CN1428241A - 三层复合包装膜 - Google Patents
三层复合包装膜 Download PDFInfo
- Publication number
- CN1428241A CN1428241A CN 01138946 CN01138946A CN1428241A CN 1428241 A CN1428241 A CN 1428241A CN 01138946 CN01138946 CN 01138946 CN 01138946 A CN01138946 A CN 01138946A CN 1428241 A CN1428241 A CN 1428241A
- Authority
- CN
- China
- Prior art keywords
- layer
- ldpe
- packaging film
- composite packaging
- layer composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种三层复合包装膜,适用于金属材料,特别是冷轧板卷的包装。这种三层复合包装膜由外层为防水层1、增强层2和防锈层3共同挤压而成。这种三层复合包装膜厚度为140~160μm,典型厚度为150μm±5%,三层的厚度比为:防水层1∶增强层2∶防锈层3=3.5~4.5∶1.5~2.5∶3.5~4.5。各层配料重量百分比为:防锈层LDPE∶VCI=75-85∶25-15,增强层LDPE∶LLDPE=45-55∶55-45,防水层LDPE∶防水剂=87-93∶13-7。防水剂由抗氧剂、增塑剂和环氧脂组成。用这种包装膜包装的金属材料外观整齐,防水防锈,效果优良,保证了金属材料产品的表观质量不受损害,且形成产品后,可回收,可降解,有利于环保。
Description
技术领域
本发明属于包装材料领域,特别是一种三层复合包装膜。
背景技术
为了对金属材料进行防水、防锈包装保护,需要有一种防水防锈保护包装膜。目前所采用的复合包装膜有三大类:一类是气相防锈纸,即VCI+PE+纸,另一类是纸塑复合膜,即VCI+织布+纸或VCI+PE+织网+纸,还有一种是防锈膜,即PE(或是PP)+VCI涂覆。这里所说的VCI是气相膜防锈剂,PE是聚乙稀,PP是聚丙稀。
上述材料的共同不足之处是:第一,透水率较高,以PE(聚乙稀)复合纸为例,A级的指标最低透水率15g/m2.24h;第二,这些复合材料不可降解,不宜回收,从而造成环境污染;第三,防锈层由于涂布VCI结晶、掉粉、吸潮而失效。
发明内容
本发明的目的在于提供一种由防水层、增强层和防锈层共同挤压而成的三层复合包装膜,用于包装金属材料,如冷轧板卷等。
按照本发明的三层复合包装材料,外层为防水层,中间层为增强层,内层为防锈层,将三层共同挤压而成,其防水防锈效果很好。
按照本发明的三层复合包装材料,其总厚度为140~160μm,三层的厚度比为:防水层∶增强层∶防锈层=3.5~4.5∶1.5~2.5∶3.5~4.5。例如,三层复合包装膜的总厚度为150μm±5%,三层的厚度比为:防水层∶增强层∶防锈层=4∶2∶4=2∶1∶2,即防水层60μm±5%,增强层30μm±5%,防锈层60μm±5%。
按照本发明的三层复合包装材料,防水层由LDPE(低密度聚乙稀)基料加防水添加剂塑化共融而构成,增强层由LDPE(低密度聚乙稀)基料加增强添加剂塑化共融而构成,防锈层由LDPE(低密度聚乙稀)基料加防锈添加剂塑化共融而构成。
按照本发明的三层复合包装材料,防锈剂采用VCI气相膜防锈剂,增强剂采用LLDPE线性低密度聚乙稀或尼龙,防水剂采用抗氧化剂、增塑剂和环氧脂等。
按照本发明,各层配料重量百分比为:防锈层的基料LDPE低密度聚乙烯和防锈剂VCI气相膜防锈剂的比例为:LDPE∶VCI=75-85∶25-15,增强层的基料LDPE低密度聚乙烯和增强剂LLDPE线性低密度聚乙烯或尼龙的比例为:LDPE∶LLDPE=45-55∶55-45,防水层的基料LDPE低密度聚乙烯和防水剂的比例为LDPE∶防水剂=87-93∶13-7。防水剂由抗氧剂、增塑剂和环氧脂组成,其中抗氧剂∶增塑剂∶环氧脂=25-35∶50-60∶5-15。
