CN1237556A - Colour tile and its preparation method - Google Patents
Colour tile and its preparation method Download PDFInfo
- Publication number
- CN1237556A CN1237556A CN 99100658 CN99100658A CN1237556A CN 1237556 A CN1237556 A CN 1237556A CN 99100658 CN99100658 CN 99100658 CN 99100658 A CN99100658 A CN 99100658A CN 1237556 A CN1237556 A CN 1237556A
- Authority
- CN
- China
- Prior art keywords
- sand
- cement
- stone
- water
- colored brick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The colour tile is made up by using cement, sand, stone, trisodium phosphate, magnesium sulfate, ammonium alum, blue copperas, propanetriol, Y colour fixing agent, colour paste, hydrocinnamyl emulsion and water through the processes of preparing materials, mixing, stirring, colouring, moulding, vibrating, drying and demoulding, and features low cost, strong compressive strength, beautiful pattern, good colour, bright surface, slip-resistance, wear-resistance and frost resistance, etc..
Description
The present invention relates to a kind of colored brick and preparation method thereof.
At present, China's indoor and outdoor New Building Materials, annual demand develops rapidly, the laying on each city, the whole nation and rural ground is more and more exquisite now, more and more towards luxurious, style, be particular about, practical direction develops, lay and cement brick is generally adopted on existing ground or overstock layer band look brick, a this cement brick and an overstocked layer band look brick do not have luminosity, not cold-resistant, not resistance to compression, easily aging, more there be not attractive in appearance saying, it is not in tune with the demand of current urban construction that leaps and human beautifying city, people urgently wish to utilize high-tech, the employing type material is synthetic, and the product pattern grace is bright in luster, surface-brightening such as mirror have wear-resisting, compressive resistance is strong, cold-resistant, the colored brick of characteristics such as anti-skidding comes out.
The object of the present invention is to provide a kind of pattern grace, bright in luster, surface-brightening such as mirror, have wear-resisting, compressive resistance strong, the colored brick of characteristics such as cold-resistant, anti-skidding and preparation method thereof.
The object of the present invention is achieved like this: it is made up of cement, sand, stone, tertiary sodium phosphate, sal epsom, amine alum, blue vitriol, glycerol, Y laking agent, mill base, benzene emulsion, water, form through batching, mixing, stirring, additive color, injection molding, vibration, drying, the demoulding, it is characterized in that it is a kind of colored brick of being made by following weight (Kg) proportion raw material:
Cement 11-13 sand 19-25
Stone 31-35 tertiary sodium phosphate 0.01
Sal epsom 0.025 amine alum 0.06
Blue vitriol 0.02 glycerol 0.005
Y laking agent 0.005 mill base 0.05
Benzene emulsion 0.004 water 6-7.
Its feature is that also it is a kind of colored brick of preferred following weight (Kg) proportion raw material preparation:
Cement 12 sand 20
Stone 32 tertiary sodium phosphates 0.01
Sal epsom 0.025 amine alum 0.06
Blue vitriol 0.02 glycerol 0.005
Y laking agent 0.005 mill base 0.05
Benzene emulsion 0.004 water 6.5.
Its feature is that also described cement is high-alumina cement or aluminate cement.
Its feature is that also described sand is quartz sand or common medium sand.
The preparation method of a kind of colored brick of the present invention is characterized in that
1. (Kg) above-mentioned raw materials that is purchased and weighs,
2. stone and sand are cleaned up, standby,
3. industrial chemicals such as tertiary sodium phosphate, sal epsom, amine alum, blue vitriol are placed in the container, add water 2.5Kg, heat to 60-100 ℃,
4. in above-mentioned industrial chemicals, throw in glycerol, Y laking agent, mill base, benzene emulsion restir again, standby,
5. water, stone and cement are dropped in the stirred pot, stirred 3 minutes, drop into standby sand and industrial chemicals again, restir 5 minutes,
6. will stir and expect jar, injection molding, vibration is fully discharged bubble,
7. seasoning, the demoulding,
8. put in order, stack, the water wet preservation promptly gets a kind of colored brick of product of the present invention.
