CN1280109C - Film coated printing film and its printing process - Google Patents
Film coated printing film and its printing process Download PDFInfo
- Publication number
- CN1280109C CN1280109C CN 03121056 CN03121056A CN1280109C CN 1280109 C CN1280109 C CN 1280109C CN 03121056 CN03121056 CN 03121056 CN 03121056 A CN03121056 A CN 03121056A CN 1280109 C CN1280109 C CN 1280109C
- Authority
- CN
- China
- Prior art keywords
- film
- water
- coating film
- printed material
- biaxially oriented
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a printing film of a coating film. The present invention has printing technology which comprises the following steps: a film body solution is prepared by 75 portions of water, 22.6 portions of PVA, 0.4 portion of glycerol, 1.25 portions of KR-101, and 0.75 portion of FA10 by weight portions; when the solution is prepared, the PVA is put into water; water with the PVA is stirred and heated, so the PVA is dissolved; the glycerol, the KR-101 and the FA10 are put into the solution and are dissolved, so the film body solution is obtained; a BOPP film is flatly laid on a platform, and the film body solution is uniformly sprayed on the BOPP film which is dried. The present invention has the printing technology that a color spraying and printing device is used for printing patterns of characters and pictures on a printing film of a coating film; the printing film of the coating film is flatly laid on the water surface, and the printing film of the coating film is printed with patterns of characters and pictures; after the printing film of the coating film is in a mixed state of solid and liquid in water, an object to be printed is pressed downwards into water. The present invention aims at providing the printing film of the coating film and the printing technology for the printing film with short production period, low cost and no need of plate making printing.
Description
Technical field
The present invention puts it briefly and relates to a kind of typography, relate in particular to a kind of on the article of surface imperfection the coating film printing film and the typography thereof of hectographic printing.
Background technology
Though existing film-covered printing process can be printed onto calligraphy and painting pattern surface configuration on glass, pottery, metal and the stone material objects of material comparatively complicated and changeable, but because existing coating membrane material can only adopt intaglio plate, gentle version, lithographic plate and the printing of bat printing technology, its plate-making cost is higher, also be not easy to print calligraphy and painting pattern on greater than 2 meters coating membrane material at fabric width, this makes the production cycle and the cost of manufacture of small lot, multi-configuration item commodity greatly improve, and has influenced the sale of product on market.
Summary of the invention
The objective of the invention is to overcome above-mentioned the deficiencies in the prior art, provide a kind of with short production cycle, cost of manufacture is low, does not need the coating film printing film and the typography thereof of Plate making printing.
Coating film printing film of the present invention, adopt following steps to make:
(1) according to weight parts water: 70-80, PVA:22-23.2, glycerine: 0.3-0.5, the product code name is the hydrophily superfine silicon dioxide of KR-101: 1-1.5, the product code name is the water treatment silicone defoaming agent of FA10: a 0.5-1 preparation film body solution, earlier water is put into the container of band heater during preparation, PVA put into that water stirs and after heating makes its dissolving, again with glycerine, the product code name is that the hydrophily superfine silicon dioxide of KR-101 and water treatment silicone defoaming agent that the product code name is FA10 add under the temperature of indoor environment and stir in the solution and make its dissolving obtain film body solution;
(2) utilize Biaxially oriented polypropylene BOPP plastic sheeting, it is tiled on the platform, the film body solution that step (1) is obtained evenly is sprayed on the surface of Biaxially oriented polypropylene BOPP plastic sheeting, and give drying, can obtain attached to the coating film printing film on the Biaxially oriented polypropylene BOPP plastic sheeting.
Coating film printing film of the present invention, in the wherein said step (1) according to weight parts water: 75, PVA:22.6, glycerine: 0.4, the product code name is the hydrophily superfine silicon dioxide of KR-101: 1.25, and the product code name is the water treatment silicone defoaming agent of FA10: 0.75 preparation film body solution.
Coating film printing film of the present invention, wherein said step (1) with PVA put into water with 70-100 rev/min speed after stirring 15 minutes under the temperature of indoor environment, solution is heated to after 90 ℃ of insulations made its dissolving in 30-60 minute, is that the hydrophily superfine silicon dioxide of KR-101 and water treatment silicone defoaming agent that the product code name is FA10 add under the temperature of indoor environment and stir in the solution and it is dissolved fully again with glycerine, product code name.
