CN100333925C - Transfer process for stone product coating film - Google Patents
Transfer process for stone product coating film Download PDFInfo
- Publication number
- CN100333925C CN100333925C CNB2004100804339A CN200410080433A CN100333925C CN 100333925 C CN100333925 C CN 100333925C CN B2004100804339 A CNB2004100804339 A CN B2004100804339A CN 200410080433 A CN200410080433 A CN 200410080433A CN 100333925 C CN100333925 C CN 100333925C
- Authority
- CN
- China
- Prior art keywords
- product
- coating film
- methyl
- stone
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to technology for transferring a coating film for stone products, which comprises the following steps: a layer of transparent waterproof paint is sprayed on the surface of a stone product; the surface of the obtained product is ground, and burrs and convex flaws on the surface are removed; a coating film is flatly laid on the water surface, and the pattern-printed surface with characters and pictures of the coating film faces upwards; activating reducing agents are uniformly sprayed on the coating film, and the obtained product is downwards pressed into water based on positions of patterns of characters and pictures floating on a horizontal surface; the obtained product is taken out of water after 20 seconds; the patterns on the coating film can be transferred and printed on the surface of the product. The obtained product is washed by water and is put into a drying furnace to be dried. Unsaturation transparent resin is poured on the surface of the product at twice. The surface of the obtained product is polished by using polishing wax. The present invention aims at providing the technology for transferring coating films for stone products, and the technology can avoid the release of radioactive elements of stone products, wherein the radioactive elements of stone products do harm to human health. Moreover, the technology can improve the additional value of stone products and can transfer and print patterns of characters and pictures on the surfaces of stone products with complicated and multivariant shapes.
Description
Technical field
The present invention puts it briefly and relates to a kind of typography, relates in particular to a kind of coating film transferring process that carries out transfer printing on the stone material article of surface imperfection.
Background technology
As everyone knows, stone materials such as marble, granite can discharge a spot of radioactive element for a long time, if this class stone product is used in indoor place, can strengthen the concentration of indoor radioactive element, and then jeopardize the health of living in people in this environment for a long time.Owing to this reason, adopt the sale of the stone product of stone materials making such as marble, granite, be subjected to bigger influence.
Summary of the invention
The object of the present invention is to provide and a kind ofly reduce or avoid stone product to discharge radioactive element, improve the added value of stone product, can be at the transfer process for stone product coating film of complex-shaped changeable stone product surface transfer calligraphy and painting pattern.
Transfer process for stone product coating film of the present invention comprises the steps:
(1) at the surface of stone product spraying layer of transparent nitrate paint;
(2) product surface that step (1) is obtained is polished, and removes the burr on surface and the fault of projection;
(3) on instant polyvinyl alcohol film, use the monomer polyurethane not have benzene ink printing calligraphy and painting pattern and make the coating film, the coating film is tiled in it on water surface faceup by being printed on calligraphy and painting pattern, by the time after the softening degraded of coating film, the activating and reducing agent is sprayed on the coating film equably, described activating and reducing agent is formed by weight percentage and is respectively again:
Carrene 7-17%,
Dimethylbenzene 25-55%,
Butyl acetate 5-27%,
Methyl acetate 5-20%,
Methyl iso-butyl ketone (MIBK) 2-10%,
The product code name be 783 butyl acetate kind solvent type drying retardant 2-10%,
The rare phenol methyl esters of methyl-prop 1-8%,
Ring ethyl ketone 2-11%,
Mylar 1-8%,
Again according to flying at the position of calligraphy and painting pattern on the horizontal plane, the product that step (2) is obtained presses downward to that 8-30 took out after second in the water, and the pattern on the coating film will be transferred on the surface of product under the pressure effect of water.
(4) the product water that step (3) is obtained washes, and removes the attachment of the membrane carrier of superficial degradation, puts it into then in the drying oven, dries under 60 ℃ of following conditions;
(5) product that step (4) is obtained is tested, and the defective of repair products picture on surface is poured into a mould unsaturated transparent resin at twice at product surface then, and air dry;
(6) the product utilization fine sandpaper polishing that step (5) is obtained is carried out surface finish with buffing wax again.
