CN108754779A - A kind of preparation method of etching lace jeans - Google Patents
A kind of preparation method of etching lace jeans Download PDFInfo
- Publication number
- CN108754779A CN108754779A CN201810785060.7A CN201810785060A CN108754779A CN 108754779 A CN108754779 A CN 108754779A CN 201810785060 A CN201810785060 A CN 201810785060A CN 108754779 A CN108754779 A CN 108754779A
- Authority
- CN
- China
- Prior art keywords
- twist
- etching
- lace
- core filaments
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to etching jeans preparation fields, and in particular to a kind of preparation method of etching lace jeans.Clothes are processed into through weft yarn, pulp, weaving, arrangement including standby, etching is washed, flatiron；It is described to want non-twist or low twist through weft yarn wrap yarn, wrap yarn made of bifilar cotton coats core filaments；Core filaments use the Polyamide Yarns between 1F to 24F, the identical bifilar opposite twist direction of rugosity, the twist to be equally mutually entwined, and overall core filaments are non-twist；Cladding is with bifilar cotton around core filaments rotation twisting；The pulp is using low temperature dyeing and tension when increase pulp；The weaving is weaved using weft non junction；Described arrange is arranged using the shrink of outsourcing cotton zero；Described that clothes are made by predetermined style, template graphics apply wintercherry etching, and 70-100 degree high temperature washes clothes, drying flatiron.Etching lace jeans prepared by the present invention do not slide comfortably, at beautiful, lace.
Description
Technical field
The invention belongs to etching jeans preparation fields, and in particular to a kind of preparation side of etching lace jeans
Method.
Background technology
The etching cowboy of existing market maturation, which refers to, to rot latitude and longitude (longitude and latitude yarns used do not have core filaments) or rotten warp stays
Lower weft forms and breaks cylinder, i.e. cylinder wound packages, beggar's dress.Beggar fills after repeatedly washing, and latitude and longitude can be washed rotten gradually at broken cylinder,
Extra line can droop outside, influence clothes beauty.
Applique cowboy exactly opens a cylinder on jeans, and the material of upper lace shape then sews and mend inside clothes.Cause
It is plus fills, it is inadequate that this clothes wear comfort level.There is suture, influences beauty.Translucent lace effect is also bad,
It is not Boardy Feeling, being exactly silk has sliding phenomenon, is difficult to promote in the market.
Invention content
The technical problem to be solved in the present invention is to provide the ripe etching flower buds not slid at a kind of comfortable, beauty, lace
The preparation method of silk jeans.
The technical solution adopted in the present invention is：A kind of preparation method of etching lace jeans：Including it is standby through weft yarn,
Clothes are processed into pulp, weaving, arrangement, and etching is washed, flatiron；It is described to be wrapped made of bifilar cotton coats core filaments through weft yarn
Yarn is covered, wrap yarn wants non-twist or low twist；Core filaments use the Polyamide Yarns between 1F to 24F, the identical bifilar opposite twist direction of rugosity, the twist one
Sample is mutually entwined, and overall core filaments are non-twist；Cladding is with bifilar cotton around core filaments rotation twisting；The pulp uses low temperature dyeing
With tension when increase pulp；The weaving is weaved using weft non junction；Described arrange is arranged using the shrink of outsourcing cotton zero；
Described that clothes are made by predetermined style, template graphics apply wintercherry etching, and 70-100 degree high temperature washes clothes, drying flatiron.
The specific preparation method of the wrap yarn is：
Step 1：Standby yarn：Using the fibers such as cotton, viscous cotton, viscose glue, tencel, fiber crops；
Doubling：It is double on double and machine using bifilar same twist direction ring spinning (assuming that two single twists are respectively N1, N2)
Stock merges；
It is pre- to twist：Twisted in advance on chopped fiber two-for-one twisting machine, it is assumed that twist n1, twist direction is opposite with single thread to be taken as positive number, twist direction with
Single thread is identical to be taken as negative；
Yarn：On the short fine pre- twist yarn of high speed cone winder to mechanical coating machine spool；
Step 2：Standby core filaments：Paraphase is the same as bright and beautiful (washing) the synthetic fibre silk of rugosity to two mechanical coating machine aluminum pipes on high-speed silk winding frame
On；Twisting, a point upper layer and lower layer is twisted in same spindle position, and the twist is identical, and twist direction is opposite；
Step 3：Cladding：Twisting is coated on mechanical coating machine：Core filaments pass through among spindle, from the pre- twist yarn on tubulation
It rotates and twists around core filaments, the twisting twist is set as n2, and twist direction is opposite with single thread (numerical value is positive number), as long as accomplishing n1+n2 and (N1
+ N2)/4 numerical value are close or equal, and twist direction is opposite with single thread twist direction；The twist is twisted in advance adds the cladding twist numerically
A quarter that is close or being equal to two single twist sums, and finished product wrap yarn twist direction is opposite with single thread.