按照本发明的三层复合包装膜的制作工艺流程为:功能性母料→分别混合→三层共挤→吹塑→冷却→人字板→牵引→卷取。
按照本发明的三层复合包装膜,由于是由三层塑料共挤而成,其中一层含有气相缓蚀剂等添加剂,加强层含有增强剂,防水层含有防水剂。因此具有很好的防水、防锈作用,而且具有较高的强度,可以回收利用。由于在本包装膜中加入了可降解母料,所以有利于环保。
经测试表明,在常温下,本发明的三层复合包装膜的抗张强度大于14Mpa,拉伸率在横向可达450%,纵向可达250%,完全适用于包装金属材料。透水率低于0.8g/m2.24h,远远低于现有包装材料的透水率,防水防锈效果特别好。
附图说明
图1为本发明的断面放大示意图。
图2为使用本发明所包装的冷轧板卷的照片。
具体实施方式
下面结合附图对本发明作进一步说明。
如图1所示,本发明的三层复合包装膜,其外层为防水层1,中间层为增强层2,内层为防锈层3。此图为这种三层复合包装膜的断面放大示意图。这种三层复合包装膜的实际总厚度为140~160μm,三层的厚度比为:防水层1∶增强层2∶防锈层3=3.5~4.5∶1.5~2.5∶3.5~4.5。
典型的三层复合包装膜总厚度为150μm±5%,三层的厚度比为:防水层1∶增强层2∶防锈层3=4∶2∶4=2∶1∶2。或者说,三层厚度分别为:防水层1厚60μm±5%,增强层2厚30μm±5%,防锈层3厚60μm±5%。各层配料比为:防锈层LDPE∶VCI=80∶20,增强层LDPE∶LLDPE=50∶50,防水层LDPE∶防水剂=90∶10,防水剂中的抗氧剂∶增塑剂∶环氧脂=30∶60∶10。抗氧剂可采用硫代二丙酸二月桂脂或硫代二丙酸二(十八)脂,增塑剂采用硬脂酸正丁脂或已二酸二辛脂。
如图2所示,采用本发明的三层复合包装膜包装的冷轧板卷外观整齐美观,防水防锈性能优良,保证了金属材料产品的表观质量不受损害,且形成产品后,可回收,可降解,有利于环保。
Claims (10)
1.一种三层复合包装膜,其特征在于此三层是:外层为防水层(1),中间层为增强层(2),内层为防锈层(3),将该三层共同挤压而成。
2.根据权利要求1所述的三层复合包装膜,其特征在于其总厚度为140~160μm,三层的厚度比为:防水层(1)∶增强层(2)∶防锈层(3)=3.5~4.5∶1.5~2.5∶3.5~4.5。
3.根据权利要求1所述的三层复合包装膜,其特征在于其总厚度为150μm±5%,三层的厚度比为∶防水层(1):增强层(2)∶防锈层(3)=4∶2∶4=2∶1∶2。
4.根据权利要求1或2所述的三层复合包装膜,其特征在于防水层(1)由低密度聚乙稀LDPE基料加防水添加剂塑化共融而构成,增强层(2)由线性低密度聚乙稀LLDPE基料加增强添加剂塑化共融而构成,防锈层(3)由低密度聚乙稀LDPE基料加防锈添加剂所塑化共融而构成。
5.根据权利要求4所述的三层复合包装膜,其特征在于:防锈剂采用VCI气相膜防锈剂,增强剂采用LLDPE线性低密度聚乙稀,防水剂采用抗氧化剂,增塑剂和环氧脂。
6.根据权利要求4所述的三层复合包装膜,其特征在于各层配料重量百分比为:防锈层的基料LDPE低密度聚乙烯和防锈剂VCI气相膜防锈剂的比例为:LDPE∶VCI=75-85∶25-15,增强层的基料LDPE低密度聚乙烯和增强剂LLDPE线性低密度聚乙烯的比例为:LDPE∶LLDPE=45-55∶55-45,防水层的基料LDPE低密度聚乙烯和防水剂的比例为LDPE∶防水剂=87-93∶13-7。
7.根据权利要求6所述的三层复合包装膜,其特征在于各层配料重量百分比为:防锈层LDPE∶VCI=80∶20,增强层LDPE∶LLDPE=50∶50,
8.根据权利要求4所述的三层复合包装膜,其特征在于防水剂由抗氧剂、增塑剂和环氧脂组成,其中抗氧剂∶增塑剂∶环氧脂=25-35∶50-60∶5-15。
9.根据权利要求8所述的三层复合包装膜,其特征在于防水剂中的抗氧剂∶增强剂∶坏氧脂=30∶60∶10。
10.根据权利要求8所述的三层复合包装膜,其特征在于抗氧剂采用硫代二丙酸二月桂脂或硫代二丙酸二(十八)脂,增塑剂采用硬脂酸正丁脂或已二酸二辛脂。