CN1390793A - Process for preparing golden marble glass mosaic - Google Patents
Process for preparing golden marble glass mosaic Download PDFInfo
- Publication number
- CN1390793A CN1390793A CN 02134452 CN02134452A CN1390793A CN 1390793 A CN1390793 A CN 1390793A CN 02134452 CN02134452 CN 02134452 CN 02134452 A CN02134452 A CN 02134452A CN 1390793 A CN1390793 A CN 1390793A
- Authority
- CN
- China
- Prior art keywords
- glass
- manufacture method
- mosaic
- scagliola
- colour mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A golden marble glass mosaic is prepared from the basic glass materials through proportioning, smelting, clarifying, homogenizing, adding pigment(s) at 1100-1400 deg.C, mixing, cooling to 700-1200 deg.C, adding reflection material, and stirring. Its advantages are less consumption of reflection material and energy, low cost, and high decorative effect.
Description
The present invention relates to a kind of manufacture method that the marble shape glass Mosaic of irregular Alectoria virens Tayl. is arranged.
Glass Mosaic is a kind of range of application material of construction very widely, not only is used for the external wall of buildings in a large number, and more and more upholstery that is applied to.The glass Mosaic style of selling on the existing market is varied, only be solid color mostly, but along with the progress of science and technology and improving constantly of people's living standard, require manufacturing enterprise to develop fashionable, ornamental stronger, mosaic that grade is higher, to be suitable for the needs in building decoration market.Chinese patent CN1100390 discloses a kind of manufacture method of metal aventurine glass mosaic.Its method is the same with existing simple glass mosaic at the parent glass material, with silica sand, calcite, soda ash be colored as raw material, forms by known mixed, adds to contain a metal aventurine glass material grain again.The product of producing by this method is a translucent body, in Venus in blocks is arranged, have certain decorative effect, but exist energy consumption bigger, the whole prod surface is covered with metal Venus, style dullness, stiff is ornamental relatively poor; Metal aventurine glass materials amount is more, costs an arm and a leg, and causes cost higher, and metal aventurine glass directly adds in the material road simultaneously, can be by high temperature evaporation and to shortcomings such as environment pollute.
The object of the present invention is to provide the manufacture method of golden marble shape glass Mosaic, the mosaic of producing with this method, uneven color mixes or two or more blend of colors is the cloud shape, and wherein reflecting material produces the irregular silk ribbon shape of golden flash of light under the irradiation of light, reaches the effect of natural marble color, improve the decoration grade of product, simultaneously, it is simple to have method, and expensive raw material consumption is few, reduce cost the characteristics of non-environmental-pollution.
The object of the present invention is achieved like this:
Composition of the present invention and prescription are:
The parent glass material is the same with existing simple glass mosaic, is raw material with silica sand, calcite, battalion's stone, feldspar, soda ash etc. and tinting material, forms by known mixed, and add tinting material and reflecting material in described parent glass material.
The tinting material that joins for the first time basestocks is the background color tinting material; The tinting material that joins for the second time colour mixture portion can select the tinting material of different color to carry out the colour mixture processing by different needs.
Manufacture method:
1, prepares the parent glass material in proportion;
2, with in the stove of parent glass material input cellar for storing things, temperature is 1200-1500 ℃, is melted into the glass metal of the host glass with background color color;
3, the glass metal through clarification, homogenizing enters the material road from the cellar for storing things stove, when temperature is 1100-1400 ℃, adds one or more tinting materials and carries out painted processing, forms spatter glass liquid;
4, spatter glass liquid enters colour mixture portion from the material road, adds reflecting material in colour mixture portion, and makes it even diffusion;
5, roll-forming in the mosaic shaper;
6, annealing finished product.
Aforesaid method, when the temperature of colour mixture portion is 700-1200 ℃, spatter glass liquid is cooled to
Viscosity is 10
2-10
6During PaS, add reflecting material,
Aforesaid method, when the temperature of colour mixture portion was 800-1000 ℃, adding reflecting material effect was better.