As another embodiment：Being added together number using two single thread, (such as two single thread are all with 32, just use
16 single thread replacements) RING SPINNING single thread production, i.e., on high speed cone winder fall yarn to mechanical coating machine spool on.
As another embodiment：1F to 24F is used in the step 2,60D to 100D polyamide fibres or dacron thread are direct
It is coated into next step yarn core.
Core filaments are non-twist in the step 3；The twist is numerically close or equal plus the cladding twist in advance for the bifilar cotton of outsourcing
In a quarter of two single twist sums, i.e. n1+n2 and (N1+N2)/4 numerical value are close or equal, and outsourcing cotton is twisted without (low), institute
It is twisted without (low) with overall on wrap yarn.
Core filaments cannot have connector at the etching, and wrap yarn will accomplish non junction in process of production when as warp thread, fixed
It is long；If any broken end, broken end wrap yarn is used as weft, not connector when weaving.
As another embodiment：The staplings is unable to connector, and bobbin, which is finished, is unable to connector.
Longitude and latitude is washed to outsourcing cotton shrinkage less than 1.5% in road after the clothes.
Beneficial effects of the present invention：
One, (low) the twirl wrap yarn of this nothing makees warp-wise, and the phenomenon that winding mutually occurs in warp-wise during avoiding pulp, greatly
The big end breakage rate reduced when leading through, lease making, makes to lead and has reached normal level through pulp speed, realizes the mesh of mass production
's.Core filaments cross winding is non-twist, ensure that under decorated fire clothes relaxed state, and the core filaments (at lace) of exposing do not slide, and increases clothes
Dress is beautiful.
Two, lace is integrated with clothes, and smooth, beautiful beautiful.
Three, the feel of clothes is not hard, and comfort level is good.
Four, it is close with human body complexion at translucent lace, it wears beautiful sexy.
Five, it is repeatedly washed through clothes user, no extra yarn droops, cleaner and tidier than beggar's dress, and people is allowed to feel more to improve grade.
Specific implementation mode
Illustrate the present invention with specific embodiment below, is not limitation of the present invention.
Embodiment one
One, production is through weft yarn (wrap yarn)
1, standby yarn：Standby 40 1000 twists/m of Z twist cotton RING SPINNING single thread.
A, doubling：All it is 40 1000 twists/m of Z twist yarns bifilar merging, i.e. N1=1000, N2 on double and machine using two
=1000.
B, pre- to twist：Pre-add Z twists 100 twirls and takes negative value, i.e. n1=- because identical as single thread twist direction on chopped fiber two-for-one twisting machine
100。
C, fall yarn：On the short fine pre- twist yarn of high speed cone winder to mechanical coating machine spool.
2, standby core filaments
A, wire inversion：On high-speed silk winding frame on the polyamide fibre of falling 40D1F bright yarn to mechanical coating machine aluminum pipe.
B, it twists：It is divided to two silks of upper layer and lower layer respectively to add 500 twirls in same spindle position, and twist direction is opposite.
Same rugosity, the same to twist, twist direction is on the contrary, so overall core filaments are non-twist.
3, it coats
Twisting is coated on upper machinery coating machine：Core filaments pass through among spindle, and pre- twist yarn is twisted around core filaments rotation plus 600, S
Twist direction takes positive value, i.e. n2=525.Core filaments are not involved in twisting.
A, (N1+N2)/4=(1000+1000)/4=500, Z twist directions.
B, n1+n2=-100+600=500, S twist direction.
A and B numerically equals, for twist direction on the contrary, so theoretically outsourcing cotton is non-twist, core filaments are non-twist, so wrap yarn is managed
By upper non-twist.
Two, pulp
It leads through pulp.Using low temperature dyeing and tension method when appropriate increase pulp.Ensure that outsourcing material contracts with core filaments
Rate is the same.Outsourcing material not arch camber, convenient for weaving.
Three, it weaves
Weaving process, longitude and latitude use 90/80 weaving density.
Lime light when weaving：
1, staplings is unable to connector.
2, bobbin, which is finished, is unable to connector.
This method ensures do not have connector fault at clothes etching, improves clothing product rate to the full extent.Half at etching
Sliding title phenomenon between transparent place's silk disappears.
Four, it arranges
After cotton-wadded quilt rots at the translucent lace of etching, structure loosely, arch camber is easy not at etching compared at non-etching
It is smooth.To ensure that the place at the translucent lace of etching with not etching is smooth consistent, is shunk and arranged using outsourcing cotton zero, that is, taken
The roads Zhuan Hou wash longitude and latitude and are less than 1.5% to outsourcing cotton shrinkage.
