂料,其特征在于由以下重量百分比的原料制成:石蜡80-90%,结合剂10-20%;所述的结合剂为三聚磷酸钠、六偏磷酸钠一种或二者组合。
2.按照权利要求1所述的环保型防钢构件热膨胀涂料,其特征在于:石蜡 80% ,三聚磷酸钠10 %,六偏磷酸钠10%。
3.按照权利要求1所述的环保型防钢构件热膨胀涂料,其特征在于:石蜡 80% ,三聚磷酸钠20 %。
4.按照权利要求1所述的环保型防钢构件热膨胀涂料,其特征在于:石蜡80%,六偏磷酸钠20%。