Aforesaid method, particulate colored dose of the glass that two kinds of tinting materials of employing high density are made 1.5-2mm in the material road carries out painted processing, forms spatter glass liquid.
Aforesaid method, colour mixture portion is an agitator, as the device that adds reflecting material, avoids adding reflecting material in hot environment Evaporation Phenomenon can take place.
Aforesaid method, the tinting material that joins basestocks for the first time is the background color tinting material; The tinting material that joins for the second time colour mixture portion can be selected tinting material such as cupric oxide, nickel oxide, cobalt oxide, potassium permanganate, selenium powder or the sulphur etc. of different color by different needs, forms the different colours mixing and is the cloud shape; Also can adopt the background color tinting material of high density, form the uneven color mixing and be the cloud shape.
Aforesaid method, the glass of the different colorant of high density being made 1.5-2mm is granular, adds in the road at material, fusible be diffused in the frit and reach the purpose of colour mixture.
Above-mentioned reflecting material is material grains such as copper gold sand, blue gold sand or green gold sand.
The consumption of above-mentioned reflecting material is the 0.3-15% of parent glass material.
The present invention has following advantage compared to existing technology:
1, manufacture method is simple, raw material sources are wide, the reflecting material consumption is few and in colour mixture portion operation, avoid in the hot environment evaporation and produce waste, simultaneously save energy, save the consumption of reflecting material, reduce cost greatly, significantly reduce pollution to environment;
When 2, this inventive method manufactures a product, add reflecting material in colour mixture portion, the reflecting material of its surface arrangement produces the banded flash of light of irregular spun gold under the shining of light, and product has multicolour, a stove polychrome, and tangible gradation sense and stereoscopic sensation are arranged;
3, product is fashionable, diversified, reaches the effect of the color of natural marble, and can form various patterns as required, improves the class of product greatly, can be widely used in the luxurious decoration of indoor and outdoor of buildings, beautifies the environment, beautifies family.
Embodiment one
1. component and prescription
(1). the parent glass material formula
Silica sand 58% (SiO2:70%)
Feldspar 16% (AL2O3:2.5-6.5%)
Calcite 7%
Soda ash 19%
(2). form the tinting material of background color
Sodium Silicofluoride 2%
(3). for the second time painted tinting material
Can use cupric oxide according to the color category and the depth, its consumption accounts for 0.3% of parent glass material.
(4). reflecting material is the copper gold sand, and its consumption accounts for 3% of parent glass material.
2. manufacture method
(1). prepare the parent glass material in proportion;
(2). parent glass material (comprising for the first time painted tinting material) drops in the stove of cellar for storing things, temperature
Be 1200 ℃, be melted into the glass metal of the host glass that is white in color;
(3). the glass metal through clarification, homogenizing enters the material road from the cellar for storing things stove, when temperature is 1250 ℃
The time, add cupric oxide and carry out painted processing, form spatter glass liquid;
(4). in colour mixture portion, it is 10 that spatter glass liquid is cooled to viscosity
2PaS, temperature is 800 ℃
The time add reflecting material copper gold sand, and stir with mechanical type and to make it even diffusion;
(5). roll-forming in the mosaic shaper; (6). the annealing finished product.
Products obtained therefrom body the be white in color end and blueness, the irregular reflecting material of surface arrangement produce the golden flash of light under the shining of light, change reflection of light, the situation that sees through or absorb, and special optical property produces the effect of natural marble.
Embodiment 2 1. components and prescription (1). parent glass material formula silica sand 58% (SiO2:70%) feldspar 12% (AL2O3:2.5-6.5%) calcite 6% soda ash 18% (2). tinting material can be used small amounts nickel according to the color category and the depth for the first time.(3). tinting material nickel oxide for the second time, its consumption are the painted one times first time.(4). reflecting material blue gold sand, its consumption accounts for 10% of parent glass material.2. manufacture method (1). prepare the parent glass material in proportion; (2). in the stove of parent glass material input cellar for storing things, temperature is 1500 ℃, is melted into the glass metal of light grey host glass; (3). the glass metal through clarification, homogenizing enters the material road from the cellar for storing things stove, when temperature is 1400 ℃, adds the painted processing of nickel oxide, forms spatter glass liquid; (4). in colour mixture portion, it is 10 that spatter glass liquid is cooled to viscosity
6PaS adds light reflecting material when temperature is 800 ℃, and stirs evenly diffusion just by hand; (5). roll-forming in the mosaic shaper; (6). the annealing finished product.