The activating and reducing agent is respectively by weight percentage in the transfer process for stone product coating film of the present invention, wherein said step (3):
Carrene 9-15%,
Dimethylbenzene 35-45%,
Butyl acetate 10-20%,
Methyl acetate 10-15%,
Methyl iso-butyl ketone (MIBK) 3-8%,
The product code name be 783 butyl acetate kind solvent type drying retardant 3-8%,
The rare phenol methyl esters of methyl-prop 3-6%,
Ring ethyl ketone 3-7%,
Mylar 3-6% forms,
The activating and reducing agent is according to 0.08-0.12kg/m
2Be sprayed on the coating film; The Kiln seasoned temperature of oven dry is to dry 15-25 minute under 40 ℃ of-50 ℃ of conditions in the described step (4).
The activating and reducing agent is respectively by weight percentage in the transfer process for stone product coating film of the present invention, wherein said step (3):
Carrene 12%,
Dimethylbenzene 40%,
Butyl acetate 15%,
Methyl acetate 12%,
Methyl iso-butyl ketone (MIBK) 5%,
The product code name be 783 butyl acetate kind solvent type drying retardant 5%,
The rare phenol methyl esters 3% of methyl-prop,
Ring ethyl ketone 5%,
Mylar 3% is formed.
The activating and reducing agent is according to 0.1kg/m
2Be sprayed on the coating film; The Kiln seasoned temperature of oven dry is 45 ℃ in the described step (4), and drying time is 20 minutes.
Transfer process for stone product coating film of the present invention, the thickness of unsaturated transparent resin is 150-300 μ m in the wherein said step (5).
The advantage and the good effect of transfer process for stone product coating film of the present invention are: it adopts unique technology, at the surface of stone product spraying layer of transparent nitrate paint, on instant polyvinyl alcohol film, use the monomer polyurethane not have benzene ink printing calligraphy and painting pattern and make the coating film, key is to pour into a mould unsaturated transparent resin at twice at product surface, and the distinctive activating and reducing agent prescription of use the present invention, make that the coating membranous layer stability after the hydrolysis is good, the rupture of membranes rate is low, so transfer process for stone product coating film of the present invention has and can reduce or avoid stone product to discharge radioactive element, improve the added value of stone product, can be in the characteristics of complex-shaped changeable stone product surface transfer calligraphy and painting pattern, and make product designer be given full play to imagination ground deisgn product planform and style, and then the image appearance and the market sale that can improve product.
The specific embodiment
Below in conjunction with specific embodiment transfer process for stone product coating film of the present invention is described further.
Embodiment 1
Transfer process for stone product coating film of the present invention comprises the steps:
(1) at the surface of stone product spraying layer of transparent nitrate paint;
(2) product surface that step (1) is obtained is polished, and removes the burr on surface and the fault of projection;
(3) on instant polyvinyl alcohol film, use the monomer polyurethane not have benzene ink printing calligraphy and painting pattern and make the coating film, the coating film is tiled in it on water surface faceup by being printed on calligraphy and painting pattern, by the time after the softening degraded of coating film, the activating and reducing agent is sprayed on the coating film equably, described activating and reducing agent is formed by weight percentage and is respectively again:
Carrene 12%,
Dimethylbenzene 40%,
Butyl acetate 15%,
Methyl acetate 12%,
Methyl iso-butyl ketone (MIBK) 5%,
The product code name be 783 butyl acetate kind solvent type drying retardant 5%,
The rare phenol methyl esters 3% of methyl-prop,
Ring ethyl ketone 5%,
Mylar 3% is formed.
The activating and reducing agent is according to 0.1kg/m
2Be sprayed on the coating film;
According to the position that flies at calligraphy and painting pattern on the horizontal plane, the product that step (2) is obtained presses downward to taking-up after 10 seconds in the water again, and the pattern on the coating film will be transferred on the surface of product under the pressure effect of water.
