CN1337441A - 工业冶金型焦 - Google Patents

工业冶金型焦 Download PDF

Info

Publication number
CN1337441A
CN1337441A CN 01127375 CN01127375A CN1337441A CN 1337441 A CN1337441 A CN 1337441A CN 01127375 CN01127375 CN 01127375 CN 01127375 A CN01127375 A CN 01127375A CN 1337441 A CN1337441 A CN 1337441A
Authority
CN
China
Prior art keywords
coal
parts
portions
water
consumption
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 01127375
Other languages
English (en)
Other versions
CN1180054C (zh
Inventor
李志远
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB011273755A priority Critical patent/CN1180054C/zh
Publication of CN1337441A publication Critical patent/CN1337441A/zh
Application granted granted Critical
Publication of CN1180054C publication Critical patent/CN1180054C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明属于煤炭加工技术领域,具体涉及一种使用粘结性煤、弱粘煤、肥煤、气肥煤等生产的工业冶金型焦,由下述重量配比的原料制成(用量为质量份),煤:100份,粘合剂:腐殖酸盐(粉状)2－5份,防粘剂:4－9份;其中,防粘剂由下述重量配比的原料制成(用量为质量份),玉米淀粉3－9份与100－200份水的混合物,氢氧化钠4－12份,聚醋酸乙烯酯与水的混合液1∶5,2－8份,淀粉浆。本发明与现有产品比较具有,设备封闭,结焦时间短;无烟尘排入,能有效的控制环境污染;块焦率高,生产成本低;能百分之百提取焦油和提出大量煤气;厂房占地面积小,生产实现连续性;型焦不结块、不变形,达到了国家冶金型焦的质量标准。

Description

工业冶金型焦
技术领域
本发明属于煤炭加工技术领域，具体涉及一种使用粘结性煤、弱粘煤、肥煤、气肥煤等生产的工业冶金型焦。
背景技术
在现有技术中，工业冶金型焦大多使用无烟煤，而且粘结剂使用煤沥青和煤焦油，生产出的型焦球无报导孔，透气性差，故障多，在焦化炉中受热易粘结成块，导致型焦不能正常出炉，直接影响型焦的生产和推广使用。
发明内容
本发明解决了粘结性煤生产型焦的技术问，提供了一种粘结性良好，使型焦在焦化炉中受热下结块，使型球成焦后仍保持原形状和各自分离的状态的工业冶金型焦。
本发明是采用下列方法实现的，工业冶金型焦，由下述重量配比的原料制成(用量为质量份)，
煤：100份
粘合剂：腐殖酸盐(粉状)2-5份，
防粘剂：4-9份；
其中，防粘剂由下述重量配比的原料制成(用量为质量份)，
a、玉米淀粉3-9份与100-200份水的混合物，
b、氢氧化钠4-12份，
c、聚醋酸乙烯脂与水的混合液1∶5，2-8份，
d、淀粉浆。
由此配方制成的型焦不结块、不变形，达到了国家冶金焦的质量标准。
本发明由下述重量配比的原料制成(用量为质量份)，
煤：100份
粘合剂：腐殖酸盐(粉状)5份，
防粘剂：5份，
其中，防粘剂由下述重量配比的原料制成(用量为质量份)，
a、玉米淀粉6份与180份水的混合物，
b、氢氧化钠9份，
c、聚醋酸乙烯脂与水的混合液1∶5，6份，
d、淀粉浆。
本发明所述的煤质为各种粘结性煤、弱粘煤、肥煤、气肥煤、瘦煤等。扩大了能源的使用范围。
本发明具有以下优点及效果，1、设备封闭，结焦时间短；2、无烟尘排入，能有效的控制环境污染；3、块焦率高，生产成本低；4、能百分之百提取焦油和提出大量煤气；5、厂房占地面积小，生产实现连续性；6、型焦机械强度高出室式焦炭很多。
具体实施方式
一、选取粘结性煤100份，粘合剂5份，防粘剂5份；首先制做防粘剂，防粘剂用下列方法配制而成，选取玉米淀粉6份与180份水的混合，加热至50-65℃，而后加入氢氧化钠9份与水的饱和溶液，搅拌使其熟化，再取玉米淀粉20-30份，加入定量水中搅拌，同时加热至25-30℃，制成淀粉浆，而后与熟化淀粉同时搅拌，最后将聚醋酸乙烯脂与水的混合液1∶5，6份，倒入上述淀粉浆中搅匀即可。
二、生产型焦的工艺流程
洗煤→干燥→粉碎→混捏→加入粘合剂→成型→干燥→防粘处理→焦化(提炼焦油、煤气)→冷却→成品。粘合剂采用腐殖酸盐3-9份。
将选取的粘结性煤经水洗后脱去灰分，然后进入干燥器中干燥，干燥后的精煤经粉碎后，加入配制好的粘合剂，添加量为5份，进行混捏、搅拌、干燥和防水处理。
防水处理后和料球进入外热式竖炉中焦化，当焦化炉中料球升温至320℃时，挥发物、焦油开始溢出，防粘剂开始分解，在隔绝空气情况下，形成一层透气性海绵状炭化层，使挥发物能够顺利溢出温度至440℃以上时，煤中胶质层溢出被防粘层阻挡，温度500℃时，胶质层固化。在上述升温状态中，由配套的设备提出全部的焦油和大量煤气。炉温升至1100-1200℃定时，焦化完成，型焦从炉底排出。

Claims (3)

1、一种工业冶金型焦，由下述重量配比的原料制成(用量为质量份)，
煤：100份
粘合剂：腐殖酸盐(粉状)2-5份，
防粘剂：4-9份；
其中，防粘剂由由下述重量配比的原料制成(用量为质量份)，
a、玉米淀粉3-9份与100-200份水的混合物，
b、氢氧化钠4-12份，
c、聚醋酸乙烯脂与水的混合液1∶5，2-8份，
d、淀粉浆。
2、根据权利要求1所述的工业冶金型焦，其特征在于由下述重量配比的原料制成(用量为质量份)，
煤：100份
粘合剂：腐殖酸盐(粉状)5份，
防粘剂：5份，
其中，防粘剂由下述重量配比的原料制成(用量为质量份)，
a、玉米淀粉6份与180份水的混合物，
b、氢氧化钠9份，
c、聚醋酸乙烯脂与水的混合液1∶5，6份，
d、淀粉浆。
3、根据利要求1所述的工业冶金型焦，其特征在于所述的煤质为各种肥煤、气肥煤、瘦煤等粘结性煤和弱粘煤。
CNB011273755A 2001-09-03 2001-09-03 工业冶金型焦 Expired - Fee Related CN1180054C (zh)