Coating film printing film of the present invention, the thickness of Biaxially oriented polypropylene BOPP plastic sheeting is the 100-120 micron in the wherein said step (2), when the fabric width of Biaxially oriented polypropylene BOPP plastic sheeting is below 4 meters the time, the film body solution that step (1) is obtained with the pneumatic spraying device according to 228-247 milliliter/square metre evenly be sprayed on the surface of Biaxially oriented polypropylene BOPP plastic sheeting, behind the natural levelling under the temperature conditions of indoor environment dry 12 hours or be placed on and carry out drying in the hothouse; When the fabric width of Biaxially oriented polypropylene BOPP plastic sheeting is below 2 meters the time, the film body solution that step (1) is obtained with coating machine or coating machine or silk screen coating machine according on the surface of 133-152 milliliter/square metre be uniformly coated on Biaxially oriented polypropylene BOPP plastic sheeting and utilize heated-air drying.
Use the typography of coating film printing film of the present invention, comprise the steps:
(1) utilize the color painting PRN device on attached to the described coating film printing film on the Biaxially oriented polypropylene BOPP plastic sheeting, to print calligraphy and painting pattern, simultaneously the surface of printed material body is cleared up, after its surperficial spot and water droplet of place to go, again to printed material surface spraying one deck glass coating, then the printed material body is placed baking box to be heated to 140 ℃-170 ℃ insulations 30-50 minute, take out after 15 minutes with the baking box cooling, naturally cool to the temperature of indoor environment;
(2) the coating film printing film that is printed with calligraphy and painting pattern that step (1) is obtained is taken off from Biaxially oriented polypropylene BOPP plastic sheeting, face up and be tiled on the water surface by being printed on calligraphy and painting pattern, more surperficial spray treatment agent is sprayed on the coating film printing film equably;
(3) after coating film printing film becomes solid-liquid mixing in water by the time, the printed material body that step (1) obtains is pressed downward in the water, utilize the pressure of water to make coating film printing film coat the printed material surface according to the position that flies at calligraphy and painting pattern on the horizontal plane;
(4) the printed material body that is printed with calligraphy and painting pattern that step (3) is obtained takes out from water, water cleans the printed material surface, then with after heated-air drying or the air dry, again to printed material surface spraying one deck glass coating, then the printed material body is placed baking box to be heated to 140 ℃-170 ℃ insulations 30-50 minute, take out after 15 minutes with the baking box cooling, naturally cool to the temperature of indoor environment.
The typography of coating film printing film of the present invention sprays glass coatings to the printed material surface according to 5 milliliters/square metre in wherein said step (1) and the step (4), and the printed material body places baking box to be heated to 160 ℃ of insulations 40 minutes.
The typography of coating film printing film of the present invention, surperficial spray treatment agent is the serigraphy cleaning agent in the wherein said step (2), described printed material body adopts glass, pottery, metal or stone material material to make.
The advantage and the good effect of coating film printing film of the present invention and typography thereof are: it adopts unique technology to make coating film printing film, can utilize the color painting PRN device on attached to the coating film printing film on the Biaxially oriented polypropylene BOPP plastic sheeting, to print calligraphy and painting pattern, utilize coating film printing film that calligraphy and painting pattern is printed onto on the complex-shaped changeable product surface, because the printed patterns that the computer of color painting PRN device can long-range reception client provides, or from the computer picture library, access multiple printed patterns for customer selecting, needn't look like intaglio plate, gentle version, lithographic plate and bat printing arts demand are made a plate, make small lot, the production cycle and the cost of manufacture of the commodity of multi-configuration item greatly reduce, can make product designer be given full play to imagination ground deisgn product planform and style, and then the image appearance and the market sale that can improve product.In addition, because the color painting PRN device can print fabric width at the film more than 2 meters, thereby enlarged the accommodation of coating film printing typography, make more products can utilize coating film printing typography at its surface printing calligraphy and painting pattern, so coating film printing film of the present invention and typography thereof have with short production cycle, cost of manufacture is low, does not need the characteristics of Plate making printing.
