CN1306465A - Mold, electronic device, and method of mfg. electronic device - Google Patents
Mold, electronic device, and method of mfg. electronic device Download PDFInfo
- Publication number
- CN1306465A CN1306465A CN99807728A CN99807728A CN1306465A CN 1306465 A CN1306465 A CN 1306465A CN 99807728 A CN99807728 A CN 99807728A CN 99807728 A CN99807728 A CN 99807728A CN 1306465 A CN1306465 A CN 1306465A
- Authority
- CN
- China
- Prior art keywords
- pin parts
- metallic solution
- metal
- mould device
- mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a metal case (20) having regular perforations (21) for an electronic device, a metal mold (30) includes pins (36) provided on its cope (31) or drag (32). The pins (36) are arranged in such a manner that the center line connecting two adjacent pins is not perpendicular to the flow of molten metal that is introduced through a cavity (35) in the metal mold (30).
Description
The light metal system e-machine that the present invention relates to computer etc. is with the structure of housing and make manufacture method, the metal mould device of this e-machine with housing.
Light metal system e-machine housing, its material mainly are to adopt magnesium alloy recently.With die casting or thixotropy method with these Alloy Forming.Though the device construction of these forming processes has nothing in common with each other,, its molding condition all is melt and dissolved alloy to 580 degree to 750 degree, being expelled to slightly, 100 degree are shaped to the metal pattern of 350 degree is inner.
Fig. 1 represents the structure of existing e-machine with housing.This e-machine is with in the housing, from the metallic solution lead-in portion of metal mould device 1 is that cast gate 2 imports metallic solution (this figure, with with just be shaped after e-machine with the corresponding part explanation of the shape of housing), make it pass through runner 3, metallic solution is imported required metal pattern inside.The metallic solution that is imported into flows through whole chamber 4 and arrives exhaust outlet 5.This exhaust outlet 5 is connecting cup 6.Therefore, metallic solution makes air be discharged to the outside by this exhaust outlet 5 after importing from cast gate 2.Like this, can under the void-free state of enclosure interior, form housing.
In addition, this e-machine housing a plurality of hole portion 7 with the preset space length assortment, and the effect of these hole portions 7 is outside heat radiations, perhaps outwards amplifies as loudspeaker.
For the interval that makes hole portion 7 keeps evenly, as depicted in figs. 1 and 2, normally this hole portion 7 is designed to clathrate and arranges.
In order to form hole portion 7, in the prior art, be that the metal pattern formed products that is shaped by metal pattern 1 is carried out punching with such arrangement.Perhaps, as shown in Figure 7, in advance in chamber 4 inside of metal mould device 1, the outstanding pin parts 8 that form the clathrate arrangement import this chamber interior to metallic solution, and it are solidified in chamber interior.Like this, just formed the hole portion 7 that clathrate is arranged that is.
In order to prevent that foreign matter etc. from sneaking into enclosure interior, the interval of above-mentioned hole portion 7 is narrower usually.Therefore, the metal pattern formed products after metal mould device 1 inner taking-up, is implemented back processing with narrow interval, hole count is many more just to bother more, and cost is also high.
Therefore, when with narrow interval pin parts 8 being set in metal mould device 1 inside in advance, when contacting with chamber 4 internal faces owing to the metallic solution that is imported into metal pattern inside, sharply cooled off and solidified, so when with narrow interval a plurality of pin parts 8 being set, its flowability is bad.
That is, shown in the arrow among Fig. 2, metallic solution as the crow flies by pin parts 8 in the ranks, and is partly solidified at this, and metallic solution can not enter in the gap of respectively selling parts 89 that constitutes these row.
Therefore, metallic solution does not enter the part of 8 of pin parts, forms not filling position, like this, can not form the hole portion 7 of predetermined arrangement, produces big not filling position.
The summary of the invention summary
The present invention makes in view of the above problems, and its purpose is to provide a kind of metal pattern, and this metal pattern internal arrangement the pin parts that make the metallic solution good fluidity and provided and adopts manufacture method these pin parts, e-machine usefulness housing.
Metal mould device of the present invention; be used to form the e-machine housing that constitutes by metal material with preset space length hole portion; have from the 1st mould or the outstanding pin parts of the 2nd mould; it is characterized in that; above-mentioned pin parts dispose like this: link the center line of hithermost adjacent pin parts, be not orthogonal to metallic solution toward the interior direction that imports of metal mould device chamber.