(4) the product water that step (3) is obtained washes, and removes the attachment of the membrane carrier of superficial degradation, puts it into then in the drying oven, and oven dry is 20 minutes under 45 ℃ of conditions;
(5) product that step (4) is obtained is tested, and the defective of repair products picture on surface is poured into a mould unsaturated transparent resin at twice at product surface then, and air dry; The thickness of unsaturated transparent resin is 225 μ m.
(6) the product utilization fine sandpaper polishing that step (5) is obtained utilizes 800-1000 purpose buffing wax to carry out surface finish.
By above-mentioned processing step, can obtain coating film transferring process goods.
Embodiment 2
(1) at the surface of stone product spraying layer of transparent nitrate paint;
(2) product surface that step (1) is obtained is polished, and removes the burr on surface and the fault of projection;
(3) on instant polyvinyl alcohol film, use the monomer polyurethane not have benzene ink printing calligraphy and painting pattern and make the coating film, the coating film is tiled in it on water surface faceup by being printed on calligraphy and painting pattern, by the time after the softening degraded of coating film, the activating and reducing agent is sprayed on the coating film equably, described activating and reducing agent is formed by weight percentage and is respectively again:
Carrene 8%,
Dimethylbenzene 55%,
Butyl acetate 5%,
Methyl acetate 8%,
Methyl iso-butyl ketone (MIBK) 10%,
The product code name be 783 butyl acetate kind solvent type drying retardant 2%,
The rare phenol methyl esters 8% of methyl-prop,
Ring ethyl ketone 2%,
Mylar 2% is formed.
The activating and reducing agent is according to 0.12kg/m
2Be sprayed on the coating film;
According to the position that flies at calligraphy and painting pattern on the horizontal plane, the product that step (2) is obtained presses downward to taking-up after 8 seconds in the water again, and the pattern on the coating film will be transferred on the surface of product under the pressure effect of water.
(4) the product water that step (3) is obtained washes, and removes the attachment of the membrane carrier of superficial degradation, puts it into then in the drying oven, and oven dry is 25 minutes under 40 ℃ of conditions;
(5) product that step (4) is obtained is tested, and the defective of repair products picture on surface is poured into a mould unsaturated transparent resin at twice at product surface then, and air dry; The thickness of unsaturated transparent resin is 150 μ m.
(6) the product utilization fine sandpaper polishing that step (5) is obtained utilizes 800-l000 purpose buffing wax to carry out surface finish.
Embodiment 3
Transfer process for stone product coating film of the present invention comprises the steps:
(1) at the surface of stone product spraying layer of transparent nitrate paint;
(2) product surface that step (1) is obtained is polished, and removes the burr on surface and the fault of projection;
(3) on instant polyvinyl alcohol film, use the monomer polyurethane not have benzene ink printing calligraphy and painting pattern and make the coating film, the coating film is tiled in it on water surface faceup by being printed on calligraphy and painting pattern, by the time after the softening degraded of coating film, the activating and reducing agent is sprayed on the coating film equably, described activating and reducing agent is formed by weight percentage and is respectively again:
Carrene 17%,
Dimethylbenzene 25%,
Butyl acetate 25%,
Methyl acetate 11%,
Methyl iso-butyl ketone (MIBK) 3%,
The product code name be 783 butyl acetate kind solvent type drying retardant 8%,
The rare phenol methyl esters 3% of methyl-prop,
Ring ethyl ketone 5%,
Mylar 3% is formed.
The activating and reducing agent is according to 0.08kg/m
2Be sprayed on the coating film;
According to the position that flies at calligraphy and painting pattern on the horizontal plane, the product that step (2) is obtained presses downward to taking-up after 30 seconds in the water again, and the pattern on the coating film will be transferred on the surface of product under the pressure effect of water.