The present invention compared with prior art, it is with low cost, compressive resistance is strong, the pattern grace is bright in luster soft, surface-brightening such as mirror, have anti-skidding, anti-ly shine, freeze proof, resistance to compression, wear-resisting, characteristics such as the life-span is long.
Embodiment
1. (Kg) the following raw material that is purchased and weighs,
Cement 12 sand 20
Stone 32 tertiary sodium phosphates 0.01
Sal epsom 0.025 amine alum 0.06
Blue vitriol 0.02 glycerol 0.005
Y laking agent 0.005 mill base 0.05
Benzene emulsion 0.004 water 6.5
2. stone and the quartz sand with above-mentioned weight cleans up, and is standby,
3. industrial chemicals such as tertiary sodium phosphate, sal epsom, amine alum, blue vitriol are placed in the container, add water 2.5Kg, heat to 80 ℃,
4. in above-mentioned industrial chemicals, throw in glycerol, Y laking agent, mill base, benzene emulsion restir again, standby,
5. water, stone and cement are dropped in the stirred pot, stirred 3 minutes, drop into standby quartz sand and industrial chemicals again, restir 5 minutes,
6. will stir and expect jar, injection molding, vibration is fully discharged bubble,
7. seasoning, the demoulding,
8. put in order, stack, the water wet preservation promptly gets the indoor a kind of colored brick of product of the present invention.
The proportioning raw material and preparation method thereof that utilizes a kind of colored brick of the present invention is except that the high-quality floor tile that can produce the various pattern deliciousness of indoor and outdoor, also can produce indoor and outdoor wall brick required in the urban construction, outfall sewer drive cap, door and window etc., abundant, bright-coloured lasting, gloss of its product pattern such as mirror, anti-shine freeze proof, compressive resistance is strong, cheap, the usage period is long.
Claims (5)
1, a kind of colored brick, it is made up of cement, sand, stone, tertiary sodium phosphate, sal epsom, amine alum, blue vitriol, glycerol, Y laking agent, mill base, benzene emulsion, water, form through batching, mixing, stirring, additive color, injection molding, vibration, drying, the demoulding, it is characterized in that it is a kind of colored brick of being made by following weight (Kg) proportion raw material:
Cement 11-13 sand 19-25
Stone 31-35 tertiary sodium phosphate 0.01
Sal epsom 0.025 amine alum 0.06
Blue vitriol 0.02 glycerol 0.005
Y laking agent 0.005 mill base 0.05
Benzene emulsion 0.004 water 6-7.
2, a kind of colored brick according to claim 1, its feature are that also it is a kind of colored brick of preferred following weight (Kg) proportion raw material preparation:
Cement 12 sand 20
Stone 32 tertiary sodium phosphates 0.01
Sal epsom 0.025 amine alum 0.06
Blue vitriol 0.02 glycerol 0.005
Y laking agent 0.005 mill base 0.05
Benzene emulsion 0.004 water 6.5.
3, according to a kind of colored brick of claim 1 or 2, its feature is that also described cement is high-alumina cement or aluminate cement.
4, according to a kind of colored brick of claim 1 or 2, its feature is that also described sand is quartz sand or common medium sand.
5, a kind of preparation method of colored brick is characterized in that:
1. (Kg) above-mentioned raw materials that is purchased and weighs,
2. stone and sand are cleaned up, standby,
3. industrial chemicals such as tertiary sodium phosphate, sal epsom, amine alum, blue vitriol are placed in the container, add water 2.5Kg, heat to 80 ℃,
4. in above-mentioned industrial chemicals, throw in glycerol, Y laking agent, mill base, benzene emulsion restir again, standby,
5. water, stone and cement are dropped in the stirred pot, stirred 3 minutes, drop into standby sand and industrial chemicals again, restir 5 minutes,
6. will stir and expect jar, injection molding, vibration is fully discharged bubble,
7. seasoning, the demoulding,
8. put in order, stack, the water wet preservation promptly gets the indoor a kind of colored brick of product of the present invention.