The manufacture method of e-machine of the present invention, being shaped with metal mould device has the e-machine of housing, and this housing is made of the metal material with preset space length hole portion, it is characterized in that, has flow process and curing process; At flow process, metallic solution is imported above-mentioned metal mould device inside; At curing process, make the metallic solution curing that imports metal mould device inside at above-mentioned flow process; Above-mentioned metal mould device is the metal mould device of each record in the claim 1 to 4.
The accompanying drawing simple declaration
Fig. 1 is the stereogram of expression conventional example e-machine with hull shape.
Fig. 2 is the pin arrangement of parts of expression conventional example and the figure of metallic solution flow regime.
Fig. 3 is stereogram e-machine, portable computer structure of expression as one embodiment of the invention.
Fig. 4 is the figure of expression metal mould device inner pin arrangement of parts state, is illustrated in and metallic solution imports the vertical direction of direction, with the stagger state of half spacing of the arrangement of pin parts.
Fig. 5 is the figure of expression metal mould device inner pin arrangement of parts state, is illustrated in and metallic solution imports the parallel direction of direction, with the stagger state of half spacing of the arrangement of pin parts.
Fig. 6 is the figure that expression is the ordered state of staggered pin parts.
Fig. 7 is the cross-sectional side view of expression metal mould device structure.
Fig. 8 is the stereogram of expression e-machine with casing structure.
Fig. 9 is that expression makes the arrangement of the importing direction of metallic solution with respect to clathrate pin parts in the variation of the present invention, the figure of predetermined oblique angle state.
The optimal morphology that carries out an invention
Below, with reference to Fig. 3 to Fig. 8, one embodiment of the invention is described.
Fig. 3 is the outside drawing of portable computer 10 shapes of expression notebook computer etc.Among this figure, portable computer 10 has computer body 11 and the display 12 that is rotatably supported on this computer body 11.Computer body 11 has housing 13.This housing 13 for example is connected lower case 14 with screw and constitutes with upper body 15.But the joint construction of lower case 14 and upper body is not limited to this, also can engage with other structure.
In the following description, the housing with being applicable to portable computer 10 e-machines such as grade describes with housing 20 as e-machine.Below, illustrate with reference to Fig. 4 to Fig. 8.
For example, by e-machines such as the light metal system computer housing 20 that magnesium alloy forms, be formed with the hole portion 21 of a plurality of thin spaces.This hole portion 21 has the effect of cooling computer inside, perhaps has the effect as loudspeaker that amplifies to the outside.
This a plurality of hole portion 21 is by importing metallic solution metal mould device 30 inner formation.
Metallic solution is a magnesium alloy solution, but also can adopt other alloy solution, for example aluminium alloy solution.
In chamber 35 inside, at above-mentioned e-machine with forming hole portion 21 on the housing 20, with this e-machine with the corresponding part of the hole portion 21 of housing 20, be provided with pin parts 36.Pin parts 36 are in the inside of the chamber 35 of above-mentioned metal mould device 30, and its arrangement is arranged as following ordered state with respect to clathrate before.
As shown in Figure 4, suppose the pin parts 36 be arranged as clathrate the time, adjacent pin parts 36 be spaced apart a, in the arrangement of pin parts 36 of the present invention, be orthogonal to the metallic solution flow direction adjacent 2 the pin parts 36 row among, the row of square cotter parts 36 opens half spacing with respect to the misarrangement of another square cotter parts 36.
Therefore, the interval of adjacent pin parts 36 is a as shown in Figure 4 before, calculates according to three squares of theorems, and changing becomes b
Like this, the interval of pin parts enlarges than the pin parts space with the clathrate arrangement.
Thereupon, in the metallic solution amount of 36 circulations of these pin parts, increase when arranging than clathrate before.That is, metallic solution flows easily.
In addition, with the arrangement of above-mentioned pin parts 36 half spacing that staggers, and the flowing without any variation of metallic solution.Therefore, metallic solution can flow the pin parts that enlarged 36.
By arranging pin parts 36 in this wise, above-mentioned pin parts 36 become stagger mode and arrange.
But the arrangement of pin parts 36 is not limited to this.That is as shown in Figure 5, among row's (row at this moment is to be parallel to the metallic solution flow direction) of adjacent 2 pin parts 36, also can be that the row of square cotter parts 36 opens half spacing with respect to the misarrangement of another square cotter parts.
