CN1408806A - Non-woven thermal smelting adesive lining and its producing process - Google Patents
Non-woven thermal smelting adesive lining and its producing process Download PDFInfo
- Publication number
- CN1408806A CN1408806A CN 02136441 CN02136441A CN1408806A CN 1408806 A CN1408806 A CN 1408806A CN 02136441 CN02136441 CN 02136441 CN 02136441 A CN02136441 A CN 02136441A CN 1408806 A CN1408806 A CN 1408806A
- Authority
- CN
- China
- Prior art keywords
- woven
- finishing composition
- thermal smelting
- silicon
- base fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the field of clothing thermal smelting adhesive lining. The present invention is one improvement of available non-woven thermal smelting adhesive lining. On non-woven base cloth, one layer of cationic silicon finishing agent is first painted, and one layer of thermal smelting adhesive matrix is then attached. Proper production process is also designed. The present invention has greatly increased bonding strength between the non-woven thermal smelting adhesive lining and the clothing face layer, especially the silicon finished clothing face layer. In addition, the present invention raises the flexibility and smoothness of the adhesive lining, reduces the friction of the clothing during wearing and raises the wash resistance.
Description
Technical field
The invention belongs to the apparel binding fibre technical field, particularly relate to a kind of structure and production technique thereof of nonwoven hot molten binding lining.
Background technology
At present, the non-woven thermal smelting adesive lining base cloth does not carry out any arrangement before producing hot molten binding lining both at home and abroad, and the non-woven thermal smelting adesive lining feel of producing behind the direct spot printing hot melt adhesive of base cloth is not smooth; Press with the garment material after silicon arrangement and to scald bonding back stripping strength lower (<8N/5 * 10cm) peels off the back and finds that the hot melt adhesive point transfers to the degree less than 5% on the garment material.
Summary of the invention
The technical problem to be solved in the present invention is for overcoming the shortcoming that above-mentioned non-woven thermal smelting adesive lining exists, and design a kind of new non-woven thermal smelting adesive lining and production technique thereof, solve hot molten binding lining with through the difficult adherent problem of the lining of silicone finish, and increase substantially its stripping strength, effectively improve the smooth property and the flexibility on hot molten binding lining surface.
Technical scheme of the present invention is:
On the basis of the common non-woven thermal smelting adesive lining that constitutes by non-woven base fabric and hot melt adhesive point coating thereof, carry out technological improvement, promptly on non-woven base fabric, be coated with one deck positively charged ion silicon finishing composition layer earlier, on this finishing composition layer, apply adhesion heat melten gel dot matrix layer then again.
The finishing composition that constitutes above-mentioned positively charged ion silicon finishing composition layer is formed by amido silicon oil, hydroxy silicon oil, phenylcarbinol or jasmal and silicon ester allotment.
The production technique of non-woven thermal smelting adesive lining of the present invention, undertaken by following processing step:
(1) positively charged ion silicon finishing composition is coated on the non-woven base fabric with the method for padding or spray;
(2) oven dry has promptly formed one deck positively charged ion silicon finishing composition layer on the non-woven base fabric surface;
(3) hot melt adhesive is coated on the finishing composition layer on non-woven base fabric surface with the cylinder printing points, and forms dot matrix type hot melt adhesive point coating;
(4) non-woven thermal smelting adesive lining of the present invention is promptly made in oven dry.
Technique effect of the present invention:
1, because non-woven base fabric before the coated heat melten gel, adopts positively charged ion silicon finishing composition to put in order earlier, form one deck finishing composition film on the non-woven base fabric surface, this film surface tension force is lower, is easy to adhesion heat melten gel point, and makes the moulding of hot melt adhesive point fuller; This adhesive lining press to be scalded when bonding with garment material, and the hot melt adhesive point is easier to shift that (after tested, metastasis degree is up to 45%, and stripping strength has surpassed 8N/5 * 10cm) on garment material; Improve the flexibility of non-woven thermal smelting adesive lining, smooth property simultaneously, reduced the friction when clothes are worn, also strengthened wash durability.
2, this non-woven thermal smelting adesive lining production technique is reasonable, and is easy and simple to handle, the economic benefit height.
Description of drawings
Fig. 1 is the cross section structure synoptic diagram of non-woven thermal smelting adesive lining of the present invention.
Fig. 2 is coated with finishing composition for base cloth with padding method, prints the process flow diagram of spot printing hot melt adhesive production adhesive lining of the present invention then with cylinder.
Fig. 3 is coated with finishing composition for base cloth with spraying method, prints the process flow diagram of spot printing hot melt adhesive production adhesive lining of the present invention then with cylinder.
Among the above-mentioned figure: 1, non-woven base fabric, 2, finish coating, 3, hot melt adhesive point coating, 4, finishing composition, 5, roll, 6, infrared heater, 7, hot melt adhesive, 8, hot melt adhesive cylinder printing device, 9, infrared heater, 10, the finishing composition spray equipment.
Embodiment
Base cloth 1 adopts the non-woven fabrics of nylon (N) fiber or nylon (N) fiber and terylene (T) blending in of fibers, and generally nylon (N) content is 40~100% in this non-woven base cloth, and terylen (T) content is 60~0%, and base cloth 1 every weight per square meter is 15~50g/m
2
Positively charged ion silicon finishing composition 4 is by amido silicon oil, hydroxy silicon oil, and phenylcarbinol or jasmal and silicon ester are formed.Its blending process is as follows:
(1) gets 20~35kg hydroxy silicon oil and pour in 70~55kg amido silicon oil, fully stir;
(2) get silicon ester 2~3kg and add 10 times of water (is good with soft water) dilution, fully stir;
(3) (2) prepared feed liquid and 5~15kg phenylcarbinol or jasmal are poured in (1) prepared feed liquid stirred successively, make the finishing composition mother liquor;
(4) the finishing composition mother liquor is diluted with 4~8 times of water, after fully stirring, promptly make the base cloth finishing composition 4 of production usefulness.
