CN1372992A - Golf club head and its surface treatment method - Google Patents
Golf club head and its surface treatment method Download PDFInfo
- Publication number
- CN1372992A CN1372992A CN01133908A CN01133908A CN1372992A CN 1372992 A CN1372992 A CN 1372992A CN 01133908 A CN01133908 A CN 01133908A CN 01133908 A CN01133908 A CN 01133908A CN 1372992 A CN1372992 A CN 1372992A
- Authority
- CN
- China
- Prior art keywords
- milled processed
- club head
- glof club
- cartridge type
- type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a golf club head, which is surface-treated when applied with a barrel polishing treatment on its metal surface, the gloss of the metal surface is finished delicately differently between a head body and a dissimilar metal member, thereby the boundary between the head body and the dissimilar metal member can be clearly identified in this design. Thus, the present invention provides an excellent golf club head that cannot be obtained with the prior arts.
Description
Technical field
The present invention relates to a kind of metal system glof club head of milled processed and surface treatment method of glof club head of being subjected to, particularly a kind of glof club head and surface treatment method thereof of on the surface, implementing wet lapping processing and dry grinding processing.
Background technology
For being the surface-treated method of the metal system glof club head of representative with the iron club head, known in the past have " electroplating processes ", " application processing ", " quality on generation material surface is handled " etc., and it is very common particularly to carry out the aforementioned surfaces processing with " quality that produces the material surface is handled (handling hereinafter referred to as quality) ".
Should " quality processing " generally constitute by " rough lapping processing " and " forming lapping processing ".Aforementioned " rough lapping processing " is the method for the profile of arrangement surface treatment object, and aforementioned " forming lapping processing " to be surface dressing with aforementioned object become finer method.
" sand paper milled processed " or " wet type cartridge type milled processed " arranged in the gimmick of these milled processed.
At first, " sand paper milled processed " carries out " rough lapping processing " with the thicker sand paper of numbering earlier, and the numbering that will grind sand paper thereafter again subtracts carefully interimly and carry out " forming lapping processing ".
On the other hand, " wet type cartridge type milled processed " uses the thicker abrasive media of granularity to carry out " rough lapping processing " earlier, and the granularity that will grind thereafter with medium subtracts carefully and carry out " forming lapping processing ".
In addition, make the surface of rod head noumenon produce gloss to rod head noumenon by implementing " polishing milled processed ".Should " polishing milled processed " after reaching the various milled processed of " forming lapping processing ", above-mentioned " rough lapping processing " carry out.
But, in the aforementioned milled processed, reach the easy uneven problem of grinding that produces of existence in " polishing milled processed " in " sand paper milled processed ".Because these milled processed are undertaken by the craft of operation, so be difficult to grind with uniform grinding pressure all surfaces of aforementioned rod head noumenon.
In addition, in aforementioned milled processed, there is the problem of this meeting variable color after milled processed of aforementioned rod head noumenon.Its reason is that grounds travel is attached on the rod head noumenon, makes the remaining and variable color of this grounds travel.In milled processed, exist abrasive power to lower the problem that can't continue good grinding because of aforementioned sand paper or aforementioned polishing again.Its reason is, grinds the surface attachment grounds travel of sand paper or polishing sand paper, causes obstruction.
Again, on the process rod head noumenon of aforementioned milled processed, in its surface meeting residual ' grinding hole '.In order to eliminate this grinding hole, it is effective implementing aforesaid polishing milled processed.But, implement this polishing milled processed after, whole glof club head can produce gloss without exception, existence can only be had the problem of the glof club head of certain gloss on the whole.
On the other hand, for the glof club head of on the part of the rod head noumenon of glof club head, burying the metal formed parts (plate etc.) different underground with aforementioned rod head noumenon, when implementing the polishing milled processed, there is the problem that is difficult to show with ' different ' of the texture of aforementioned dissimilar materials and even gloss.
Because aforesaid polishing milled processed generally is to carry out with handwork, so when aforementioned each dissimilar metal changed extruding force on lapping device and grind, production efficiency descended, and inappropriate.Therefore, because the whole surface of glof club head is ground together, so make it to produce certain gloss.
Therefore, the object of the present invention is to provide a kind of glof club head and its surperficial processing method, on the glof club head to imposing in fact toward the extremely new surface treatment of on glof club head, not carried out, by on the surface of glof club head, initiatively forming treated side, can easily improve the appearance of glof club head with various luster.
In addition, another object of the present invention is to provide a kind of glof club head and surface treatment method thereof, multiple metal material is constituted glof club head, expose the glof club head on a plurality of surfaces of different metal to having the part, utilize the difference of metal grinding effect to form a plurality of surfaces with various luster.