At this moment, the interval of adjacent pin parts 36 as shown in Figure 5, changes to b from before a similarly
。Therefore, the interval of adjacent pin parts 36 increases when arranging pin parts 36 than clathrate, and metallic solution flows easily.
As mentioned above, will sell stagger respectively half spacing ground of parts 36 and form staggered arrangement, but staggered arrangement is not limited thereto, various arrangements can be arranged.Promptly, basic arrangement is not a clathrate, but the shape that is rectangle, substantially arrange respectively from this pin parts 36 to be staggered with staggering half spacing at longitudinal direction or transverse direction, can form and have shown in Figure 6 staggered (among Fig. 6 with Fig. 4 different angles, in longitudinal direction half spacing that staggers, the result, the pin parts 36 of staggered arrangement become the clathrate of predetermined oblique angle with basic oblong-shaped).
At this moment, the the 1st and the 4th, the 2nd and the 4th, the 4th and the 6th ... Deng pin parts 36 the most adjacent.At this moment, owing to be staggered configuration, clearance portion 37 metallic solutions betwixt pass through easily.
At this moment, the arrangement of pin parts 36 is: connect near the center line of adjacent pin parts 36, be not orthogonal to the metallic solution flow direction, but become the oblique state with predetermined angular.Like this, compare during perpendicular to flow direction, can enlarge the gap of 36 of these pin parts, can prevent that it from stoping flowing of metallic solution, increases the flow of metallic solution with adjacent pin parts 36.
In addition, the arrangement of above-mentioned pin parts 36 is: get perpendicular or parallel adjacent 2 rows that sell parts 36 in the metallic solution flow direction, will sell the opposing party's misarrangement of parts 36 respectively and open half spacing.But the amount of movement that staggers of pin parts 36 is not limited to half spacing, and this amount of movement can be set at any value, as long as metallic solution can flow well in the position of 36 of pin parts.
Metallic solution is imported metal mould device 30 inside with this arrangement from cast gate 33, make this metallic solution diffusion, import chamber 35 inside from runner 34.At this moment, the importing in the past chamber 35 of metallic solution imports metallic solution diffusion back by runner 34, so, become concurrent flow in chamber 35 inside.In addition, the importing of this metallic solution is that the internal face ground that is parallel to chamber 35 imports.
At this moment, melt and dissolved magnesium alloy is for example applied pressure about 250t, carry out the injection moulding of e-machine, and carry out this importing with housing 20.
By such importing, the part 36 of the pin parts of above-mentioned arrangement can flow through metallic solution at large.That is, to shown in Figure 6, even the clearance portion 37 of 36 of adjacent pin parts, metallic solution also can enter as Fig. 4.
Like this, in the part that is provided with pin parts 36, can not produce and the filling position metallic solution is filled in the chamber 35, then, this metallic solution arrives exhaust outlet 38.
The effect of exhaust outlet 38 is to make the air of metal mould device 30 inside be discharged to the outside, is connecting cup 39 on this exhaust outlet 38.Like this, import the metallic solution in the metal mould device 30, while prevent to arrive cup 39 in the chamber 35 inner spaces that produce.
When importing metallic solutions toward chamber 35 is inner, the temperature of metal mould device 30 be about 100 degree to 350 degree, promptly 580 degree are to 750 degree to be lower than the temperature of melt and dissolved magnesium alloy, so this metallic solution contacts with metal mould device 30, temperature reduces immediately and solidifies.
As mentioned above, because metallic solution is exerted pressure, and sell the above-mentioned arrangement that is arranged as of parts 36, so metallic solution promptly arrives exhaust outlet 38 before it solidifies, metallic solution solidifies again then.
After metallic solution solidifies, open the engagement of patrix 31 and counterdie 32, release the metal pattern formed products with the pushing pin, form e-machine housing 20 as shown in Figure 8, this housing 20 has the hole portion 21 corresponding with the arrangement of pin parts 36.Like this, it is staggered that the arrangement of this hole portion 21 also is, and perhaps the interval of adjacent holes portion 21 enlarges.
But on same area, the formation number of hole portion 21 is constant substantially, the heat sinking function of hole portion 21 and as the sound amplification function of loudspeaker also without any problem.