The specific embodiment
Below in conjunction with specific embodiment coating film printing film of the present invention and typography thereof are described further.
Embodiment 1
Coating film printing film of the present invention, adopt following steps to make:
(1) according to weight parts water: 75, PVA:22.6, glycerine: 0.4; The product code name is the hydrophily superfine silicon dioxide of KR-101: 1.25, the product code name is the water treatment silicone defoaming agent of FA10: 0.75 preparation film body solution, earlier water is put into the rustless steel container of band heater during preparation, with PVA put into water with 85 rev/mins speed after stirring 15 minutes under the temperature of indoor environment, solution is heated to after 90 ℃ of insulations dissolved it in 50 minutes fully, again with glycerine, the product code name is that the hydrophily superfine silicon dioxide of KR-101 and water treatment silicone defoaming agent that the product code name is FA10 add to stir in the solution and it is dissolved fully under the temperature of indoor environment and obtain film body solution;
(2) utilizing thickness is 100 microns Biaxially oriented polypropylene BOPP plastic sheeting, it is tiled on the platform, when the fabric width of Biaxially oriented polypropylene BOPP plastic sheeting is below 4 meters the time, the film body solution that step (1) is obtained with the pneumatic spraying device according on 228 milliliters of/square metre surfaces that evenly are sprayed on Biaxially oriented polypropylene BOPP plastic sheeting, behind the natural levelling under the temperature conditions of indoor environment dry 12 hours or be placed on and carry out drying in the hothouse; When the fabric width of Biaxially oriented polypropylene BOPP plastic sheeting is below 2 meters the time, the film body solution that step (1) is obtained, can obtain attached to the coating film printing film on the Biaxially oriented polypropylene BOPP plastic sheeting according on 133 milliliters of/square metre surfaces that are uniformly coated on Biaxially oriented polypropylene BOPP plastic sheeting and utilize heated-air drying with coating machine or coating machine or silk screen coating machine.
Use the typography of coating film printing film of the present invention, comprise the steps:
(1) client is provided or the computer of selected calligraphy and painting pattern input color air brushing PRN device, utilize the color painting PRN device on attached to the described coating film printing film on the Biaxially oriented polypropylene BOPP plastic sheeting, to print calligraphy and painting pattern, simultaneously the surface of printed material body is cleared up, after its surperficial spot and water droplet of place to go, spray one deck glass coatings to the printed material surface that glass material is made according to 5 milliliters/square metre again, then the printed material body is placed baking box to be heated to 160 ℃ of insulations 40 minutes, take out after 15 minutes with the baking box cooling, naturally cool to the temperature of indoor environment;
(2) the coating film printing film that is printed with calligraphy and painting pattern that step (1) is obtained is taken off from Biaxially oriented polypropylene BOPP plastic sheeting, face up and be tiled on the water surface by being printed on calligraphy and painting pattern, to note between coating film printing film and the water bubble being arranged during tiling, can not there be the globule film of coating simultaneously printing film upper surface, the serigraphy cleaning agent is sprayed on the coating film printing film equably according to 5 milliliters/square metre again;
(3) after coating film printing film becomes solid-liquid mixing in water by the time, according to the position that flies at calligraphy and painting pattern on the horizontal plane printed material body that step (1) obtains is pressed downward in the water, utilize the pressure of water to make coating film printing film coat the printed material surface fully;
(4) the printed material body that is printed with calligraphy and painting pattern that step (3) is obtained takes out from water, water cleans the printed material surface, then with after heated-air drying or the air dry, spray one deck glass coatings to the printed material surface according to 5 milliliters/square metre again, then the printed material body is placed baking box to be heated to 160 ℃ of insulations 40 minutes, take out after 15 minutes with the baking box cooling, naturally cool to the temperature of indoor environment.