Another purpose of the present invention is to provide a kind of glof club head, can be energetically to the demander glof club head of high-tech of having showed the utilization that constitutes by aforementioned multiple metallic combination.
Promptly, the object of the present invention is to provide a kind of glof club head and surperficial special treatment method thereof, in order to improve the performance that impacts golf,, combination hardness and the different glof club head that metal constituted of proportion can be presented at the outside on one's own initiative by in its surface treatment, working hard.
The object of the present invention is to provide a kind of glof club head,, in the surface treatment of metal glof club head, can stablize and continue to carry out high efficiency appropriate milled processed, and make its surface have desired gloss for solving above-mentioned problem.
Summary of the invention
The present invention reaches above-mentioned purpose by the formation of following announcement.
Glof club head of the present invention is after utilizing forging or casting to be formed, at first implement to utilize sand paper grinding etc. to carry out the basal plane milled processed operation that basal plane grinds, then this glof club head is implemented to utilize the cartridge type milled processed operation of cartridge type milled processed.Aforementioned cartridge type milled processed operation includes wet type cartridge type milled processed and dry type cartridge type milled processed.Grind certain hour to implementing the dry type cartridge type again behind the rod head noumenon implementation wet type cartridge type grinding earlier certain hour.That is glof club head of the present invention is characterised in that: particularly form by implement dry type cartridge type milled processed again after implementing wet type cartridge type milled processed.The glof club head of the metal surface with shaping attractive in appearance can be provided by combination wet type cartridge type milled processed and dry type cartridge type milled processed thus.
Glof club head of the present invention is realized by implementing following concrete operation.
At first, use the metal of soft iron, titanium, stainless steel etc. to form the rod head noumenon that constitutes glof club head by casting or forging.
Then aforementioned rod head noumenon being implemented basal plane handles.This basal plane is handled in order to make cartridge type milled processed described later effective, so in the elder generation of aforementioned cartridge type milled processed the metal surface of rod head noumenon is put in order.The metal surface of this rod head noumenon is a matsurface when casting or the aforementioned rod head noumenon of forging formation, and is formed with burr etc.This basal plane is handled to grind by all enforcement sand paper to the metal surface of rod head noumenon and is realized.This sand paper grinds and for example can use numbering #40 to the grinding sand paper implementation of numbering #600.
Then to implementing glof club head combination enforcement wet type cartridge type milled processed and the dry type cartridge type milled processed that aforementioned basal plane is handled.Again, these cartridge type milled processed can be made up according to the flow chart of Fig. 2, specifically can consider various combinations as shown in Figure 3.
At this, among the present invention, so-called " cartridge type grinding " is to become glof club head and the medium (grinding stone) that grinds object to dropping in the tube, stirred by the content that aforementioned cylindrical shell revolution or vibration etc. will be dropped in the aforementioned cylindrical shell, thus the metal surface of grinding aforementioned glof club head.Among the present invention, particularly in " wet type cartridge type milled processed ", remove above-mentioned input beyond the region of objective existence and also drop into and grind material and water is ground.
Can be by carrying out this kind " cartridge type grinding " with the surface dressing of glof club head, this produces gloss.This cartridge type milled processed comprises the cartridge type milled processed that flows, vibration cartridge type milled processed, rotation drum type milled processed or centrifugal cartridge type milled processed etc.
About this cartridge type milled processed wet type cartridge type milled processed is described at first.This wet type cartridge type milled processed makes the grinding marks digestion on the metal surface that is formed at glof club head when carrying out aforesaid basal plane milled processed, and the metal surface of this glof club head is shaped to level and smooth shape.This wet type cartridge type milled processed belongs to step 1 to 4 in the flow chart of Fig. 2.Comply with this flow chart, the wet type cartridge type milled processed combination among the present invention utilizes the milled processed and the milled processed of utilizing centrifugal cartridge type device of vibration cartridge type device, perhaps, from then on selects a use in the two and also can.
In this wet type cartridge type is ground, as above-mentioned, in cylindrical shell, drop into glof club head and medium and water, can drop into aqueous grinding material as required, carry out milled processed.Employed medium can use " the plastic cement medium " that be made of mylar and silicon material or with aluminium oxide (Al in this wet type cartridge type milled processed
2O
3) be principal component " alumina series medium " etc., specifically can use the following medium that discloses.
That is so-called plastic cement medium refers to mylar 35% and silicon (SiO among the present invention
2) the 65% mixed polymerization body that is constituted (hereinafter referred to as " medium 1 ").This medium 1 can suitably be used to vibrate the cartridge type grinding or centrifugal cartridge type is ground.
On the other hand, so-called alumina series medium refers to as described above like that with aluminium oxide (Al
2O
3) be the medium of principal component.Among the present invention, can use the alumina series medium (hereinafter referred to as medium 2 to 4) of three kinds shown below.