Five, clothes are processed into, etching is washed, flatiron
Clothes are made by predetermined style, apply wintercherry etching by template graphics, 90 degree of high temperature wash clothes, drying flatiron.
Embodiment two
One, production is through weft yarn (wrap yarn)
1, standby yarn：Standby 32 850 twists/m of Z are twisted twists CR RING SPINNING single thread with 40 1000 twists/m of Z, and CR is than 60/40.
A, doubling：Bifilar merging, i.e. N1=850, N2=1000 on double and machine.
B, pre- to twist：Pre-add Z twists 100 twirls and takes negative value, i.e. n1=- because identical as single thread twist direction on chopped fiber two-for-one twisting machine
100。
C, fall yarn：On the short fine pre- twist yarn of high speed cone winder to mechanical coating machine spool.
2, standby core filaments
A, wire inversion：On high-speed silk winding frame on the polyamide fibre of falling 50D1F bright yarn to mechanical coating machine aluminum pipe.
B, it twists：It is divided to two silks of upper layer and lower layer respectively to add 500 twirls in same spindle position, and twist direction is opposite.
Same rugosity, the same to twist, twist direction is on the contrary, so overall core filaments are non-twist.
3, it coats
Twisting is coated on upper machinery coating machine：Core filaments pass through among spindle, and pre- twist yarn is twisted around core filaments rotation plus 562, S
Twist direction takes positive value, i.e. n2=562.Core filaments are not involved in twisting.
A, (N1+N2)/4=(850+1000)/4=462.5, Z twist directions.
B, n1+n2=-100+562=462, S twist direction.
A is numerically close with B, and twist direction is on the contrary, so theoretically outsourcing cotton low twist, core filaments are non-twist, so wrap yarn is managed
By upper low twist.
Two, pulp
It leads through pulp.Using low temperature dyeing and tension method when appropriate increase pulp.Ensure that outsourcing material contracts with core filaments
Rate is the same.Outsourcing material not arch camber, convenient for weaving.
Three, it weaves
Weaving process, longitude and latitude use 87/68 weaving density.
Lime light when weaving：
1, staplings is unable to connector.
2, bobbin, which is finished, is unable to connector.
This method ensures do not have connector fault at clothes etching, improves clothing product rate to the full extent.Half at etching
Sliding title phenomenon between transparent place's silk disappears.
Four, it arranges
After cotton-wadded quilt rots at the translucent lace of etching, structure loosely, arch camber is easy not at etching compared at non-etching
It is smooth.To ensure that the place at the translucent lace of etching with not etching is smooth consistent, is shunk and arranged using outsourcing cotton zero, that is, taken
The roads Zhuan Hou wash longitude and latitude and are less than 1.5% to outsourcing cotton shrinkage.
Five, clothes are processed into, etching is washed, flatiron
Clothes are made by predetermined style, apply wintercherry etching by template graphics, 90 degree of high temperature wash clothes, drying flatiron.
Embodiment three
One, production is through weft yarn (wrap yarn)
1, standby yarn：Standby 32 850 twists/m of Z twist cotton and twist numb RING SPINNING ring single thread with 32 750 twists/m of Z.
A, doubling：Bifilar merging, i.e. N1=850, N2=750 on double and machine.
B, pre- to twist：Pre-add S twists 100 twirls on chopped fiber two-for-one twisting machine, because with single thread twist direction on the contrary, take positive value, i.e. n1=
100。
C, fall yarn：On the short fine pre- twist yarn of high speed cone winder to mechanical coating machine spool.
2, standby core filaments
A, wire inversion：On high-speed silk winding frame on the polyamide fibre of falling 50D1F bright yarn to mechanical coating machine aluminum pipe.
B, it twists：It is divided to two silks of upper layer and lower layer respectively to add 500 twirls in same spindle position, and twist direction is opposite.
Same rugosity, the same to twist, twist direction is on the contrary, so overall core filaments are non-twist.
3, it coats
Twisting is coated on upper machinery coating machine：Core filaments pass through among spindle, and pre- twist yarn is twisted around core filaments rotation plus 300, S
Twist direction takes positive value, i.e. n2=300.Core filaments are not involved in twisting.
A, (N1+N2)/4=(850+750)/4=400, Z twist directions.
B, n1+n2=100+300=400, S twist direction.
A and B numerically equals, for twist direction on the contrary, so theoretically outsourcing cotton is non-twist, core filaments are non-twist, so wrap yarn is managed
By upper non-twist
Two, pulp
It leads through pulp.Using low temperature dyeing and tension method when appropriate increase pulp.Ensure that outsourcing material contracts with core filaments
Rate is the same.Outsourcing material not arch camber, convenient for weaving.
Three, it weaves
Weaving process, longitude and latitude use 86/70 weaving density.
Lime light when weaving：
1, staplings is unable to connector.