Embodiment 2
Coating film printing film of the present invention, adopt following steps to make:
(1) according to weight parts water: 77, PVA:22, glycerine: 0.3, the product code name is the hydrophily superfine silicon dioxide of KR-101: 1, the product code name is the water treatment silicone defoaming agent of FA10: 0.5 preparation film body solution, earlier water is put into the rustless steel container of band heater during preparation, with PVA put into water with 70 rev/mins speed after stirring 15 minutes under the temperature of indoor environment, solution is heated to after 90 ℃ of insulations dissolved it in 30 minutes fully, again with glycerine, the product code name is that the hydrophily superfine silicon dioxide of KR-101 and water treatment silicone defoaming agent that the product code name is FA10 add to stir in the solution and it is dissolved fully under the temperature of indoor environment and obtain film body solution;
(2) utilizing thickness is 120 microns Biaxially oriented polypropylene BOPP plastic sheeting, it is tiled on the platform, when the fabric width of Biaxially oriented polypropylene BOPP plastic sheeting is below 4 meters the time, the film body solution that step (1) is obtained with the pneumatic spraying device according on 247 milliliters of/square metre surfaces that evenly are sprayed on Biaxially oriented polypropylene BOPP plastic sheeting, behind the natural levelling under the temperature conditions of indoor environment dry 12 hours or be placed on and carry out drying in the hothouse; When the fabric width of Biaxially oriented polypropylene BOPP plastic sheeting is below 2 meters the time, the film body solution that step (1) is obtained, can obtain attached to the coating film printing film on the Biaxially oriented polypropylene BOPP plastic sheeting according on 152 milliliters of/square metre surfaces that are uniformly coated on Biaxially oriented polypropylene BOPP plastic sheeting and utilize heated-air drying with coating machine or coating machine or silk screen coating machine.
Use the typography of coating film printing film of the present invention, comprise the steps:
(1) client is provided or the computer of selected calligraphy and painting pattern input color air brushing PRN device, utilize the color painting PRN device on attached to the described coating film printing film on the Biaxially oriented polypropylene BOPP plastic sheeting, to print calligraphy and painting pattern, simultaneously the surface of printed material body is cleared up, after its surperficial spot and water droplet of place to go, spray one deck glass coatings to the printed material surface that ceramic material is made according to 5 milliliters/square metre again, then the printed material body is placed baking box to be heated to 140 ℃ of insulations 30 minutes, take out after 15 minutes with the baking box cooling, naturally cool to the temperature of indoor environment;
(2) the coating film printing film that is printed with calligraphy and painting pattern that step (1) is obtained is taken off from Biaxially oriented polypropylene BOPP plastic sheeting, face up and be tiled on the water surface by being printed on calligraphy and painting pattern, to note between coating film printing film and the water bubble being arranged during tiling, can not there be the globule film of coating simultaneously printing film upper surface, the serigraphy cleaning agent is sprayed on the coating film printing film equably according to 5 milliliters/square metre again;
(3) after coating film printing film becomes solid-liquid mixing in water by the time, according to the position that flies at calligraphy and painting pattern on the horizontal plane printed material body that step (1) obtains is pressed downward in the water, utilize the pressure of water to make coating film printing film coat the printed material surface fully;
(4) the printed material body that is printed with calligraphy and painting pattern that step (3) is obtained takes out from water, water cleans the printed material surface, then with after heated-air drying or the air dry, spray one deck glass coatings to the printed material surface according to 5 milliliters/square metre again, then the printed material body is placed baking box to be heated to 160 ℃ of insulations 30 minutes, take out after 15 minutes with the baking box cooling, naturally cool to the temperature of indoor environment.
