Background technology
Folded yarn on the market is generally two plying now, and this double twisted yarn at first is that the formation raw material is single, it can only be a kind of or two kinds of raw materials constitute, as the cotton yarn of pooling capital is to be twisted with the fingers by two strands of cotton yarns, and the plying man-made fibre yarn is to be twisted with the fingers or twisted with the fingers by two different chemical fibre silks of raw material by two chemical fibre silks of same materials.This drawback of bringing owing to the unicity of raw material formation is: when being made into lining with this kind double twisted yarn, the lining that is woven is relatively poor at aspects such as gas permeability, water imbibition, shrinkage resistance, anti-washing property.Next is that the twisted technology of this double twisted yarn is also comparatively simple, the twist is also lower, but this double twisted yarn if on common two-for-one twister just twisted obtain, and this because twisted technology simple, the low deficiency of bringing of the twist also makes the face that weaves relatively poor at aspects such as gas permeability, water imbibition, shrinkage resistance, anti-washing property.
Summary of the invention
The technical problem to be solved in the present invention is at above-mentioned deficiency, develops the production technology of a kind of highly twisted multi-strand knitting yarn and this kind highly twisted multi-strand knitting yarn.
Highly twisted multi-strand knitting yarn of the present invention, it comprises three rhizoids of mutual twisted, one in this three rhizoid is acrylic filaments, two or be silk or for the bamboo fiber or for wood pulp fibre or be in silk, bamboo fiber, the wood pulp fibre two kinds in addition.
The production technology of above-mentioned highly twisted multi-strand knitting yarn: its technological process is with three rhizoids after pre-process, wherein one should be acrylic filaments, be placed on the two-for-one twister, acrylic filaments and other two rhizoids are twisted in the mode that S twists with the fingers, in carrying out twisting process, untwisting limit, acrylic filaments limit and other two rhizoid twisteds, the folded yarn that comes out at last carries out post processing then.
With the lining that highly twisted multi-strand knitting yarn of the present invention is produced, its gas permeability, water imbibition, shrinkage resistance, anti-washing property are all preferable, and with the clothes that this lining is made ABRASION RESISTANCE, anti-pilling, anti-Zhongchang property, stiffness, the property of feeling nice and cool etc. are preferably arranged.
The specific embodiment
The invention will be further described below in conjunction with embodiment.
Highly twisted multi-strand knitting yarn of the present invention comprises three rhizoids of mutual twisted, and one in this three rhizoid is acrylic filaments, and two is silk in addition, and these two silks are long silk, by eight monofilament and close and form.
Three rhizoids of above-mentioned formation highly twisted multi-strand knitting yarn also can be: one for acrylic filaments, and two or be the bamboo fiber in addition, or be wood pulp fibre, or be in silk, bamboo fiber, the wood pulp fibre two kinds.The bamboo fiber is processed by bamboo pulp, and wood pulp fibre is to be processed by wood pulp.
The technological process of production of highly twisted multi-strand knitting yarn of the present invention is: three rhizoids that will be after pre-process, wherein one should be acrylic filaments, two is silk in addition, be placed on the two-for-one twister, acrylic filaments and other two silks are twisted in the mode that S twists with the fingers, in carrying out twisting process, untwisting limit, acrylic filaments limit and other two silk twisteds, the high stocking yarn of twisting with the fingers at last comes out, carry out post processing, i.e. dyeing processing then, the high stocking yarn of twisting with the fingers can only dye once, also can carry out the dyeing second time after having dyed once again.
In the production technology of above-mentioned highly twisted multi-strand knitting yarn, pre-process comprises the pre-process of silk and the pre-process of acrylic filaments.Pre-process to silk is: eight monofilament that will constitute silk, carry out single sth. made by twisting simultaneously, single sth. made by twisting back monofilament is one group with per two monofilament to carry out and twists with the fingers, with four cocainines that obtain after also twisting with the fingers is that a unit carries out once more and sth. made by twisting with per two groups equally, and obtain two joint stock wires, and these two joint stock wires are carried out last also twisting with the fingers, obtain twisting count at last and can reach the silk of twisting with the fingers 1600 more, winder then, silk are twisted with the fingers the mode twisted with Z in whole twisted process.Pre-process to acrylic filaments is: at first be that the multiply filament that constitutes acrylic filaments is carried out network processes, this network processes process is to make a bounding point is arranged between each adjacent filament across a certain distance, and the acrylic filaments after network processes twisted in Z sth. made by twisting mode, obtaining twisting count at last is 600 to 800 acrylic filaments of twisting with the fingers, winders then.
In the technological process of production of highly twisted multi-strand knitting yarn of the present invention, in three rhizoids after pre-process except that acrylic filaments wherein is constant, two silks also can replace with the bamboo fiber in addition, or wood pulp fibre replaces, or two kinds of replacements in the silk, bamboo fiber, wood pulp fibre.The pre-process of bamboo fiber is that the bamboo fiber is carried out the twisting that Z twists with the fingers mode, winder then.The pre-process of wood pulp fibre is that wood pulp fibre is carried out the twisting that Z twists with the fingers mode, winder then.
Silk behind the above-mentioned winder, acrylic filaments, bamboo fiber and wood pulp fibre are directly sent to plying, and the height that obtains of at this moment pooling capital is twisted with the fingers the post processing that stocking yarn need dye.Silk behind the above-mentioned winder, acrylic filaments, bamboo fiber and wood pulp fibre also can be distinguished earlier dyed, are used further to plying, and the height that obtains of at this moment pooling capital is twisted with the fingers the post processing that stocking yarn just needn't dye.