(4) the product water that step (3) is obtained washes, and removes the attachment of the membrane carrier of superficial degradation, puts it into then in the drying oven, and oven dry is 15-25 minute under 40 ℃ of-50 ℃ of conditions;
(5) product that step (4) is obtained is tested, and the defective of repair products picture on surface is poured into a mould unsaturated transparent resin at twice at product surface then, and air dry; The thickness of unsaturated transparent resin is 300 μ m.
(6) the product utilization fine sandpaper polishing that step (5) is obtained utilizes 800-1000 purpose buffing wax to carry out surface finish.
Embodiment 4
Transfer process for stone product coating film of the present invention comprises the steps:
(1) at the surface of stone product spraying layer of transparent nitrate paint;
(2) product surface that step (1) is obtained is polished, and removes the burr on surface and the fault of projection;
(3) on instant polyvinyl alcohol film, use the monomer polyurethane not have benzene ink printing calligraphy and painting pattern and make the coating film, the coating film is tiled in it on water surface faceup by being printed on calligraphy and painting pattern, by the time after the softening degraded of coating film, the activating and reducing agent is sprayed on the coating film equably, described activating and reducing agent is formed by weight percentage and is respectively again:
Carrene 15%,
Dimethylbenzene 35%,
Butyl acetate 15%,
Methyl acetate 10%,
Methyl iso-butyl ketone (MIBK) 5%,
The product code name be 783 butyl acetate kind solvent type drying retardant 5%,
The rare phenol methyl esters 5% of methyl-prop,
Ring ethyl ketone 5%,
Mylar 5% is formed.
The activating and reducing agent is according to 0.09kg/m
2Be sprayed on the coating film;
According to the position that flies at calligraphy and painting pattern on the horizontal plane, the product that step (2) is obtained presses downward to taking-up after 15 seconds in the water again, and the pattern on the coating film will be transferred on the surface of product under the pressure effect of water.
(4) the product water that step (3) is obtained washes, and removes the attachment of the membrane carrier of superficial degradation, puts it into then in the drying oven, and oven dry is 24 minutes under 42 ℃ of conditions;
(5) product that step (4) is obtained is tested, and the defective of repair products picture on surface is poured into a mould unsaturated transparent resin at twice at product surface then, and air dry; The thickness of unsaturated transparent resin is 180 μ m.
(6) the product utilization fine sandpaper polishing that step (5) is obtained utilizes 800-1000 purpose buffing wax to carry out surface finish.
Embodiment 5
Transfer process for stone product coating film of the present invention comprises the steps:
(1) at the surface of stone product spraying layer of transparent nitrate paint;
(2) product surface that step (1) is obtained is polished, and removes the burr on surface and the fault of projection;
(3) on instant polyvinyl alcohol film, use the monomer polyurethane not have benzene ink printing calligraphy and painting pattern and make the coating film, the coating film is tiled in it on water surface faceup by being printed on calligraphy and painting pattern, by the time after the softening degraded of coating film, the activating and reducing agent is sprayed on the coating film equably, described activating and reducing agent is formed by weight percentage and is respectively again:
Carrene 9%,
Dimethylbenzene 43%,
Butyl acetate 20%,
Methyl acetate 7%,
Methyl iso-butyl ketone (MIBK) 8%,
The product code name be 783 butyl acetate kind solvent type drying retardant 2%,
The rare phenol methyl esters 3% of methyl-prop,
Ring ethyl ketone 4%,
Mylar 4% is formed.
The activating and reducing agent is according to 0.1kg/m
2Be sprayed on the coating film;
Again according to flying at the position of calligraphy and painting pattern on the horizontal plane, the product that step (2) is obtained presses downward to that 10-30 took out after second in the water, and the pattern on the coating film will be transferred on the surface of product under the pressure effect of water.