Medium 2 is by aluminium oxide (Al
2O
3) 93.4%, silica (SiO
2) 5.2%, calcium oxide (CaO), magnesia (MgO) 1.1%, sodium oxide molybdena (Na
2O), potassium oxide (K
2O) 0.2% and titanium oxide (TiO
2) 0.1% medium that is constituted.It is more suitable that this medium 2 is used in when flowing the cartridge type grinding.
Medium 3 is by aluminium oxide (Al
2O
3) 51%, silica (SiO
2) 44%, sodium oxide molybdena (Na
2O) 2.0%, iron oxide (Fe
2O
3) 1.0%, potassium oxide (K
2O) 1.0% and titanium oxide (TiO
2) 1.0% medium that is constituted.It is more suitable when this medium 3 is used in the grinding of vibration cartridge type.
Medium 4 is by aluminium oxide (Al
2O
3) 21.4%, silica (SiO
2) 74.0%, potassium oxide (K
2O) 3.0%, calcium oxide (CaO) 1.0% and iron oxide (Fe
2O
3) 0.6% medium that is constituted, more suitable when this medium 4 is used in the grinding of vibration cartridge type.
In the aforementioned wet type cartridge type milled processed of the present invention, can use following three kinds of abrasives (hereinafter referred to as " abrasive 1 to 3 ") again.At first, can use composition to include the abrasive 1 of inorganic sodium, alkyl phenolic type ionic surfactant, fatty acid anion plant promoting agent, vegetalitas sulfonated oil sodium salt and water.This abrasive 1 is specially adapted to centrifugal cartridge type and grinds.Then can use and have polyester and aluminium oxide abrasive 2 for its composition.This abrasive 2 is specially adapted to centrifugal cartridge type and grinds.Also can use composition to include the abrasive 3 of higher fatty acid salt, borate, interfacial agent, silicate and wood powder.This abrasive 3 is specially adapted to vibrate cartridge type and grinds.Above-mentioned each abrasive is together dropped into the metal surface that is used to grind glof club head in the cylindrical shell with aforementioned medium in wet type cartridge type milled processed.
On the other hand, the dry type cartridge type handle will through the metal surface of the glof club head of aforementioned wet type cartridge type milled processed grind put in order the more careful or implementation forming lapping of more aforementioned wet type cartridge type milled processed.This dry type cartridge type milled processed is equivalent to step 5 to 10 in the flow chart of Fig. 2.Shown in the flow chart, dry type cartridge type milled processed makes up or selects one and carries out aforementioned " rough lapping processing " and " forming lapping processing " according to this, and perhaps mixing is carried out the medium that is used for aforementioned each milled processed and implemented " processing of dry type mixed grinding ".
Among the present invention, it is preferable that dry type cartridge type milled processed particularly adopts centrifugal cylindrical grinding device, can be divided into three kinds of forms of " dry type rough lapping processing ", " dry pressing milled processed " and " processing of dry type mixed grinding " according to the kind that drops into the medium in this centrifugal cylindrical grinding device.Below describe respectively.
At first, " dry type rough lapping processing " will through the metal surface of the glof club head of aforementioned wet type cartridge type milled processed grind be organized into more careful than aforementioned wet type cartridge type milled processed.Can use two kinds of resin media shown below (hereinafter referred to as " medium 5 to 6 ") as the medium that is used in this " dry type rough lapping processing ".At first, so-called medium 5 is to be that minuteness particle or carborundum are the article that hardening of resin constituted of usefulness phenolic resins, nylon resin, urea resin, melamin resin or polyamide etc. such as minuteness particle with alumina series minuteness particle, titanium, forms the granularity of #60～#400 degree.Follow so-called medium 6 and be meant the formed medium of alumina balls that aforementioned medium 5 its granularities of adding is formed #100～#400 degree.
Secondly, the metal surface of " dry pressing milled processed " glof club head that will handle through aforementioned wet type cartridge type milled processed or dry type rough lapping is ground more carefully and make its generation gloss than aforementioned milled processed.Can use following two kinds to plant physical property medium (hereinafter referred to as " medium 7 to 8 ") as the medium that is used in this " dry pressing milled processed ".At first, medium 7 is to pulverous English walnut shell (mother metal: add the grinding material of aluminium oxide, chromium oxide or iron oxide etc. and the coating agent of grease system and form English walnut) strongly.On the other hand, medium 8 is to pulverous corn nuclear (mother metal: corn) add the grinding material of aluminium oxide, chromium oxide or iron oxide etc. and the article that coating agent became of grease system strongly.
