CN1293164A - Method for producing baking-free building blocks - Google Patents
Method for producing baking-free building blocks Download PDFInfo
- Publication number
- CN1293164A CN1293164A CN00133264A CN00133264A CN1293164A CN 1293164 A CN1293164 A CN 1293164A CN 00133264 A CN00133264 A CN 00133264A CN 00133264 A CN00133264 A CN 00133264A CN 1293164 A CN1293164 A CN 1293164A
- Authority
- CN
- China
- Prior art keywords
- building block
- baking
- mould
- free
- batching
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A technology for producing burning-free building blocks includes such steps as mixing phosphorus ore tailings or waste casting dregs or metallurgical slags with cement and water, uniformly stirring to stickiness, press mocelding, and curing at 0-50 deg.C for 60 hr or more. Its advantages are low cost decreased by 25-30%, high strength and aesthetic appearance.
Description
The present invention relates to a kind of production method of baking-free building block, particularly a kind of production method of utilizing the abandoned mine slag to produce baking-free building block.
Architectural used mostly be the sintering common brick, common brick is to be to form behind the raw material sintering with clay, because clay is a kind of natural resources, and this natural resources will reduce along with the increase of sintering fragment of brick usage quantity, the production cost of sintering fragment of brick also can progressively raise, and the process of baking bricks needs consume fuel, has wasted a large amount of energy.In order to save the soil, reduce the consumption of natural resources clay, country advocates the production novel wall material energetically, in the prior art, the production method of baking-free building block is to adopt cinder and cement etc. to mix the back to drop into mould molding, after being solidified, it is finished product, the shortcoming of its existence is: the cinder many aspects such as construction that can be used for paving the way, its comprehensive utilization scope is very extensive, therefore caused raw material sources comparatively nervous, the building block block cost that utilizes cinder to produce is higher, and price is expensive, can not satisfy the demand of the construction market of quick growth.
The objective of the invention is to propose a kind of method of utilizing the abandoned mine slag to produce baking-free building block.
The objective of the invention is to be reached by following technical scheme: the production method of baking-free building block of the present invention is characterized in: will by the weight ratio that comprises following building block batching
Phosphor tail slag or casting waste residue or metallurgical slag 4.2-12.6 part
Cement 1.4-9.8 part
Water 1-5 part
Mixing and stirring drops into it in mould after be clamminess, and compression moulding is that maintenance is no less than 60 hours under 0-50 ℃ the environment in temperature.
The major ingredient phosphor tail slag that use is made a low multiple use or casting waste residue or metallurgical slag substitute the high cinder of comprehensive utilization ratio, are used to produce unburned slag building block, product is very firm, easy fracture not, and good watertightness is arranged, will strengthen the intensity of baking-free building block greatly.
Purpose of the present invention can also further reach by following scheme.Aforesaid baking-free building block is characterized in evenly being coated with the last layer lime white at mould inner wall earlier before the building block batching that stirs drops into mould.Make building block be easy to the demoulding in process of production.
Purpose of the present invention can also further reach by following scheme.Aforesaid baking-free building block is characterized in: also comprise 0-8.4 part cinder in the building block batching.Can under the prerequisite of proof strength, alleviate the deadweight of building block like this, can save cement simultaneously.
The present invention compared with prior art, reduced 25-30% than breeze block production cost, and product is specious, the intensity height, and raw material is easy to get, it is energy-conservation to economize soil, harmless, found a valuable approach for useless scoriaceous comprehensive utilization, created wealth, the accumulation that has reduced phosphor tail slag, casting waste residue, metallurgical slag is taken up an area of and to the pollution of environment, tangible economic benefit and social benefit is arranged.
Following is described in further detail the specific embodiment of the present invention in conjunction with the embodiments.
Embodiment one: a kind of production method of baking-free building block, and will by the weight ratio that comprises following building block batching
4.2 kilograms of phosphor tail slags
9.8 kilograms of No. 325 cement of normal silicate
5 kilograms in water
Mixing and stirring drops into it in mould of block forming machine after be clamminess, and through the machine pressing moulding, is under 0 ℃ the environment in temperature, maintenance 72 hours.Be finished product after condensing firmly, product adopt national standard " common building block test method " (GB/T4111-1997) and national standard " normal concrete building block standard " (GB8239-1997) check, strength grade is: MU10.
Embodiment two: a kind of production method of baking-free building block, and will by the weight ratio that comprises following building block batching
4.2 kilograms of phosphor tail slags
8.4 kilograms of cinders
1.4 kilograms of No. 625 cement of normal silicate
1 kilogram in water
Mixing and stirring drops into it in mould of block forming machine after be clamminess, and through the machine pressing moulding, is under 50 ℃ the environment in temperature, maintenance 120 hours.Be finished product after condensing firmly, product adopt national standard " common building block test method " (GB/T4111-1997) and national standard " normal concrete building block standard " (GB8239-1997) check, strength grade is: MU3.5.
Embodiment three: a kind of production method of baking-free building block, and will by the weight ratio that comprises following building block batching
8.4 kilograms of phosphor tail slags
5.6 kilograms of No. 425 cement of normal silicate
3 kilograms in water
Mixing and stirring evenly is coated with the last layer lime white at mould inner wall after be clamminess, the building block batching that stirs can be dropped in the mould of block forming machine again, and through the machine pressing moulding, be under 18 ℃ the environment in temperature, maintenance 60 hours.Be finished product after condensing firmly, product adopt national standard " common building block test method " (GB/T4111-1997) and national standard " normal concrete building block standard " (GB8239-1997) check, strength grade is: MU7.5.
Embodiment four: a kind of production method of baking-free building block, and will by the weight ratio that comprises following building block batching
12.6 kilograms in casting waste residue
1.4 kilograms of No. 625 cement of normal silicate
3 kilograms of mixing and stirring of water are after be clamminess, evenly be coated with the last layer lime white at mould inner wall, the building block batching that stirs can be dropped in the mould of block forming machine, through the machine pressing moulding again, be under 40 ℃ the environment in temperature, maintenance 144 hours.Be finished product after condensing firmly, product adopt national standard " common building block test method " (GB/T4111-1997) and national standard " normal concrete building block standard " (GB8239-1997) check, strength grade is: MU3.5.
Embodiment five: a kind of production method of baking-free building block, and will by the weight ratio that comprises following building block batching
5.6 kilograms in casting waste residue
5.6 kilograms of cinders
2.8 kilograms of No. 525 cement of normal silicate
4 kilograms of mixing and stirring of water are after be clamminess, evenly be coated with the last layer lime white at mould inner wall, the building block batching that stirs can be dropped in the mould of block forming machine, through the machine pressing moulding again, be under 25 ℃ the environment in temperature, maintenance 144 hours.Be finished product after condensing firmly, product adopt national standard " common building block test method " (GB/T4111-1997) and national standard " normal concrete building block standard " (GB8239-1997) check, strength grade is: MU5.0.
Claims (3)
1, a kind of production method of baking-free building block is characterized in that: will by the weight ratio that comprises following building block batching
Phosphor tail slag or casting waste residue or metallurgical slag 4.2-12.6 part
Cement 1.4-9.8 part
Water 1-5 part
Mixing and stirring drops into it in mould after be clamminess, and compression moulding is that maintenance is no less than 60 hours under 0-50 ℃ the environment in temperature.
2, according to the described baking-free building block of claim 1, it is characterized in that: before the building block batching that stirs drops into mould, evenly be coated with the last layer lime white at mould inner wall earlier.
3, according to the described baking-free building block of claim 1, it is characterized in that: in the building block batching, also comprise 0-8.4 part cinder.