(4) the product water that step (3) is obtained washes, and removes the attachment of the membrane carrier of superficial degradation, puts it into then in the drying oven, and oven dry is 18 minutes under 57 ℃ of conditions;
(5) product that step (4) is obtained is tested, and the defective of repair products picture on surface is poured into a mould unsaturated transparent resin at twice at product surface then, and air dry; The thickness of unsaturated transparent resin is 250 μ m.
(6) the product utilization fine sandpaper polishing that step (5) is obtained utilizes 800-1000 purpose buffing wax to carry out surface finish.
Embodiment 6
Transfer process for stone product coating film of the present invention comprises the steps:
(1) at the surface of stone product spraying layer of transparent nitrate paint;
(2) product surface that step (1) is obtained is polished, and removes the burr on surface and the fault of projection;
(3) on instant polyvinyl alcohol film, use the monomer polyurethane not have benzene ink printing calligraphy and painting pattern and make the coating film, the coating film is tiled in it on water surface faceup by being printed on calligraphy and painting pattern, by the time after the softening degraded of coating film, the activating and reducing agent is sprayed on the coating film equably, described activating and reducing agent is formed by weight percentage and is respectively again:
Carrene 10%,
Dimethylbenzene 35%,
Butyl acetate 20%,
Methyl acetate 14%,
Methyl iso-butyl ketone (MIBK) 3%,
The product code name be 783 butyl acetate kind solvent type drying retardant 5%,
The rare phenol methyl esters 3% of methyl-prop,
Ring ethyl ketone 7%,
Mylar 3% is formed.
The activating and reducing agent is according to 0.11kg/m
2Be sprayed on the coating film;
Again according to flying at the position of calligraphy and painting pattern on the horizontal plane, the product that step (2) is obtained presses downward to that 10-30 took out after second in the water, and the pattern on the coating film will be transferred on the surface of product under the pressure effect of water.
(4) the product water that step (3) is obtained washes, and removes the attachment of the membrane carrier of superficial degradation, puts it into then in the drying oven, and oven dry is 15 minutes under 60 ℃ of conditions;
(5) product that step (4) is obtained is tested, and the defective of repair products picture on surface is poured into a mould unsaturated transparent resin at twice at product surface then, and air dry; The thickness of unsaturated transparent resin is 280 μ m.
(6) the product utilization fine sandpaper polishing that step (5) is obtained utilizes 800-1000 purpose buffing wax to carry out surface finish.
Embodiment 7
Transfer process for stone product coating film of the present invention comprises the steps:
(1) at the surface of stone product spraying layer of transparent nitrate paint;
(2) product surface that step (1) is obtained is polished, and removes the burr on surface and the fault of projection;
(3) on instant polyvinyl alcohol film, use the monomer polyurethane not have benzene ink printing calligraphy and painting pattern and make the coating film, the coating film is tiled in it on water surface faceup by being printed on calligraphy and painting pattern, by the time after the softening degraded of coating film, the activating and reducing agent is sprayed on the coating film equably, described activating and reducing agent is formed by weight percentage and is respectively again:
Carrene 15%,
Dimethylbenzene 35%,
Butyl acetate 10%,
Methyl acetate 21%,
Methyl iso-butyl ketone (MIBK) 5%,
The product code name be 783 butyl acetate kind solvent type drying retardant 4%,
The rare phenol methyl esters 3% of methyl-prop,
Ring ethyl ketone 4%,
Mylar 3% is formed.
The activating and reducing agent is according to 0.1kg/m
2Be sprayed on the coating film;
According to the position that flies at calligraphy and painting pattern on the horizontal plane, the product that step (2) is obtained presses downward to taking-up after 28 seconds in the water again, and the pattern on the coating film will be transferred on the surface of product under the pressure effect of water.
(4) the product water that step (3) is obtained washes, and removes the attachment of the membrane carrier of superficial degradation, puts it into then in the drying oven, and oven dry is 24 minutes under 41 ℃ of conditions;
(5) product that step (4) is obtained is tested, and the defective of repair products picture on surface is poured into a mould unsaturated transparent resin at twice at product surface then, and air dry; The thickness of unsaturated transparent resin is 160 μ m.