Embodiment 3
Coating film printing film of the present invention, adopt following steps to make:
(1) according to weight parts water: 70, PVA:23.2, glycerine: 0.5; The product code name is the hydrophily superfine silicon dioxide of KR-101: 1.5, the product code name is the water treatment silicone defoaming agent of FA10: 1 preparation film body solution, earlier water is put into the rustless steel container of band heater during preparation, with PVA put into water with 100 rev/mins speed after stirring 15 minutes under the temperature of indoor environment, solution is heated to after 90 ℃ of insulations dissolved it in 60 minutes fully, again with glycerine, the product code name is that the hydrophily superfine silicon dioxide of KR-101 and water treatment silicone defoaming agent that the product code name is FA10 add to stir in the solution and it is dissolved fully under the temperature of indoor environment and obtain film body solution;
(2) utilizing thickness is 110 microns Biaxially oriented polypropylene BOPP plastic sheeting, it is tiled on the platform, when the fabric width of Biaxially oriented polypropylene BOPP plastic sheeting is below 4 meters the time, the film body solution that step (1) is obtained with the pneumatic spraying device according on 237 milliliters of/square metre surfaces that evenly are sprayed on Biaxially oriented polypropylene BOPP plastic sheeting, behind the natural levelling under the temperature conditions of indoor environment dry 12 hours or be placed on and carry out drying in the hothouse; When the fabric width of Biaxially oriented polypropylene BOPP plastic sheeting is below 2 meters the time, the film body solution that step (1) is obtained, can obtain attached to the coating film printing film on the Biaxially oriented polypropylene BOPP plastic sheeting according on 142 milliliters of/square metre surfaces that are uniformly coated on Biaxially oriented polypropylene BOPP plastic sheeting and utilize heated-air drying with coating machine or coating machine or silk screen coating machine.
Use the typography of coating film printing film of the present invention, comprise the steps:
(1) client is provided or the computer of selected calligraphy and painting pattern input color air brushing PRN device, utilize the color painting PRN device on attached to the described coating film printing film on the Biaxially oriented polypropylene BOPP plastic sheeting, to print calligraphy and painting pattern, simultaneously the surface of printed material body is cleared up, after its surperficial spot and water droplet of place to go, spray one deck glass coatings to the printed material surface that metal material is made according to 5 milliliters/square metre again, then the printed material body is placed baking box to be heated to 170 ℃ of insulations 50 minutes, take out after 15 minutes with the baking box cooling, naturally cool to the temperature of indoor environment;
(2) the coating film printing film that is printed with calligraphy and painting pattern that step (1) is obtained is taken off from Biaxially oriented polypropylene BOPP plastic sheeting, face up and be tiled on the water surface by being printed on calligraphy and painting pattern, to note between coating film printing film and the water bubble being arranged during tiling, can not there be the globule film of coating simultaneously printing film upper surface, the serigraphy cleaning agent is sprayed on the coating film printing film equably according to 5 milliliters/square metre again;
(3) after coating film printing film becomes solid-liquid mixing in water by the time, according to the position that flies at calligraphy and painting pattern on the horizontal plane printed material body that step (1) obtains is pressed downward in the water, utilize the pressure of water to make coating film printing film coat the printed material surface fully;
(4) the printed material body that is printed with calligraphy and painting pattern that step (3) is obtained takes out from water, water cleans the printed material surface, then with after heated-air drying or the air dry, spray one deck glass coatings to the printed material surface according to 5 milliliters/square metre again, then the printed material body is placed baking box to be heated to 170 ℃ of insulations 60 minutes, take out after 15 minutes with the baking box cooling, naturally cool to the temperature of indoor environment.
Embodiment 4
Coating film printing film of the present invention, adopt following steps to make:
(1) according to weight parts water: 80, PVA:23, glycerine: 0.35, the product code name is the hydrophily superfine silicon dioxide of KR-101: 1.3, the product code name is the water treatment silicone defoaming agent of FA10: 0.65 preparation film body solution, earlier water is put into the rustless steel container of band heater during preparation, with PVA put into water with 75 rev/mins speed after stirring 15 minutes under the temperature of indoor environment, solution is heated to after 90 ℃ of insulations dissolved it in 40 minutes fully, again with glycerine, the product code name is that the hydrophily superfine silicon dioxide of KR-101 and water treatment silicone defoaming agent that the product code name is FA10 add to stir in the solution and it is dissolved fully under the temperature of indoor environment and obtain film body solution;
(2) utilizing thickness is 120 microns Biaxially oriented polypropylene BOPP plastic sheeting, it is tiled on the platform, when the fabric width of Biaxially oriented polypropylene BOPP plastic sheeting is below 4 meters the time, the film body solution that step (1) is obtained with the pneumatic spraying device according on 230 milliliters of/square metre surfaces that evenly are sprayed on Biaxially oriented polypropylene BOPP plastic sheeting, behind the natural levelling under the temperature conditions of indoor environment dry 12 hours or be placed on and carry out drying in the hothouse; When the fabric width of Biaxially oriented polypropylene BOPP plastic sheeting is below 2 meters the time, the film body solution that step (1) is obtained, can obtain attached to the coating film printing film on the Biaxially oriented polypropylene BOPP plastic sheeting according on 138 milliliters of/square metre surfaces that are uniformly coated on Biaxially oriented polypropylene BOPP plastic sheeting and utilize heated-air drying with coating machine or coating machine or silk screen coating machine.
