CN1425812A - 涤纶有色短纤维的生产方法 - Google Patents

涤纶有色短纤维的生产方法 Download PDF

Info

Publication number
CN1425812A
CN1425812A CN 02160667 CN02160667A CN1425812A CN 1425812 A CN1425812 A CN 1425812A CN 02160667 CN02160667 CN 02160667 CN 02160667 A CN02160667 A CN 02160667A CN 1425812 A CN1425812 A CN 1425812A
Authority
CN
China
Prior art keywords
color
terylene
polyester staple
colored polyester
masterbatch
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 02160667
Other languages
English (en)
Inventor
陈建忠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
XIAKE COLOR SPINNING CO Ltd
Original Assignee
XIAKE COLOR SPINNING CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by XIAKE COLOR SPINNING CO Ltd filed Critical XIAKE COLOR SPINNING CO Ltd
Priority to CN 02160667 priority Critical patent/CN1425812A/zh
Publication of CN1425812A publication Critical patent/CN1425812A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种涤纶有色短纤维的生产方法。属化学纤维技术领域。其特点是在涤纶聚酯原料中加入色母粒直接纺成有色丝。由于本发明不需经染色工艺，因此生产工艺简单、生产成本低、污染少，产品色差小、色牢度好，不易褪色。且还具有色谱广泛、色泽鲜艳等特点。

Description

涤纶有色短纤维的生产方法
技术领域：
本发明涉及一种涤纶有色短纤维的生产方法。属化学纤维技术领域。
背景技术：
涤纶(复纺)有色短纤维广泛应用于纺织、地毯、服装面料等各个领域。传统的涤纶有色短纤维的生产方法是采用涤纶聚脂原料先经纺丝后染色。由于涤纶的分子结构比较紧密、结晶度高，所以其染色较困难，并且染色工艺复杂，污染较严重，成本又高，产品色差大，色牢度差，易褪色。
发明内容：
本发明的目的在于克服现有技术存在的不足，提供一种工艺简单、成本低、污染少、产品色差小、色牢度好的涤纶有色短纤维的生产方法。
本发明的目的是通过下述方法实现的：一种涤纶有色短纤维的生产方法，其特点是在涤纶聚脂原料中加入色母粒直接纺成有色丝。
由于本发明采用将色母粒加入到涤纶聚脂原料中直接纺成有色丝。不需经染色工艺，因此生产工艺简单、生产成本低、污染少，产品色差小、色牢度好，不易褪色。且还具有色谱广泛、色泽鲜艳等特点。
附图说明：
图1为本发明的生产工艺流程图。
具体实施方式：
色母粒是将超常量的颜料均匀的附着于聚脂中而制得的聚集体。一般主要由着色剂、载体和分散剂三部分构成。
着色剂可分为有机和无机两大类：无机类主要是指碳黑；有机类需选择耐温性能优的颜料或染料。
载体是使着色剂能均匀分布且使色母粒呈颗粒状。选择载体要考虑其与被着色纤维的相容性，还应有良好的分散性，因此载体应选用熔体指数较大的同类高聚物。
分散剂主要对颜料表面进行润湿，有利于进一步分散并稳定在涤纶熔体中，同时，必须与熔体有很好的相容性。不影响产品的品质。一般采用低分子量的硬脂酸镁、聚乙烯酯。
如图1，本发明方法是将色母粒与聚脂原料按照一定比例投入转鼓中充分混合后，加入螺杆挤压纺丝机中进行纺丝，后经卷绕、落桶后进入后纺。由于色母粒所用的颜料已经过预处理，使用载体均为涤纶，且颜料颗粒经过双螺杆挤压机后颗粒只有1μm左右，并已混合均匀，所以色母粒的加入不会对涤纶纺丝有大的影响。其还具有计量准确、适用生产各种深浅色泽的纤维，可以保证批量纤维不存在色差的特点，经过实践，使用色母粒法是生产涤纶有色短纤维的最佳途径。
实施例1：生产1.5D大红纤维
取白色涤纶聚脂原料800kg和大红色母粒58kg，经投料斗加入转鼓中均匀混合，干燥10小时，加入螺杆挤压纺丝机中进行纺丝，经卷绕、落桶进入后纺。
实施例2：生产1.5D藏青纤维
取绿色涤纶聚脂原料800kg和藏青色母粒58kg，其余同例1。
实施例3：生产1.5D浅黄纤维
取白色涤纶聚脂原料800kg和浅黄色母粒25kg，其余同例1。

Claims (2)

1、一种有色涤纶短纤维的生产方法，其特征在于在涤纶聚脂原料中加入色母粒直接纺成有色丝。
2、根据权利要求1所述的一种有色涤纶短纤维的生产方法，其特征在于色母粒着色载体为涤纶聚脂。
CN 02160667 2002-12-31 2002-12-31 涤纶有色短纤维的生产方法 Pending CN1425812A (zh)