CN1318600A - Wall paint and its production process - Google Patents
Wall paint and its production process Download PDFInfo
- Publication number
- CN1318600A CN1318600A CN 00113386 CN00113386A CN1318600A CN 1318600 A CN1318600 A CN 1318600A CN 00113386 CN00113386 CN 00113386 CN 00113386 A CN00113386 A CN 00113386A CN 1318600 A CN1318600 A CN 1318600A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- solution
- tributyl phosphate
- limit edged
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The paint suitable for inner and outer wall is produced with the material including styrene-acrylic emulsion, No.2020 leveling agent, proplylene glycol, propanetriol, benzoic alcohol, calgon, methyl silicon oil, tributyl phosphate, mildew preventive, preservative, borax, ammonia water and water and through stirring, dissolving and other steps. It is waterproof, antifouling, low in cost and easy in application.
Description
The present invention relates to a kind of coating for wall surface and preparation method thereof.
Along with the fast development of building trade, the decoration of buildings is more and more attractive in appearance, practical.With regard to wall body decoration, exterior wall is based on furring brick, glass curtain wall, also has with coating to whitewash, interior wall is many based on stenciling coating, and wallpaper is also arranged.Generally speaking, utilization coatings decoration body of wall is not limited by the body of wall shape, and cost is lower, and job schedule is fast.But general coating for wall surface also has its defective, as the emulsion paint wall paint, main composition is the polymkeric substance of EVA or Vinyl Acetate Copolymer or ACRYLIC EMULSION and above-claimed cpd, their shortcoming is that waterproof, didirtresistance are poor, uncomfortable cooperation exterior coating in case pollute, is difficult to repair, and exposing to the weather drenches with rain, and very easily peels off, fades.
The object of the present invention is to provide a kind of antifouling water-repellancy strong, be fit to coating for wall surface of inside and outside body of wall decoration and preparation method thereof.
Technology contents mainly is: it is a kind of coating for wall surface of being made by the following weight proportion raw material: benzene emulsion 300-400 part, 2020 flow agent 5-12 parts, propylene glycol 5-10 part, glycerol 8-15 part, phenylcarbinol 10-35 part, Sodium hexametaphosphate 99 1-2 part, methyl-silicone oil 5-10 part, 1 part of tributyl phosphate, mould inhibitor 0.3-0.5 part, sanitas 0.3-0.5 part, borax 5-15 part, ammoniacal liquor transfer PH-8-10, mill base to add water 500-600 part according to required color.Coating preferred weight proportioning of the present invention is: 350 parts of benzene emulsions, 6 parts of 2020 flow agents, 10 parts of propylene glycol, 10 parts of glycerol, 30 parts of phenylcarbinols, 2 parts of Sodium hexametaphosphate 99s, 10 parts of methyl-silicone oils, 1 part of tributyl phosphate, 0.5 part of mould inhibitor, 0.5 part of sanitas, 10 parts of boraxs.The preparation method of coating of the present invention is: a. takes by weighing each raw material by formula rate; B. after borax being used 50 parts of stirring and dissolving of boiling water, join in the remaining water; C. 2020 flow agents, propylene glycol, glycerol, phenylcarbinol, Sodium hexametaphosphate 99, methyl-silicone oil, tributyl phosphate, mould inhibitor, sanitas limit edged are stirred in the solution that is added to step b generation and go; D. benzene emulsion is added in the solution that the c step produces and go, stir; E. tributyl phosphate is joined in the solution that the d step produces and go, the limit edged stirs, and is advisable up to the foam of cancellation solution; F. ammoniacal liquor is joined in the solution of e step generation, the limit edged stirs, and tests its potential of hydrogen, is advisable with PH=9; G. the coating of above-mentioned steps generation is white transparence, makes colo(u)r coating as need, and mill base is added according to required color, and the limit edged stirs, and mixes promptly.
During use, in two kinds of situation, a kind of is the direct brushing on cement wall surface of this coating of will be furnished with mill base, another kind is originally as transparent liquid because of this coating that is unworthy of mill base, therefore generally be used for firmization metope or other common coating metope of having constructed, twice coating of brushing again on this metope forms a kind of transparent film.
