CN1381647A - 防尘拉力湿部添加剂 - Google Patents
防尘拉力湿部添加剂 Download PDFInfo
- Publication number
- CN1381647A CN1381647A CN 01107366 CN01107366A CN1381647A CN 1381647 A CN1381647 A CN 1381647A CN 01107366 CN01107366 CN 01107366 CN 01107366 A CN01107366 A CN 01107366A CN 1381647 A CN1381647 A CN 1381647A
- Authority
- CN
- China
- Prior art keywords
- paper
- dust
- sodium
- increasing additive
- acrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种防尘拉力湿部添加剂,含有下列组份:聚乙烯醇4－6,磷酸三钠6－9,偏硅酸钠4－6,变性淀粉20－25,糊精5－7,元明粉16－22,硫酸铝3－4,丙烯酸酯5－7,羧甲基纤维素钠6－8,松香胶4－6,本添加剂可提高纤维回收率20－36%,提高纸张拉力16－25%,降低成本22－32%。
Description
本发明涉及一种造纸用添加剂，尤其是一种防尘拉力湿部添加剂。
众所周知，在造纸过程中，纸浆回收率高低是个至关重要的问题，尤其在废纸的回收过程中，短纤维的比重较高，在蒸煮制浆过程中，纸纤维流失量大，对环境污染大，纸的产量低，同时短纤维比重高也易使纸的质量降低，细小纸纤维飞扬，抗拉强度低，经济效益不高，到目前为止，尚无一个较好的解决办法。
本发明的目的在于克服现有技术的不足，提供一种可提高纸纤维回收率、增加纸的抗拉强度、光洁度和柔软度，减少纸纤维飞扬，减少污染，降低成本的造纸用防尘拉力湿部添加剂。
本发明的目的通过下述技术方案来实现：
按下列组份和重量比备料配制：
聚乙烯醇 4-6 磷酸三钠 6-9
偏硅酸钠 4-6 变性淀粉 20-25
糊精 5-7 元明粉 16-22
硫酸铝 3-4 丙烯酸酯 5-7
羧甲基纤维素钠 6-8 松香胶 4-6
配制方法：将聚乙烯醇粉碎至80-120目与元明粉、硫酸铝、羧甲基纤维素钠相混合，加入变性淀粉、糊精、丙烯酸酯、松香胶混合均匀后，再加入偏硅酸钠混合均匀后包装即可，本发明主要是通过硫酸铝的凝聚作用，及丙烯酸酯、羧甲基纤维素钠的加强纤维作用，再通过聚乙烯醇悬浮作用，从而大大提高纸纤维的回收率。并通过磷酸三钠的渗透作用及松香胶的分散作用，从而使充填剂淀粉糊精等与纸纤维均匀分散，提高附着力，并通过偏硅酸钠等造型作用，及各组份的协同作用，从而使纸的强度增加，光洁度和柔软度提高，减少尘埃飞扬，最终达到提高纸品质量和数量，降低造纸成本。
经过四川省数家造纸厂实际使用，效果令人满意，可提高纤维回收率20-36％，提高纸张拉力16-25％，降低成本22-32％。
表1 防尘拉力湿部添加剂使用效果
| 使用效果使用单位 | 提高纤维回收率％ | 提高纸张拉力％ | 降低成本％ |
| 嘉陵胜科纸厂 | 30 | 18 | 29 |
| 永安造纸厂 | 20 | 16 | 22 |
| 李渡造纸厂 | 36 | 25 | 32 |
| 兴降造纸厂 | 28 | 22 | 27 |
从上述情况可知，本发明的目的是可以实现的。
使用时，每吨绝干浆加入防尘拉力湿部添加剂2.1kg左右即可，具体加入方法为在纸浆水洗后徐徐加入即可达到满意效果，另外可根据蜡光纸、复印纸、彩印纸、文化纸、卫生纸、餐巾纸等不同适比加入“钙”粉和“镁”粉，其效果会更好。
下面结合实施例，对本发明作进一步说明：
实施例1：
按下列组份和重量备料：
聚乙烯醇 4kg 磷酸三钠 8kg
偏硅酸钠 6kg 变性淀粉 20kg
糊精 6kg 元明粉 22kg
硫酸铝 3kg 丙烯酸酯 6kg
羧甲基纤维素钠 8kg 松香胶 5kg
配制方法：将聚乙烯醇粉碎至100目与元明粉、硫酸铝、羧甲基纤维素钠相混合，加入变性淀粉、糊精、丙烯酸酯、松香胶混合均匀后，再加入偏硅酸钠混合均匀后包装即可。
实施例2：
聚乙烯醇 5kg 磷酸三钠 9kg
偏硅酸钠 4kg 变性淀粉 23kg
糊精 7kg 元明粉 16kg
硫酸铝 3.5kg 丙烯酸酯 7kg
羧甲基纤维素钠 6kg 松香胶 4kg
配制方法：将聚乙烯醇粉碎至120目与元明粉、硫酸铝、羧甲基纤维素钠相混合，加入变性淀粉、糊精、丙烯酸酯、松香胶混合均匀后，再加入偏硅酸钠混合均匀后包装即可。
实施例3：
聚乙烯醇 6kg 磷酸三钠 6kg
偏硅酸钠 5kg 变性淀粉 25kg
糊精 5kg 元明粉 20kg
硫酸铝 4kg 丙烯酸酯 5kg
羧甲基纤维素钠 7kg 松香胶 6kg
配制方法：将聚乙烯醇粉碎至80目与元明粉、硫酸铝、羧甲基纤维素钠相混合，加入变性淀粉、糊精、丙烯酸酯、松香胶混合均匀后，再加入偏硅酸钠混合均匀后包装即可。
Claims (2)
1、一种防尘拉力湿部添加剂，其特征在于：由下列组份和重量比配制而成：聚乙烯醇4-6，磷酸三钠6-9，偏硅酸钠4-6，变性淀粉20-25，糊精5-7，元明粉16-22，硫酸铝3-4，丙烯酸酯5-7，羧甲基纤维素钠6-8，松香胶4-6。
2、一种防尘拉力湿部添加剂的生产方法，其特征在于：将聚乙烯醇粉碎至80-120目与元明粉、硫酸铝、羧甲基纤维素钠相混合，加入变性淀粉、糊精、丙烯酸酯、松香胶混合均匀后，再加入偏硅酸钠混合均匀后包装即可。