In addition, " processing of dry type mixed grinding " above-mentioned to implement simultaneously " dry type rough lapping processing " is its purpose with " dry pressing milled processed ".This " processing of dry type mixed grinding " employed medium can use the mixture of above-mentioned medium 5 and medium 6 or medium 7 and medium 8.
In this dry type cartridge type milled processed, particularly use centrifugal cartridge type device preferable, be defined in this especially, also can use other lapping devices of vibration cartridge type device etc. but have more than.
In addition, about the lapping mode of cartridge type milled processed according to all modes shown in the table that can include Fig. 3 shown in the flow chart of Fig. 2.That is the present invention is by constituting implementing dry type cartridge type milled processed again after the glof club head enforcement wet type cartridge type milled processed.Therefore, according to the present invention, at first given size is cut or be ground in the metal surface of glof club head by implementing wet type cartridge type milled processed.By implement dry type cartridge type milled processed carry out the forming lapping etc. of the metal surface of aforementioned glof club head thereafter.Therefore can easily implement the surface treatment of glof club head.
In addition, because of implementing the cartridge type milled processed,, can continue stable grinding well among the present invention so the metal surface of glof club head can be ground with average grinding pressure.Again, embodiment all grinding conditions formability of variable milled processed then of implementing the granularity of medium of time of aforementioned wet type cartridge type milled processed and dry type cartridge type milled processed and use or hardness or input amount or the like by change like that as described later.That is then can provide glof club head repeatedly if set certain grinding condition with desired surface state according to the present invention.
On the other hand, glof club head of the present invention is preferably in that assembling is the different formed dissimilar metal parts of metal by the metal that forms with aforementioned rod head noumenon on any part on the rod head noumenon.That is, when being changed, the proportion of the part of glof club head can adjust the weight balancing of this glof club head.
These dissimilar metal parts form tabular or block with the metal different with aforementioned rod head noumenon proportion of wolfram steel or titanium or beallon or brass etc. and are embedded in certain position of aforementioned rod head noumenon.Can enumerate " setting ", " being pressed into ", " welding ", " welding " etc. as the mode that this kind dissimilar metal parts is embedded in rod head noumenon.
Again, the shape of these dissimilar metal parts has more than and is defined in above-mentioned tabularly or block, and it can form all shapes such as literal, figure or style and above-mentioned cartridge type milled processed forms the fluctuating shape or the subsidence shape also can by implementing after being embedded in rod head noumenon.Thus, these dissimilar metal parts also can be used in the purpose that constitutes good appearance intention except that the purpose of the weight balancing of adjusting glof club head.
Perhaps, making the different metal of hardness or abrasion performance make part on the surface of glof club head exposes and constitutes glof club head and also can.This kind formation can improve the batting ability of glof club head or thereby the durability of raising glof club head can constitute good appearance intention by making.
When the surface treatment of carrying out by the glof club head that these composites constituted, also implement aforesaid basal plane and handle and the cartridge type milled processed.That is, the rod head noumenon of burying the dissimilar metal parts underground is at first implemented the basal plane processing by implementing the sand paper grinding.This sand paper milled processed is effectively to implement for the cartridge type milled processed that makes the back operation, the whole metal surface of grinding aforementioned glof club head with the grinding sand paper of numbering #40～#60.
Above-mentioned wet type cartridge type milled processed and dry type cartridge type milled processed had been implemented through the glof club head that aforementioned basal plane is handled.At first, wet type cartridge type milled processed is formed at the grinding marks of the metal surface of rod head noumenon and dissimilar metal parts and is eliminated in the time of will carrying out aforementioned basal plane milled processed, and puts in order the metal surface of this glof club head more level and smooth.In addition, about the detailed situation of this wet type cartridge type milled processed at preceding detailed description, so omit its narration at this.
On the other hand, dry type cartridge type milled processed will be ground through the metal surface of the glof club head of above-mentioned wet type cartridge type milled processed and be put in order more carefully or carry out forming lapping than aforementioned wet type cartridge type milled processed.In addition, before also being described in about the details of this dry type cartridge type milled processed, so omit its narration at this.
, the partially-formed one-tenth of boundary of each metal surface on the metal of the aforementioned composite of formation can be discerned clearly by after above-mentioned each the cartridge type milled processed of the formed glof club head enforcement of composite for above-mentioned.That is, constitute in each parts of aforementioned composite, one side's parts and the opposing party's parts are formed with the metal of different hardness respectively, and implement aforementioned milled processed and can make the formability of the gloss of metal surface of aforementioned each metal and texture etc. produce difference by making up these parts.That is, when glof club head of the present invention is formed by rod head noumenon and dissimilar metal and makes it have difference of hardness, utilize each different hardness to make the abrasive forming of metal surface produce difference.In specific words, rod head noumenon is formed with stainless steel, the dissimilar metal parts are formed with wolfram steel, the metal surface of the rod head noumenon part that forms with stainless steel when constituting glof club head by making up these parts will produce strong gloss, on the other hand, the metal surface of the part of the dissimilar metal parts that form with wolfram steel then produces dim a little gloss.
