CN101852006B - Method for producing ceramic ground line brick - Google Patents
Method for producing ceramic ground line brick Download PDFInfo
- Publication number
- CN101852006B CN101852006B CN2010101685629A CN201010168562A CN101852006B CN 101852006 B CN101852006 B CN 101852006B CN 2010101685629 A CN2010101685629 A CN 2010101685629A CN 201010168562 A CN201010168562 A CN 201010168562A CN 101852006 B CN101852006 B CN 101852006B
- Authority
- CN
- China
- Prior art keywords
- ceramic
- ground line
- brick
- treatment
- production method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a method for producing a ceramic ground line brick, and aims to provide the method for producing the ceramic ground line brick. The method is implemented through the following technical scheme with steps of: firstly, performing coarse grinding treatment on the surface of a ceramic bottom brick to flatten the surface thereof; secondly, coating a layer of anti-drop paint on the ceramic bottom brick; thirdly, after the anti-drop paint is dry, printing patterns on the ceramic bottom brick by using glitter powder through a decorating machine to perform decoration treatment; and finally, performing surface production process on the decorated ceramic ground line. The method is mainly used for the production of ceramic ground line brick manufacturers.
Description
Technical field
The present invention relates to a kind of production method of ground line brick, relate in particular to a kind of production method of ceramic ground line brick.
Background technology
Society is along with social material and cultural life is perfect day by day now, the finishing in house required increasingly high, and ornament materials is progressively refinement also.On ground foot install additional ground line brick over the ground foot's metope protect, make cleaning the time can prevent that sealing infilters metope, and play and beautify the indoor environment effect.Ground line brick uses more and more widely at interior decoration, and ground line brick generally is divided into ceramic ground line brick and glass ground line brick, and the advantage of glass ground line brick is a rich patterns and with low cost, but its weatherability, resistance to acids and bases are undesirable.And the floor tile waste materials that use carry out producing in reprocessing more in the ceramic ground line brick industry, because of ceramic surface is difficult for colouring, can not carry out the decoration of multiple pattern, thereby color pattern is not abundant.Now on the market, have directly to be coated with the ceramic ground line brick that glaze is fired, its price is higher relatively; Also there is direct subsides facing paper to carry out the ceramic ground line brick of surface protection technology again, not enough but facing paper and ceramic bottom brick attach power, be easy to after being heated, making moist damage.
Summary of the invention
The invention discloses a kind of production method of ceramic ground line brick, have ground line brick weatherability, resistance to acids and bases and the single shortcoming of pattern now to solve, and applicability is wide, production prices are cheap, and to resource recycling, reached the purpose of protection environment.
For realizing above-mentioned purpose, technical solution of the present invention is: a kind of production method of ceramic ground line brick, and its production process is following:
1) coarse grinding treatment is carried out on the ceramic bottom brick surface, make its surfacing;
2) on ceramic bottom brick, apply layer of anti-drop paint;
3) treat that anti-drop paint parches the back and uses the glitter powder impressing pattern to carry out decorative Treatment with printing machine;
4) ceramic ground line brick that carries out after the decorative Treatment is carried out the surface protection PROCESS FOR TREATMENT.
Described step 1 uses emery wheel that coarse grinding treatment is carried out on the ceramic bottom brick surface.
Before the described step 2 ceramic bottom brick after the corase grind is carried out clean, make the ceramic bottom brick cleaning surfaces, strengthen the absorption affinity of anti-drop paint.
The used anti-drop paint of described step 2 is the water-based encarpus tile lacquer of a kind of water resistance, strong adhesion and good weatherability.
Described step 3 is spread oarse-grained glitter powder earlier on anti-drop paint, re-uses printing machine silk-screen granule glitter powder pattern and carries out decorative Treatment, forms the glitter powder decorative layer after decorative Treatment is accomplished.
The surface protection PROCESS FOR TREATMENT that described step 4 is carried out is the UV surfacing, forms sealer.
The invention has the beneficial effects as follows: used water resistance, tack is strong and the water-based encarpus tile lacquer of good weatherability as anti-drop paint; Improved the adhesive power of glitter powder decorative layer and ceramic bottom brick; The surface protection that the UV surfacing has increased ceramic ground line brick has been carried out on the surface, and the weatherability, resistance to acids and bases and the pattern decorative that have improved ceramic ground line brick are abundant.And encaustic tile lacquer can use on arbitrary material as anti-drop paint, thereby has improved its applicable scope, and the encaustic tile lacquer is water-based; Do not exhale pernicious gases; And use the floor tile waste material as ceramic bottom brick when producing, reached and recycle and nonhazardous, protected environment.