(6) the product utilization fine sandpaper polishing that step (5) is obtained utilizes 800-1000 purpose buffing wax to carry out surface finish.
Embodiment 8
Transfer process for stone product coating film of the present invention comprises the steps:
(1) at the surface of stone product spraying layer of transparent nitrate paint;
(2) product surface that step (1) is obtained is polished, and removes the burr on surface and the fault of projection;
(3) on instant polyvinyl alcohol film, use the monomer polyurethane not have benzene ink printing calligraphy and painting pattern and make the coating film, the coating film is tiled in it on water surface faceup by being printed on calligraphy and painting pattern, by the time after the softening degraded of coating film, the activating and reducing agent is sprayed on the coating film equably, described activating and reducing agent is formed by weight percentage and is respectively again:
Carrene 10%,
Dimethylbenzene 50%,
Butyl acetate 10%,
Methyl acetate 9%,
Methyl iso-butyl ketone (MIBK) 3%,
The product code name be 783 butyl acetate kind solvent type drying retardant 2%,
The rare phenol methyl esters 3% of methyl-prop,
Ring ethyl ketone 5%,
Mylar 8% is formed.
The activating and reducing agent is according to 0.12kg/m
2Be sprayed on the coating film;
According to the position that flies at calligraphy and painting pattern on the horizontal plane, the product that step (2) is obtained presses downward to taking-up after 12 seconds in the water again, and the pattern on the coating film will be transferred on the surface of product under the pressure effect of water.
(4) the product water that step (3) is obtained washes, and removes the attachment of the membrane carrier of superficial degradation, puts it into then in the drying oven, and oven dry is 15-25 minute under 40 ℃ of-60 ℃ of conditions;
(5) product that step (4) is obtained is tested, and the defective of repair products picture on surface is poured into a mould unsaturated transparent resin at twice at product surface then, and air dry; The thickness of unsaturated transparent resin is 270 μ m.
(6) the product utilization fine sandpaper polishing that step (5) is obtained utilizes 800-1000 purpose buffing wax to carry out surface finish.
Embodiment 9
Transfer process for stone product coating film of the present invention comprises the steps:
(1) at the surface of stone product spraying layer of transparent nitrate paint:
(2) product surface that step (1) is obtained is polished, and removes the burr on surface and the fault of projection;
(3) on instant polyvinyl alcohol film, use the monomer polyurethane not have benzene ink printing calligraphy and painting pattern and make the coating film, the coating film is tiled in it on water surface faceup by being printed on calligraphy and painting pattern, by the time after the softening degraded of coating film, the activating and reducing agent is sprayed on the coating film equably, described activating and reducing agent is formed by weight percentage and is respectively again:
Carrene 10%,
Dimethylbenzene 38%,
Butyl acetate 12%,
Methyl acetate 15%,
Methyl iso-butyl ketone (MIBK) 5%,
The product code name be 783 butyl acetate kind solvent type drying retardant 5%,
The rare phenol methyl esters 5% of methyl-prop,
Ring ethyl ketone 5%,
Mylar 5% is formed.
The activating and reducing agent is according to 0.1kg/m
2Be sprayed on the coating film;
Again according to flying at the position of calligraphy and painting pattern on the horizontal plane, the product that step (2) is obtained presses downward to that 10-30 took out after second in the water, and the pattern on the coating film will be transferred on the surface of product under the pressure effect of water.
(4) the product water that step (3) is obtained washes, and removes the attachment of the membrane carrier of superficial degradation, puts it into then in the drying oven, and oven dry is 15-25 minute under 40 ℃ of-50 ℃ of conditions;
(5) product that step (4) is obtained is tested, and the defective of repair products picture on surface is poured into a mould unsaturated transparent resin at twice at product surface then, and air dry; The thickness of unsaturated transparent resin is 150-300 μ m.
(6) the product utilization fine sandpaper polishing that step (5) is obtained utilizes 800-1000 purpose buffing wax to carry out surface finish.
