CN1286991C - 一种不锈钢造渣除气精炼剂 - Google Patents
一种不锈钢造渣除气精炼剂 Download PDFInfo
- Publication number
- CN1286991C CN1286991C CN 200510038467 CN200510038467A CN1286991C CN 1286991 C CN1286991 C CN 1286991C CN 200510038467 CN200510038467 CN 200510038467 CN 200510038467 A CN200510038467 A CN 200510038467A CN 1286991 C CN1286991 C CN 1286991C
- Authority
- CN
- China
- Prior art keywords
- molten steel
- present
- slagging
- stainless steel
- refining agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种不锈钢造渣除气精炼剂，具体地说是用于净化不锈钢钢液表面，提高不锈钢质量的铸造辅助材料，属于铸造行业金属表面处理技术领域。其主要取白云石为：70-80重量%、铝粉为：10-15重量%、萤石为：6-15重量%，在常温下均匀混合，包装为成品。本发明能保护炉衬，使炉衬寿命可达200次以上；造渣效果好，大幅减少了工件的皮下黑点，抛光件的表面黑点和麻点，产品的成品率大大提高；保温除气效果好，它始终浮在钢液的表面，避免钢液热量的散失，钢液与空气的接触氧化，氢气、氮气的吸入，使钢液夹杂物大大减少，气体含量大大降低，从而使钢液更加洁净，性能更加优良。
Description
技术领域
本发明涉及一种不锈钢造渣除气精炼剂，具体地说是用于净化不锈钢钢液，提高不锈钢质量的铸造辅助材料，属于铸造冶金行业技术领域。
背景技术
本发明作出以前，在已有技术中，不锈钢铸造行业中对钢液表面处理的造渣除气精炼剂通常是采用以下三种方案：1、采用石灰(CaO)、萤石(CaF2)混合而成；2、采用石灰(CaO)、氧化镁(MgO)、萤石(CaF2)混合制成；3、采用石灰(CaO)、萤石(CaF2)、铝粉(Al2O3)混合制成。该几种造渣除气精炼剂主要用在大型钢厂使用，在铸造厂使用较少。其主要原因是：1、使用效果不明显，不能减少工件的皮下黑点，抛光件的表面黑点和麻点，从而使产品的成品率大大降低；2、保温除气效果不理想，除渣麻烦，夹渣仍很多；3、侵蚀炉壁严重，由于炉衬是由镁砂(MgO)制成的，钢液在炉衬里翻滚，会冲刷炉衬，少量镁砂会落在钢液里，导致炉衬的损耗，在正常情况下，一个炉衬可用150-180次，而用造渣剂后，只能使用在100次以内。
发明内容
本发明的目的在于克服上述不足之处，从而提供一种制作方法简单，能保护炉衬，炉衬使用寿命长；能大幅减少工件的皮下黑点，抛光件的表面黑点和麻点，提高产品成品率；能使钢液夹杂物大大减少，气体含量大大降低，从而使钢液更加洁净，性能更加优良的不锈钢造渣除气精炼剂。
本发明的主要解决方案是这样实现的：
本发明造渣除气精炼剂其组成配比(按重量百分数计)：
本发明主要取白云石(CaMgCO3)、铝粉(Al2O3)、萤石(CaF2)在常温下均匀混合，称量、包装为成品。
本发明中白云石(CaMgCO3)为：70-80、铝粉(Al2O3)为：10-15、萤石(CaF2)为：6-15。
本发明与已有技术相比具有以下优点：
本发明由于采用了大量的白云石，其在900℃左右分解成造渣材料氧化钙，氧化镁，氧化镁能补充一部分到炉衬，能保护炉衬，使炉衬寿命可达200炉以上；造渣效果好，使用后效果明显，大幅减少了工件的皮下黑点，抛光件的表面黑点和麻点，产品的成品率大大提高；保温除气效果好，它始终浮在钢液的表面，避免钢液热量的散失，钢液与空气的接触氧化，氢气、氮气的吸入，使钢液夹杂物大大减少，气体含量大大降低，从而使钢液更加洁净，性能更加优良。
具体实施方式
下面本发明将结合附图中的实施例作进一步描述：
本发明实施例中其组份配比(按重量百分数计)：
实施例一：
本发明实施例中取白云石(CaMgCO3)为：70、铝粉(Al2O3)为：15、萤石(CaF2)为：15，在常温下经混合均匀搅拌制成造渣除气精炼剂，按需要进行称量包袋，成品包装入库。白云石、萤石为粉状。
采用本实施例中配方制成的造渣除气精炼剂使用方法如下：在某大型钢厂使用。将钢液重量的0.3-0.5造渣除气精炼剂置于炉底，当钢水满位测温达到熔炼工艺要求的温度时再往上调整20-30℃，然后关上电源，使其静置期间轻微晃动钢液，使渣尽快上浮。此时不做任何除渣动作(即不用洒上除渣剂)，若温度有下降之虑，则洒上保温。待2分钟左右再开电源，放入钙矽锰，洒上除渣剂除渣，测温，反复进行。操作时，放置锰铁、矽铁时勿使用除渣剂盖于炉顶。
通过使用能在钢液表面形成一层保护层，起到保温作用，可有效地防止了钢液吸气；可改善钢液与熔渣的表面张力、界面张力，使液渣更易分离；粘渣能力强，将浮上来的渣聚集在一起，形成大颗粒熔渣，漂浮于钢液上；通过液气混合，可有效地排除氢气，防止了针孔的产生；通过熔渣和氢气的排除，净化了钢液，可大幅度减少工件表面及皮下黑点和麻点，使产品更加洁净、白亮，并能提高抛光件及加工件的成品率。
实施例二：
本发明实施例中取白云石(CaMgCO3)为：75、铝粉(Al2O3)为：12.5、萤石(CaF2)为：10.5，在常温下经混合均匀搅拌制成造渣除气精炼剂，按需要进行称量包袋，成品包装入库。上述各组份百分比之和为100重量％。采用本实施例中配方制成的造渣除气精炼剂，并采用实施例一中的使用方法，在大型钢厂使用可达到与实施例一中同样的使用效果，纯净的钢液使产品综合性能得到提高。
实施例三：
本发明实施例中取白云石(CaMgCO3)为：80、铝粉(Al2O3)为：10、萤石(CaF2)为：6，在常温下经混合均匀搅拌制成造渣除气精炼剂，按需要进行称量包袋，成品包装入库。上述各组份百分比之和为100重量％。采用本实施例中配方制成的造渣除气精炼剂，经在铸造厂使用同样使钢液更加洁净，性能更加优良。
Claims (1)
1、一种不锈钢造渣除气精炼剂，其特征是取：白云石为：70-80重量％、铝粉为：10-15重量％、萤石为：6-15重量％，在常温下均匀混合，包装为成品。