The products obtained therefrom body is light grey and the irregular strip of Dark grey, and the reflecting material of surface arrangement produces the flash of light of inclined to one side green gold star under the shining of light, form the effect of the color of natural marble.
Embodiment three
(1). the parent glass material formula is identical with embodiment one
(2). tinting material adopts the nickel oxide of high high density, glass that cobalt oxide is made 1.5-2mm granular, adds in the material road, fusible be diffused in the frit and reach the purpose of colour mixture.
(3). reflecting material chromium Venus, its consumption accounts for 0.3% of parent glass material.
2. manufacture method
(1). prepare the parent glass material in proportion;
(2). in the stove of parent glass material input cellar for storing things, temperature is 1350 ℃, is melted into the glass metal of host glass;
(3). particulate colored dose of the glass that two kinds of tinting materials of nickel oxide, cobalt oxide of employing high density are made 1.5-2mm in the material road, at high temperature molten loosing carried out painted processing, forms spatter glass liquid.
(4). the glass metal through clarification, homogenizing enters colour mixture portion from the material road, and being cooled to viscosity is 10
6PaS adds reflecting material when temperature is 1000 ℃;
(5). roll-forming in the mosaic shaper, wherein reflecting material evenly spreads;
(6). the annealing finished product.
Claims (9)
1, a kind of manufacture method of golden marble glass mosaic is:
(1), prepares the parent glass material in proportion;
(2), with in the stove of parent glass material input cellar for storing things, temperature is 1200-1500 ℃, is melted into the glass metal of the host glass with background color color;
(5), roll-forming in the mosaic shaper;
(6), annealing;
It is characterized in that:
(3), enter the material road from the cellar for storing things stove, when temperature is 1100-1400 ℃, adds one or more tinting materials and carry out painted processing, form spatter glass liquid through the glass metal of clarification, homogenizing;
(4), spatter glass liquid from the material road enter colour mixture portion, in colour mixture portion, add reflecting material, and make it even diffusion.
2, by the manufacture method of the described spun gold scagliola of claim 1 glass Mosaic, it is characterized in that the temperature when colour mixture portion is 700-1200 ℃, the spatter glass fluid viscosity is 10
2-10
6During PaS, add reflecting material.
3, by the manufacture method of the described spun gold scagliola of claim 1 glass Mosaic, it is characterized in that when the temperature of colour mixture portion is 800-1000 ℃, add reflecting material.
4, by the manufacture method of the described spun gold scagliola of claim 1 glass Mosaic, particulate colored dose of the glass that two kinds of tinting materials of employing high density are made 1.5-2mm in it is characterized in that expecting carries out painted processing, forms spatter glass liquid.
5, press the manufacture method of the described spun gold scagliola of claim 1 glass Mosaic, its
Be characterised in that the tinting material that joins basestocks is the background color tinting material; The tinting material that joins colour mixture portion can adopt the background color tinting material of high density.
6,, it is characterized in that colour mixture portion is for adding the device of reflecting material by the manufacture method of the described spun gold scagliola of claim 1 glass Mosaic.
7,, it is characterized in that above-mentioned reflecting material is material grains such as copper gold sand, blue gold sand or green gold sand by the manufacture method of the described spun gold scagliola of claim 1 glass Mosaic.
8,, it is characterized in that colour mixture portion is for adding the agitator of reflecting material by the manufacture method of the described spun gold scagliola of claim 6 glass Mosaic.
9, by the manufacture method of the described spun gold scagliola of claim 7 glass Mosaic, it is characterized in that above-mentioned reflecting material is copper gold sand, blue gold sand or green gold sand material grain, its charging capacity is the 0.3-15% of parent glass material.