In addition, to above-mentioned when implementing various cartridge type milled processed by the formed glof club head of composite employed medium use the article of following explanation preferable.That is the medium of hardness that use can be cut the high rigidity metal that respectively constitutes metal by the glof club head that composite constituted in the cartridge type milled processed that preceding operation is implemented or granularity is preferable.The medium of the hardness of the degree of use machinable soft metal or granularity is preferable in the cartridge type milled processed that the back operation is implemented on the other hand.
Glof club head of the present invention is because of making it finish surface treatment by the cartridge type milled processed is implemented in its metal surface, so the gloss of each metal surface of rod head noumenon and dissimilar metal parts can be shaped as delicate difference, but intention goes out the brainchild that the boundary of rod head noumenon and dissimilar metal parts can clearly be discerned.
Therefore, according to the present invention can easily reach positively provide in the past the glof club head with good intention that can't obtain.
Have again, these except that above-mentioned " combination of stainless steel and wolfram steel ", also can create " combination of titanium alloy and wolfram steel ", " combination of soft iron and wolfram steel ", " combination of soft iron and titanium alloy " or the like by the combination of rod head noumenon and the formed metal of dissimilar metal parts.
Description of drawings
Fig. 1 is the schematic diagram of the outward appearance of glof club head of the present invention;
Fig. 2 is a flow chart of glof club head being implemented each cartridge type milled processed of the present invention;
Fig. 3 is a schematic diagram of glof club head of the present invention being implemented the form of each milled processed.
The specific embodiment
Most preferred embodiment of the present invention below is described with reference to the accompanying drawings.
Fig. 1 is the figure of the head that the glof club head 1 of present embodiment formed the iron club head and use.The glof club head 1 of this embodiment is constituted the position that is equivalent to " bottom " that the formed dissimilar metal parts 3 of wolfram steel are embedded in the formed rod head noumenon 2 of stainless steel.The present invention system implements the basal plane milled processed to this glof club head 1, implements " wet type cartridge type milled processed " thereafter as each lapping mode as shown in Figure 3 and becomes with " dry type cartridge type milled processed ".
The formation of glof club head 1 and " the basal plane processing " that this glof club head 1 is implemented at first are described.
The glof club head 1 of present embodiment is made of rod head noumenon 2 and dissimilar metal parts 3 as described above like that.Aforementioned rod head noumenon 2 is that mother metal passes through casting and forms with the stainless steel.On the other hand, aforementioned dissimilar metal parts 3 are that mother metal forms with wolfram steel.Again, make up these parts and constitute glof club head 1, the basal plane that all enforcement of the metal surface of this glof club head 1 utilizes sand paper to grind is handled.
This basal plane is handled the grinding sand paper that at first uses numbering #60 all enforcement of the metal surface 4 of aforementioned glof club head 1 is ground.Then the grinding sand paper with numbering #180 grinds all enforcement of the metal surface 4 of aforementioned glof club head 1, and the grinding sand paper with numbering #400 grinds then.
After implementing aforesaid " basal plane milled processed ", implement " wet type cartridge type milled processed " and reach " dry type cartridge type milled processed ".Among the present invention, can implement the arbitrary milled processed of the A to J in the lapping mode shown in Figure 3.The situation of these lapping modes below is described respectively.
Lapping mode A in above-mentioned each lapping mode at first is described.This lapping mode A implements wet type cartridge type milled processed to the glof club head 1 of implementing the basal plane milled processed by two stages, implements dry type cartridge type milled processed by two stages simultaneously.The also dry grinding of implementation step 5,6,7,8 processing is simultaneously handled in the wet lapping of this lapping mode A implementation step 1,2,3,4 in flow chart shown in Figure 2.
That is wet type cartridge type milled processed is at first implemented four hours milled processed with vibration cartridge type device, implements one hour milled processed thereafter with centrifugal cylindrical grinding device.Working medium 1 and abrasive material 3 in the milled processed of aforementioned vibration cylindrical grinding device, on the other hand, working medium 1, abrasive material 1 and abrasive material 2 in the aforementioned milled processed of utilizing centrifugal cylindrical grinding device.
