CN1302909C - 共挤热封双向拉伸聚丙烯抗磨花烟用包装薄膜的制法 - Google Patents
共挤热封双向拉伸聚丙烯抗磨花烟用包装薄膜的制法 Download PDFInfo
- Publication number
- CN1302909C CN1302909C CNB2004100654971A CN200410065497A CN1302909C CN 1302909 C CN1302909 C CN 1302909C CN B2004100654971 A CNB2004100654971 A CN B2004100654971A CN 200410065497 A CN200410065497 A CN 200410065497A CN 1302909 C CN1302909 C CN 1302909C
- Authority
- CN
- China
- Prior art keywords
- film
- base material
- heat
- sealing base
- stretching
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种共挤热封双向拉伸聚丙烯抗磨花烟用包装薄膜的制法。该制法是：1)选用表面质地较硬的二元共聚聚丙烯作为薄膜表层热封基层材料；2)在薄膜表层热封基层材料中加入占材料总重量0.1～1%的聚甲基丙烯酸甲酯弹性体作为受力缓冲层；3)在薄膜表层热封基层材料中加入占材料总重量0.1～1%的经表面络合处理的玻璃微球作为抗粘材料；4)通过纵向拉伸和横向拉伸工艺的调整提高结晶度，控制芯层添加剂的析出速度。本发明的优点是：减轻或消除烟包起磨花的现象，提高烟包的包装美观度。
Description
技术领域：
本发明涉及一种香烟用外包装薄膜的制备方法。尤其是涉及一种共挤热封双向拉伸聚丙烯抗磨花烟用包装薄膜的制法。属包装材料技术领域。
背景技术：
长期以来，在香烟条包和小包的外包装面存在因运输、配送而引起摩擦，形成一团团白粉状外观，其分布位置不固定，烟草行业一般称之为“磨花”现象。该现象在深色盒皮上尤为明显。目前在行业内没有其它成熟的方案。磨花过的烟包破坏了烟包原有的装潢效果和美观，使消费者产生了坏感。
发明内容：
本发明的目的在于克服上述不足，提供一种能减轻或消除烟包起磨花的现象，提高烟包的包装美观度的共挤热封双向拉伸聚丙烯抗磨花烟用包装薄膜的制法。
本发明的目的是这样实现的：一种共挤热封双向拉伸聚丙烯抗磨花烟用包装薄膜的制法，其特点是：
1、选用二元共聚聚丙烯作为薄膜表层热封基层材料；
2、在薄膜表层热封基层材料中加入占材料总重量0.1～1％的聚甲基丙烯酸甲酯弹性体作为受力的缓冲层；
3、在薄膜表层热封基层材料中加入占材料总重量0.1～1％的经表面络合处理的玻璃微球，作为抗粘材料；
4、调整薄膜生产的纵向拉伸和横向位伸工艺参数：纵向拉伸倍数为5～7，拉伸温度为70～90℃；横向拉伸倍数为6～10，拉伸温度为140～155℃。
由于玻璃与聚丙烯(PP)之间相容性不好，所以在加入前须将玻璃微球用络合剂进行表面处理，以增加其与聚丙烯之间的相容性。具体用络合剂异丙基三硬脂酰基钛酸酯和二元共聚聚丙烯进行熔融挤出共混进行表面络合处理。
在制法中：选用质地较硬的二元共聚聚丙烯作为薄膜表层热封基层材料，是为了增加薄膜表面硬度，减少摩擦碎屑；选用聚甲基丙烯酸甲酯弹性体，以对运输过程中的碰撞力进行缓冲，减少摩擦碰撞力；用玻璃微球作为表面抗粘材料，由于玻璃微球是圆形颗粒，其形状很规则，减小了磨擦力，使抗粘剂外形规整，薄膜表面呈类似滚动摩擦，减小接触面积，同时玻璃的透光率很好，不会影响薄膜的光学性能；调整薄膜生产的纵向拉伸和横向位伸工艺参数，提高薄膜纵向拉伸和横向拉伸倍率，降低拉伸温度，以提高结晶度，提高薄膜表面硬度，控制芯层助剂析出速度。
通过高倍数的透射电子显微镜、扫描电子显微镜来观察磨花的膜面，磨花部位主要是一些抗粘剂的尖锐部位断裂、二元共聚物的碎屑和析出的抗静电体剂吸水形成的乳化物。
因此，利用共挤热封双向拉伸聚丙烯抗磨花烟用包装薄膜对香烟条包或小包进行包装，可以减轻或消除烟包起磨花的现象，满足烟包抗磨花的要求，使烟盒精美的印刷图案得到清晰再现，使烟包外观洁净美观。
具体实施方式：
本发明为一种共挤热封双向拉伸聚丙烯抗磨花烟用包装薄膜的制法。其特点是：
1、选用二元共聚聚丙烯作为薄膜表层热封基层材料；
2、在薄膜表层热封基层材料中加入占材料总重量0.1～1％的聚甲基丙烯酸甲酯(PMMA)弹性体；
3、在薄膜表层热封基层材料中加入占材料总重量0.1～1％的经表面络合处理的玻璃微球，在加入前用络合剂异丙基三硬脂酰基钛酸酯和二元共聚聚丙烯进行熔融挤出共混进行表面处理；
4、调整薄膜生产的纵向拉伸和横向位伸工艺参数：纵向拉伸倍数为5～7，拉伸温度为70～90℃；横向拉伸倍数为6～10，拉伸温度为140～155℃。
Claims (2)
1、一种共挤热封双向拉伸聚丙烯抗磨花烟用包装薄膜的制法，其特征在于：
1)、选用二元共聚聚丙烯作为薄膜表层热封基层材料；
2)、在薄膜表层热封基层材料中加入占材料总重量0.1～1％的聚甲基丙烯酸甲酯弹性体；
3)、在薄膜表层热封基层材料中加入占材料总重量0.1～1％的经表面络合处理的玻璃微球；
4)、调整薄膜生产的纵向拉伸和横向拉伸工艺参数：纵向拉伸倍数为5～7，拉伸温度为70～90℃；横向拉伸倍数为6～10，拉伸温度为140～155℃。
2、根据权利要求1所述的一种共挤热封双向拉伸聚丙烯抗磨花烟用包装薄膜的制法，其特点在于用络合剂异丙基三硬脂酰基钛酸酯和二元共聚聚丙烯进行熔融挤出共混对玻璃微球进行表面络合处理。