CN1290791C - Construction material product produced by industrial solid was and building refuse - Google Patents
Construction material product produced by industrial solid was and building refuse Download PDFInfo
- Publication number
- CN1290791C CN1290791C CNB2004100767664A CN200410076766A CN1290791C CN 1290791 C CN1290791 C CN 1290791C CN B2004100767664 A CNB2004100767664 A CN B2004100767664A CN 200410076766 A CN200410076766 A CN 200410076766A CN 1290791 C CN1290791 C CN 1290791C
- Authority
- CN
- China
- Prior art keywords
- building
- product
- brick
- industrial solid
- produce
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to a construction material product produced by industrial solid waste and building refuse. The said product is prepared by material at the following weight ratio and method: 18-22 portion of fly ash; 38-46 portion of slag; 8-13 portion ofcoal slack; 8-13 portion of builders rubbish; 5-10 portion of lime; 1.5-6 portion of gypsum; 0.05-0.1 portion of binder. The said raw material is crushed into the particle size of 5mm, and after dry mixing each constituent, adding water and agitating, in-mold vibration and compression are performed to mould. After 12-24 hours of product maintenance and 5-7 days of dry wet curing, natural seasoning is ok. The invention maximizes improving the enviroment to realize the cyclic utilization of waste and regeneration of resource to make the cost lower and the range of building materials larger. The invention can produce building block, mark brick, insulating brick for building wall and also can produce gtound hardening series such as plaza brick, footpath brick; and also can producebearing wall material; and also can produce warming plate, plasterer mortar and the other building materials.
Description
Technical field
The invention belongs to building material technical field, be specifically related to a kind of building materials series product of producing with industrial solid castoff and building waste.
Background technology
Along with China's development of economic construction, the quickening day by day of urbanization process paces, the continuous growth of the solid waste of bringing because of the expansion of various commercial production scale and a large amount of building wastes that urban facilities upgrades and reconstruction of the old city town brings, not only take up room, and serious environment pollution, bring very big harm to existent environment of people.Disclose a kind of name for Chinese patent application CN02151561 number and be called " a kind of wall floor tile of producing with building waste ", need not fire with this method, refuse is effectively utilized, more in the past when producing building material product such as clay brick etc., form building material product that this method produces and compare that to have cost of goods manifactured low by going into the kiln high-temperature firing again after good by certain proportioning raw materials, manufacturing cycle is short, but while save energy and raw-material advantage, but, because the restriction of its proportioning raw materials, the scope of producible building material product is subjected to certain restriction, simultaneously, owing to added cement in its raw material, like this, cost is higher relatively again.
Summary of the invention
The invention solves prior art and make the building material product cost more single technical problem of building material product higher and that only produce, a kind of building materials series product of producing with industrial solid castoff and building waste are provided with building waste.
The present invention is achieved through the following technical solutions: a kind of building materials series product of producing with industrial solid castoff and building waste, and it is prepared by following weight proportion raw material and method:
Flyash 18-22 part slag 38-46 part
Coal gangue 8-13 part building waste 8-13 part
Lime 5-10 part gypsum 1.5-6 part
Binding agent 0.05-0.1 part
---described binding agent is water glass or sodium sulfate or carboxymethyl cellulose.
Binding agent of the present invention can only use a kind of material in use as required, also can use two or more materials simultaneously.
It is 5mm that above-mentioned materials of weight proportions is crushed to granularity with physical method, and dried being mixed of each component added water after even and stir, and goes into mould vibration extrusion forming, and the product maintenance is after 12-24 hour, and through doing wet curing 5-7 days, seasoning gets final product again.Specifically can select different proportioning raw materials combinations according to different building material products.
The present invention compared with prior art, its beneficial effect is: maximizing improve environment, realize the regeneration of the cyclic utilization of waste and resource, can make cost of goods manifactured lower, because can be by the building material product of the different purposes of different proportioning raw materials combinations produce, thereby can make the scope of the building material product of being produced bigger, product reaches the service requirements of construction material through the house construction engineering quality of materials supervision and inspection station check of Shanxi Province Bureau of Technical Supervision.The present invention both can make construction wall building block, standard brick, insulating brick etc.; Also can produce hardened ground series (as: paving tile, pavement bricks etc.); Also can produce bearing wall material; Also can make warming plate, motar and other material of construction etc.
Embodiment
Below be embodiments of the invention, embodiment be used for illustrating of the present invention, rather than right
The present invention imposes any restrictions.It is to be prepared from by following weight proportion raw material and method:
41 parts in 22 parts of slags of flyash
13 parts of 13 parts of building wastes of coal gangue
1.5 parts in 10 parts of gypsum of lime
0.05 part of binding agent
---described binding agent is water glass or sodium sulfate or carboxymethyl cellulose.
Binding agent can only use a kind of material in use as required, also can use two or more materials simultaneously.
It is 5mm that above-mentioned materials of weight proportions is crushed to granularity with physical method, and dried being mixed of each component added water after even and stir, and goes into mould vibration extrusion forming, and the product maintenance is after 12-24 hour, and through doing wet curing 5-7 days, seasoning gets final product again.
Claims (2)
1, a kind of building material product of producing with industrial solid castoff and building waste is characterized in that it is made up of the following weight proportion raw material and is prepared by following method:
Flyash 18-22 part slag 38-46 part
Coal gangue 8-13 part building waste 8-13 part
Lime 5-10 part gypsum 1.5-6 part
Binding agent 0.05-0.1 part
--------described binding agent is water glass or sodium sulfate or carboxymethyl cellulose,
It is 5mm that above-mentioned materials of weight proportions is crushed to granularity with physical method, and dried being mixed of each component added water after even and stir, and goes into mould vibration extrusion forming, and the product maintenance is after 12-24 hour, and through doing wet curing 5-7 days, seasoning gets final product again.
2, the building material product of producing with industrial solid castoff and building waste according to claim 1 is characterized in that described binding agent can only use a kind of material, also can use two or more materials simultaneously.