Implementing to implement dry type cartridge type milled processed after these wet type cartridge types are ground.This dry type cartridge type milled processed will utilize the milled processed of centrifugal cylindrical grinding device to be divided into for two stages, implement respectively two hours.That is " rough lapping " at first carried out two hours with centrifugal cylindrical grinding device carries out two hours " forming lapping " with centrifugal cylindrical grinding device thereafter.In these dry grindings are handled, " rough lapping " working medium 5 will make it not clear clear by the grinding marks cancellation that aforementioned wet lapping processing is formed at the metal surface 4 of glof club head 1.On the other hand, working medium 7 in " forming lapping ", make the metal surface 4 of aforementioned glof club head 1 produce gloss.
Lapping mode B then is described.Glof club head 1 two stage wet type cartridge type milled processed of enforcement and the dry type cartridge type milled processed that this lapping mode B handled implementing basal plane.The wet lapping of this lapping mode B implementation step 1,2,3,4 in flow chart shown in Figure 2 is handled, and the dry grinding of implementation step 5,6,7 is handled simultaneously.
That is wet type cartridge type milled processed is at first implemented the milled processed of four hours utilization vibration cartridge type device, implements one hour the milled processed of utilizing centrifugal cylindrical grinding device then.Working medium 1 and abrasive material 3 in the milled processed of aforementioned utilization vibration cylindrical grinding device, on the other hand, working medium 1, abrasive material 1 and abrasive material 2 in utilizing the milled processed of aforementioned centrifugal cylindrical grinding device.
Implementing to implement dry type cartridge type milled processed after these wet type cartridge types are ground.This dry type cartridge type milled processed is implemented two hours the milled processed of utilizing centrifugal cylindrical grinding device.This dry grinding is handled working medium 5 and is utilized centrifugal cylindrical grinding device to implement.
Lapping mode C is described.This lapping mode C implements two stage wet type cartridge type milled processed and dry type cartridge type milled processed to the glof club head 1 of implementing the basal plane milled processed.The wet lapping of this lapping mode C implementation step 1,2,3,4 in the flow chart of Fig. 2 is handled and the dry grinding of implementation step 5,9,10 is handled.
That is the milled processed of wet type cartridge type milled processed four hours utilization of enforcement earlier vibration cartridge type device, implement one hour the milled processed of utilizing centrifugal cylindrical grinding device then.Working medium 1 and abrasive material 3 in the milled processed of aforementioned utilization vibration cylindrical grinding device, on the other hand, working medium 1, abrasive material 1 and abrasive material 2 in the aforementioned milled processed of utilizing centrifugal cylindrical grinding device.
Implementing to implement dry type cartridge type milled processed after these wet type cartridge types are ground.This dry type cartridge type milled processed is implemented two hours the milled processed of utilizing centrifugal cylindrical grinding device.In this dry grinding is handled, mix working medium 5 and medium 7, implement by centrifugal cylindrical grinding device.Thus, can shorten the time of implementing dry type cartridge type milled processed by mixing working medium 5 and medium 7.
Lapping mode D is described.This lapping mode D implements wet type cartridge type milled processed and dry type cartridge type milled processed to the glof club head 1 of implementing the basal plane milled processed.The wet lapping of this lapping mode D implementation step 1,2,3 in flow chart shown in Figure 2 is handled and the dry grinding of implementation step 5,9,10 is handled.
That is at first, wet type cartridge type milled processed is implemented the milled processed of four hours utilization vibration cartridge type device earlier.This utilizes the milled processed working medium 1 and the abrasive material 3 of vibration cylindrical grinding device.Implementing to implement dry type cartridge type milled processed after this wet type cartridge type is ground.Aforementioned dry type cartridge type milled processed is the milled processed of implementing two hours of utilizing centrifugal cylindrical grinding device.It is to mix working medium 5 and medium 7 that this dry grinding is handled, and implements by centrifugal cylindrical grinding device.Can shorten the time of implementing dry type cartridge type milled processed by mixing working medium 5 with medium 7 thus.
Lapping mode E is described.This lapping mode E implements wet type cartridge type milled processed and dry type cartridge type milled processed to the glof club head 1 of implementing the basal plane milled processed.The also dry grinding of implementation step 5,6,7 processing is simultaneously handled in the wet lapping of this kind lapping mode E implementation step 1,2,3 in flow chart shown in Figure 2.
That is wet type cartridge type milled processed is at first implemented the milled processed of four hours utilization vibration cartridge type device.This utilizes the milled processed working medium 1 and abrasive material 3 of vibration cylindrical grinding device.After implementing this wet type cartridge type milled processed, implement dry type cartridge type milled processed.This dry type cartridge type milled processed is implemented two hours the milled processed of utilizing centrifugal cylindrical grinding device.Working medium 5 in this dry grinding is handled is implemented by centrifugal cylindrical grinding device.So working medium 5 and dry-type centrifugal cylindrical grinding device are implemented the state that " rough lapping " can be processed into metal surface 4 shapings of glof club head 1 elimination gloss.
