CN1288080A - Polypropylene fiber and cotton blend fabric and its prodn. method - Google Patents
Polypropylene fiber and cotton blend fabric and its prodn. method Download PDFInfo
- Publication number
- CN1288080A CN1288080A CN 99113804 CN99113804A CN1288080A CN 1288080 A CN1288080 A CN 1288080A CN 99113804 CN99113804 CN 99113804 CN 99113804 A CN99113804 A CN 99113804A CN 1288080 A CN1288080 A CN 1288080A
- Authority
- CN
- China
- Prior art keywords
- slurry
- polypropylene
- filament yarn
- polypropylene filament
- blend fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A mixed polypropylene-cotton cloth uses cotton yarn or cotton-polyester yarn as weft and polypropylene filament as warp. Before weaving, the polypropylene filament is warped by a roller, half of which in immersed in size in the size tank between creel bank and drum. The rotation direction of said roller is different from the advance direction of polypropylene filament. Its advantages include: high strength, and wear and corrosion resistance, low specific weight and low cost.
Description
The present invention relates to a kind of cloth and weaving method thereof.
Postal canvas or automobile-used, the sail duck that uses, what use for many years is pure cotton canvas always, is that raw material is made into cotton textiles.This canvas intensity is low, and the warp-wise ultimate strength is 1330.6 newton, and the broadwise ultimate strength is 1077.4 newton; This canvas is not wear-resisting, uses the 150# emery wheel, load 1000 grams, and rubbing three with same direction yarn only is 159 times; Acidproof, alkaline-resisting ability is all strong inadequately.
The objective of the invention is provides a kind of polypropylene fiber and cotton blend fabric in order to overcome above-mentioned weak point, and intensity height, warp-wise ultimate strength are 3137.6 newton, and the broadwise ultimate strength is 1250 newton; Polypropylene fiber and cotton blend fabric is wear-resisting, uses the 150# emery wheel, load 1000 grams, and rubbing three with same direction yarn is 664 times; Acidproof, the alkaline-resisting ability of polypropylene fiber and cotton blend fabric is all strong.
Description of the present invention is as follows: the used broadwise material of polypropylene fiber and cotton blend fabric is cotton yarn or polyester, and used warp-wise material is a polypropylene filament yarn.Preparatory stage carries out warping to polypropylene filament yarn and handles before knitting, and between the creel of polypropylene filament yarn and swift, stock tank is installed, splendid attire antistatic slurry in the stock tank.The parallel slurry roller that is equipped with above stock tank, half of slurry roller be not in slurry, and the opposite spin of slurry roller and polypropylene filament yarn trend, make slurry roller side face spread slurry, polypropylene filament yarn along slurry roller last week along around the time to swift, simultaneously polypropylene filament yarn is carried out warping and handle, make that polypropylene filament yarn is antistatic, soft, have the obvolvent effect.Antistatic slurry is made up of converted starch, polyvinyl alcohol, acrylate, bisnaphthol, bleeding agent, pure water.By weight, the shared percentage of each component is:
Converted starch 15.02～22.54%
Polyvinyl alcohol 11.26～16.90%
Methyl esters 2.40～3.61%
Acrylate 11.26～16.90%
Bisnaphthol 0.03～0.04%
Bleeding agent 0.03～0.04%
Pure water 40～60%
Polypropylene filament yarn through warping is handled carries out beaming by prior art, as machine on the warp, is made into polypropylene fiber and cotton blend fabric with cotton yarn or polyester as parallel.
Description of drawings:
Figure carries out the device schematic diagram that warping is handled to polypropylene filament yarn among the present invention.1-creel among the figure, the 2-pressure roller, 3-starches roller, and 4-swift, 5-deflector roll, 6-be through axle, 7-stock tank, 8-slurry, 9-polypropylene filament yarn.
To produce the embodiment of postal turnover bag as polypropylene fiber and cotton blend fabric of the present invention.The used broadwise material of polypropylene fiber and cotton blend fabric is cotton yarn or washs continuous yarn, and the warp-wise material is that polypropylene filament yarn is joined (9), and it is the high-strength polypropylene filament yarn of 66.7tex that polypropylene filament yarn is selected line density for use.Warping processing to high-strength polypropylene filament yarn (9) is provided with a beaming appliance, as shown in the figure, between creel (1) and swift (4), stock tank (7) is installed, the interior splendid attire antistatic slurry of stock tank (7) (8).The parallel slurry roller (3) that is equipped with in stock tank (7) top, half of slurry roller (3) be not in slurry (8), and the opposite spin of slurry roller (3) and polypropylene filament yarn (9) trend, make slurry roller (3) side face spread slurry (8), polypropylene filament yarn (9) along slurry roller (3) last week along around when swift (4), simultaneously polypropylene filament yarn (9) is carried out warping and handle, make that polypropylene filament yarn is antistatic, soft, have the obvolvent effect.The linear velocity of polypropylene filament yarn is 30 meters/minute.How form by phenol, bleeding agent, pure water by converted starch, polyvinyl alcohol, methyl alcohol, acrylate, two for antistatic slurry.By weight, the shared percentage of each component is:
Converted starch 17.64～19.52%
Polyvinyl alcohol 13.23～14.64%
Methyl esters 2.82～3.12%
Acrylate 13.23～14.64%
Bisnaphthol 0.03～0.04%
Bleeding agent 0.03～0.04%
Pure water 53～48%
Polypropylene filament yarn through warping is handled carries out beaming by prior art, as machine on the warp, is made into polypropylene fiber and cotton blend fabric with cotton yarn or polyester as parallel.
Advantage of the present invention: polypropylene fiber and cotton blend fabric intensity height, wear-resisting, acidproof, alkaline-resisting, light specific gravity, cost is low, Be particularly useful for the mailbag cloth.
Claims (4)
1, a kind of polypropylene fiber and cotton blend fabric is characterized in that the broadwise material is cotton yarn or polyester, and the warp-wise material is a polypropylene filament yarn.
2, a kind of weaving method of polypropylene fiber and cotton blend fabric is characterized in that knitting the preceding preparatory stage, polypropylene filament yarn is carried out warping handle, between the creel and swift of polypropylene filament yarn, stock tank is installed, splendid attire antistatic slurry in the stock tank, antistatic slurry by weight, the shared percentage of each component is:
Converted starch 15.02～22.54%
Polyvinyl alcohol 11.26～16.90%
Methyl esters 2.40～3.61%
Acrylate 11.26～16.90%
Bisnaphthol 0.03～0.04%
Bleeding agent 0.03～0.04%
Pure water 40～60%
3, the weaving method of polypropylene fiber and cotton blend fabric according to claim 2, in the device that it is characterized in that the warping of polypropylene filament yarn is handled, the parallel slurry roller that is equipped with above stock tank, half of slurry roller be not in slurry, and the opposite spin of slurry roller and polypropylene filament yarn trend, polypropylene filament yarn along slurry roller edge last week around to swift.
4, the weaving method of polypropylene fiber and cotton blend fabric according to claim 2 is characterized in that antistatic slurry by weight, the shared percentage of each component can also for:
Converted starch 17.64～19.52%
Polyvinyl alcohol 13.23～14.64%
Methyl esters 2.82～3.12%
Acrylate 13.23～14.64%
Bisnaphthol 0.03～0.04%
Bleeding agent 0.03～0.04%
Pure water 53～48%