Use the typography of coating film printing film of the present invention, comprise the steps:
(1) client is provided or the computer of selected calligraphy and painting pattern input color air brushing PRN device, utilize the color painting PRN device on attached to the described coating film printing film on the Biaxially oriented polypropylene BOPP plastic sheeting, to print calligraphy and painting pattern, simultaneously the surface of printed material body is cleared up, after its surperficial spot and water droplet of place to go, spray one deck glass coatings to the printed material surface that the stone material material is made according to 5 milliliters/square metre again, then the printed material body is placed baking box to be heated to 140 ℃ of insulations 60 minutes, take out after 15 minutes with the baking box cooling, naturally cool to the temperature of indoor environment;
(2) the coating film printing film that is printed with calligraphy and painting pattern that step (1) is obtained is taken off from Biaxially oriented polypropylene BOPP plastic sheeting, face up and be tiled on the water surface by being printed on calligraphy and painting pattern, to note between coating film printing film and the water bubble being arranged during tiling, can not there be the globule film of coating simultaneously printing film upper surface, the serigraphy cleaning agent is sprayed on the coating film printing film equably according to 5 milliliters/square metre again;
(3) after coating film printing film becomes solid-liquid mixing in water by the time, according to the position that flies at calligraphy and painting pattern on the horizontal plane printed material body that step (1) obtains is pressed downward in the water, utilize the pressure of water to make coating film printing film coat the printed material surface fully;
(4) the printed material body that is printed with calligraphy and painting pattern that step (3) is obtained takes out from water, water cleans the printed material surface, then with after heated-air drying or the air dry, spray one deck glass coatings to the printed material surface according to 5 milliliters/square metre again, then the printed material body is placed baking box to be heated to 140 ℃ of insulations 60 minutes, take out after 15 minutes with the baking box cooling, naturally cool to the temperature of indoor environment.
The said goods code name is that the hydrophily superfine silicon dioxide of KR-101 is the product code name of hydrophily superfine silicon dioxide, and manufacturer comprises U.S. DEGUSSA company, Tianjin Chemical Research ﹠ Desing Inst; The product code name is that the water treatment silicone defoaming agent of FA10 is the product code name of water treatment silicone defoaming agent, and manufacturer comprises Beijing state China new chemical materials company, CompanyAddress; Three seas, Jiu Gong township, Daxing District, Beijing; Biaxially oriented polypropylene BOPP plastic sheeting is the product code name of Biaxially oriented polypropylene plastic sheeting, and manufacturer comprises Jiangyin, economic and technological development zone, Jiangyin City Shen Da group; PVA is the product code name of polyvinyl alcohol resin, and manufacturer comprises Beijing Organic Chemical Plant, as long as according to the relevant producer of the said goods code name consulting, just can buy corresponding product.
Claims (7)
1. coating film printing film is characterized in that adopting following steps to make:
(1) according to weight parts water: 70-80, PVA:22-23.2, glycerine: 0.3-0.5, the product code name is the hydrophily superfine silicon dioxide of KR-101: 1-1.5, the product code name is the water treatment silicone defoaming agent of FA10: a 0.5-1 preparation film body solution, earlier water is put into the container of band heater during preparation, PVA put into water stirs and heating makes its dissolving, again with glycerine, the product code name is that the hydrophily superfine silicon dioxide of KR-101 and water treatment silicone defoaming agent that the product code name is FA10 add to stir in the solution and it is dissolved fully under the temperature of indoor environment and obtain film body solution;
(2) utilize Biaxially oriented polypropylene BOPP plastic sheeting, it is tiled on the platform, the film body solution that step (1) is obtained evenly is sprayed on the surface of Biaxially oriented polypropylene BOPP plastic sheeting, and give drying, can obtain attached to the coating film printing film on the Biaxially oriented polypropylene BOPP plastic sheeting.