Lapping mode F is described.This lapping mode F is implementing to divide after wet lapping is handled two classes to implement dry type cartridge type milled processed to the glof club head 1 of implementing the basal plane milled processed.The wet lapping of this lapping mode F implementation step 1,2,3 in flow chart shown in Figure 2 is handled and the dry grinding of implementation step 5,6,7,8 is handled.
That is wet type cartridge type milled processed is to implement the milled processed of four hours utilization vibration cylindrical grinding device.This utilizes the milled processed working medium 1 and the abrasive material 3 of vibration cylindrical grinding device.
State the wet type cartridge type on the implementation and grind back enforcement dry type cartridge type milled processed.This dry type cartridge type milled processed is that the milled processed that will utilize centrifugal cylindrical grinding device is divided into two classes, implements respectively two hours.That is, at first carry out two hours " rough lapping " with centrifugal cylindrical grinding device, carry out two hours " forming lapping " thereafter with centrifugal cylindrical grinding device.In this dry grinding was handled, " rough lapping " utilized medium 5, handled the grinding marks that is produced on the metal surface 4 of cancellation glof club head 1 by aforementioned wet lapping, can make grinding marks not clear clear.On the other hand, " forming lapping " working medium 7 makes the metal surface 4 of aforementioned glof club head 1 produce gloss.
Lapping mode G is described.This lapping mode G implements wet type cartridge type milled processed and dry type cartridge type milled processed to the glof club head 1 of implementing the basal plane milled processed.The also dry grinding of implementation step 5,6,7 processing is simultaneously handled in the wet lapping of this lapping mode G implementation step 1,4 in flow chart shown in Figure 2.
That is at first, wet type cartridge type milled processed is implemented one hour the milled processed of utilizing centrifugal cartridge type device.The milled processed working medium 1 of this centrifugal cylindrical grinding device.Implementing to implement dry type cartridge type milled processed after this wet type cartridge type is ground.This dry type cartridge type milled processed is the milled processed of implementing two hours of utilizing centrifugal cylindrical grinding device.This dry grinding is handled working medium 5, implements by centrifugal cylindrical grinding device.So working medium 5 and dry-type centrifugal cylindrical grinding device are implemented the state that " rough lapping " can be processed into metal surface 4 shapings of glof club head 1 elimination gloss.
Lapping mode H is described.This lapping mode H implements wet type cartridge type milled processed and dry type cartridge type milled processed to the glof club head 1 of implementing the basal plane milled processed.The wet lapping of this lapping mode H implementation step 1,4 in flow chart shown in Figure 2 is handled and the dry grinding of implementation step 5,9,8 is handled.
That is at first, wet type cartridge type milled processed is implemented one hour the milled processed of utilizing centrifugal cartridge type device.Utilize working medium 1 in the milled processed of centrifugal cylindrical grinding device at this.Implementing to implement dry type cartridge type milled processed after this wet type cartridge type is ground.This dry type cartridge type milled processed is the milled processed of implementing two hours of utilizing centrifugal cylindrical grinding device.In this dry grinding is handled, be to use medium 7, implement by centrifugal cylindrical grinding device.So working medium 7 is carried out the metal surface 4 generation gloss that " forming lapping " can make glof club head 1 with the dry-type centrifugal cylindrical grinding device.
Lapping mode I is described.This lapping mode I implements wet type cartridge type milled processed to the glof club head 1 of implementing the basal plane milled processed, divides two classes to implement dry type cartridge type milled processed then.The wet lapping of this lapping mode I implementation step 1,4 in flow chart shown in Figure 2 is handled and the dry grinding of implementation step 5,6,7,8 is handled.
That is wet type cartridge type milled processed is the milled processed of implementing a hour of utilizing centrifugal cylindrical grinding device.This utilizes the milled processed working medium 1 and the abrasive material 3 of centrifugal cylindrical grinding device.
State the wet type cartridge type on the implementation and grind back enforcement dry type cartridge type milled processed.This dry type cartridge type milled processed will utilize the milled processed of centrifugal cylindrical grinding device to be divided into for two stages, implement respectively two hours.That is at first carry out two hours " rough lapping " with centrifugal cylindrical grinding device, carry out two hours " forming lapping " thereafter with centrifugal cylindrical grinding device.During these dry grindings were handled, " rough lapping " utilized medium 5, handled the grinding marks that is produced by eliminating because of aforementioned wet lapping on the metal surface 4 of glof club head 1, can make it not clear clear.On the other hand, working medium 7 in " forming lapping ", can make the metal surface 4 of aforementioned glof club head 1 produce gloss.