According to the metal mould device 30 of this structure and e-machine manufacture method with housing 20, the arrangement of above-mentioned pin parts 36 is: import in the arrangement of adjacent 2 pin parts 36 of direction in metallic solution perpendicular or parallel, the arrangement of square cotter parts 36 is with respect to the arrangement of another square cotter parts 36 half spacing that slightly staggers.Therefore, can enlarge the interval of 36 of adjacent pin parts.
Like this, can make more metallic solution flow through the part of 36 of these pin parts, in addition, compare, metallic solution is entered between the pin parts 36 with the pin parts 36 that clathrate is arranged.
Therefore, even sell the clearance portion 37 of 36 of parts, metallic solution also can enter, and can prevent to produce not pack portion.
Therefore, do not have not pack portion, can make shaping good electron machine, improve yield rate with housing 20.
In addition, as mentioned above, pin parts 36, even be not another general plan with adjacent pin parts 36 staggered that half spacing forms of staggering, but during other staggered, be not orthogonal to the metallic solution flow direction owing to link the center line of adjacent pin parts 36, so, in this case, also than being the flow that can increase metallic solution when clathrate is arranged.
In addition, pin parts 36 are arranged to so staggered arrangement, compare when arranging with clathrate, the arrangement of adjacent pin parts 36 is not parallel to the metallic solution flow direction, like this, metallic solution is revolution in the clearance portion 37 of 36 of these pin parts easily, and metallic solution can enter well.Like this, can prevent to produce not filling position, prevent that e-machine is bad with the shaping of housing.
In addition, import the row of adjacent 2 pin parts 36 of direction perpendicular to metallic solution, another square cotter parts 36 slightly stagger with respect to square cotter parts 36 in the structure of half spacing, and pin parts 36 hinder the linearity of metallic solutions to flow, and can flow agley between pin parts 36.Therefore, metallic solution is well flowed between pin parts 36.
One embodiment of the present of invention have been described above, but the present invention can also have other various variation.The following describes it.
In the foregoing description, the arrangement of pin parts 36 has been described, be about half spacing is staggered in the side arrangement of adjacent pin parts 36 and form staggered, or other is staggered.But, in addition, as shown in Figure 9, also pin parts 36 can be arranged in clathrate, make the pin parts 36 of the importing direction of metallic solution, predetermined oblique angle with respect to this arrangement.
At this moment, metallic solution is passed among Fig. 9 between the pin parts 36 shown in the arrow.Like this, be arranged in clathrate,, metallic solution entered in the clearance portion 37 of 36 of these pin parts as long as the importing direction of metallic solution is tilted even will sell parts 36.
In addition, in the scope that does not change purport of the present invention, can do various distortion.
Claims (7)
1. metal mould device; be used to form and have e-machine housing preset space length hole portion, that constitute by metal material; have from the 1st mould or the outstanding pin parts of the 2nd mould; it is characterized in that; above-mentioned pin parts dispose like this: link the center line of the most close adjacent pin parts, be not orthogonal to metallic solution toward the interior direction that imports of metal mould device chamber.
2. metal mould device; be used to form and have e-machine housing preset space length hole portion, that constitute by metal material; have from the 1st mould or the outstanding pin parts of the 2nd mould; it is characterized in that; above-mentioned pin parts dispose like this: among the row of adjacent 2 pin parts; the row of another square cotter parts is with respect to the row of square cotter parts, in this row's direction about half spacing that staggers.
3. metal mould device, be used to form have preset space length hole portion, by the e-machine housing that metal material constitutes, have from the 1st mould or the outstanding pin parts of the 2nd mould, it is characterized in that above-mentioned pin parts are staggered arrangement.
4. metal mould device; be used to form have preset space length hole portion, by the e-machine housing that metal material constitutes, have from the outstanding pin parts of the 1st mould or the 2nd mould, it is characterized in that; with respect to the importing direction of metallic solution, the pin parts are staggered arrangement.
5. the manufacture method of e-machine, being shaped with metal mould device has the e-machine of housing, and this housing is made of the metal material with preset space length hole portion, it is characterized in that, has flow process and curing process; At flow process, metallic solution is imported above-mentioned metal mould device inside; At curing process, make the metallic solution curing that imports metal mould device inside at above-mentioned flow process; Above-mentioned metal mould device is the metal mould device of each record in the claim 1 to 4.
6. e-machine has the e-machine housing, and this housing is made of the metal material with preset space length hole portion, it is characterized in that, above-mentioned e-machine housing forms with casting.
7. e-machine as claimed in claim 6 is characterized in that above-mentioned metal material is a magnesium alloy.