Description of drawings
Accompanying drawing is to utilize the present invention to produce the structural representation of product;
Among the figure: 1-ceramic bottom brick, 2-anti-drop paint, 3-glitter powder decorative layer, 4-sealer.
The specific embodiment
Explain further details below in conjunction with the specific embodiment of accompanying drawing to the utility model.
Referring to accompanying drawing, production process of the present invention is following:
1) coarse grinding treatment is carried out on ceramic bottom brick 1 surface, make its surfacing;
2) on ceramic bottom brick 1, apply layer of anti-drop paint 2;
3) treat that anti-drop paint 2 parches the back and uses the glitter powder impressing pattern to carry out decorative Treatment with printing machine;
4) ceramic ground line brick that carries out after the decorative Treatment is carried out the surface protection PROCESS FOR TREATMENT.
Described step 1 uses emery wheel that coarse grinding treatment is carried out on ceramic bottom brick 1 surface.
Before the described step 2 ceramic bottom brick 1 after the corase grind is carried out clean, make ceramic bottom brick 1 cleaning surfaces, strengthen the absorption affinity of anti-drop paint 2.
The used anti-drop paint 2 of described step 2 is water-based encarpus tile lacquers of a kind of water resistance, strong adhesion and good weatherability.
Described step 3 is spread oarse-grained glitter powder earlier on anti-drop paint, re-uses printing machine silk-screen granule glitter powder pattern and carries out decorative Treatment, forms glitter powder decorative layer 3 after decorative Treatment is accomplished.
The surface protection PROCESS FOR TREATMENT that described step 4 is carried out is the UV surfacing, forms sealer 4.
Get a floor tile waste material, use cutting machine to cut into suitable stick, process ceramic bottom brick 1, with emery wheel ceramic bottom brick 1 surface rubbing.Wash the dust and the greasy dirt on ceramic bottom brick 1 surface then with clear water, and its oven dry.Treat the water-based encarpus tile lacquer of ceramic bottom brick 1 dried back, form anti-drop paint layer 2 after the encaustic tile lacquer is done in ceramic bottom brick 1 surface-coated one deck water resistance, strong adhesion and good weatherability.Treat to sprinkle oarse-grained glitter powder above that after it parches; And use granule glitter powder screen printing pattern at ceramic brick surface with printing machine; To form glitter powder decorative layer 3; Treat on glitter powder decorative layer 3, to apply one deck UV coating after pattern is printed completion, and make it solidify to form sealer 4 to play the effect of protection through the UV machine.
Claims (6)
1. the production method of a ceramic ground line brick, its production process is following:
1) coarse grinding treatment is carried out on ceramic bottom brick (1) surface, make its surfacing;
2) go up coating layer of anti-drop paint (2) in ceramic bottom brick (1);
3) treat that anti-drop paint (2) parches the back and uses the glitter powder impressing pattern to carry out decorative Treatment with printing machine;
4) ceramic ground line brick that carries out after the decorative Treatment is carried out the surface protection PROCESS FOR TREATMENT.
2. the production method of ceramic ground line brick according to claim 1 is characterized in that: described step 1 uses emery wheel that coarse grinding treatment is carried out on ceramic bottom brick (1) surface.
3. the production method of ceramic ground line brick according to claim 1 is characterized in that: before the described step 2 ceramic bottom brick (1) after the corase grind is carried out clean, make ceramic bottom brick (1) cleaning surfaces, strengthen the absorption affinity of anti-drop paint (2).
4. the production method of ceramic ground line brick according to claim 1 is characterized in that: the used anti-drop paint (2) of described step 2 is the water-based encarpus tile lacquer of a kind of water resistance, strong adhesion and good weatherability.
5. the production method of ceramic ground line brick according to claim 1; It is characterized in that: described step 3 is spread oarse-grained glitter powder earlier on anti-drop paint; Re-use printing machine silk-screen granule glitter powder pattern and carry out decorative Treatment, form glitter powder decorative layer (3) after decorative Treatment is accomplished.
6. the production method of ceramic ground line brick according to claim 1, it is characterized in that: the surface protection PROCESS FOR TREATMENT that described step 4 is carried out is the UV surfacing, forms sealer (4).