2, bobbin, which is finished, is unable to connector.
This method ensures do not have connector fault at clothes etching, improves clothing product rate to the full extent.Half at etching
Sliding title phenomenon between transparent place's silk disappears.
Four, it arranges
After cotton-wadded quilt rots at the translucent lace of etching, structure loosely, arch camber is easy not at etching compared at non-etching
It is smooth.To ensure that the place at the translucent lace of etching with not etching is smooth consistent, is shunk and arranged using outsourcing cotton zero, that is, taken
The roads Zhuan Hou wash longitude and latitude and are less than 1.5% to outsourcing cotton shrinkage.
Five, clothes are processed into, etching is washed, flatiron
Clothes are made by predetermined style, apply wintercherry etching by template graphics, 90 degree of high temperature wash clothes, drying flatiron.
Although the present invention has been described by way of example and in terms of the preferred embodiments, it is not limited to the present invention, any to be familiar with this skill
The people of art can do various change and modification, therefore the protection model of the present invention without departing from the spirit and scope of the present invention
Enclosing be subject to what claims were defined.
Claims (10)
1. a kind of preparation method of etching lace jeans：It is characterized in that：Including standby through weft yarn, pulp, weaving, arrangement,
Clothes are processed into, etching is washed, flatiron；The wrap yarn made of bifilar cotton coats core filaments through weft yarn, wrap yarn will nothing
Twirl or low twist；Core filaments use the Polyamide Yarns between 1F to 24F, the identical bifilar opposite twist direction of rugosity, the twist to be equally mutually entwined,
Overall core filaments are non-twist；For cladding with bifilar cotton around core filaments rotation twisting, core filaments are not involved in twisting；The pulp is using increase pulp
When tension；The weaving is weaved using weft non junction；Described arrange is arranged using the shrink of outsourcing cotton zero；It is described to press primecost sum
Clothes are made in formula, spray wintercherry etching by predetermined pattern, high temperature washes clothes, drying flatiron.
2. a kind of preparation method of etching lace jeans according to claim 1：It is characterized in that：The wrap yarn
Specific preparation method be：
Step 1：Standby yarn：Single thread is using the fibers such as cotton, viscous cotton, viscose glue, tencel, fiber crops；
Doubling：Two single thread are used with twist direction ring spinning, the bifilar merging on double and machine；
It is pre- to twist：It is twisted in advance on two-for-one twister；
Yarn：On the short fine pre- twist yarn of high speed cone winder to mechanical coating machine spool；
Step 2：Standby core filaments：With Polyamide Yarns 30D to the 70D of rugosity, 1 to 24F twists a Z using a S twists with twist twist direction phase
Anti-cross is intertwined；
Step 3：Cladding：Twisting is coated on mechanical coating machine：Core filaments pass through among spindle, the mechanical pre- twist yarn of coating machine spool
It rotates and twists around core filaments, twist direction is opposite with single thread.
3. a kind of preparation method of etching lace jeans according to claim 2：It is characterized in that：The step 1
In two single thread be identical material identical number or identical material difference number or different materials, identical number, or different
Material, different numbers.
4. a kind of preparation method of etching lace jeans according to claim 2：It is characterized in that：The step 1
The middle RING SPINNING single thread production that number is added together using two single thread falls yarn to machinery coating machine spool that is, on high speed cone winder
On.
5. a kind of preparation method of etching lace jeans according to claim 2：It is characterized in that：The step 2
Middle between 1F to 24F, 60D to 100D polyamide fibres are not processed, and are used directly as core filaments.
6. a kind of preparation method of etching lace jeans according to claim 2：It is characterized in that：The step 2
Middle Polyamide Yarns is replaced with dacron thread.
7. a kind of preparation method of etching lace jeans according to claim 2：It is characterized in that：The step 3
In in advance twist direction it is identical as single thread twist direction, numerically the cladding twisting twist subtracts the pre- twirl twist and is mutually summed it up with two single twists
A quarter it is close or equal；Or twist direction is twisted with single thread twist direction on the contrary, numerically coating twisting in advance in the step 3
Degree is close or equal with a quarter that two single twists mutually sum it up plus the pre- twirl twist.
8. a kind of preparation method of etching lace jeans according to claim 2：It is characterized in that：The step 3
Middle core filaments are non-twist, low twist or non-twist on wrap yarn.
9. a kind of preparation method of etching lace jeans according to claim 1：It is characterized in that：At the etching
Core filaments cannot have connector, wrap yarn that cannot have connector in process of production.
10. a kind of preparation method of etching lace jeans according to claim 1：It is characterized in that：The fabric
Longitude and latitude will ensure that clothes shrinkage in washing is less than 1.5% to outsourcing cotton when arrangement, that is, do longitude and latitude and arranged to the shrink of outsourcing cotton zero.