Hot melt adhesive 7 adopts following component allotment to form: polyacrylate(s) material 1~2kg, copolyesters (PES) or copolyamide (PA) polymkeric substance 30~40kg, softening agent 3~4kg, dispersion agent 3~5kg, thickening material 0.5~1kg, water 60~70kg.
Production craft step:
(1) the above-mentioned positively charged ion silicon finishing composition 4 for preparing is coated on the non-woven base fabric 1 with the method for padding or spray;
(2), control 100~130 ℃ temperature oven dry base cloth finish coating 2 with infrared heater 6;
(3) hot melt adhesive 7 usefulness cylinder printing devices 8 are coated on the base cloth finishing composition layer 2, and form dot matrix type hot melt adhesive point coating 3;
(4) with infrared heater 9 oven dry hot melt adhesive point coatings 3, temperature is controlled at 120~150 ℃.Promptly make non-woven thermal smelting adesive lining of the present invention.
Tabulate the quality test situation of the processing parameter and the products obtained therefrom of three specific embodiments below.
Column | Embodiment 1 | Embodiment 2 | Embodiment 3 | ||
Base cloth | Unit weight (g/m 2) | ????15 | ????25 | ????40 | |
Composition (%) | ????N | ????50 | ????80 | ????100 | |
????T | ????50 | ????20 | ????0 | ||
Positively charged ion silicon finishing composition composition and consumption (kg) | Amido silicon oil | ????55 | ????60 | ????70 | |
Hydroxy silicon oil | ????35 | ????30 | ????20 | ||
Phenylcarbinol or jasmal | ????15 | ????10 | ????8 | ||
Silicon ester | ????3.0 | ????2.5 | ????3.0 | ||
The water extension rate | ????4 | ????6 | ????8 | ||
The composition of hot melt adhesive wet pulp and consumption (kg) | The polyacrylate(s) material | ????1.2 | ????1.5 | ????2 | |
PES or PA polymkeric substance | ????35 | ????38 | ????40 | ||
Shape-intensifying agent | ????3.0 | ????3.0 | ????3.5 | ||
Dispersion agent | ????3.5 | ????4.0 | ????5.0 | ||
Thickening material | ????0.3 | ????0.5 | ????0.8 | ||
?????H 2O | ????65 | ????70 | ????70 | ||
Hot melt adhesive wet pulp dry weight (kg) | ????7 | ????10 | ????13 | ||
The storing temperature of infrared heater 6 ℃ | ????110 | ????120 | ????130 | ||
The storing temperature of infrared heater 9 ℃ | ????130 | ????150 | ????150 | ||
Production rate V (m/min) | ????35 | ????30 | ????25 | ||
The gained adhesive lining with press the quality product test case of scalding after bonding through the garment material of silicon arrangement | Stripping strength (N/5 * 10cm) | ????9 | ????10 | ????9.5 | |
Glue point metastasis degree (%) | ????55 | ????50 | ????45 |
Claims (6)
1, a kind of non-woven thermal smelting adesive lining, comprise non-woven base fabric (1) and hot melt adhesive point coating (3), it is characterized in that on non-woven base fabric (1), being coated with earlier one deck positively charged ion silicon finishing composition layer (2), on this finishing composition layer (2), apply adhesion heat melten gel dot matrix layer (3) more then.
2, by the described non-woven thermal smelting adesive lining of claim 1, the positively charged ion silicon finishing composition that it is characterized in that constituting non-woven base fabric (1) finishing composition layer (2) is to be formed by amido silicon oil, hydroxy silicon oil, phenylcarbinol or jasmal, silicon ester allotment.
3, by the production technique of the described non-woven thermal smelting adesive lining of claim 1, it is characterized in that being undertaken by following processing step:
1. positively charged ion silicon finishing composition (4) is coated on the non-woven base fabric (1) with the method for padding or spray;
2. oven dry has promptly formed one deck positively charged ion silicon finishing composition layer (2) on non-woven base fabric (1) surface;
3. hot melt adhesive (7) is coated on the finishing composition layer (2) on non-woven base fabric (1) surface with the cylinder printing points, and forms dot matrix type hot melt adhesive point coating (3);
4. non-woven thermal smelting adesive lining of the present invention is promptly made in oven dry.
4, by the described non-woven thermal smelting adesive lining production technique of claim 3, it is characterized in that the finishing composition layer (2) of non-woven base fabric (1) surface-coated is dried, employing be infrared heater (6), bake out temperature is controlled at 100~130 ℃.
5, by the described non-woven thermal smelting adesive lining production technique of claim 3, it is characterized in that being coated in the oven dry of the dot matrix type hot melt adhesive point coating (3) on the finish layer (2), employing be infrared heater (9), bake out temperature is controlled at 120~150 ℃.
6, by the described non-woven thermal smelting adesive lining production technique of claim 3, it is characterized in that the blending process of positively charged ion silicon finishing composition (4) is as follows:
1. get 20~35kg hydroxy silicon oil and pour in 70~55kg amido silicon oil, fully stir;
2. get silicon ester 2~3kg and add 10 times of water (is good with soft water) dilution, fully stir;
3. successively will be 2. prepared feed liquid and 5~15kg phenylcarbinol or jasmal pour into and stir in the 1. prepared feed liquid, make the finishing composition mother liquor;
4. the finishing composition mother liquor is diluted with 4~8 times of water, fully stir, promptly make the positively charged ion silicon finishing composition (4) of production usefulness.