The invention has the advantages that: 1. waterproof.Water can be condensed into the globule immediately and fall down on this metope, do not soak metope; 2. antifouling.Ink blok, dust, the greasy dirt metope of making dirty, available 0.5% washing powder scrub water is clean, and metope still maintains the original state, and keeps dry and comfortable.3. other latex wall paint price of market is hanged down 10--20 unit/kg relatively; 4. construction is easy, and employing is wiped, brushed, rolls constructional method and constructs.
Embodiment 1: choose raw material, take by weighing by prescription.350 parts of benzene emulsions, 6 parts of 2020 flow agents, 10 parts of propylene glycol, 10 parts of glycerol, 30 parts of phenylcarbinols, 2 parts of Sodium hexametaphosphate 99s, 10 parts of methyl-silicone oils, 1 part of tributyl phosphate, 0.5 part of mould inhibitor, 0.5 part of sanitas, 10 parts of boraxs, ammoniacal liquor are transferred PH=9, mill base adds according to required color, 570 parts in water.A during making, take by weighing each raw material by formula rate, b, with borax with 50 parts of stirring and dissolving of boiling water after, join in the remaining water; C, 2020 flow agents, propylene glycol, glycerol, phenylcarbinol, Sodium hexametaphosphate 99, methyl-silicone oil, tributyl phosphate, mould inhibitor, sanitas limit edged are stirred to be added in the solution that step b produces go; D, benzene emulsion joined in the solution that step c produces go, stir; E, tributyl phosphate joined in the solution that steps d produces go, the limit edged stirs, and is advisable up to the foam of cancellation solution; F, ammoniacal liquor is joined in the solution that step e produces, the limit edged stirs, and tests its potential of hydrogen, is advisable with PH=9.The coating that g, above-mentioned steps produce is white transparence, makes colo(u)r coating as need, and mill base is added according to required color, and the limit edged stirs, and mixes promptly.
Claims (3)
1. coating for wall surface, it is characterized in that: it is a kind of coating of being made by the following weight proportion raw material: benzene emulsion 300-400 part, 2020 flow agent 5-12 parts, propylene glycol 5-10 part, glycerol 8-15 part, phenylcarbinol 10-35 part, Sodium hexametaphosphate 99 1-2 part, methyl-silicone oil 5-10 part, 1 part of tributyl phosphate, mould inhibitor 0.3-0.5 part, sanitas 0.3-0.5, borax 5-15 part, ammoniacal liquor are transferred PH=8-10, mill base adds according to required color, water 500-600 part.
2. coating for wall surface according to claim 1, it is characterized in that: wherein the weight proportion of each raw material is: 350 parts of benzene emulsions, 6 parts of 2020 flow agents, 10 parts of propylene glycol, 10 parts of glycerol, 30 parts of phenylcarbinols, 2 parts of Sodium hexametaphosphate 99s, 10 parts of methyl-silicone oils, 1 part of tributyl phosphate, 0.5 part of mould inhibitor, 0.5 part of sanitas, 10 parts of boraxs, ammoniacal liquor transfer PH=9, mill base to add 570 parts in water according to required color.
3. according to the preparation method of the described coating of claim 1, it is characterized in that:
A. take by weighing each raw material by formula rate;
B. after borax being used 50 parts of stirring and dissolving of boiling water, join in the remaining water;
C. 2020 flow agents, propylene glycol, glycerol, phenylcarbinol, Sodium hexametaphosphate 99, methyl-silicone oil, tributyl phosphate, mould inhibitor, sanitas limit edged are stirred in the solution that is added to step b generation and go;
D. benzene emulsion is added in the solution that the c step produces and go, stir;
E. tributyl phosphate is joined in the solution that the d step produces and go, the limit edged stirs, and is advisable up to the foam of cancellation solution;
F. ammoniacal liquor is joined in the solution of e step generation, the limit edged stirs, and tests its potential of hydrogen, is advisable with PH=9;
G. the coating of above-mentioned steps generation is white transparence, makes colo(u)r coating as need, and mill base is added according to required color, and the limit edged stirs, and mixes promptly.