2. coating film printing film according to claim 1, it is characterized in that in the described step (1) according to weight parts water: 75, PVA:22.6, glycerine: 0.4, the product code name is the hydrophily superfine silicon dioxide of KR-101: 1.25, and the product code name is the water treatment silicone defoaming agent of FA10: 0.75 preparation film body solution.
3. coating film printing film according to claim 2, it is characterized in that described step (1) with PVA put into water with 70-100 rev/min speed after stirring 15 minutes under the temperature of indoor environment, solution is heated to after 90 ℃ of insulations dissolved it in 30-60 minute fully, is that the hydrophily superfine silicon dioxide of KR-101 and water treatment silicone defoaming agent that the product code name is FA10 add under the temperature of indoor environment and stir in the solution and make its dissolving again with glycerine, product code name.
4. coating film printing film according to claim 3, the thickness that it is characterized in that Biaxially oriented polypropylene BOPP plastic sheeting in the described step (2) is the 100-120 micron, when the fabric width of Biaxially oriented polypropylene BOPP plastic sheeting is below 4 meters the time, the film body solution that step (1) is obtained with the pneumatic spraying device according to 228-247 milliliter/square metre evenly be sprayed on the surface of Biaxially oriented polypropylene BOPP plastic sheeting, behind the natural levelling under the temperature conditions of indoor environment dry 12 hours or be placed on and carry out drying in the hothouse; When the fabric width of Biaxially oriented polypropylene BOPP plastic sheeting is below 2 meters the time, the film body solution that step (1) is obtained with coating machine or coating machine or silk screen coating machine according on the surface of 133-152 milliliter/square metre be uniformly coated on Biaxially oriented polypropylene BOPP plastic sheeting and utilize heated-air drying.
5. use the typography of any one described coating film printing film in the claim 1 to 4, it is characterized in that comprising the steps:
(1) utilize the color painting PRN device on attached to the described coating film printing film on the Biaxially oriented polypropylene BOPP plastic sheeting, to print calligraphy and painting pattern, simultaneously the surface of printed material body is cleared up, after its surperficial spot and water droplet of place to go, again to printed material surface spraying one deck glass coating, then the printed material body is placed baking box to be heated to 140 ℃-170 ℃ insulations 30-50 minute, take out after 15 minutes with the baking box cooling, naturally cool to the temperature of indoor environment;
(2) the coating film printing film that is printed with calligraphy and painting pattern that step (1) is obtained is taken off from Biaxially oriented polypropylene BOPP plastic sheeting, face up and be tiled on the water surface by being printed on calligraphy and painting pattern, more surperficial spray treatment agent is sprayed on the coating film printing film equably;
(3) after coating film printing film becomes solid-liquid mixing in water by the time, the printed material body that step (1) obtains is pressed downward in the water, utilize the pressure of water to make coating film printing film coat the printed material surface according to the position that flies at calligraphy and painting pattern on the horizontal plane;
(4) the printed material body that is printed with calligraphy and painting pattern that step (3) is obtained takes out from water, water cleans the printed material surface, then with after heated-air drying or the air dry, again to printed material surface spraying one deck glass coating, then the printed material body is placed baking box to be heated to 140 ℃-170 ℃ insulations 30-50 minute, take out after 15 minutes with the baking box cooling, naturally cool to the temperature of indoor environment.
6. the typography of coating film printing film according to claim 5, it is characterized in that spraying glass coatings to the printed material surface according to 5 milliliters/square metre in described step (1) and the step (4), the printed material body places baking box to be heated to 160 ℃ of insulations 40 minutes.
7. the typography of coating film printing film according to claim 6 is characterized in that surperficial spray treatment agent is the serigraphy cleaning agent in the described step (2), and described printed material body adopts glass, pottery, metal or stone material material to make.