By above-mentioned processing step, can obtain coating film transferring process goods.
783 type drying retardants are that formal name used at school is the product code name that butyl acetate kind solvent type drying retardant manufacturer uses on market, as long as according to the relevant producer of the said goods code name consulting, just can buy corresponding product.Manufacturer comprises Liaoning Rentian Science ﹠ Technology Co., Ltd., the address of Liaoning Rentian Science ﹠ Technology Co., Ltd.: No. 8, Tieling, Liaoning Province new and high-tech development zone new estrade town 102 national highways.
Claims (4)
1. transfer process for stone product coating film is characterized in that comprising the steps:
(1) at the surface of stone product spraying layer of transparent nitrate paint;
(2) product surface that step (1) is obtained is polished, and removes the burr on surface and the fault of projection;
(3) on instant polyvinyl alcohol film, use the monomer polyurethane not have benzene ink printing calligraphy and painting pattern and make the coating film, the coating film is tiled in it on water surface faceup by being printed on calligraphy and painting pattern, by the time after the softening degraded of coating film, the activating and reducing agent is sprayed on the coating film equably, described activating and reducing agent is formed by weight percentage and is respectively again:
Carrene 7-17%,
Dimethylbenzene 25-55%,
Butyl acetate 5-27%,
Methyl acetate 5-20%,
Methyl iso-butyl ketone (MIBK) 2-10%,
The product code name be 783 butyl acetate kind solvent type drying retardant 2-10%,
The rare phenol methyl esters of methyl-prop 1-8%,
Ring ethyl ketone 2-11%,
Mylar 1-8%,
Again according to flying at the position of calligraphy and painting pattern on the horizontal plane, the product that step (2) is obtained presses downward to that 8-30 took out after second in the water, and the pattern on the coating film will be transferred on the surface of product under the pressure effect of water.
(4) the product water that step (3) is obtained washes, and removes the attachment of the membrane carrier of superficial degradation, puts it into then in the drying oven, dries under 60 ℃ of following conditions;
(5) product that step (4) is obtained is tested, and the defective of repair products picture on surface is poured into a mould unsaturated transparent resin at twice at product surface then, and air dry;
(6) the product utilization fine sandpaper polishing that step (5) is obtained is carried out surface finish with buffing wax again.
2. transfer process for stone product coating film according to claim 1 is characterized in that the activating and reducing agent is respectively by weight percentage in the described step (3):
Carrene 9-15%,
Dimethylbenzene 35-45%,
Butyl acetate 10-20%,
Methyl acetate 10-15%,
Methyl iso-butyl ketone (MIBK) 3-8%,
The product code name be 783 butyl acetate kind solvent type drying retardant 3-8%,
The rare phenol methyl esters of methyl-prop 3-6%,
Ring ethyl ketone 3-7%,
Mylar 3-6% forms,
The activating and reducing agent is according to 0.08-0.12kg/m
2Be sprayed on the coating film; The Kiln seasoned temperature of oven dry is to dry 15-25 minute under 40 ℃ of-50 ℃ of conditions in the described step (4).
3. transfer process for stone product coating film according to claim 2 is characterized in that the activating and reducing agent is respectively by weight percentage in the described step (3):
Carrene 12%,
Dimethylbenzene 40%,
Butyl acetate 15%,
Methyl acetate 12%,
Methyl iso-butyl ketone (MIBK) 5%,
The product code name be 783 butyl acetate kind solvent type drying retardant 5%,
The rare phenol methyl esters 3% of methyl-prop,
Ring ethyl ketone 5%,
Mylar 3% is formed.
The activating and reducing agent is according to 0.1kg/m
2Be sprayed on the coating film; The Kiln seasoned temperature of oven dry is 45 ℃ in the described step (4), and drying time is 20 minutes.
4. transfer process for stone product coating film according to claim 3, the thickness that it is characterized in that unsaturated transparent resin in the described step (5) are 150-300 μ m.