Lapping mode J is described.This lapping mode J implements wet type cartridge type milled processed and dry type cartridge type milled processed to the glof club head 1 of implementing the basal plane milled processed.The wet lapping of this lapping mode J implementation step 1,4 in flow chart shown in Figure 2 is handled and the dry grinding of implementation step 5,9,10 is handled.
That is at first, wet type cartridge type milled processed is the milled processed of implementing a hour of utilizing centrifugal cartridge type device.This utilizes the milled processed working medium 1 and the abrasive material 3 of centrifugal cylindrical grinding device.Implementing to implement dry type cartridge type milled processed after this centrifugal cartridge type is ground.This dry type cartridge type milled processed is the milled processed of implementing two hours of utilizing centrifugal cylindrical grinding device.This dry grinding is handled and is mixed working medium 5 and medium 7, and utilizes centrifugal cylindrical grinding device to implement.So can shorten the enforcement time of dry type cartridge type milled processed by mixing working medium 5 and medium 7.
Implemented the glof club head 1 of the milled processed of above-mentioned each lapping mode, implement the result of wet type cartridge type milled processed and dry type cartridge type milled processed rod head noumenon 2 being buried underground glof club head 1 combination that dissimilar metal parts 3 are constituted, make the different gloss of metal surface 4 generations of metal surface 4 and other parts of the part of burying dissimilar metal parts 3 underground of this glof club head 1.Particularly, form rod head noumenon 2 and form dissimilar metal parts 3, when the glof club head 1 that these parts combinations are become is implemented the milled processed of lapping mode A, can reach following formability with wolfram steel with stainless steel.That is the metal surface 4 of rod head noumenon 2 parts that form with stainless steel will be sent strong gloss and be produced dim slightly gloss with the metal surface 4 of formed dissimilar metal parts 3 parts of wolfram steel.
The glof club head 1 of present embodiment forms surface treatment formation thing by the cartridge type milled processed is implemented in its metal surface 4, so can make rod head noumenon 2 and dissimilar metal parts 3 metal surface 4 separately produce delicate gloss difference, but intention goes out the creation that the boundary of rod head noumenon 2 and dissimilar metal parts 3 can clearly be discerned.
Again, the glof club head 1 of iron has been described in the present embodiment, has been limited to this embodiment but have more than, also applicable as the bar head that other golf of aluminum medal wood and push rod etc. are used.
Again, the iron bar head of the dissimilar metal that compound proportion is different has been described in the present embodiment, be limited to this embodiment but have more than, for example the bar head used of the iron club head that constitutes with single metal or aluminum medal wood and push rod etc. other golf of being representative is also applicable.
Claims (8)
1. a glof club head is characterized in that: after implementing to utilize the rough lapping of wet type cartridge type milled processed, implement to utilize the forming lapping of dry type cartridge type milled processed again, form the metal surface of glof club head thus.
2. glof club head is characterized in that: carry out implementing wet type cartridge type milled processed eliminate gloss and grind after, implement dry type cartridge type milled processed again and carry out gloss and grind, form the metal surface of glof club head thus.
3. glof club head as claimed in claim 1 or 2 is characterized in that: described glof club head is that compound rod head noumenon becomes with the dissimilar metal parts, and described dissimilar metal parts are embedded on the part of described rod head noumenon.
4. glof club head as claimed in claim 3 is characterized in that: rod head noumenon and dissimilar metal parts are formed with the different metal of proportion respectively and by forming these parts are compound.
5. glof club head, constitute by multiple dissimilar metal parts, have local by the formed surface of unlike material, it is characterized in that: this glof club head is implemented wet type cartridge type milled processed and made most metal surfaces form the frosted shape, thereafter, this glof club head is implemented dry type cartridge type milled processed only make on a part of metal surface and produce gloss, form local surface with various luster.
6. glof club head, constituted and had local by multiple dissimilar metal parts by the formed surface of unlike material, it is characterized in that: implement dry type cartridge type milled processed after wet type cartridge type milled processed, the gloss that forms the metal surface has the change type glof club head of variation.
7. the surface treatment method of a glof club head, have a plurality of cartridge type milled processed operations, it is characterized in that having: as the wet type cartridge type milled processed operation of the preceding operation of carrying out rough lapping, with dry type cartridge type milled processed operation as the postprocessing working procedures of carrying out forming lapping.
8. the surface treatment method of a glof club head, it is the surface treatment method of the glof club head that become of compound dissimilar metal parts, it is characterized in that: after the dissimilar metal of glof club head surface being carried out rough lapping and making that the gloss on surface is whole and reduce or make the wet type cartridge type milled processed operation of its disappearance, carry out the difference of the grinding effect that utilizes described dissimilar metal surface again and make the dissimilar metal surface of glof club head produce the dry type cartridge type milled processed of different gloss.